• The Journal of the Korea Contents Association
• /
• v.22 no.3
• /
• pp.586-592
• /
• 2022

In this study cerium nano particles(CNPs) with 0-4.0 wt% was incorporated to the conventional dental pit and fissure sealant(ConciseTM) to produce new pit and fissure sealant the physical properties and cytotoxicity. The physical properties were measured for polymerizing depth the degree of water absorption and solubility. The cytotoxicity of cell viability was analyzed by MTT assay using immortalized human oral keratinocyte(IHOK). As a result of this preceding study the polymerizing depth was decreased by the increasing of the amount of CNPs. The solubility degree of the sealant added CNPs with 2.0 wt% showed was the lower and the water absorption showed no significantly difference with the control groups(p>0.05). The cytotoxicity test results showed high survival rates in all experimental groups. Therefore, pit and fissure sealant by the addition of CNPs excellent cell viability be produced without weaken the physical property of the cell viability fissure sealant containing CNPs does not weaken physical properties and has no cytotoxic effects biocompatibility. Considering its properties effect of CNPs, further studies are required for distribution technology application.

• Journal of Korean society of Dental Hygiene
• /
• v.20 no.4
• /
• pp.535-543
• /
• 2020

Objectives: The aim of this study was to investigated the surface roughness and change in the amount of adhesion of Streptococcus mutans to the commercial pit and fissure sealant containing cerium oxide nano particles(CNPs). Methods: The CNPs was incorporated into a commercial pit and fissure sealant at 0-4.0 wt%. Disk Specimens (ϕ 10 mm × 2 mm) were prepared by light polymerization the front and back for 40s. Average surface roughness was measured and Streptococcus mutans adhesion was observed under confocal laser scanning microscopy (CLSM) after 24 hour. Data were statistically analyzed by one-way ANOVA and Tukey HSD^a post-hoc test. Results: Difference of the surface roughness(Ra) between groups was not statistically significant in both non CNPs group and CNPs group(p>0.05). In CNPs group, the amount of S. mutans adhesion was significantly different between control group and decreased in order of CNPs 4.0, CNPs 0.5, CNPs 1.0 and CNPs 2.0(p<0.05). Conclusions: Within the limitation of this study, these aspects of oral bacteria performances suggest potential usefulness of the CNPs incorporation, especially CNPs 1% and 2%, in pit and fissure sealant for inducing antibacterial effect.

• Korean Journal of Materials Research
• /
• v.24 no.1
• /
• pp.33-36
• /
• 2014

This study was aimed at synthesizing and characterizing cerium-doped titania. Cerium-doped anatase titania powders were prepared by sol-gel process, with ammonium (IV) nitrate and titanium (IV) butoxide as the raw materials. The characteristics of pure $TiO_2$ and cerium-doped $TiO_2$ were investigated by XRD, TG/DTA, FE-SEM, and UV-vis spectroscopy. The results of this study show that anatase type of $TiO_2$ was obtained in as-prepared and calcined $TiO_2$ and Ce-$TiO_2$ powder. A DTA curve was also observed as the crystallization temperature decreased with increasing cerium contents. We found that the crystallite size of the obtained anatase particles decreased from 55 nm to 25 nm and the particle size decreased with increasing cerium contents. Moreover, UV-vis spectra showed that anatase titania powders with various cerium contents effectively extend the light absorption properties to the visible region.

• Korean Journal of Materials Research
• /
• v.15 no.12
• /
• pp.818-823
• /
• 2005

Sub-micron colloidal silica particles coated with nano-sized ceria were prepared by mixing of its silica and cerium salts hydrolysis, and modified by hydrothermal reaction. By using the slurries with and without hydrothermal modification containing above particles, oxide film coated on silicon wafer was polished. The modified slurries had higher polish rate due to increase of ceria fraction to silica through hydrothermal reaction. They revealed higher stability in wide range of pH $2\~10$ than ceria coated silica slurries without its modification.

• The Journal of the Korea Contents Association
• /
• v.20 no.6
• /
• pp.433-438
• /
• 2020

The aim of this study was to investigate the mechanical properties of pit and fissure sealant containing cerium oxide nano particles(CNP). Used to mix with pit and fissure sealant (Concise^TM, USA). CNP was added into liquid (0- 4.0 wt%) of pit and fissure sealant. The specimens for the vickers hardness (VHN; 10 × 2 mm), Three-point flexure (FS; 2 × 2 × 25 mm) with flexure modulus (FM) were obtained from cements at 1, 7, and 14 days after storing in (37±1)℃ distilled water. All mechanical strength tests were conducted using machine (Instron 3344) with a cross-head speed of 1 mm/min. Data were statistically analyzed by one-way ANOVA and Duncan posthoc test(p<0.05). Mechanical properties of conventional pit and fissure sealant could be enhanced by addition of CNP. Three-point flexure and modulus of pit and fissure sealant containing CNP were showed a slightly higher value not significantly with the group(p>0.05). The vickers hardness values were increase significantly with incubation time(p<0.05). Results indicated that CNP can be used considered as potential reinforcing agent for increasing mechanical properties for conventional pit and fissure sealant. Therefore, it was suggest that the additional effects of CNP and research on a wide range of substances.

• Korean Journal of Materials Research
• /
• v.23 no.1
• /
• pp.31-34
• /
• 2013

Trivalent cerium-ion-doped $Y_3(Al,\;Ga)_5O_{12}$ nanoparticle phosphor nanoparticles were synthesized using the reverse micelle process. The Ce doped $Y_3(Al,\;Ga)_5O_{12}$ particles were obtained from nitrate solutions dispersed in the nanosized aqueous domains of a micro emulsion consisting of cyclohexane as the oil phase and poly(oxyethylene) nonylphenyl ether (Igepal CO-520) as the non-ionic surfactant. The crystallinity, morphology, and thermal properties of the synthesized $Y_3(Al,\;Ga)_5O_{12}:Ce^{3+}$ powders were characterized by thermogravimetry-differential thermal analysis (TGA-DTA), X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), and transmission electron microscopy. The crystallinity, morphology, and chemical states of the ions were characterized; the photo-physical properties were studied by taking absorption, excitation, and emission spectra for various concentrations of cerium. The photo physical properties of the synthesized $Y_3(Al,\;Ga)_5O_{12}:Ce^{3+}$ powders were studied by taking the excitation and emission spectra for various concentrations of cerium. The average particle size of the synthesized YAG powders was below $1{\mu}m$. Excitation spectra of the $Y_3Al_5O_{12}$ and $Y_3Al_{3.97}Ga_{1.03}O_{12}$ samples were 485 nm and 475 nm, respectively. The emission spectra of the $Y_3Al_5O_{12}$ and $Y_3Al_{3.97}Ga_{1.03}O_{12}$ were around 560 nm and 545 nm, respectively. $Y_3(Al,\;Ga)_5O_{12}:Ce^{3+}$ is a red-emitting phosphor; it has a high efficiency for operation under near UV excitation, and may be a promising candidate for photonic applications.

• Journal of the Korean Ceramic Society
• /
• v.40 no.8
• /
• pp.798-803
• /
• 2003

In synthesis of nano powders, the hard agglomeration for the synthesized powders occurred during the drying processing. In order to avoid hard agglomeration in particles the freeze drying process was used in this experiment. e fabricated the Yttira-Doped Ceria(YDC) nano powder by co-precipitation. Starting materials used in experiments were the cerium(III) nitrate and yttrium(III) nitrate solution with 야-water, which two solutions were mixed and then the precipitated hydroxides were prepared for adding sodium hydroxide. The co-precipitated powders were dried by the thermal drying at 8$0^{\circ}C$ for 24 h and by freeze drying at -4$0^{\circ}C$, 30 mtorr for 72 h. The lattice parameter and crystallite size as a function of calcination temperature was characterized by XRD analysis. The lattice parameter of YDC was decreased with addition amount of yttrium and was estimated as 5.401683 $\AA$ at $700^{\circ}C$. Crystallite size were calculated by XRD-LB method, and morphologies were confirmed with the observation of TEM and SEM. The freeze dried YDC powders had medium diameter of 17 nm with more uniform size distribution than the thermal dried YDC posers, which were mainly ascribed to the difference of agglomerates formation during drying stage.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.18-21
• /
• 2017

In this study, spherical monodispersed cerium-doped yttrium aluminum garnet (YAG : $Ce^{3+}$) phosphor particles were synthesized via homogeneous precipitation method using the mixed solution of yttrium nitrate, cerium nitrate, aluminum nitrate, ammonium aluminum sulfate, and urea as a precipitant. During the process of precursors of monodispersed YAG : $Ce^{3+}$, aluminum ions which form spherical aluminum compounds precipitated first and yttrium compounds precipitated onto the surface of the existing spherical aluminum compounds. Drying process using lyophilization could obtain monodispered spherical YAG : $Ce^{3+}$ particles compare to using oven. The thermal calcination process of YAG : $Ce^{3+}$ precursors under the temperature of $1200^{\circ}C$ for 6 h was enough to obtain 400~500 nm sized YAG particles with pure YAG phase.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.487-487
• /
• 2009

One of the critical consumables in chemical mechanical polishing (CMP) is a specialized solution or slurry, which typically contains both abrasives and chemicals acting together to planarize films. In single abrasive slurry (SAS), the solid phase consists of only one type of abrasive particle. On the other hand, mixed abrasive slurry (MAS) consists of a mixture of at least two types of abrasive particles. In this paper, we have studied the CMP characteristics of mixed abrasive slurry (MAS) retreated by adding of $CeO_2$ abrasives within 1:10 diluted silica slurry (DSS). The slurry designed for optimal performance should produce reasonable removal rates, acceptable polishing selectivity with respect to the underlying layer, low surface defects after polishing, and good slurry stability. The modified abrasives in MAS are evaluated with respect to their particle size distribution, surface morphology, and CMP performances such as removal rate and non-uniformity. As an experimental result, we obtained the comparable slurry characteristics compared with original silica slurry in the viewpoint of high removal rate and low non-uniformity.

• Korean Journal of Materials Research
• /
• v.20 no.9
• /
• pp.472-477
• /
• 2010

$Al_2O_3$ has received wide attention with established use as a catalyst and growing application in structural or functional ceramic materials. On the other hand, the boehmite (AlO(OH)) obtained by sol-gel process has exhibited a decrease in surface area during phase transformation due to a decline in surface active site at high temperature. In this work, $Al_2O_3$-CuO/ZnO (ACZ) and $Al_2O_3$-CuO/CeO (ACC) composite materials were synthesized with aluminum isopropoxide, copper (II) nitrate hemi (pentahydrate), and cerium (III) nitrate hexahydrate or zinc (II) nitrate hexahydrate. Moreover, the Span 80 as the template block copolymer was added to the ACZ/ACC composition to make nano size particles and to keep increasing the surface area. The ACZ/ACC synthesized powders were characterized by Thermogravimetry-Differential Thermal analysis (TG/DTA), X-ray Diffractometer (XRD), Field-Emmision Scanning Electron Microscope (FE-SEM), Bruner-Emmett-Teller (BET) surface analysis and thermal electrical conductivity (ZEM-2:M8/L). An enhancement of surface area with the addition to Span 80 surfactant was observed in the ACZ powders from 105 $m^2$/g to 142 $m^2$/g, and the ACC powders from 103 $m^2$/g to 140 $m^2$/g, respectively.