Many in the industrial world that consume high amounts of energy are trying to reduce energy when manufacturing their products. Energy saving during manufacturing is a cost reduction. Reduced cost is necessary for profit improvement. The Piston Under Drive Brake used in the current study is an automotive transmission part. The original machining after hot forging was changed to machining after cold forging of a plate in order to save energy and cost. Two extrusion shapes along the outer diameter caused decreased tool life because of the interrupted cut during turning. Therefore, a thickness reduction of two extrusion areas in the outer diameter was needed. The current study suggests an effective way to reduce the thickness of interrupted cut by using progressive blanking.

• 공업화학
• /
• 제9권7호
• /
• pp.1011-1017
• /
• 1998

$YBa_2Cu_3O_{6+x}(Y123)-Ag$ 초전도 선재를 0/20 wt%의 은(Ag)을 첨가한 발화합성분말과 고상반응분말을 사용하여 플라스틱 압출법으로 제조하였다. 플라스틱 압출법은 분말제조, 플라스틱 paste 제조, 다이 압축, binder 소각 및 소결공정을 포함한다. 양질의 초전도체를 제조하려면 원료물질이 균질하고 미세한 분말이어야 한다. 0/20 wt%를 첨가한 $Y_2O_3-BaCO_3-CuO$ precursor 분말을 발화합성(PS)법과 고상반응(MM)법으로 제조하였다. 원료분말이 Y123 초전도상으로 전이되는 생성속도를 공기중에서 여러온도와 시간별로 반응시켜 알아보았다. 발화합성법으로 제조한 분말이 고상반응법으로 제조한 분말보다 Y123상으로 빠르게 전이되었다. 이것은 PS법으로 제조한 분말이 미세한 크기와 균질한 화학적 조성으로 인해 Y123상으로 빠른 전이를 한 것이기 때문이다. 플라스틱 압출법으로 제조한 Y123-Ag 초전도 선재의 임계전류밀도($J_c$)는 원료분말의 특징에 따라 $150{\sim}230A/cm^2$값을 나타내었다. 은을 20 wt.% 첨가한 발화합성분말로 제조한 선재의 $J_c$는 $230A/cm^2$이었다.

• 한국산학기술학회논문지
• /
• 제17권9호
• /
• pp.228-234
• /
• 2016

본 이 연구의 목적은 이중 고온용융 압출법을 이용하여 기존의 방법으로 가지기 어려운 이상성의 약물방출 양상을 가지는 제형을 개발하는 것이다. 이 고온용융 압출물은 동회전 능을 가지는 두 개의 스크류가 장착된 압출기를 이용하여 제조되었다. Hydroxpropylmethylcellulose(HPMC) 같은 상대적으로 유리전이 온도가 높은 고분자를 이용하여 1차로 고온용융 압출물이 제조되었고, 이 1차 압출물과 상대적으로 유리전이 온도가 낮은 HPMC-AS(Acceate succinate)나 PEO(polyethlene oxide)를 이용하여 2차로 고온용융 압출물이 제조되었다. 또한 이중 고온용융 압출물과의 비교시험을 위해 같은 조성과 같은 조건하에서 일반적인 한 번의 고온용융 압출물도 제조되었다. 시차주사 열량계를 통해 물리적인 성질이 평가되었고, 미국약전의 제 1법에 따라 $37{\pm}0.5^{\circ}C$와 100 rpm의 조건에서 약물방출 시험이 진행되었으며 그 약물방출은 유사성인자($f_2$)를 이용하여 평가되었다. 시차주사 열량계 결과는 이부프로펜의 결정성이 이중 고온용융 압출법에서나 한번 고온용융 압출법 모두에서 무정형으로 변화된 것을 확인할 수 있었으며, 용출시험에서는 이중 고온용융 압출법에서 더욱 더 이상적인 이부프로펜의 방출을 인공위액(pH 1.2)에서 2시간, 0차 방출을 인공장액(pH 6.8)에서 6시간 동안 확인할 수 있었다. 빠른방출이 요구되는 글리메피라이드의 경우는 이중 고온용융 압출물에서는 60분에 80% 이상의 빠른 약물 방출을 보인 반면, 한번 고온용융 압출물에서는 약물방출이 HPMC와의 상호작용 때문에 느려져서 기준을 만족하지 못했다. 유사성 인자($f_2$) 값도 28.5로 매우 다른 방출을 보여주고 있음이 통계적으로 확인되었다. 이상의 결과들을 종합해 볼 때, 이중 고온용융 압출법은 완건성이 좋은 또 원하는 약물방출을 얻을 수 있는 방법이라 할 수 있다.

• Korean Chemical Engineering Research
• /
• 제49권6호
• /
• pp.804-809
• /
• 2011

$Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ 조성의 관형 분리막을 압출 성형 방법으로 제조하였다. 압출성형 직후 분리막의 TGA 분석결과 3단계의 무게감소로 첨가제와 탄산염이 분해되었고, 건조 수축율은 68 h 경과 후 변화가 없었으며 외경이 큰 분리막에서 높게 나타났다. 소결 후 분리막의 XRD 및 SEM 분석결과, 분리막은 단일상의 페롭스카이트 구조를 갖는 치밀한 막을 보였고, EDS 분석을 통해 $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$와 유사한 성분함량을 가짐을 확인하였다. 두께 0.95 mm $Ba_{0.5}Sr_{0.5}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ 관형 분리막의 압환강도(radial crushing strength)는 5.7 kgf/$mm^2$이였으며, $950^{\circ}C$에서 산소투과량은 146.85 mL/min($Jo_2$=2.33 mL/$min{\cdot}cm^2$)를 나타냈었다. 투과 측의 진공펌프 사용이 쓸개 가스를 활용한 것보다 산소 투과량 증진에 효과가 있음을 알 수 있었다.

• Elastomers and Composites
• /
• 제59권2호
• /
• pp.51-63
• /
• 2024

Polypropylene (PP) is a commodity plastic that is widely used owing to its cost-effectiveness, lightweight nature, easy processability, and outstanding chemical and thermomechanical characteristics. However, the imperative to address energy and environmental crises has spurred global initiatives toward a circular economy, necessitating sustainable alternatives to traditional fossil-fuel-derived plastics. In this study, we conducted a series of comparative investigations of bio-based polypropylene (bio-PP) blends with current PP of the same and different grades. An extrusion-based processing methodology was employed for the bio-PP composites. Talc was used as an active filler for the preparation of the composites. A comparative analysis with the current petroleum-based PP indicated that the thermal properties and tensile characteristics of the bio-PP blends and composites remained largely unaltered, signifying the feasibility of bio-PP as a potential substitute for the current PP. To achieve a higher Young's modulus, elongation at break (EAB), and melt flow index (MFI), we prepared different composites of PP of different grades and bio-PP with varying talc contents. Interestingly, at higher biomass contents, the composites exhibited higher MFI and EAB values with comparable Young's moduli. Notably, the impact strengths of the composites with various biomass and talc contents remained unaltered. In-depth investigations through surface analysis confirmed the uniform dispersion of talc within the composite matrix. Furthermore, the moldability of the bio-PP composites was substantiated by comprehensive rheological property assessments encompassing shear rate and shear viscosity. Thus, from these outcomes, the fabricated bio-PP-based composites could be an alternative to petroleum-based PP composites for sustainable automobile applications.

• Korea-Australia Rheology Journal
• /
• 제18권2호
• /
• pp.83-90
• /
• 2006

Supercritical carbon dioxide ($scCO_2$) has advantages of being incorporated in polymer with high solubility and of being recovered easily by depressurizing. $scCO_2$ reduces the viscosity of polymer melt and it is expected to be use as a plasticizing agent. In this work, we studied on the effect of $scCO_2$ on the rheological properties of polymer melts during extrusion process. Slit die attached to twin screw extruder was used to measure the viscosity of polymer melts plasticized by supercritical $CO_2$. A gas injection system was devised to accurately meter the supercritical $CO_2$ into the extruder barrel. Measurements of pressure drop within the die, confirmed the presence of a one phase mixture and a fully developed flow during the measurements. The viscosity measurement of polypropylene was performed at experimental conditions of various temperatures, pressures and $CO_2$ concentrations. We observed that melt viscosity of polymer was dramatically reduced by $CO_2$ addition.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.340-341
• /
• 2005

Three different composition 130um thickness PZT were fabricated by extrusion method and burned out at $550^{\circ}C$ and sintered at $1260^{\circ}C$/2.5hrs. Actuator was fabricated using glass and Si(100) wafer by MEMS process. From XRD data, in case of DECH, perovskite phase peak strength is higher than others. We were able to obtain the information of grain growth and porosity by SEM images. Also DECH PZT on glass membrane(100um thickness) have larger displacement than others.

• 한국포장학회지
• /
• 제24권3호
• /
• pp.149-157
• /
• 2018

Low density polyethylene (LDPE) has been researched in many industrial applications, and LDPE/zeolite 4A composites has been extensively studied for many applications such as microporous, breathable film and so on. LDPE/zeolite composite have a great potential for carbon dioxide adsorption film due to its high adsorption ability. In this study, LDPE/zeolite 4A composites with various contents were prepared by melt mixing process, and co-extrusion process was applied to develop a $CO_2$ adsorption conventional film and foamed film. The thermal, rheological, mechanical, physical and morphological properties of composite films has been characterized, and $CO_2$ adsorption of the composite films evaluated by thermogravimetric analysis (TGA) and the performance was found to be about 18 cc/g at 30.9 wt% of the zeolite content.

• International Journal of Ocean Engineering and Technology Speciallssue:Selected Papers
• /
• 제5권1호
• /
• pp.53-57
• /
• 2002

Most of the heli-decks are constructed with aluminum extrusions. The heli-deck product company supplies structural analysis data to the shipbuilding companies: so, if the shipbuilding co. needs to make up for the weak points in the current system, they only need to analyze the substructure through the FEA. In this paper, we will concentrate on the following issues: analysis of aluminium extrusions regarding the structural analysis data, and check safety about the substructure through the FEA.

• 폴리머
• /
• 제32권2호
• /
• pp.116-124
• /
• 2008

본 연구는 식물유래 생분해성 고분자인 poly(lactic acid)(PLA)의 가공성을 향상시키기 위하여 기능성 단량체인 glycidyl methacrylate(GMA)와 반응 개시제를 첨가하여 반응압출법으로 PLA를 개질한 후 겔화도, 열적성질, 유변학적 특성 및 생분해도를 조사하였다. 개질 PLA및 순수 PLA의 열적특성은 시차열량분석기(DSC)를 이용하여 측정하였고 유변학적 특성은 복합점도(${\eta}^*$), 저장 탄성률(G'), log G' vs. log G" 선도를 이용하여 분석 비교하였다. GMA가 포함되지 않고 개시제로만 개질된 PLA의 복합점도 및 저장탄성률도 순수 PLA보다 증가하였지만, 여기에 GMA를 첨가하여 개질하면 더욱 향상된 복합점도와 저장탄성률을 갖는 개질 PLA를 얻을 수 있었다. 개시제의 함량에 따라 최고 높은 복합점도 및 저장탄성률 증가 효과를 보이는 최적의 GMA함량이 존재하였다. 그리고 GMA가 함유된 개질 PLA의 생분해도는 약간 낮아지는 경향을 보였다.