• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2007년도 춘계학술논문 발표대회
• /
• pp.9-12
• /
• 2007

Recently, research and development related to high strength concrete for the high rise and large scale reinforced concrete building has been actively promoted in worldwide by national and private research project. But, it is reported that violent explosive explosion would be happened when it was exposed in fire. In the existed study, a explosion in a reinforced concrete structure looses the organism by the different contraction and expansion of hardened cement paste and aggregate, and causes crack by thermal stress. In case of the Europe, Japan and America, they have studied the explosion for a long time. However it would hardly study the explosion in domestic, So it is needed base on mechanical properties of fire deterioration in high strength concrete. Therefore, this study is intend as an mechanical properties of specimen to high heating by heating and load test machine and $700^{\circ}C$. As a result, it is willing to propose fundamental data for quick and accurate diagnosis of deteriorated concrete structure by fire damage with experiment according to the design high strength concrete.

• 한국지구물리탐사학회:학술대회논문집
• /
• 한국지구물리탐사학회 2003년도 Proceedings of the international symposium on the fusion technology
• /
• pp.464-469
• /
• 2003

The traditional and still most widely used, test methods for concrete structures are destructive method, such as coring, drilling or otherwise removing part of the structure to permit visual inspection of the interior. While these methods are highly reliable, they are also time consuming and expensive, and the defects they leave behind often become focal point for deterioration. In this study, tomography by theoretical inversion method in case of elastic wave using impact-echo method among concrete non-destruction test method was made. Taken model experiments are theoretical inversion method and time domain and frequency domain test on pier test model at laboratory level. Also experiment concerning frequency domain on 3 kinds of tunnel model with I-dimension form was carried out.

• 자원환경지질
• /
• 제40권5호
• /
• pp.661-673
• /
• 2007

안성 청룡사삼층석탑의 구성암석은 대부분 편마상 복운모 화강암과 세립질 화강암으로 이루어져 있다. 이 석탑은 거의 전면에 걸쳐 나타나는 부재의 균열과 결실이 탑의 구조안정성을 위협한다. 또한 표면의 무기오염물과 다양한 서식형태를 갖는 생물침해는 석재표면의 손상을 가중시키고 있다. 따라서 이 연구에서는 석탑에 대한 종합적인 비파괴훼손도 진단을 수행하고 이를 근거로 풍화를 저감시키기 위해 최소한의 보존처리를 수행하였다. 보존처리에서는 석탑의 전면에 걸쳐 자생하는 지의류 및 생물오염물을 건식 및 습식 세정하였으며, 과거 이 석탑의 보수에 사용되었던 노화된 콘크리트를 제거하고 합성수지를 이용하여 복원하였다. 부재사이에 삽입된 부식된 철편은 티타늄 강철 합금으로 교체하였으며, 모든 공정이 완료된 후에 석질 강화처리를 실시하였다. 또한 석탑의 지반과 주위환경을 보강하고 정비하였으며 관람객에 의한 손상을 제어하기 위한 보호시설을 설치하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제11권6호
• /
• pp.152-158
• /
• 2007

염해는 구조물 열화의 원인이 되는 주요인자 중의 하나이다. 고속도로 교량에 있어서 제설제는 동결작용으로 인한 표면 스켈링을 매우 증가시킨다. 열화된 콘크리트는 염해환경에서 내구성이 저하된다. 본 연구에서는 147개 교량의 진단보고서를 조사하고 21개 교량 바닥판의 코어샘플에 대하여 실험과 분석을 실시하였다. 시험결과는 콘크리트 바닥판의 피복두께는 공용수명 30년 이상을 사용하려면 8cm이상이 필요하다는 것을 보여준다.

• 보존과학회지
• /
• 제28권3호
• /
• pp.235-245
• /
• 2012

이 연구에서는 경북 영양 용화광산 선광장(등록문화재 제255호)을 대상으로 비파괴 훼손도 진단을 실시하였다. 훼손지도를 작성하여 구조물에 대한 훼손상태를 파악한 결과, 6열과 7열 구조물을 기점으로 하여 용화광산 선광장 상부(7~13열)에서는 생물, 토사에 의한 훼손율이 높은 반면 하부(1~6열)에서는 탈락, 균열, 표면변색의 훼손율이 매우 높게 나타났다. 이는 기계적인 공정과 화학적인 공정이 동시에 진행되는 하부 구조물에서 화학용액들이 구조물의 콘크리트와 반응하면서 물리화학적 풍화작용을 촉진시켰기 때문으로 판단된다. 선광장 구조물의 물성을 파악하기 위해 초음파속도를 측정한 결과, 평균 초음파속도는 2,462m/s(압축강도 $529kgf/cm^2$)로 측정되었다. P-XRF를 활용한 표면변색 오염물질의 분석에서는 용화광산에서 채굴하였던 광석들의 주요성분(Cu, Zn, Pb, Fe, As)과 동일한 것으로 나타났다. 선광장 주변 토양에는 Cu, Zn, Pb, As와 같은 중금속의 함량이 상당히 높았다. 이와 같은 성분들은 선광장 구조물뿐만 아니라 자연환경에도 영향을 줄 수 있기 때문에 구조물의 보존처리와 함께 토양의 정화도 병행해야 할 것이다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2004년도 학술.기술논문발표회
• /
• pp.41-44
• /
• 2004

Recently, in the case of domestic, for all that the deterioration environment about the carbonation of reinforced concrete structures is accelerated, systematic diagnosis and researches are not completed. And the selection techniques of repair material and method used under the situation that the indicator and the performance evaluation method are nor established are dependant on existing experience. Therefore, the purpose of this study is intend to present fundamental data for the reasonable selection of repair material and method. durability design and longevity on the deteriorated reinforced concrete structures, through computing the carbonation depth and velocity coefficient by accelerating carbonation test under various accelerating conditions and investigating the application of carbonation evaluation method. The results of this study are as follow; The resistances to carbonation are increased when the W/C ratio if lower and the treatment of surface coating is executed. And the carbonation depth and velocity coefficient according to accelerating carbonation test conditions are increased when the conditions of temperature, relative humidity and $CO_2$density are higher individually.

• 콘크리트학회논문집
• /
• 제15권6호
• /
• pp.794-801
• /
• 2003

건축물의 요구성능에 대한 관심이 점차 높아짐에 따라 건축물의 성능평가를 통하여 사용연한을 예측하고 건축물의 수명을 연장시키거나, 새롭게 재구성하려는 노력이 계속되고 있다. 그러나 아직 염화물에 의한 성능저하 평가에 있어 그 비용의 문제와 평가과정의 전문성 등의 많은 난점을 가지고 있다. 본 연구는 콘크리트 내부의 염화물침투 깊이를 측정하는 간이적 방법인 비색판별법을 이용하여 염화물에 의한 성능저하평가를 하고자 비색판별법의 적용가능성을 검토 후 변색위치의 침투염화물량을 정량분석하였다. 또한, 이를 이용하여 콘크리트 표면염화물량을 산정하고 철근위치 염화물량의 예측 및 한계염화물량에 도달시간 예측의 실용적 평가수단을 제시하였다. 염화물에 의한 철근콘크리트 구조물의 성능평가에 있어 간이평가 수단인 비색판별법의 활용에 따라 샘플수의 다량확보를 통한 신뢰수준의 향상을 이룰 수 있을 것으로 사료된다.

• 대한원격탐사학회:학술대회논문집
• /
• 대한원격탐사학회 2003년도 Proceedings of ACRS 2003 ISRS
• /
• pp.493-495
• /
• 2003

The establishment of the investigation and the maintenance technique is required for preservation of old structures in Japan. This study attempts to diagnose the deterioration status of the historic structures using the thermal infrared camera. In some structures, the difference of the spatio-temporal change was observed in the surface temperature. For example, the cold joint of concrete was examined using this method effectively. As a result of this study, we have found useful guidelines in developing methodology to conduct diagnosis of historic buildings by using thermal infrared camera.

• 한국구조물진단유지관리공학회 논문집
• /
• 제26권6호
• /
• pp.23-32
• /
• 2022

PSCB 거더교는 고속도로에서 공용중인 교량의 4%로 많은 비중을 차지하고 있지는 않지만, PSCB 거더교의 약 98%가 1·2종 교량이며 전체 교량 연장의 약 16%(192km)를 차지하는 만큼 유지관리가 매우 중요한 교량 형식 중 하나이다. PSCB 거더교의 손상유형을 분석하기 위해 고속도로 공용중 교량의 가설공법, 제설환경 노출등급 비율을 고려한 62개소(477경간) 정밀안전진단 보고서를 선정하여 상세 분석을 수행함과 동시에 실제 열화·손상이 발생한 교량의 현장조사를 수행하였으며, 그 결과 대부분의 열화·손상 원인은 교면포장으로 유입된 우수(염수)가 상부플랜지와 계면 사이에 체수되어 콘크리트가 열화되고, 이후 교면포장의 균열 및 파손, 철근의 부식·팽창으로 인한 콘크리트 박락 등으로 진전되어 나타난 것으로 조사되었다. 또한, 상부플랜지 하면에 발생한 교축방향 균열 원인은 수화열, 건조수축 등으로 인한 균열로 판단된다. 결론적으로 PSCB 거더교의 특성을 고려한 합리적인 유지관리를 위해서는 시공초기 발생되는 상부플랜지 하면 교축방향 균열 제어를 위한 설계측면의 개선 방안이 제시되어야 할 것이며, 공용중 발생되는 열화는 상부플랜지 열화 이전 교면포장의 유지관리를 통한 선제적 대응과 제설환경 노출등급에 따른 차별화된 유지관리 방안이 제시되어야 할 것으로 판단된다.

• 한국터널지하공간학회 논문집
• /
• 제21권1호
• /
• pp.1-29
• /
• 2019

NATM (무근)터널의 라이닝 균열을 분석한 논문과 연계하여 NATM (철근)터널의 결함을 정밀안전진단 사례를 정리하여 결함별 원인을 분석하고자 하였다. NATM (철근)터널에서 콘크리트라이닝은 그 역할에 따라 철근과 같은 보강재를 사용하게 된다. 지반이 불량하거나 안전성 확보를 위한 라이닝 두께의 증가는 굴착단면의 증가와 라이닝 타설 물량의 증가를 유발하나, 철근보강 단면을 설계하여 경제성과 안전성을 함께 도모하게 된다. 시설물안전법에 의한 국내 1종 터널 시설물 중에서 NATM으로 시공된 구간에 철근보강을 실시한 라이닝의 결함 특성을 정리하여 형태별 발생원인을 분석하고자 하였다. 단철근, 복철근과 무근라이닝에 발생되는 균열을 비교하여 철근으로 인한 균열제어 효과를 분석하였다. 다양한 위치에서의 철근노출 사례와 함께 기술하였고 터널에서 고려될 수 있는 라이닝 두께 부족의 원인으로 정밀시공 미흡, 박락, 공용중 라이닝 화재에 의한 폭열, 지진, 용탈의 사례를 기존 연구와 비교하여 분석하였다. 향후 본 연구를 통해 정밀안전진단(터널) 세부지침의 보완 및 개정방향 등을 제시하고자 한다.