• Journal of the Korean Ceramic Society
• /
• v.56 no.2
• /
• pp.173-177
• /
• 2019

Thermal properties of a SiO₂-B₂O₃-BaO ternary glass system depending on compositional change of BaO have been examined to find a proper sealing material for reversible oxide cells. Glass transition temperature and thermal expansion coefficients increased simultaneously up to 55 mol% of BaO content. The structural role of BaO with regard to the thermal properties has been discussed on the basis of Raman spectroscopy results. Flowability of the glass at sealing temperature has been examined with packed glass powders of 12 mm diameter along with a high temperature optical microscope. The practical sealing property of the glass was also examined with YSZ coated with NiO-yittria stabilized zirconia (NiO-YSZ) and it showed good adhesion without noticeable reaction with NiO-YSZ layer.

• Journal of the Korean Ceramic Society
• /
• v.25 no.1
• /
• pp.59-65
• /
• 1988

To develop porous glass membranes used for a effective membrane-separation process, porous glasses and glass membranes were prepared from the sodium borosilicate parent glass by the phaseseparation technique and effects of heat-treatment and leaching conditions on their characteristics were investigated. The crack-free glass membranes could be fabricated from the 9.4 Na2-O-30.7 B2O3-59.2 SiO2-0.7 Al2O3(wt%) parent glass by heat-treatment at the lower temperature(550-570$^{\circ}C$) and for longer than 45 hrs for the phase separation, followed by leaching with 3N-HCl＋60% ethylene glycol solution at 90$^{\circ}C$ over 25 hrs. Porous glasses prepared in this work showed large specific surface areas(400㎡/g) and narrow pore size distribution with the mean pore radius of 14${\AA}$ enough for the application as reverse osmosis membranes. The salt-rejection efficiency and product-flux of the glass membranes heat-treated at 570$^{\circ}C$ for 80 hrs were found to be 51.8% and 270cc/㎡. hr, respectively. This result suggests that the porous glass membranes fabricated in this study could be applied for the reverse osmosis process.

• Journal of the Korean Ceramic Society
• /
• v.54 no.6
• /
• pp.484-491
• /
• 2017

Chalcogenide glasses have been investigated in their thermodynamic, structural, and optical properties for application in various opto-electronic devices. In this study, the $Sb_{20}Se_{80-x}Ge_x$ with x = 10, 15, 20, and 25 were selected to investigate the glass stability according to germanium ratios. The thermal, structural, and optical properties of these glasses were measured by differential scanning calorimetry (DSC), X-ray diffraction (XRD), and UV-Vis-IR Spectrophotometry, respectively. The DSC results revealed that $Ge_{20}Sb_{20}Se_{60}$ composition showing the best glass stability theoretically results due to a lower glass transition activation energy of 230 kJ/mol and higher crystallization activation energy of 260 kJ/mol. The structural and optical analyses of annealed thin films were carried out. The XRD analysis reveals obvious results associated with glass stabilities. The values of slope U, derived from optical analysis, offered information on the atomic and electronic configuration in Urbach tails, associated with the glass stability.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.221-243
• /
• 1997

The objective of this study was to characterize the mechanical properties of $Y_{2}O_{3}$-containing glass infiltrated ceramic core material, which was made by pressureless powder packing method. A pure alumina powder with a grain size of about $4{\mu}m$ was packed without pressure is silicon mold to form a bar shaped sample, and applied PVA solution as a binder. Samples were sinterd at $1350^{\circ}C$ for 1 hour. After cooling, $Y_{2}O_{3}$-containing glass($SiO_{2},\;Y_{2}O_{3},\;B_{2}O_{3},\;Al_{2}O_{3}$, ect) was infiltrated to the sinterd samples at $1300^{\circ}C$ for 2 hours and cooled. Six different proportions $Y_{2}O_{3}$ of were used to know the effect of the mismatch of the thermal expansion coefficient between alumina powder and glass. The samples were ground to $3{\times}3{\times}30$ mm size and polished with $1{\mu}m$ diamond paste. Flexural strength, fracture toughness, hardness and other physical properties were obtained, and the fractured surface was examined with SEM and EPMA. Ten samples of each group were tested and compared with In-Ceram(tm) core materials of same size made in dental laboratory. The results were as follows : 1. The flexural strengths of group 1 and 3 were significantly not different with that of In-Ceram, but other experimental groups were lower than In-Ceram. 2. The shrinkage rate of samples was 0.42% after first firing, and 0.45% after glass infiltration. Total shrinkage rate was 0.87%. 3. After first firing, porosity rate of experimental groups was 50%, compared with 22.25% of In-Ceram. After glass infiltration, porosity rate of experimental groups was 2%, and 1% in In-Ceram. 4. There was no statistical difference in hardness between two materials tested, but in fracture toughness, group 2 and 3 were higher than In-Ceram. 5. The thermal expansion coefficients of experimental groups were varied to $4.51-5.35{\times}10^{-6}/^{\circ}C$ according to glass composition, also the flexural strengths of samples were varied. 6. In a view of SEM, many microparticles about $0.5{\mu}m$ diameter and $4{\mu}m$ diameter were observed in In-Ceram. But in experimental group, the size of most particles was about $4{\mu}m$, and a little microparticles was observed. The results obtained in this study showed that the mismatch of the thermal expansion coefficients between alumina powder and infiltrated glass affect the flexural strength of alumin/glass composite. The $Y_{2}O_{3}$-containing glass infiltrated ceramic core made by powder packing method will takes less time and cost with sufficient flexural strength similar to all ceramic crown made with slip casting technique.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.6
• /
• pp.263-271
• /
• 2015

Commercial AR(Alkali Resistant)-glass fiber has a good chemical resistant property, but also has a problem of difficulty in fiberizing process because of high viscosity in melted glass compare with E-glass fiber which is the most widely used for reinforced fiber of composite materials. In this study, we fabricated AR-glass fiber with low zirconia contents compare with commercial AR-glass fiber relatively, and measured properties against E-glass fiber. We obtained transparent clear glass with zirconia contents of 0.5~16 wt% by melting at $1600^{\circ}C$ for 2 hours. These AR-glass samples had high visible transmittance of 89~90 %, softening temperature of $703{\sim}887^{\circ}C$. And softening temperatures of them were increased according to the increasing zirconia contents. Compare with E-glass, AR-glass contains 4 wt% zirconia has different value of $-94^{\circ}C$ in softening temperature, $+68^{\circ}C$ at Log3 temperature and $-13^{\circ}C$ at Log5 temperature in viscosity. We could verify good alkali resistant property of the AR-glass fiber with SEM after dipping in alkali solution for 48~72 hours, and also high tensile strength, 1.7 times compare with E-glass fiber at 48 hours and 2.2 times at 72 hours. We conclude that this AR-glass fiber can be widely used as general alkali resistant glass fiber because of easy manufacturing condition and good properties even though it has low zirconia contents.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.5
• /
• pp.256-261
• /
• 2009

Hydrophilic and transparent $TiO_2$ thin film was fabricated by sol-gel method and the properties of contact angle, surface morphology, and transmittance were measured. In addition, surfactant Tween 80 was used for increasing the hydrophilic property of thin film. When the contents of Tween 80 in $TiO_2$ solution was 0, 10, 30, 50wt%, the contact angles of $TiO_2$ thin film were $41.4^{\circ}$, $18.2^{\circ}$, $16.0^{\circ}$, $13.2^{\circ}$, respectively. Fabricated $TiO_2$ thin film showed the photocatalytic property that decomposed methylene blue and decreased the absorbance of solution after UV irradiation. $TiO_2$ thin films fabricated with the solution of 30 wt% Tween 80 were deposited on glass (bare), antimony tin oxide (ATO), fluorine tin oxide (FTO), indium tin oxide (ITO) coated glass substrates, and the contact angle and transmittance of thin film was measured. The contact angles of thin films deposited on four substrates were $16.2\sim27.1^{\circ}$ and was decreased to the range of $13.2\sim17.6^{\circ}$ after UV irradiation, Especially, the thin films coated on ATO and FTO glass substrate showed high transmittance of 74.6% in visible range, respectively, and low transmittance of 54.2% and 40.4% in infrared range, respectively.

• The Korean Journal of Ceramics
• /
• v.5 no.4
• /
• pp.336-340
• /
• 1999

Glasses in the system $CaO-TiO_2-SiO_2-Al_2O_3-ZrO_2-B_2O_3$ were investigated to find the glass seal compositions suitable for use in the planar solid oxide fuel cell (SOFC). Glass-ceramics prepared from the glasses by one-stage heat treatment at $1,000^{\circ}C$ showed various thermal expansion coefficients (i,e., $8.6\times10^{-6^{\circ}}C^{-1}$ to $42.7\times10^{-6^{\circ}}C^{-1}$ in the range 25-$1,000^{\circ}C$) due to the viscoelastic response of glass phase. The average values of contact angles between the zirconia substrate and the glass particles heated at 1,000-$1,200^{\circ}C$ were in the range of $131^{\circ}\pm4^{\circ}$~$137^{\circ}\pm9^{\circ}$, indicating that the glass-ceramic was in partial non-wetting condition with the zirconia substrate. With increasing heat treatment time of glass samples from 0.5 to 24 h at $1,100^{\circ}C$, the DC electrical conductivity of the resultant glass-ceramics decreased from at $800^{\circ}C$. Isothermal hold of the glass sample at $1100^{\circ}C$ for 48h resulted in diffusion of Ca, Si, and Al ions from glass phase into the zirconia substrate through the glass/zirconia bonding interface. Glass phase and diffusion of the moving ion such as $Ca^{2+}$ in glass phase is responsible for the electrical conduction in the glass-ceramics.

• Journal of the Semiconductor & Display Technology
• /
• v.21 no.3
• /
• pp.57-62
• /
• 2022

The plasma resistance of multi-component glasses containing La, Gd, Ti, Zn, Y, Zr, Nb, and Ta was analyzed in this study. The plasma etching was performed via inductively coupled plasma-reactive ion etching (ICP-RIE) using CF₄/O₂/Ar mixed gas. After the reaction, the glass with a low fluoride sublimation temperature and high content of P, Si, and Ti elements showed a high etching rate. On the other hand, the glass containing a high fluoride sublimation temperature component such as Ca, La, Gd, Y, and Zr exhibited high plasma resistance because the etch rate was lower than that of sapphire. Glass with low plasma resistance increased surface roughness after etching or nanoholes were formed on the surface, but glass with high plasma resistance showed little change in surface microstructure. Thus, the results of this study demonstrate the potential for the development of plasma-resistant glasses (PRGs) with other compositions besides alumino-silicate glasses, which are conventionally referred to as plasma-resistant glasses.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.3
• /
• pp.259-268
• /
• 2007

purpose: This study was to evaluate the shear bond strength of Lithium Disilicate Glass-Ceramic by removable method of temporary cement on the abutment tooth. Material and Method: Sixty molar teeth of human with the occlusal surface up were mounted in acrylic resin blocks. The 45 specimens were prepared to exposure dentin by diamond bur and the eugenol-containing temporary cement($Cavitec^{TM}$ ($KERR^{(R)}$, U.S.A)was applied to the dentin surfaces. After initial removal of the cement with a dental explorer, the specimens were divided into 4 groups of 15 specimens each. The dentin surfaces of the specimens were treated by rotary instrument with as follow pastes: $Zircate^{(R)}$ prophy paste(Dentsply, U.S.A), Radent Prophy Paste(Pascal company,inc. U.S.A), and Dental pumice(Wip mix corporation,U.S.A). An adhesive resin luting agent(Variolink $II^{(R)}$, Ivoclar Vivadent, Leichtenstein) including Monobond-S and $Excite^{(R)}$ was applied to all specimens. The ceramic specimens were made with an A1 ingot of IPS Empress $II^{(R)}$ (Ivoclar Vivadent, Leichtenstein). After the specimens were stored in distilled water for 48hr, the shear bond strength(MPa) was measured by a Universal testing machine(Zwick 145641, Zwick, Germany) at a 1mm/min cross-head speed. The data were statistically analyzed by one-way ANOVA and Duncan's multiple range test. Results: In all group, there were no significant differences in comparison with the control group(p>0.05). The pattern of most failure showed the mixed type of cohesive and adhesive failure. Conclusion: Resin bond strength of IPS Empress $II^{(R)}$ was not affected by removal method of the temporary cement.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.6
• /
• pp.449-456
• /
• 2016

PURPOSE. This in vitro study evaluated the effects of four different cements on the color attributes of a zirconia ceramic. MATERIALS AND METHODS. 40 zirconia ceramic disk specimens (0.5 mm thickness, 10 mm diameter, 0.1 mm cement space) were fabricated by a computer-aided design and computer-aided manufacturing system. The specimens were divided into 4 groups of 10 specimens and cemented to composite substrates using four different cements including: Glass Ionomer, Panavia F2.0, Zinc Phosphate, and TempBond. The $L^*$, $a^*$, and $b^*$ color attributes of the specimens were measured before and after cementation by a spectrophotometer. Additionally, ${\Delta}E$ values were measured to determine color changes for the groups and then compared with the perceptional threshold of ${\Delta}E=3.3$. Repeated Measures ANOVA, Tukey Post Hoc, Bonferroni, One-way ANOVA, and One-sample t-test tests were used to analyze the data. All tests were carried out at the 0.05 level of significance. RESULTS. Statistically significant differences were detected in the ${\Delta}E$ values for Zinc Phosphate (P<.0001) and TempBond (P<.0001) groups. However, there were no statistically significant differences in this respect for Glass Ionomer (P=.99) and Panavia F2.0 (P=1) groups. The means and standard deviations of the ${\Delta}E$ values for Glass Ionomer, Panavia F2.0, Zinc Phosphate, and Tempbond groups were $2.11{\pm}0.66$, $0.94{\pm}0.39$, $5.77{\pm}0.83$, and $7.50{\pm}1.16$ Unit, respectively. CONCLUSION. Within the limitations of this study, it was concluded that Zinc Phosphate and Tempbond cements affected the color attributes of the tested zirconia ceramic beyond the perceptional threshold. However, Glass Ionomer and Panavia F2.0 cements created acceptable color changes.