• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.36-37
• /
• 2019

In domestic construction industry progress, construction and quality control of large structures are considered to be important as the superstructure and mass scale of structures. In the case of mass concrete, high hydration heat caused by cement hydration generates temperature stress by generating internal temperature difference with the concrete surface. These temperature stresses cause cracks to penetrate the concrete structure. A method of lowering the heat generation by incorporating Urea in order to reduce the concrete temperature crack has been proposed. In this study, the heat function coefficient for the FEM temperature crack analysis of the mass concrete containing the element was derived and the adiabatic temperature rise test was carried out according to the incorporation of the element. As a result of this experiment, the maximum temperature of 41 ± 1℃ was obtained irrespective of the amount of urea, and the maximum temperature decreased by 16.9℃ in concrete containing 40kg/㎥ of urea.

• Journal of Environmental Science International
• /
• v.19 no.1
• /
• pp.105-114
• /
• 2010

The objective of the paper is to experimentally investigate the compressive strength of the concrete incorporating fly ash. Ordinary Portland cement(OPC). Water to binder ratio(W/B) ranging from 30% to 60% and curing temperature ranging from $-10^{\circ}{\sim}65^{\circ}C$ were also adopted for experimental parameters. Fly ash was replaced by 30% of cement contents. According to the results, strength development of concrete contained with fly ash is lower than that of plain concrete in low temperature at early age and maturity. In high curing temperature, the concrete with fly ash has higher strength development than that of low temperature regardless of the elapse of age and maturity. Fly ash can have much effect on the strength development of concrete at the condition of mass concrete, hot weather concreting and the concrete products for the steam curing.

• International Journal of Highway Engineering
• /
• v.7 no.3 s.25
• /
• pp.79-91
• /
• 2005

The temperature patterns in Portland cement concrete (PCC) pavements were measured and comprehensively analyzed from the beginning of the concrete placement based on the temperature measurement technique developed using innovative and inexpensive temperature measurement sensors. The temperature measurements in PCC pavements were taken at several different locations forvarious slab thicknesses. The concrete temperature patterns in the vertical and longitudinal directions of the pavement were analyzed and the effects of the pavement surface reflectivity, shading, and covering on the concrete temperatures were evaluated. The results of this study showed that the significant differences in the maximum concrete temperatures on the placement day were observed according to the concrete placement time. Since the zero-stress temperature is a function of the maximum concrete temperature on the placement day, the placement time would be an important factor that affects the behavior and performance of concrete pavements. The surface conditions of the pavement, such as the surface color, shading, and covering also affected the temperature patterns in PCC pavements significantly.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.128-131
• /
• 2004

This paper is to investigate the mock up test results of mass concrete for transfer girder using setting time difference with super retarding agent(SRA) to reduce hydration heat. According to test results, the temperature history of plain concrete without placing lift had a steep rising curvature, and plain concrete had a big temperature difference between surface and middle section of mass concrete, which may result in occurrence of temperature crack. However, considering placing method B, because setting time of middle section concrete was retarded with an increase in SRA contents, higher hydration heat temperature was observed at surface section concrete compared with that at middle section concrete at early age, which can lower the possibility of hydration heat crack. In case of placing method C, although peak temperature of hydration heat was much lower, at early age, high crack occurrence possibility of the hydration heat attributable to the big temperature difference between middle section and bottom section of concrete was expected at bottom section concrete. Therefore, the structure above the ground like transfer girder is not applicable to consider the placing method C.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.11a
• /
• pp.26-27
• /
• 2014

Study on high temperature properties of concrete and internal force estimation of structural member subjected to high temperature mainly applied high temperature strength model based on experimental results with concrete under 40MPa. However, it is reported that degradation of internal force at high temperature and spalling of ultra high strength concrete are higher than that of normal strength concrete. Therefore, this study attempts to propose compressive strength degradation model which is suitable to ultra high strength concrete comparing to existing model by evaluating high temperature properties of ultra high strength concrete.

• Advances in concrete construction
• /
• v.6 no.6
• /
• pp.645-658
• /
• 2018

Despite being one of the most abundantly used construction materials because of its exceptional properties, concrete is susceptible to deterioration and damage due to various factors particularly corrosion, improper loading, poor workmanship and design discrepancies, and as a result concrete structures require retrofitting and strengthening. In recent times, Fiber Reinforced Polymer (FRP) composites have substituted the conventional techniques of retrofitting and strengthening of damaged concrete. Most of the research studies related to concrete strengthening using FRP have been performed on undamaged test specimens. This contribution presents the results of an experimental study in which concrete specimens were damaged by mechanical loading and elevated temperature in laboratory prior to application of Carbon Fiber Reinforced Polymer (CFRP) sheets for strengthening. The test specimens prepared using concrete of target compressive strength of 28 MPa at 28 days were subjected to compressive and splitting tensile testing up to failure and the intact pieces of the failed specimens were collected for the purpose of repair. In order to induce damage as a result of elevated temperature, the concrete cylinders were subjected to $400^{\circ}C$ and $800^{\circ}C$ temperature for two hours duration. Concrete cylinders damaged under compressive and split tensile loads were re-cast using concrete and rich cement-sand mortar, respectively and then strengthened using CFRP wrap. Concrete cylinders damaged due to elevated temperature were also strengthened using CFRP wrap. Re-cast and strengthened concrete cylinders were tested in compression and splitting tension. The obtained results revealed that re-casting of specimens damaged by mechanical loadings using concrete & mortar, and then strengthened by single layer CFRP wrap exhibited strength even higher than their original values. In case of specimens damaged by elevated temperature, the results indicated that concrete strength is significantly dropped and strengthening using CFRP wrap made it possible to not only recover the lost strength but also resulted in concrete strength greater than the original value.

• Magazine of the Korea Concrete Institute
• /
• v.7 no.1
• /
• pp.97-108
• /
• 1995

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.22 no.5
• /
• pp.596-606
• /
• 1998

Thermophysical properties and the compressive strength of concrete used in nuclear power plants in Korea were measured. The chemical composition of the concrete was also analyzed. The measured thermophysical properties include the density, the thermal conductivity, the thermal diffusivity and the specific heat for a wide temperature range of 20.deg. C to 1100.deg. C. The chemical composition of Korean concrete is similar to that of US basaltic concrete and the thermophysical properties are strongly temperature dependent. The density, the conductivity and the diffusivity decrease with an increase in temperature, and particularly the conductivity and the diffusivity are a 50-perdent decrease at 900.deg. C as compared with these values at room temperature. The specific heat increases until 500.deg. C, decreases from 700.deg. C to 900 .deg. C, and then increases again when temperature is above 900.deg. C. The measurement beyond 1100.deg. C is not acceptably accurate because the concrete decomposes to a liquid phase from a solid phase at that temperature. The results of this study can be applied, for example, to an analysis of the molten core-concrete interaction (MCCI) phenomenon of concrete structures at high temperature will also require those property data, especially for high temperature ranges.

• Journal of the Korea Computer Industry Society
• /
• v.9 no.3
• /
• pp.99-104
• /
• 2008

The thermal stresses due to hydration heat in massive concrete structures are affected by ambient temperature and placing concrete temperature. It is needed to predict the thermal stresses considering ambient temperature and placing concrete temperature. In this study, hydration heat analyses of coping were carried out. After the maximum tensile stress was occurred at 2,75 days the crack index was increased. Therefore the possibility of crack occurrence was rare. The possibility of crack occurrence can be reduced by placing concrete temperature drop. Therefore some method to drop the placing concrete temperature may be effective to reduce the possibility of crack occurrence.

• International Journal of Highway Engineering
• /
• v.18 no.2
• /
• pp.19-27
• /
• 2016

PURPOSES: The behavior of a concrete pavement in a tunnel was investigated, based on temperature data obtained from the field and FEM analysis. METHODS: The concrete pavement in a tunnel was evaluated via two methods. First, temperature data was collected in air and inside the concrete pavement both outside and inside the tunnel. Second, FEM analysis was used to evaluate the stress condition associated with the slab thickness, joint spacing, dowel, and rock foundation, based on temperature data from the field. RESULTS : Temperature monitoring revealed that the temperature change in the tunnel was lower and more stable than that outside the tunnel. Furthermore, the temperature difference between the top and bottom of the slab was lower inside the tunnel than outside. FEM analysis showed that, in many cases, the stress in the concrete pavement in the tunnel was lower than that outside the tunnel. CONCLUSIONS : Temperature monitoring and the behavior of the concrete pavement in the tunnel revealed that, from an environmental point of view, the condition in the tunnel is advantageous to that outside the tunnel. The behavior in the tunnel was significantly less extreme, and therefore the concrete pavement in the tunnel could be designed more economically, than that outside the tunnel.