• Journal of Magnetics
• /
• 제5권2호
• /
• pp.40-43
• /
• 2000

Acicular $\alpha-FeOOH\; and\; Ba(OH)_2\cdot8H_2O$ are starting materials in this study. This paper presents the characteristics of the contents of citric acid and heating condition for preparing acicular barium ferrite powder. They control particle shape, crystalline phase, magnetic properties of acicular barium ferrite powder So the effects of the contents of citric acid and heating condition are studied. The experimental condition for starting materials were 800~1000$\circ C$ in firing and 0~40 wt% citric acid, respectively, Ba-ferrite particles fired at the range of 800 $\circ C$to 900 $\circ C$ were maintained as acicular particle shape, but there were mixed particles of acicular and round shape after fired at 950 $\circ C$. Ba-ferrite powder of the single phase was obtained in firing at 900~1000$\circ C$ and with 20 wt.% citric acid. There were unreacted phase of $\alpha-Fe_2O_3 \;and \; BaFe_2O_4$ phases as a second phase in case of sintering at below 850 $\circ C$. Acicular barium ferrite powder of single phase was also produced in firing at 900 $\circ C$ with 20 wt.% citric acid. The saturation magnetization of single phase of acicular $BaFe_12O_19$powder was about 51 emu/g and coercivity was about 4200 Oe.

• 한국자기학회지
• /
• 제3권2호
• /
• pp.143-148
• /
• 1993

열 분해법으로 $Bi_{x}Dy_{3-x}Al_{1}Fe_{4}O_{12}$(x=1, 1.2, 1.5) 자기 가넷 박막을 유리기판 위에 제조하였다. Bi 치환량을 증가시켰을 때 $M_{s}$ 값은 5 emu/cc에서 12 emu/cc로 증가하였고, 제조된 모든 박막이 수직 자기 이방성을 나타내었다. Bi 양의 증가에 따라 파장 780 nm의 광원을 사용했을 때 패러디 회전각이 $0.11^{\circ}/\mu\textrm{m}$에서 $0.20^{\circ}/\mu\textrm{m}$로 증가 하였으며 가넷 결정화 온도는 $660^{\circ}C$에서 $630^{\circ}C$로 감소하였다. 또한 보자력은 1200 Oe에서 600 Oe로 감소하였으며 결정립의 크기가 증가하였다. 박막의 두께를 $2000\;{\AA}$에서 $4000\;{\AA}$으로 증가시킴에 따라 $H_{c}$가 1750 Oe에서 1200 Oe로 감소했으며 ${\theta}_F$는 반사광의 간섭 효과에 의해 증가하였다.

• 한국자기학회지
• /
• 제27권4호
• /
• pp.123-128
• /
• 2017

PtMn계 스핀밸브(Spin Valve, SV) 다층박막의 하부층 구조를 달리하여 제작된 시료를 열처리 후 측정한 자기저항(magnetoresistance, MR) 곡선과 자기이력 곡선(MH loop)으로부터 얻은 등방성의 자기적 특성을 조사하였다. PtMn층이 없는 스핀밸브 구조의 Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/Ta(4 nm) 다층박막으로 측정한 MR 곡선에서 얻은 교환결합력($H_{ex}$), 보자력($H_c$), 자기저항비(MR(%))는 각각 0 Oe, 약 25 Oe, 3.3 %이었다. Glass/Ta(10 nm)/CoFe(6 nm)/Cu(2.5 nm)/CoFe(3 nm)/PtMn(6 nm)/Ta(4 nm) 다층박막으로 측정한 MR 곡선에서 반강자성체인 PtMn 박막으로 나타낸 효과로 하여금 나비 날개 형태로 얻은 $H_{ex}$, $H_c$, MR(%)는 각각 2 Oe, 316 Oe, 4.4 %이었다. 반강자성체인 PtMn층이 중간층으로 삽입된 이중 GMR-SV 다층박막으로 측정한 MR 곡선과 MH loop에서 얻은 $H_c$는 각각 37.5 Oe과 386 Oe이었으며, MR(%)는 각각 3.5 %와 6.5 %로 2개의 히스테리시스에서 사각비가 뚜렷하게 대칭적으로 나눠져 자기적 특성을 나타내었다. PtMn계 CoFe 스핀밸브 박막의 매우 작은 $H_{ex}$ 값과 미미한 형상이방성을 갖는 효과로 하여금 비등방성을 갖는 자기적 특성을 잃게 되었다. 이러한 결과는 PtMn 박막의 하부층과 상부층에 있는 SV 다층박막에서 각 강자성체의 자화 스핀배열로 일어나는 효과를 나타내었다.

• 한국세라믹학회지
• /
• 제39권8호
• /
• pp.789-794
• /
• 2002

본 연구에서는 TMS[Tetramethylsilane:$Si(CH_3)_4$], $NH_3$와 $H2$를 이용하여 나노크기의 Si-C-N precursor 분말을 합성하기 위하여 CVC법을 이용하였으며 반응온도, TMS/$NH_3$ 비 그리고 TMS/$H_2$ 비를 변화시켰다. XRD와 FESEM 분석을 통해서 결정상과 입자의 크기 그리고 입자의 형태를 관찰하고자 하였으며, 그 결과 제조된 분말은 모든 실험 조건하에서 87∼130 nm 크기를 지닌 균일한 구형의 비정질 분말이 얻어졌다. 입자 크기는 반응온도의 감소에 따라 감소하였으며, 또한 TMS/$NH_3$, TMS/$H_2$ 비가 작아질수록 감소하였다. EA 분석 결과 제조된 분말은 Si, N, C, H로 이루어졌음을 알 수 있었으며 FT-IR를 통하여 Si-N, C-N, Si-C 결합을 가진 Si-C-N precursor 분말이 제조되었다.

• 한국자기학회지
• /
• 제18권5호
• /
• pp.185-189
• /
• 2008

수직자기이방성을 갖는 [Pd(0.6 nm)/$Co(0.2)]_5$/FeMn(10) 다층박막 구조를 이용하여 삽입층 물질과 각 물질의 두께 증가에 따른 보자력(coercivity, $H_c$)과 교환력(exchange bias, $H_{ex}$)의 변화를 관찰하였다. $[Pd(0.6 nm)/Co(0.2)]_4$/Pd(0.6)/NiFe(t)/FeMn(10) 구조에서 Co 대신에 NiFe를 삽입하였을 때 0.78 nm와 1.28 nm에서 360 Oe의 교환바이어스를 얻었다. [Pd(0.6 nm)/$Co(0.2)]_5$/FeMn(10) 다층박막 구조에서 Co/FeMn 사이 계면에 $Co_8Fe_2$와 $Co_9Fe_1$ 물질을 삽입하여 두께 증가에 따라 $Co_8Fe_2$의 경우 0.68 nm에서 30 Oe 증가한 380 Oe의 교환바이어스를 얻었다. $Co_9Fe_1$ 경우 두께 0.52 nm에서 약 200 Oe 증가한 580 Oe 가장 큰 교환바이어스를 얻었다.

• 한국자기학회지
• /
• 제25권4호
• /
• pp.117-122
• /
• 2015

고감도 바이오센서용 거대자기저항-스핀밸브(Giant magnetoresistance-spin valve; GMR-SV) 박막소자의 미세패턴 공정으로 인한 교환결합력과 보자력 약화 문제를 해결하고자 전자사이크로트론 공명(Electron Cyclotron Resonance) Ar-이온 밀링을 이용하여 GMR-SV 박막에 지름 $35{\mu}m$인 원형 모양의 홀(Hole)을 패턴닝 하였다. GMR-SV를 4-단자법으로 측정한 자기저항 곡선으로부터 홀 개수가 많아질수록 자기저항비와 자장감응도는 홀이 없을 때 측정된 초기값과 같은 값을 유지하였고, 교환결합세기와 보자력은 120 Oe에서 190 Oe, 10 Oe에서 41 Oe로 크게 향상되었다. 이러한 현상은 GMR-SV 박막내의 자화용이축과 같은 방향을 띄고 센싱 전류의 방향과 수직인 공간에 위치하는 용이 자구영역(Easy magnetic domain; EMD)의 역할에 기인하는 결과를 보여주었다. GMR-SV 바이오 소자 제작시 폭을 넓게 하고 소자내부에 홀의 개수를 증가시켜 발생하는 EMD 효과가 자기저항특성을 향상시킬 수 있었다.

• 한국세라믹학회지
• /
• 제31권12호
• /
• pp.1501-1506
• /
• 1994

The precipitate of FeCl2.4H2O and NaOH, Fe(OH)2 was rapidly made to oxidize by H2O2 to prepare $\delta$-FeOOH. The particle size, surface and morphology of $\delta$-FeOOH, and the shape and structure of thermally decomposed $\delta$-FeOOH were investigated by the use of high resolution STEM. $\delta$-FeOOH prepared under the condition of reaction temperature of Fe(OH)2 at 4$0^{\circ}C$, [OH-][Fe2+]=5 and aging time of 2 hr Fe(OH)2, had 630$\AA$ mean particle size, 4~5 aspect ratio, 20.8 emu/g saturation magnetization and 210 Oe coercivity. The edges of $\delta$-FeOOH were inclined to (001) about 41$^{\circ}$, 60$^{\circ}$ and coincident with (102), (101) respectively. When $\delta$-FeOOH was thermally decomposed at 25$0^{\circ}C$ for 2 hr in vacuo, which had micropores of 0.9 nm thickness and crystallites of 2.4 nm thickness. (001)hex, [10]hex. of $\delta$-FeOOH parallel with (001)hex, [100]hex. of $\alpha$-Fe2O3 respectively. This showed three dimensional topotaxial structure transition, which was investigated by SADP (Selected Area Diffraction Pattern) of STEM.

• Journal of Magnetics
• /
• 제3권1호
• /
• pp.31-35
• /
• 1998

Metal/cobalt ferrite composite thin films with the saturation magnetization (M_s$)of~580 emu/cm3 and the coercivity(Hc) of 1700 Oe were prepared by the reactive sputtering. With increasing substrate temperature, Ms of the thin films increased, while Hc of the thin films decrease. This sttributed to the precipitation of $Co_xFe_{1-x}(x {\appro}x0.62)$ metal phase in the thin films. The metal phase showed the BCC structure ($a_0$=2.89 $\AA$) and Im3m space group. Also, the cobalt ferrite phase was identified as$ CoFe_2O_4$ with a cubic structure ($a_0=8.39 $\AA$$) and a space group of Fd3m. For the higher cobalt content than the stoichiometric composition,$ Co_{37.8}Fe_{62.2}$, the thin films with high Ms and Hc could be obtained in the wide substrate temperature range (200-40$0^{\circ}C$).

• The Korean Journal of Ceramics
• /
• 제6권3호
• /
• pp.315-317
• /
• 2000

A magnetoplumbite type of Ba ferrite(BaM) layers were deposited on Pt(111) and Pt(200) layers, and their c-axis orientation and magnetic characteristics were compared each other. The as-deposited BaM layer on Pt(111) one at the substrate temperature $T_s$ above $500^{\circ}C$ revealed remarkable c-axis orientation. The saturation magnetization 4$\piM_s$ and the perpendicular coercivity $H_{c⊥}$ of the films as-deposited at $T_s$ of $600^{\circ}C$ were 4.0kG and 2.5kOe, respectively. On the other hand, BaM ferrite layer deposited on Pt(200) layer at $T_s$ as relatively low as $500^{\circ}C$ also revealed weak c-axis orientation as well as (107) one and the films as-deposited at $T_s$ of $600^{\circ}C$ exhibited 4$\piMs_{and}$ $H_{c⊥}$ of 2.8kG and 2.5kOe, respectively. It was suggested that although chemical activity of Pt surface was effective for the formation of BaM crystallites, the lattice matching was also important for obtaining BaM layer with good c-axis orientation and large perpendicular anisotropy.sotropy.

• 한국자기학회지
• /
• 제15권2호
• /
• pp.130-132
• /
• 2005

Tungsten carbon nitride (W-C-N) thin films were produced by reactive radio frequency (RF) magnetron sputter-ing of tungsten in $Ar-N_2$ gas mixture. The effects of the variation of nitrogen partial pressure on the composition, and structural properties of these films as well as the influence of post-deposition annealing have been studied. When $La_{0.67}Sr_{0.33}MnO_3$ was coated on the W-C-N/Si substrate, coercivity ($H_c$) and magnetization at room temperature shows 58.73 Oe, and 29.4 emu/cc, respectively. In order to improve the diffusion barrier characteristics, we have studied the impurity behaviors to control the ratios of nitrogen and carbon concentrations.