• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.297-297
• /
• 2007

The $(B_{0.5},Sr_{0.5})TiO_3$ ceramics, which added with low sintering materials $Li_2CO_3$ and ZnBO, was investigated for LTCC(low temperature co-fired ceramic) applications. To compare sintering temperature of $(B_{0.5},Sr_{0.5})TiO_3$ respectively, we added 1, 2, 3, 4, and 5wt% of $Li_2CO_3$ and ZnBO to $(B_{0.5},Sr_{0.5})TiO_3$. For confirming the sintering temperature, the respective specimens were sintered from $750^{\circ}C$ to $1200^{\circ}C$ by $50^{\circ}C$. The case of $Li_2CO_3$ greatly lowered the sintering temperature of $(B_{0.5},Sr_{0.5})TiO_3$ ($1350^{\circ}C$) below $900^{\circ}C$. The addition of ZnBO improved the loss tangent of $(B_{0.5},Sr_{0.5})TiO_3$. The crystalline structure of $LiCO_3$ doped $(B_{0.5},Sr_{0.5})TiO_3$ and ZnBO doped $(B_{0.5},Sr_{0.5})TiO_3$ was analyzed with the X-ray diffraction (XRD) analysis. The dielectric permittivity and loss tangent of $Li_2CO_3$ doped BST and ZnBO doped BST were measured with the HP 4284A precision. From the electrical characterization, we respectively obtained the dielectric permittivity 1361, loss tangent $6.94{\times}10^{-3}$ at $Li_2CO_3$ doped $(B_{0.5},Sr_{0.5})TiO_3$ (3wt%) and the dielectric constant 1180, loss tangent $3.70{\times}10^{-3}$ at ZnBO doped $(B_{0.5},Sr_{0.5})TiO_3$(5wt%).

• 한국건설순환자원학회논문집
• /
• 제9권4호
• /
• pp.514-520
• /
• 2021

본 연구에서는 건설현장에서 가장 많이 사용되는 재료 중 콘크리트에 EMP차폐 성능을 부여하기 위해 전기로 산화슬래그를 사용하여 EMP차폐 성능 평가를 실시하였다. 평가 결과 전기로산화슬래그의 성분은 Fe₂O₃ 함량 34%로 나타났으며 MgO 성분 또한 4.8%가량 포함하는 것으로 나타났다. 또한 MgO 성분으로 인한 팽창우려로 골재안정성 평가를 실시한 결과 KS기준에 적합한 것으로 사료된다. EMP 차폐성능 평가결가 압축강도에 따른 EMP차폐성능은 상관성이 없었으며 일반골재는 EMP차폐가 되지 않은 것으로 나타났다. 그러나 전기로산화슬래그를 사용한 골재는 EMP 차폐성능이 우수 했으며 두께가 증가할수록 차폐성능은 향상되는 것을 알 수 있었다. 내구성 평가결과 EMP 차폐 콘크리트는 일반 콘크리트와 유산한 내구성을 보유하는 것으로 나타났다. 이를 통해 향후 EMP차폐 구조물 구축시 전기로 산화슬래그를 사용하여 콘크리트를 제조한다면 차폐율 향상에 좋을 것으로 사료된다.

• 헤리티지:역사와 과학
• /
• 제50권4호
• /
• pp.20-37
• /
• 2017

북제시기 유도 중에는 흰색 혹은 옅은 황색 유약 바탕에 녹색, 갈색, 황색 등으로 채색한 것이 있는데, 이는 "채회유도(彩繪釉陶)"로 통칭된다. 1971년 하남성(河南省) 안양시(安陽市) 홍하둔촌(洪河屯村)에 소재한 범수묘(範粹墓)에서 백유녹채삼계관(白釉綠彩三系罐)과 백유녹채장경병(白釉綠彩長頸甁)이 출토되었으나, 연구자들의 주목을 받지 못한 채 공반 출토된 백유기(白釉器)만이 중국에서 기년 자료가 확실한 가장 이른 백자의 증거로 제시되어 끊임없는 논쟁이 이루어졌다. 필자는 이 채회유도에 주목하여, 지금까지 무덤과 가마터에서 발견된 자료들을 정리하였으며, 이를 바탕으로 장식특징과 제작 기술을 파악하였다. 또한 이들이 부장된 무덤의 연대를 통한 출현 상한시점 및 피장자의 신분을 특정하여 채회유도의 사회적 가치를 알아보았다. 북제시기 채회유도는 이전 시기와 구별되는 제작특징이 확인되었는데, 구체적으로는 자토(瓷土)를 이용한 태토, 2차 소성, 유상회채(釉上繪彩) 기법이 새로 채용되었다. 이러한 특징은 이미 북위(北魏) 시기 유도에서 일부 나타난 변화로, 이것이 북제까지 이어져 백유 채회유도의 출현으로 나타났다고 볼 수 있다. 또한 채회유도의 기형은 동시기 남방지역 자기 기형과 북위시기 이래 생산된 채회의 속성이 결합되어 형성되었음을 확인하였다.

• 대한한의학회지
• /
• 제40권3호
• /
• pp.112-138
• /
• 2019

Objectives: The purpose of this study is to organize the research methods and results of studies related to the temperature of the warm needle for systematic utilization of warm needling technique. Methods: This study used the databases of nine (Pubmed, Science Direct, Cochrane Central, 4 Korean databases, CNKI, CiNii) to analyze temperature-related studies of the warm needle from 2000 to June 2019. Results: A total of 19 papers were included. Of these, 15 were used for mugwort, 2 for high frequency, and 1 for both mugwort and high frequency, and the other one for a ceramic heater. The maximum temperature rises as the amount of moxibustion increases. It is also affected by the density of moxa and the ignition part. There were 16 papers using stainless steel needles and 4 papers using a needle made of gold or silver to compare. In the area of the needle, the closer it is to moxibustion, the hotter it is. Compared to stainless steel needles, gold and silver needles showed almost twice the temperature. The effects of environment and radiant heat should be considered during warm needle procedures. Conclusions: There are various experimental methods such as warm needle technique materials, methods, measuring parts, measuring instruments, etc. The results were also very diverse. When setting the heating source, ignition part, size of moxibustion, etc. of warm needles, it should be implemented in a way that takes safety and validity into account. Considerations for temperature characteristics, radiant heat, etc. of warm needles will be needed when making warm needle apparatus.

• 한국초전도ㆍ저온공학회논문지
• /
• 제21권1호
• /
• pp.18-24
• /
• 2019

This study was carried out to investigate the effect of milling of boron (B), which is one of raw materials of $MgB_2$, on the critical current density ($J_c$) of $MgB_2$. B powder used in this study is semi-amorphous B (Pavezyum, Turkey, 97% purity, 1 micron). The size of B powder was reduced by planetary milling using $ZrO_2$ balls (a diameter of 2 mm). The B powder and balls with a ratio of 1:20 were charged in a ceramic jar and then the jar was filled with toluene. The milling time was varied from 0 to 8 h. The milled B powders were mixed with Mg powder in the composition of (Mg+2B), and the powder mixtures were uniaxially pressed at 3 tons. The powder compacts were heat-treated at $700^{\circ}C$ for 1 h in flowing argon gas. Powder X-ray diffraction and FWHM (Full width at half maximum) were used to analyze the phase formation and crystallinity of $MgB_2$. The superconducting transition temperature ($T_c$) and $J_c$ of $MgB_2$ were measured using a magnetic property measurement system (MPMS). It was found that $B_2O_3$ was formed by B milling and the subsequent drying process, and the volume fraction of $B_2O_3$ increased as milling time increased. The $T_c$ of $MgB_2$ decreased with increasing milling time, which was explained in terms of the decreased volume fraction of $MgB_2$, the line broadening of $MgB_2$ peaks and the formation of $B_2O_3$. The $J_c$ at 5 K increased with increasing milling time. The $J_c$ increase is more remarkable at the magnetic field higher than 3 T. The $J_c$ at 5 K and 4 T was the highest as $4.37{\times}10^4A/cm^2$ when milling time was 2 h. The $J_c$ at 20 K also increased with increasing milling time. However, The $J_c$ of the samples with the prolonged milling for 6 and 8 h were lower than that of the non-milled sample.

• 박물관보존과학
• /
• 제25권
• /
• pp.35-50
• /
• 2021

본 연구는 매곡토의 기본적인 특성과 점토물질 첨가에 따른 물리화학적 특성 변화를 분석하여 도자기 제작에 활용할 수 있는 흙에 대한 과학적 특성 정보를 제시하고자 하였다. 매곡토는 자갈과 굵은모래, 가는모래가 전체의 73%를 차지하여 수비과정을 거쳐야 태토로 사용이 가능하였으며, 수비 후에는 세사와 점토가 전체의 95%로 증가하였으나 가소성과 점력이 부족하여 분청토를 추가하여야 했다. 매곡토와 분청토를 7:3 비율로 혼합하였을 때는 점력이 증가하고, 소성 후에도 적당한 도자기 태토의 조직 특성을 보였으며, 흡수율이 0.40으로 감소하여 태토로써의 기능이 개선되었다. 따라서, 주변 흙으로 도자기를 제작하고자 할 때에는 수비와 같은 물리적 전처리를 거친 후 소성 시 기물로써 형태를 유지할 수 있도록 특정 성분이 포함되어 있는 점토 물질을 추가한다면, 본래 흙의 특성을 개선할 수 있다.

• 청정기술
• /
• 제27권1호
• /
• pp.24-32
• /
• 2021

미연 탄소(unburned carbon, UC)는 대두유를 포수제로 사용하여 부유선별공정을 통해 최대 85.8 wt%까지 비산재로부터 성공적으로 회수되었다. CM (ceramic microsphere)은 부유선별공정 다음 공정인 하이드로 사이클론 분리공정으로부터 18 wt%의 수율을 얻을 수 있었고 회수한 UC와 CM을 각각 고무증량재와 플라스틱(polypropylene) 충진재의 대체재로 사용하여 산업재로 활용 가능성을 조사하였다. 입자가 큰 UC는 볼밀을 사용하여 평균입경 10.2 ㎛로 작게 분쇄하였다. 분쇄된 UC를 점토 대신에 고무증량재로 사용하였을 때 인장강도와 신율이 다소 낮게 나와 고무제품의 표준조건을 만족시키지는 못하였다. 따라서 표준조건을 충족시키기 위해 UC는 고무와 보다 긴밀한 결합이 필요하였고, 이를 위한 표면 에너지를 향상시키는 추가적인 처리가 필요하였다. CM은 평균입경이 5 ㎛의 구형입자로 관찰되었으며, 입자의 표면을 페놀수지, 폴리올, 스테아린산, 올레인산으로 개질하였다. 표면 개질된 CM은 PP (polypropylene) 충진재로 사용되었다. 표면 개질된 CM을 사용한 제품은 흐름성은 양호하였으나 결합력 부족으로 충격강도 및 굴곡강도는 향상되지 못하였다. 그러나 표면 개질된 CM에 유기물과 무기물의 대표적 컬플링제인 실란 1 wt%을 추가적으로 혼합함으로써 충격강도 및 굴곡강도가 크게 향상되는 효과를 얻을 수 있었다.

• 한국융합학회논문지
• /
• 제13권3호
• /
• pp.281-289
• /
• 2022

플라즈마오존은 높은 살균성능으로 인해 다양한 살균분야에서 활용되고 있다. DBD(유전체 장벽방전)에 사용되는 유전체는 주로 석영, 세라믹, 폴리머 등이 주로 사용된다. 유전체로 이루어진 레이어는 공급되는 전하의 양을 제한시키고 플라즈마가 유전체 면 위에서 고르게 발생할 수 있도록 하는 역할을 한다. 이러한 DBD를 이용한 플라즈마, 오존살균은 살균대상이나 주변 환경이 복잡한 구조로 된 경우가 많아 공간살균에 대한 개념을 수립하고 이에 대한 연구와 학문적 체계가 필요하다. 본 연구에서는 플라즈마라디칼과 오존 생성을 위해 대기압에서 DBD방식을 이용한다. 플라즈마오존의 발생을 위한 반응기의 구조는 세라믹 튜브 유전체와 스테인리스 도체를 일정한 간격으로 배치하여 유전체 장벽방전을 발생시키는 형태이다. 공간살균장치로서의 플라즈마오존 발생은 성능 면에서 우수한 살균장치로 인식되고 있으므로 장치의 설계와 검증을 통해 공간살균장치의 최적설계를 확립하고자 하며 제안된 방법을 기반으로 다양한 살균 어플리케이션을 개발하는데 기초를 제공한다.

• Composites Research
• /
• 제36권4호
• /
• pp.246-252
• /
• 2023

멤브레인 형 LNG 화물창시스템(Cargo containment system, CCS) 내 유리섬유 강화 복합재료 기반 2차 방벽 설치 시 본딩 자동화 머신(automatic bonding machine, ABM) 활용한 prolonged 구조임과 동시에 양단 접착 고정 사이 비 접착(non-bonding, N-B) 영역의 복합재에서 극저온 열 수축 기인한 상당한 열 응력이 발생하기 때문에 이를 고려한 구조 안전성평가 관점에서 수행된 연구가 있으나 실제로 무한히 긴 길이 고려한 기계적 물성 평가를 수행한 연구는 찾아볼 수가 없었다. 해당 복합재는 파단강도 분산이 큰 세라믹 재료 취성 파괴임을 고려하여 2-파라미터 Weibull 통계분석을 통해 실제 길이 대상 신뢰도 있는 기계적 물성치 값을 표준화 하였으며 LNG 운반 환경을 고려한 극저온 환경까지의 특정 온도별 단축 인장실험을 수행하였다. 실험결과, -70℃에서 기계적 강도가 -20℃에 비해 약 1.5배 급증하고 초기 권축 섬유 신장의 비선형 거동이 억제되었다. 또한, 극저온 환경까지 온도가 낮아질수록 기계적 강도는 계속해서 증가하였으나 반대로 연신은 줄어드는 저온 취성의 현상이 확인되었다. 본 연구에서 제시하는 기계적 물성치 데이터는 멤브레인 형 LNG 화물창 구조 안전성 평가 시 신뢰도 높은 해석 지원 물성치 확보 측면에서 유용하게 적용되어지리라 사료된다.

• 한국결정성장학회지
• /
• 제33권5호
• /
• pp.174-180
• /
• 2023

본 연구는 백자와 청자 소지에 철/코발트 황하물의 안료를 시유하여 1250℃에서 소성한 도자기 표면의 상형성을 연구하였다. 시편의 특성은 X-선 회절분석기, 전계방사형 주사전자현미경, 에너지 분산형 엑스선분석기 및 UV-vis 분광계를 이용하였다. X-선 리트벨트 정밀화 분석으로 백자소지는 석영과 뮬라이트가, 청자소지는 뮬라이트와 plagioclase가 주 결정상이다. 백자와 청자소지에 철/코발트 황하물의 안료를 시유한 경우 백자는 스피넬상이 청자는 andradite 상의 이차상이 형성되었다. 시편 소지의 색상은 밝기인 L^* 값은 백자와 청자소지가 72.01, 60.92이고 백자가 청자소지 보다는 백색도가 높다. 철/코발트 황하물의 안료를 도포한 시편에서 백자와 청자 시편의 경우, L^* 값은 44.89, 52.27, a^* 값은 2.12, 1.40, b^* 값은 1.4 5, 13.79를 각각 보이고 있다. L^* 값은 백자소지에 안료를 도포한 시편에서 큰 변화가 있으며, b^* 값은 소지에 따라 크게 차이가 나는 것을 알 수가 있다. 이는 표면층에 생성되는 Fe₂O₃ 상과 andradite 결정상 생성과 밀접한 관련이 있다.