• Journal of Powder Materials
• /
• v.18 no.4
• /
• pp.322-326
• /
• 2011

Inkjet printing was successfully done using Cu nano powder ink after these Cu nano powders were dry-coated with 1-octanethiol for oxidation prevention. 1-octanethiol, which is Self-Assembled Multi-layers (SAMs), was coated approximately 10-nm thick on the surface of Cu nano powders. 1-Octanol, which has the same chain length as that for 1-octanethiol, was used as a solvent to make the ink for inkjet printing. As a result, the fabricated ink was dispersed for about 4 weeks, and after printing and heat treatment at $350^{\circ}C$ for 4 hours, the resistivity for the printed pattern was measured to be $1.15{\times}10^{-5}{\Omega}{\cdot}cm$.

• Journal of the Korean Ceramic Society
• /
• v.44 no.1 s.296
• /
• pp.32-36
• /
• 2007

Zinc gallate $(ZnGa_2O_4)$ thin film phosphors have been formed on ITO glass substrates by a sol-gel spinning coating method. For the formation of the film phosphors, the starting materials of zinc acetate dihydrate, gallium nitrate hydrate and 2-methoxyethanol as a solution were used. The thin films deposited were firstly dried at $100^{\circ}C$ and fired at $500^{\circ}C\;or\;600^{\circ}C$ for 30 min and then, annealed $500^{\circ}C\;or\;600^{\circ}C$ at for 30 min under an annealing atmosphere of 3% $H_2/Ar$. The thin films deposited on ITO glass plates showed the (220), (222), (400), (422), (511), and (440) peaks of spinel structure as well as the (311) peak indicating a standard powder diffraction pattern. The surface morphologies of the thin film phosphors were observed with a firing and an annealing condition. The $ZnGa_2O_4$ film phosphors showed the blue emission spectra around 410 nm as well as the emission spectra in the UV region (360-380 nm).

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.455-460
• /
• 2005

Deposition of TiN$_{x}$ film was conducted with a DC sputtering technique. The effect of the processing parameters such as substrate temperature, deposition time, working pressure, bias power, and volumetric flowing rate ratio of Ar to N$_{2}$ gas on the resistivity of TiN$_{x}$ film was systematically investigated. Three kinds of substrates, soda-lime glass, (100) Si wafer, and 111m thermally grown (111) SiO$_{2}$ wafer were used to explore the effect of substrate. The phase of TiN$_{x}$ film was analyzed by XRD peak pattern and deposition rate was determined by measuring the thickness of TiNx film through SEM cross-sectional view. Resistance was obtained by 4 point probe method as a function of processing parameters and types of substrates. Finally, optimum condition for synthesizing TiN$_{x}$ film having lowest resistivity was discussed.

• Journal of Electrochemical Science and Technology
• /
• v.3 no.2
• /
• pp.72-79
• /
• 2012

$Li_2MnSiO_4$ was synthesized using the solid-state method under an Ar atmosphere at three different calcination temperatures (900, 950, and $1000^{\circ}C$). The optimization of the carbon coating was also carried out using various molar concentrations of adipic acid as the carbon source. The XRD pattern confirmed that the resulting $Li_2MnSiO_4$ particles exhibited an orthorhombic structure with a $Pmn2_1$ space group. Cyclic voltammetry was utilized to investigate the capacitive behavior of $Li_2MnSiO_4$ along with activated carbon (AC) in a hybrid supercapacitor with a two-electrode cell configuration. The $Li_2MnSiO_4$/AC cell exhibited a high discharge capacitance and energy density of $43.2Fg^{-1}$ and $54Whkg^{-1}$, respectively, at $1.0mAcm^{-2}$. The $Li_2MnSiO_4$/AC hybrid supercapacitor exhibited an excellent cycling stability over 1000 measured cycles with coulombic efficiency over > 99 %. Electrochemical impedance spectroscopy was conducted to corroborate the results that were obtained and described.

• Molecular & Cellular Toxicology
• /
• v.5 no.1
• /
• pp.23-31
• /
• 2009

To compare the effects of nanometer-sized silver ions and support materials (nano-silver coating material, NM-silver) and silver ions, we exposed zebrafish embryos to both types of nano-silver ions and compared the acute responses during embryogenesis. The amount of silver in the NM-silver (17.16%) was greater than that in the silver ion (4.56%). Both of these materials have different atomic compositions. The silver ion-exposed groups (10 and 20 ppt) showed lower survival rates than the NM-silver-exposed groups (10 and 20 ppt). NM-silver penetrated the skin and blood tube of zebrafish larvae as aggregated particles, whereas, silver ions penetrated the organelles, nucleus and yolk in a spread-out pattern. Micro-array analysis of RNA from zebrafish larvae (72 hours post-fertilization) that were treated with either NM-silver or silver ions, showed alteration in expression of the BMP, activin, TGF-$\beta$, and $GSK3{\beta}$ genes pathway. Additionally, $GSK3{\beta}$ gene pathway for apoptosis that was related with left-right asymmetry. Gene expression changes in the NM-silver or silver ions-treated zebrafish embryo led to phenotypic changes in the hatched larvae, reflecting increased apoptosis and incomplete formation of an axis.

• 한국태양에너지학회:학술대회논문집
• /
• 2012.03a
• /
• pp.260-266
• /
• 2012

Syngas and hydrogen from the $CeO_2/ZrO_2$ coated foam devices were investigated under simulated solar radiation. The $CeO_2/ZrO_2$ coated SiC, Ni and Cu foam device were prepared using drop-coating method. Syngas production step was performed at $900^{\circ}C$, and hydrogen production process was performed for ten repeated cycles to compare the CeO2 conversion in syngas production step, $H_2$ yield in hydrogen production step and cycle reproducibility. The produced syngas had the $H_2$/CO ratio of 2, which was suitable for methanol synthesis or Fischer-Tropsch synthesis process. In addition, syngas and hydrogen production process is one of the promising chemical pathway for storage and transportation of solar heat by converting solar energy to chemical energy. After ten cycles of redox reaction, the $CeO_2/ZrO_2$ was analyzed using XRD pattern and SEM image in order to characterize the physical and chemical change of metal oxide at the high temperature.

• Applied Microscopy
• /
• v.43 no.2
• /
• pp.88-97
• /
• 2013

Technical investigation to figure out the problems arising during in-situ heating electron backscatter diffraction (EBSD) analysis inside scanning electron microscopy (SEM) was carried out. EBSD patterns were successfully acquired up to $830^{\circ}C$ without degradation of EBSD pattern quality in steels. Several technical problems such as image drift and surface microstructure pinning were taking place during in-situ experiments. Image drift problem was successfully prevented in constant current supplying mode. It was revealed that the surface pinning problem was resulted from the $TiO_2$ oxide particle formation during heating inside SEM chamber. Surface pinning phenomenon was fairly reduced by additional platinum and carbon multi-layer coating before in-situ heating experiment, furthermore was perfectly prevented by improvement of vacuum level of SEM chamber via leakage control. Plane view in-situ observation provides better understanding on the overall feature of recrystallization phenomena and cross sectional in-situ observation provides clearer understanding on the recrystallization mechanism.

• Aerospace Engineering and Technology
• /
• v.6 no.2
• /
• pp.141-149
• /
• 2007

It was carried out hot-firing test with a regenerative-cooled sub-scale combustor which was applied regenerative-cooling, film cooling and thermal barrier coating. Test results showed that cooling methods used in the combustor play an full role in the operation of the combustor under the design condition but it is occurred high frequency combustion instability due to unsteady flow of fuel by structural support ring inserted in fuel manifold. The flow pattern of fuel was improved by excluding the ring and it will be carried out additional hot-firing test to verify the combustion stability of modified combustor.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2010.05a
• /
• pp.30.1-30.1
• /
• 2010

Hydrogen silsesquioxane (HSQ)는 spin-on glass (SOG)의 일종으로 spin-coating이 가능하며 $400^{\circ}C$ 이상의 고온에서의 어닐링을 통해 silica로 변환되는 물질이다. 이 물질은 가시광선 영역에서 95% 이상의 높은 투과도를 나타내며 산화물로의 변환 공정이 간단하며 표면 개질이 용이하기 때문에 나노 바이오, 반도체, 광전자 소자 등의 다양한 분야로의 적용이 기대되는 물질이다. 최근 나노 기술의 발전에 따라 다양한 나노 구조물을 이용하여 소자들의 효율을 향상시키는 연구가 활발하게 진행되고 있다. 따라서 HSQ를 이용하는 소자의 효율을 높이기 위해서는 쉽고 간단하면서 생산성이 높은 HSQ 나노 구조물 제작 기술에 대한 연구가 필요하다. 현재 개발된 대면적 HSQ 나노 구조물 제작 기술로는 e-beam lithography, x-ray lithography, room temperature nanoimprint lithography 등이 있다. 하지만 이와 같은 나노 패터닝 기술들은 생산성이 낮거나 공정이 복잡한 단점이 있다. 본 연구에서는 poly(dimethylsiloxane) (PDMS) mold를 이용한 직접 printing 기술을 통해 HSQ 나노 구조물을 제작하는 기술을 개발하였다. 이 기술은 대면적에 간단한 기술로 HSQ 나노 패턴을 제작할 수 있으며 master mold의 패턴이 그대로 HSQ layer로 전사되기 때문에 제작이 까다로운 아날로그 패턴도 손쉽게 제작할 수 있는 장점을 가지고 있다. 따라서 이와 같은 HSQ 직접 printing 기술을 이용하여 HSQ 아날로그 나노 패턴을 제작하고 이의 응용기술에 대한 연구를 진행하였다.

• Journal of the Korean institute of surface engineering
• /
• v.23 no.1
• /
• pp.16-26
• /
• 1990

The standrd electrolyte for the electrodeposition of chromium were preparwith reagent grade chromic acid(200g/L), sulfuric acid(pH=1.8)and oxalic acalic acid(640g/L)as additive. Carbon content in chromium plating varied about2.0-3.8 wt% with current density and temperatures of the bath. The hardeness of chromium platings incresed with increasing the annealing temperatures and showed maximum value of about Hv 1700 after annealing at$ 700^{\circ}C$for 60min. But, decreased it as annealing at above $700^{\circ}C$. The reason for varing thee hardness of chromium codeposited with carbon gradually foumed chromium carbide(Cr7C3), but that changed to Cr23C6 as annealing temperature at above $^700{\circ}C$. The X-ray diffraction pattern indicated that chromium carbides, such as Cr7C3 or Cr3C2, formed at formed at above $300^{\circ}C$. titanium coating sputtered on the on surface of chromium plating had performed and determined the hardness after annealing at 500, 600, $700^{\circ}C$ for 60min. the maximum hardeness was about Hv 2400 as annealing at $700^{\circ}C$. The titanium carbide formed in layer was identified by X-ray diffraction. It was confirmed that chromium and titanium carbide has effect of increasing the hardness.