• Textile Coloration and Finishing
• /
• v.9 no.4
• /
• pp.47-53
• /
• 1997

To improve the interfacial bonding of carbon fiber-nylon 6 composite, carbon fiber(CF) were oxidized by nitric acid treatment, and two types of graft polymer(GP) of nylon 6-g-polyacrylamide (PAAm) -water dispersable GP(WDGP) and m-cresol solu ble GP(CSGP) were treated as coupling agents. Introduction of polar groups such as -COOH, -OH, etc, on the surface of the oxidized CF was confirmed by IR spectra. The stem polymer of nylon 6 in the coupling agent (GP) could be compatible with'matrix nylon 5, and the grafted branch of PAAm on GP could react to the polar groups on the oxidized CF in composite. The interfacial strength was measured by the transverse tensile test to the fiber direction for single CF embedded nylon 6 film especially prepared and by the pull-out test method. The interfacial strength of the composite reinforced with oxidized CF is greater than that reinforced with unoxidized CF. The interfacial strength of the composite was increased by treatment of coupling agents(GPs) considerably, and the increasing tendency by the WDGP is greater than that by the CSGP. The optimum conditions of coupling agent treatment are as follows: the concentration, adsorption tlme of GP, and curing temperature are 2%, 20 minutes, and $170^{\circ}$, respectively.

• Journal of Adhesion and Interface
• /
• v.8 no.1
• /
• pp.15-27
• /
• 2007

Polyimide (PI) surface modification was carried out by ion-beam treatment and silane-imidazole coupling agent to improve the adhesion between polyimide film and copper. Silane-imidazole coupling agent contains imidazole functional groups for the formation of a complex with copper metal through a coordination bonding and methoxy silane groups for the formation of siloxane polymers. The PI film surface was first treated by argon (Ar)/oxygen ($O_2$) ion-beam, followed by dipping it into a modified silane-imidazole coupling agent solution. The results of X-ray photoelectron spectroscopy (XPS) spectra revealed that the $Ar/O_2$ plasma treatment formed oxygen functional groups such as hydroxyl and carbonyl groups on the polyimide film surface and confirmed that the PI surface was modified by a coupling reaction with imidazole-silane coupling agent. Adhesion between copper and the treated PI film by ion-beam and coupling agent was superior to that with untreated PI film. In addition, adhesion of PI film treated by an $Ar/O_2$ plasma to copper was better than that of PI film treated by a coupling agent. The peeled-off layers from the copper-PI film joint were completely different in chemical composition each other. The layer of PI film side showed similar C1s, N1s, O1s spectra to the original Upilex-S and no Si and Cu atoms appeared. On the other hand the layer of copper side showed different C1s and N1s spectra from the original PI film and many Si and Cu atoms appeared. This indicates that the failure occurs at an interface between the imidazole-silane and PI film layers rather than within the PI layers.

• Proceedings of the KIEE Conference
• /
• 1991.11a
• /
• pp.282-285
• /
• 1991

Optimum conditions of fabrication and the effects of silane coupling agent on Glass-cloth/unsaturated Polyester composite materials were investigated. Dielectric strength and mechanical tensile strength were significantly improved in the sample with epoxy silane treatment, compared with the case without epoxy silane treatment. Treatment rate of interface coupling agent in composite materials were increased with increases of glass-fiber layers and content of glass fiber.

• Carbon letters
• /
• v.19
• /
• pp.47-56
• /
• 2016

In this study, the fracture behavior of a thermoplastic-modified epoxy resin reinforced with continuous carbon fibers for two levels of fiber-matrix adhesion was performed. A carbon fiber with commercial sizing was used and also treated with a known silane, (3-glycidoxy propyl trimethoxysilane) coupling agent. Toughness was determined using the double cantilever test, together with surface analysis after failure using scanning electron microscope. The presence of polysulfone particles improved the fracture behavior of the composite, but fiber-matrix adhesion seemed to play a very important role in the performance of the composite material. There appeared to be a synergy between the matrix modifier and the fiber-matrix adhesion coupling agent.

• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.353-355
• /
• 1989

Composite insulating materials have the defect of interface. To minimize the defect of interface of GFRP (glass cloth reinforced plastics), coupling agent is treated. In this paper, the method of coupling agent treatment has been studied. The result shows that the optimum electric and mechanical properties is obtained for the sample treated on the glass fiber with 0.3% amino silane water solution.

• Proceedings of the KIEE Conference
• /
• 1989.11a
• /
• pp.68-71
• /
• 1989

This paper is to investigate the optimal condition of fabrication for glass-cloth/epoxy composite material. According to the result in this paper, in fabrication of composite materials, the optimal condition of treatment for epoxy silane coupling agent is 1.5% water solution of silane coupling agent by weight. Then, % weight ratio of silane coupling agent VS, glass cloth is about 0.3%. And the optimal post cured condition of glass cloth/epoxy composite material is about 30 hours at 100$^{\circ}C$.

• Elastomers and Composites
• /
• v.50 no.3
• /
• pp.159-166
• /
• 2015

Silica which is used for reinforcing filler in tire industry is widely known as eco-friendly material exerting $CO_2$ reduction effect through decrease of rolling resistance and improvement of wet grip. Generally silica is classified as a highly polar filler because it contains a large number of silanol (Si-OH) group on its surface. And also silica gives a lower reinforcing effect than carbon black due to its poorer rubber-filler interaction. Therefore silica is treated with silane coupling agent or activator, then following the conventional rubber blend method, vulcanized sheets were prepared using a hot press, and cure characteristics, mechanical properties and abrasion resistance of the test specimens were investigated. It was found that with an increase in the silane coupling agent content the tensile strength, 300% modulus and abrasion resistance increased while Mooney viscosity decreased and crosslink density slightly increased with an increase of activator.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.3
• /
• pp.149-152
• /
• 2012

The effects of amino silane coupling agent on the AC electrical treeing and breakdown behaviors in an epoxy/layered silicate (1 wt%) were examined in needle-plate electrode geometry. A layered silicate was exfoliated in an epoxy base resin by using our AC electric field apparatus. To measure the tree initiation and propagation and the breakdown rate, an alternating current (AC) of 10 kV (60 Hz) was applied to the specimen in needle-plate electrode arrangement with a $30^{\circ}C$ insulating oil bath. In the epoxy/amino silane system, the tree initiation time was 11.5 times higher and the breakdown time was 17.9 times higher than those of the neat epoxy resin. The tree initiation time in the epoxy/layered silicate (1 wt%) system with the amino silane was 2.0 times higher, and the breakdown time was 1.5 times higher than those of the epoxy/layered silicate (1 wt%) system.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.62 no.2
• /
• pp.213-218
• /
• 2013

In this study, epoxy/mica composite was prepared by mixing with mechanical stirrer together with homogenizer, and the effect of amino-type silane coupling agent was also studied. To reduce the viscosity without any decrement of other properties, 1,4-Butanediol diglycidyl ether (1,4-BDGE) as an aliphatic epoxy reactive diluent was introduced to the epoxy/mica composite in order to use as vanish for high voltage motor and generator stator winding. It was confirmed by scanning electron microscopy (SEM) observation that interfacial characteristics between organic epoxy and inorganic mica was modified by coupling agent treatment so that glass transition temperature increased, and tensile strength and electrical breakdown strength increased. The properties were estimated by Weibull statistical analysis and the ac electrical breakdown strength was 20.2% modified by treating silane coupling agent.

• Elastomers and Composites
• /
• v.55 no.4
• /
• pp.339-346
• /
• 2020

We functionalized a wear-resistant carbon-based MoS2 filler to solve its limited wear condition problem. The filler exhibits excellent lubricative properties. The surface modification of MoS2 was carried out using a (3-glycidyloxypropyl)trimethoxysilane (GPTMS) silane coupling agent to improve the low compatibility and dispersibility of the filler that generally degrade the performance of composites. A silane coupling agent was employed for the functionalization of MoS2, and its effect on the wear resistance of MoS2/Polyamide-6,6 was investigated. The silanization of MoS2 was identified by contact angle analysis and Fourier-transform infrared, energy dispersive X-ray, and X-ray photoelectron spectroscopies. The wear resistance of the composite was found to be improved significantly by the surface functionalization of MoS2.