• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.435-444
• /
• 2001

WC-( $Ti_{1-x}$ A $l_{x}$) N coatings of constant changing Al concentration were deposited on S45C substrates by high-ionization sputtered PVD method. The Al concentration could be controlled by using evaporation source for Al and fixing the evaporation rate of the metals (i.e, WC- $Ti_{0.86}$A $l_{0.14}$N, WC- $Ti_{0.72}$A $l_{0.28}$N, and WC- $Ti_{0.58}$A $l_{0.42}$N). The corrosion behavior of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings in a deaerated 3.5% NaCl solution was investigated by electrochemical corrosion tests and surface analyses. The measured galvanic corrosion currents between coating and substrate indicated that WC- $Ti_{0.72}$A $l_{0.28}$N coating showed the best resistance of the coating tested. The results of potentiodynamic polarization tests showed that the WC- $Ti_{0.72}$A $l_{0.28}$N coating deposited with 32W/c $m^2$ of Al target revealed higher corrosion resistance. This indicated that the WC- $Ti_{0.72}$A $l_{0.28}$N coating is effective in improving corrosion resistance. In EIS, the WC- $Ti_{0.72}$A $l_{0.28}$N coating showed one time constant loop and increased a polarization resistance of coating ( $R_{coat}$) relative to other samples. Compositional variations of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings were analyzed by EDS and XRD analysis was performed to evaluate the crystal structure and compounds formation behavior. Surface morphologies of the films were observed using SEM and AFM. Scratch test was performed to measure film adhesion strength.strength. adhesion strength.strength.

• Membrane and Water Treatment
• /
• v.10 no.4
• /
• pp.287-298
• /
• 2019

Lotus leaf has a special dual micro and nano surface structure which gives its highly hydrophobic surface characteristics and so-called self cleaning effect. In order to endow PVDF hollow fiber membrane with this special structure and improve the hydrophobicity of membrane surface, PVDF hollow fiber composite membranes was obtained through the immersion coating of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) dilute solution on the outside surface of PVDF support membrane. The prepared PVDF composite membranes were used in the vacuum membrane distillation (VMD) for the desalination. The effects of PVDF-HFP dilute solution concentration in the dope solution and coating time on VMD separation performance was studied. Membranes were characterized by SEM, WCA measurement, porosity, and liquid entry pressure of water. VMD test was carried out using $35g{\cdot}L^{-1}$ NaCl aqueous solution as the feed solution at feed temperature of $30^{\circ}C$ and the permeate pressure of 31.3 kPa. The vapour flux reached a maximum when PVDF-HFP concentration in the dilute solution was 5 wt% and the coating time was kept in the range of 10-60 s. This was attributed to the well configuration of micro-nano rods which was similar with the dual micro-nano structure on the lotus leaf. Compared with the original PVDF membrane, the salt rejection can be well maintained which was greater than 99.99 % meanwhile permeation water conductivity was kept at a low value of $7-9{\mu}S{\cdot}cm^{-1}$ during the continuous testing for 360 h.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.05a
• /
• pp.244-245
• /
• 2009

Sol-gel coatings of $TiO_2$ have been prepared from $TiO_2$ sol and deposited by dip-coating technique on 316L stainless steel sheets in order to study the electrochemical behaviorin corrosive solutions. The influence of the coatings on the chemical corrosion of the substrate has been evaluated by potentiodynamic polarization curves in different aqueous NaCl solution at $25^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.359-366
• /
• 1994

Tow types of supports were made using $\alpha$-Al2O3 powder and optimum conditions to prepare for supports were provided. Sol solution for coating was synthesized by sol-gel method with aluminum isopropoxide. Supports were coated and heat-treatemented, where the thickness of coating layer was controlled by dipping time. Flux and permeability of alumina membrane were measured by liquid and gas filtration apparatus and these were compared with the provided model. It was confirmed that the coating was done very well without micro~crack and defect.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.9 no.1
• /
• pp.1-11
• /
• 1991

In this reseach, double-layered photoconductor consist of the carrier generation layer(CGL) of $\varepsilon$ type copper phthalocyanine thin film by an aqueous coating method and the carrier transport layer(CGL) of polyvinyl carbazol(PVK) by spin coating. We inverstigated effect of the surfactant solution and cathod electrolysis to the crystal type of $\varepsilon$-CuPc in CGL with TEM, SEM and X- ray diffraction spectroscopy and studied the mechanism of an aqueous coating for the preparation of CGL. The effect of the washing of CGL about the electrophotographic characteristics of the $\varepsilon$-CuPc/PVK doublelayered photoconductors is studied also.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.1
• /
• pp.32-38
• /
• 2007

Ni coating layers were formed using a newly developed electroless Ni plating solution. The properties of Ni coating layer such as internal stress, hardness, surface roughness, crystallinity, solderability and surface morphology were investigated using various tools. Results revealed that internal stress decreased with plating time and reached $40N/mm^2$ at 20 minutes of the plating time. Hardness increased with increasing P content and thickness. Surface roughness of the pad decreased with Ni and Ni/Au plating. Crystallinity decreased with increasing P content. Solderability based on wettability decreased with Ni and Ni/Au plating. Based on surface morphology, it is expected that Ni coating layer formed using a newly developed electroless Ni plating solution is lower than that formed using a commercial electroless Ni plating solution in possibility of black pad occurrence.

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.102-107
• /
• 2017

Porous polytetrafluoroethylene (PTFE) thin films are fabricated by spin-coating using a dispersion solution containing PTFE powders, and their crystalline properties are investigated after thermal annealing at various temperatures ranging from 300 to $500^{\circ}C$. Before thermal annealing, the film is densely packed and consists of many granular particles 200-300 nm in diameter. However, after thermal annealing, the film contains many voids and fibrous grains on the surface. In addition, the film thickness decreases after thermal annealing owing to evaporation of the surfactant, binder, and solvent composing the PTFE dispersion solution. The film thickness is systematically controlled from 2 to $6.5{\mu}m$ by decreasing the spin speed from 1,500 to 500 rpm. A triboelectric nanogenerator is fabricated by spin-coating PTFE thin films onto polished Cu foils, where they act as an active layer to convert mechanical energy to electrical energy. A triboelectric nanogenerator consisting of a PTFE layer and Al metal foil pair shows typical output characteristics, exhibiting positive and negative peaks during applied strain and relief cycles due to charging and discharging of electrical charge carriers. Further, the voltage and current outputs increase with increasing strain cycle owing to accumulation of electrical charge carriers during charge-discharge.

• Korean Journal of Materials Research
• /
• v.30 no.3
• /
• pp.131-135
• /
• 2020

Silver nanowire (AgNW) networks have been adopted as a front electrode in Cu(In,Ga)Se2 (CIGS) thin film solar cells due to their low cost and compatibility with the solution process. When an AgNW network is applied to a CIGS thin film solar cell, reflection loss can increase because the CdS layer, with a relatively high refractive index (n ~ 2.5 at 550 nm), is exposed to air. To resolve the issue, we apply solution-processed ZnO nanorods to the AgNW network as an anti-reflective coating. To obtain high performance of the optical and electrical properties of the ZnO nanorod and AgNW network composite, we optimize the process parameters - the spin coating of AgNWs and the concentration of zinc nitrate and hexamethylene tetramine (HMT - to fabricate ZnO nanorods. We verify that 10 mM of zinc nitrate and HMT show the lowest reflectance and 10% cell efficiency increase when applied to CIGS thin film solar cells.

• Korean Journal of Materials Research
• /
• v.25 no.10
• /
• pp.503-508
• /
• 2015

In this work, ceramic coatings were prepared on Al7075 aluminum alloy using microarc oxidation (MAO) process in a silicate-fluoride based electrolyte solution. The effect of $OH^-$ concentration, by adding NaOH to the solution on the microstructural and mechanical properties of the coating was investigated. Surface morphology and cross sectional view of the coating was analyzed using SEM while XRD was used to examine the phase compositions of the coatings. From XRD ${\alpha}-Al_2O_3$ phase was found to be increased by adding NaOH to the electrolyte. Thereby, the hardness and the wear properties of the MAO coatings were found to be superior to those of the coatings prepared without NaOH addition or with amount maximum than 2 g/l NaOH. Moreover, the morphology of the coatings was transformed form nodule-based cluster to crater based structure with the addition of NaOH to the MAO electrolyte solution.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.46 no.3
• /
• pp.73-81
• /
• 2004

FRP reinforcing bars(rebars) are produced through a variety of manufacturing process includes pultrusion, and filament winding and braiding etc. Each manufacturing method produces a different surface condition of FRP rebar. The surface properties of FRP rebar is an important property for mechanical bond with concrete. Current methods of providing surface deformation to FRP rebars include helical wrapping, surfaces and coating and rib molding. The problem with the helical wrapping method is that it can not provide enough surface deformation for good bond and it can be easily sheard off from the FRP rebars. Sand coating and rib molding provide surface deformation only to the outer FRP skins. Therefore, FRP rebar has about 60% of bond strength of steel rebar. The main objective was to evaluate the bond properties of FRP rebar after environmental exposure. Five types of FRP rebar includes CFRP ISO, GFRP Aslan, AFRP Technora CFRP(Korea), and GFRP(Korea) rebars performed direct bond tests. Also, FRP rebar bond specimens were subjected to exposure conditions including alkaline solution, acid solution, salt solution and deionized water etc. According to bond test results, CFRP(Korea) and CFRP(Korea) rebars were found to have better bond strength with concrete than previous FRP rebars. Also, FRP(Korea) rebar had more than about 70% in bond strength of steel rebar.