• 한국정밀공학회지
• /
• 제18권5호
• /
• pp.98-104
• /
• 2001

A dynamic fracture toughness test method with a chevron notched ceramic specimens is proposed. The notch angles of the chevron specimens were 90, 100$^{\circ}$and 110$^{\circ}$. Finite element analysis(FEA) were done to determine the geometrical properties of chevron-notch specimens according to notch angles. The static fracture toughness of the chevron notched alumina specimen was 3.8MP$\alpha$√m similar to that of the general fracture specimen with a precrack. Dynamic fracture toughness was 4.5 MP$\alpha$√m slightly higher than the static one. These research showed the possibility of the split Hopkinson pressure bar test method using the newly proposed chevron notched specimens to get the dynamic fracture toughness of extremely brittle materials such as ceramics.

• 한국세라믹학회지
• /
• 제35권12호
• /
• pp.1316-1322
• /
• 1998

The amount of VC and C/N ratio in Ti(CN) was varied to investigate the effect of VC addition on the mi-crostructural change in Ti(CN)-Ni system. As the amount of VC addition increases in Ti(C0.7N0.3)-20Ni sys-tem a complete solid solution was observed in Ti(C0.7N0.3)-20Ni-25VC system. It implies that the ratio of the dissolution rates of Ti(C0.7N0.3)to that of VC is nearly 2:1 at the sintering conditions used in this study. It was found from the experiments that the system composed of the Ti(C0.7N0.3) phase exhibits a rimless structure and relatively small amount of solid solution. That is among Ti(C0.7N0.3) phase exhibits a rimless structure and relatively small amount of solid solution. This is among Ti(C1-xNx) phases the dissolution rate of Ti(C0.3N0.7) is the lowest. Also fracture toughness(KIC) of the cermet was measured by indentation method. Attentions were paid to crack propagation path to look for a dominant fracture mode and to cor-relate it with fracture toughness values. The fracture toughness was relatively high with the addition of VC content. But the addition of a large VC content reduced the overall toughness of the cermet. This result is explained with the difference in fracture mode.

• 대한치과보철학회지
• /
• 제40권5호
• /
• pp.441-450
• /
• 2002

The purpose of this study was compare the fracture strength of the IPS Empress ceramic crown according to the occlusal depth (1.5mm, 2.0mm, 2.5mm) and axial inclination ($4^{\circ},\;8^{\circ},\;12^{\circ}$) of the lower second premolar. After 10 metal dies were made for each group, the IPS Empress ceramic crowns were fabricated and cemented with resin cement. The cemented crowns were mounted on the testing jig with inclination of 30 degrees and the universal testing machine was used to measure the fracture strength. The results of this study were as follows : 1. The fracture strength of the ceramic crown with 2.5mm depth and $12^{\circ}$ inclination was the highest (1284 N). Crowns of 1.5mm depth and $8^{\circ}$ inclination had the lowest strength (951 N). 2. There were no significant differences in the fracture strength by axial inclination of the same occlusal depth group. 3. Most fracture lines began at the loading area and extended through proximal surface perpendicular to the margin, irrespective of occlusal depth.

• 대한치과보철학회지
• /
• 제38권5호
• /
• pp.606-617
• /
• 2000

The purpose of this study was to measure the marginal fidelities and the fracture strength of IPS Empress $2^{(R)}\;and\;In-Ceram^{(R)}$ ceramic crowns. After constructed of 12 experimental dies for each group, ceramic crowns were fabricated on the metal master dies prepared on the maxillary right premolar Marginal gaps were measured on the specimen between the margin of each crown and finish-ing line of the metal master die by using stereo-microscope($SZ-ST^{(R)}$ Olympus, Japan) and all specimens were cemented on the metal master die with Bistite $II^{(R)}$ (Tokuyama soda Co, LTD., Japan) resin cement. Finally marginal gaps were measured again. To measure of the fracture strength, buccal incline on the functional cusp of specimens were loaded until the catastrophic failure occurred by using the AGS-1000 $D^{(R)}$(Shimadzu, Japan). The result of marginal fidelities and fracture strength were statistically analyzed with the SPSS version 8.0 programs. The results of this study were as follows : 1. No significant difference was found in the mean marginal fidelities and fracture strength between the IPS Empress $2^{(R)}\;and\;In-Ceram^{(R)}$. 2. In comparison of marginal fidelities between before and after cementation, there was significant difference(P<0.05). The IPS Empress 2 system was shown in this study that had good marginal fidelities and fracture strength compared to In-Ceram ceramics. Although this system was acceptable to clinical applications, the system still has to be considered long-term researches about marginal fidelities and fracture strength due to the lack of data about the clinical researches.

• 구강회복응용과학지
• /
• 제20권1호
• /
• pp.19-29
• /
• 2004

The purpose of this study was to compare the fracture strength of the IPS Empress ceramic crown according to the incisal reduction(2.0mm, 2.5mm, 3.0mm) and axial inclination ($4^{\circ}$, $8^{\circ}$, $12^{\circ}$) of the lower canine. After 10 metal dies were made for each group, the IPS Empress ceramic crowns were fabricated and each crown was cemented on each metal die with resin cement. The cemented crowns mounted on the testing jig were inclined 30 degrees and a universal testing machine was used to measure the fracture strength. The results of this study were as follows : 1. The fracture strength of the ceramic crown with 3.0mm depth and $12^{\circ}$ inclination was the highest(1377N). Crowns of 2.0mm depth and $4^{\circ}$ inclination had the lowest strength (731 N). 2. There were no significant differences of the fracture strength by axial inclination in same incisal reduction group. 3. The fracture mode of the crowns was similar. Most of fracture lines began at the loading area and extended through proximal surface perpendicular to the margin irrespective of incisal reduction.

• 대한치과보철학회지
• /
• 제41권1호
• /
• pp.48-60
• /
• 2003

The purpose of this study was to compare the fracture strength of the IPS Empress ceramic crown according to the occlusal depth (1.5mm, 2.0mm, 2.5mm) and axial inclination ($4^{\circ},\;8^{\circ},\;12^{\circ}$) of the lower First Molar. After 10 metal dies were made for each group, the IPS Empress ceramic crowns were fabricated and cemented with resin cement(Bistite resin cement, Tokuyama Soda Co. LTD., Japan). The cemented crowns were mounted on the testing jig with inclination of 30 degrees and the universal testing machine(Zwick Z020, Zwick, Germany)was used to measure the fracture strength. The results of this study were as follows : 1. The fracture strength of the ceramic crown with 2.5mm depth and $12^{\circ}$ inclination was the highest (1789 N). Crowns of 1.5mm depth and $4^{\circ}$ inclination had the lowest strength (1091 N). 2. There were no significant differences in the fracture strength by axial inclination of the same occlusal depth group. 3. Most fracture lines began at the loading area and extended through proximal surface perpendicular to the margin, irrespective of occlusal depth. Size of fragment was affected by the amount of occlusal reduction.

• The Journal of Advanced Prosthodontics
• /
• 제4권3호
• /
• pp.162-169
• /
• 2012

PURPOSE. Fracture of the veneering material of zirconia restorations frequently occurs in clinical situations. The purpose of this in vitro study was to compare the fracture strengths of zirconia crowns veneered with various ceramic materials by various techniques. MATERIALS AND METHODS. A 1.2 mm, $360^{\circ}$ chamfer preparation and occlusal reduction of 2 mm were performed on a first mandibular molar, and 45 model dies were fabricated in a titanium alloy by CAD/CAM system. Forty-five zirconia copings were fabricated and divided into three groups. In the first group (LT) zirconia copings were veneered with feldspathic porcelain by the layering technique. In the second group (HT) the glass ceramic was heat-pressed on the zirconia coping, and for the third group (ST) a CAD/CAM-fabricated high-strength anatomically shaped veneering cap was sintered onto the zirconia coping. All crowns were cemented onto their titanium dies with Rely $X^{TM}$ Unicem (3M ESPE) and loaded with a universal testing machine (Instron 5583) until failure. The mean fracture values were compared by an one-way ANOVA and a multiple comparison post-hoc test (${\alpha}$= 0.05). Scanning electron microscope was used to investigate the fractured interface. RESULTS. Mean fracture load and standard deviation was $4263.8{\pm}1110.8$ N for Group LT, $5070.8{\pm}1016.4$ for Group HT and $6242.0{\pm}1759.5$ N for Group ST. The values of Group ST were significantly higher than those of the other groups. CONCLUSION. Zirconia crowns veneered with CAD/CAM generated glass ceramics by the sintering technique are superior to those veneered with feldspathic porcelain by the layering technique or veneered with glass ceramics by the heat-pressing technique in terms of fracture strength.

• 대한치과보철학회지
• /
• 제34권1호
• /
• pp.169-186
• /
• 1996

The purpose of this study was to investigate the mechanical properities and biocompatibility with crystallization temperature and time of a bioactive glass-ceramic system $41.4wt%SiO_{2}-35.0wt%CaO-3.0wt%MgO-12.0wt%P_{2}O_{5}-8.6wt%Al_{2}O_{3}$ with same molar percent of $Al_{2}O_{3}\;and\;P_{2}O_{5}$. The crystallization behaviors were investigated with DTA, XRD and SEM. Fracture toughness with the change of crystallization temperature and time was measured by indentation fracture method. Also, biocompatibility was evaluated by culture of mouse fibroblast cell line L929. The results obtained were as follows ; 1. The major crystalline phases were apatite and anorthite, and relative intensity of anorthite phase was increased at $1004^{\circ}C$. 2. The hardness and fracture toughness were gradually increased with the increase in ceraming temperature to $1004^{\circ}C$. 3. When the glass ceramic was heat-treated for 4 hours at ceraming temperature of $1004^{\circ}C$, hardness and fracture toughness showed the maximum values $578.84k/mm^2\;and\;2.07MPa\;m^{1/2}$, respectively. 4. The growth rate and cytotoxic of L929 fibroblast cells for bioactive glass ceramic were better than those of stainless steel and titanium.

• 대한치과보철학회지
• /
• 제46권3호
• /
• pp.298-306
• /
• 2008

STATEMENT OF PROBLEM: Effect of surface treatment of ceramic under loading does not appear to have been investigated. PURPOSE: The aim of this study was to investigate the effect of surface treatment of esthetic ceramic, which is performed to increase the bonding strength, on the fracture stress under controlled cyclic loading condition. MATERIAL AND METHODS: Sixty 1.0 mm-thick specimens were made from Mark II Vitablocs (Vita Zahnfabrik, Germany) and divided into 3 groups: polished (control), sandblasted, and etched. Specimens of each group were bonded to a dentin analog material base including micro-channels to facilitate the flow of water to the bonding interface. Bonded ceramics were cyclically loaded with a flat-end piston in the water (500,000 cycles, 15Hz). Following completion of cyclic loading, specimens were examined for subsurface crack formation and subsequent stress was determined and loaded to next specimen by the staircase method according to the crack existence. RESULTS: There were significant differences of mean fatigue limit in the sandblasted (222.86 ${\pm}$ 23.42 N) and etched group (222.86 ${\pm}$ 14.16 N) when compared to polished group (251.43 ${\pm}$ 10.6 N) (P<.05; Wald-type pair-wise comparison and post hoc Bonferroni test). Of cracked specimens, surface treated group showed longer crack propagation after 24 hours. All failures originated from the radial cracking without cone crack. Fracture resistance of this study was very low and comparable to failure load in the oral cavity. CONCLUSION: Well controlled cyclic loading could induce clinically relevant cracks and fracture resistance of Mark II ceramic was relatively low applicable only to anterior restorations. Surface treatment of inner surface of feldspathic porcelain in the matsicatory area could influence lifetime of restorations.

• 한국세라믹학회지
• /
• 제38권12호
• /
• pp.1080-1084
• /
• 2001

Alumina-based nanocomposites have improved mechanical properties such as hardness, fracture toughness and fracture strength compared to monolithic ceramics. In this study, alumina with 5 vol% of nanosized SiC was sintered by a hot pressing technique at 1600$\^{C}$, 30 MPa for 1h in an argon gas atmosphere. Microstructures and mechanical properties in alumina-SiC nanocomposite were investigated. Moreover, tribological properties in air and water were compared each other. Relationships of wear properties with mechanical properties such as hardness, strength, and fracture toughness as well as microstructure were studied. Based on experimental results it was found that nanosized SiC retarded grain growth of matrix alumina. Mechanical properties such as hardness, fracture toughness and strength were improved by the addition of nanosized SiC in alumina. Improved mechanical properties resulted in increased sliding wear resistance. Tribological behavior of nanocomposites in water seemed to be governed by abrasive wear.