• Journal of the Korean Vacuum Society
• /
• v.9 no.1
• /
• pp.30-35
• /
• 2000

Indium-Tin Oxide (ITO) thin films were deposited on the commercial glass substrate by rf-magnetron sputtering. The ITO films with the thickness of 2,000~2,400 $\AA$ were prepared by changing the oxygen partial pressures of 2, 3, and 5%, as well as by changing the substrate temperature of $300^{\circ}C$ and $500^{\circ}C$. spectrophotometer, XRD, SEM, AFM, 4-point probe and Hall effect system were employed to characterize the ITO films. The optimum deposition conditions were the substrate temperature of $500^{\circ}C$ and oxygen partial pressure of 2-3%. At theses conditions, the ITO film showed the transmittance of 91%, the resistivity of $5.4\times10^{-3}\Omega$cm, the carrier concentration of $1.0\times10^{19}\textrm{cm}^{-3}$, and the carrier mobility of 150$\textrm{cm}^2$/Vsec. In XRD spectra, the (222) and (400) $In_2O_3$ planes were dominant under the optimum deposition conditions When the substrate was cleaned only by the method of ultrasonic cleaning without both pre-annealing and chemical treatment of the substrate, the ITO film exhibited the transmittance of 86%, the carrier concentration of $5.4\times10^{19}\textrm{cm}^{-3}$ and the mobility of 24$\textrm{cm}^2$/Vsec.

• Journal of Advanced Marine Engineering and Technology
• /
• v.24 no.6
• /
• pp.61-69
• /
• 2000

Indium-Tin Oxide (ITO) films were prepared on the commercial glass substrate by the Magnetron Sputtering method. The target was a 90wt.% $In_2O_3$-10wt.% $SnO_2$with 99.99% purity. The ITO films deposited by changing the partial pressure of oxygen gas ($O_2$/(Ar+$O_2$)) of 2, 3 and 5% as well as by changing the substrate temperature of $300^{\circ}C$ or $500^{\circ}C$. The influence of substrate pre-annealing and pre-cleaning on the quality of ITO film were examined, in which the substrate temperature was $500^{\circ}C$ and oxygen partial pressure was 3%. The characteristics of films were examined by the 4-point probe, Hall effect measurement system, SEM, AFM, Spectrophotometer, and X-ray diffraction. The optimum ITO films have been obtained when the substrate temperature is $500^{\circ}C$ and oxygen partial pressure is 3%. At optimum condition, the film showed transmittance of 81%, sheet resistivity of $226\Omegatextrm{cm}^2$, resistivity($\rho$) of $5.4\times10^{-3}\Omega$cm, carrier concentration of $1.0\times10^{19}cm^{-3}$, and carrier mobility of $150textrm{cm}^2$Vsec. From XRD spectrum, c(222) plane was dominant in the case of substrate temperature at $300^{\circ}C$, without regarding to oxygen partial pressure. However, in the case of substrate temperature at $500^{\circ}C$, c(400) plane was grown together with c(222) plane, only for oxygen partial pressure of 2 and 3%. In both case of chemical and ultrasonic cleaning without pre-annealing the substrate, it showed much almost same sheet resistivity, resistivity($\rho$), transmittance, carrier concentration, and carrier mobility. In case of $500^{\circ}C$/60min pre-annealing before ITO film deposited, both transimittance and carrier mobility are better than no pre-annealing, because pre-annealing is supposed to remove alkari ions diffusion from substrate. ITO film deposited on the Corning 0080 sybstrate showed a little bit better sheet resistivity, resistivity($\rho$), transimittance, carrier concentration than the film deposited on commercial glass. But no differences between Corning substrate and pre-annealed commercial glass substrate are found.

• Journal of the Korean institute of surface engineering
• /
• v.52 no.6
• /
• pp.342-349
• /
• 2019

Titanium nitride(TiN) thin films have been deposited on PEN(Polyethylene naphthalate) substrate by reactive RF(13.56 MHz) magnetron sputtering in a 25% N₂/Ar mixed gas atmosphere. The pulsed DC bias voltage of -50V on substrates was applied with a frequency of 350 kHz, and duty ratio of 40%(1.1 ㎲). The effects of pulsed DC substrate bias voltage on the crystallinity, color, electrical properties of TiN_x films have been investigated using XRD, SEM, XPS and measurement of the electrical properties such as electrical conductivity, carrier concentration, mobility. The deposition rates of TiN_x films was decreased with application of the pulsed DC substrate bias voltage. The TiN_x films deposited without and with pulsed bias of -50V to substrate exhibits gray and gold colors, respectively. XPS depth profiling revealed that the introduction of the substrate bias voltage resulted in decreasing oxygen concentration in TiN_x films, and increasing the electrical conductivities, carrier concentration, and mobility to about 10 times, 5 times, and 2 times degree, respectively.

• Journal of the Korean Vacuum Society
• /
• v.12 no.4
• /
• pp.269-274
• /
• 2003

The electrical, optical and structural properties of ZnNiO thin _ films deposited on Si substrates using rf-magnetron sputtering method have been investigated before and after the thermal annealing processes. The crystallinity of the ZnNiO thin film become degraded with increasing the Ni contents. This is mainly because the lattice of the thin film was expanded due to the oxygen-deficient conditions. Concerning the electrical properties of the thin film, the carrier concentration increases ($6.81\times10^{14}\textrm{cm}^{-2}$) and Hall mobility decreases (36.3 $\textrm{cm}^2$/Vㆍs) with higher doping concentration of Ni. However, the carrier concentration and Hall mobility became low ($1.10\times10^{14}\textrm{cm}^2$ and high (209.6 $\textrm{cm}^2$/Vㆍs), respectively, after the thermal annealing process at $1000 ^{\circ}C$. We also observed a strong luminescene center peaking at 546 nm in photoluminescence spectra, which was caused by a deep level center in the ZnO band gap with oxygen deficient ZnNiO structure.

• Polymer(Korea)
• /
• v.25 no.5
• /
• pp.719-727
• /
• 2001

Recently it was found that the charge carrier transport properties are significantly enhanced due to effective intermolecular $\pi$-orbital overlapping and low disorder of hopping sites caused by self-organization of liquid crystal molecules. In this study, the xerographic properties of a double-layer photoconductor doped with nematic liquid crystal, 4-pentyl-4'-cyanoterphenyl (5CT), as a charge-carrier transport material to enhance the charge-tarrier mobility were investigated. From the results of measured surface voltage properties for the photoconductor doped with various concentrations of liquid crystal, 5CT, the initial voltage was found to increase with the concentration of 5CT and the dark decay decreased with the concentration of 5CT. The highest sensitivity was obtained at a specific concentration, 40wt% 5CT. The fluorescence behavior of the carrier transport layer (CTL) was also investigated. It was found that the charge-carrier transport properties of the organic photoconductor depend on the charge-carrier transport properties of the complex. The TNF : 5CT (40 wt%) and OXD : 5CT (40 wt%)samples showed the highest sensitivity because the greatest charge transport complex was termed between the charge-carrier transport materials in these samples.

• Korean Journal of Materials Research
• /
• v.15 no.8
• /
• pp.518-520
• /
• 2005

Effects of the $O_2/Ar$ flow ratio in the sputtering process on the crystallinity, surface roughness, carrier concentration, carrier mobility, and optical properties of Al-doped ZnO thin films deposited on sapphire (001) substrates by RF magnetron sputtering were investigated. XRD spectra showed a preferred orientation along the c-axis and a minimum FWHM of the (002) XRD intensity peak for the $O_2/Ar$ flow ratio of 0.5. The (101)peak also appeared and the degree of preferred orientation decreased as the $O_2/Ar$ flow ratio increased from 0.5 to 1.0. AFM analysis results showed that the surface roughness was lowest at the $O_2/Ar$ flow ratio of 0.5 and tended to increase owing to the increase of the grain size as the $O_2/Ar$ flow ratio increased further. According to the Hall measurement results the carrier concentration and carrier mobility of the fan decreased and thus the resistivity increased as the $O_2/Ar$ flow ratio increased. The transmittance of the ZnO:Al film deposited on the glass substrate was characteristic of a standing wave. The transmittance increased as the $O_2/Ar$ flow ratio in-RF magnetron sputtering increased up to 0.5. Considering the effects of the $O_2/Ar$ flow ratio on the surface roughness, electrical resistivity and transmittance properties of the ZnO:Al film the optimum $O_2/Ar$ flow ratio was 0.5 in the RF magnetron sputter deposition of the ZnO:Al film.

• Journal of the Semiconductor & Display Technology
• /
• v.12 no.4
• /
• pp.49-54
• /
• 2013

In this study, we have investigated the effect of the substrate temperature and oxygen flow rate on the characteristics of IZO thin films for the OLED (organic light emitting diodes) devices. For this purpose, IZO thin films were deposited by RF magnetron sputtering at room temperature and $300^{\circ}C$ with various $O_2$ flow rate. In order to investigate the influences of the oxygen, the flow rate of oxygen in argon mixing gas has been changed from 0.1sccm to 0.5sccm. IZO thin films deposited at room temperature show amorphous structure, whereas IZO thin films deposited at $300^{\circ}C$ show crystalline structure having an (222) preferential orientation regardless of $O_2$ flow rate. The electrical resistivity of IZO film increased with increasing flow rate of $O_2$ under Ar+$O_2$. The change of electrical resistivity with increasing flow rate of $O_2$ was mainly interpreted in terms of the charge carrier concentration rather than the charge carrier mobility. The electrical resistivity of the amorphous-IZO films deposited at R.T. was lower than that of the crystalline-IZO thin films deposited at $300^{\circ}C$. The change of electrical resistivity with increasing substrate temperature was mainly interpreted in terms of the charge carrier mobility rather than the charge carrier concentration. All the films showed the average transmittance over 85% in the visible range. The current density and the luminance of OLED devices with IZO thin films deposited at room temperature in 0.1sccm $O_2$ ambient gas are the highest amongst all other films. The optical band gap energy of IZO thin films plays a major role in OLED device performance, especially the current density and luminance.

• Journal of the Semiconductor & Display Technology
• /
• v.12 no.2
• /
• pp.33-37
• /
• 2013

In this study, we have investigated the effect of the substrate temperature and hydrogen flow rate on the characteristics of IZO thin films for the organic light emitting diodes (OLED) devices. For this purpose, IZO thin films were deposited by RF magnetron sputtering at room temperature and $300^{\circ}C$ with various $H_2$ flow rate. In order to investigate the influences of the oxygen, the flow rate of hydrogen in argon mixing gas has been changed from 0.1sccm to 0.9sccm. IZO thin films deposited at room temperature show amorphous structure, whereas IZO thin films deposited at $300^{\circ}C$ show crystalline structure having an (222) preferential orientation regardless of $H_2$ flow rate. The electrical resistivity of IZO film decreased with increasing flow rate of $H_2$ under Ar+$H_2$. The change of electrical resistivity with increasing flow rate of $H_2$ was mainly interpreted in terms of the charge carrier concentration rather than the charge carrier mobility. The electrical resistivity of the amorphous-IZO films deposited at R.T. was lower than that of the crystalline-IZO thin films deposited at $300^{\circ}C$. The increase of electrical resistivity with increasing substrate temperature was interpreted in terms of the decrease of the charge carrier mobility and the charge carrier concentration. All the films showed the average transmittance over 83% in the visible range.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.7
• /
• pp.527-534
• /
• 1998

Thin film deposition of InN, which is a less-studied III-nitride compound semiconductor because of the difficulty if crystal growth, was performed by rf reactive sputtering method using In target and $N_2$reactive gas. The structrual, electrical, and optical properties of the produced films were measured and disussed according to the sputtering parameters such as deposition pressure, rf power, and substrate temperature. From the result of deposition pressure, rf power, and substrate temperature, we could obtain optimal conditions of 5m Torr, 60W, $60^{\circ}C$ for preparing InN thin film with high crystallinity, low carrier concentration, and high Hall mobility. The carrier concentration, Hall mobility, and optical bandgap of the fabricated InN thin films at optimal condition were $6.242\times10^{18}cm^{-3}, 212.526cm^2/V\cdot$ｓ, and 1.912eV, respectively.

• Journal of the Semiconductor & Display Technology
• /
• v.11 no.4
• /
• pp.25-30
• /
• 2012

In this study, we have investigated the effect of the substrate temperature and oxygen flow rate on the characteristics of IZO thin films for the organic light emitting diodes (OLED) devices. For this purpose, IZO thin films were deposited by RF magnetron sputtering at room temperature and $300^{\circ}C$ with various $O_2$ flow rate. In order to investigate the influences of the oxygen, the flow rate of oxygen in argon mixing gas has been changed from 0.1sccm to 0.5sccm. IZO thin films deposited at room temperature show amorphous structure, whereas IZO thin films deposited at $300^{\circ}C$ show crystalline structure having an (222) preferential orientation regardless of $O_2$ flow rate. The electrical resistivity of IZO film increased with increasing flow rate of $O_2$ under $Ar+O_2$. The change of electrical resistivity with increasing flow rate of $O_2$ was mainly interpreted in terms of the charge carrier concentration rather than the charge carrier mobility. The electrical resistivity of the amorphous-IZO films deposited at R.T. was lower than that of the crystalline-IZO thin films deposited at $300^{\circ}C$. The change of electrical resistivity with increasing substrate temperature was mainly interpreted in terms of the charge carrier mobility rather than the charge carrier concentration. All the films showed the average transmittance over 83% in the visible range.