Abstract
Recently it was found that the charge carrier transport properties are significantly enhanced due to effective intermolecular $\pi$-orbital overlapping and low disorder of hopping sites caused by self-organization of liquid crystal molecules. In this study, the xerographic properties of a double-layer photoconductor doped with nematic liquid crystal, 4-pentyl-4'-cyanoterphenyl (5CT), as a charge-carrier transport material to enhance the charge-tarrier mobility were investigated. From the results of measured surface voltage properties for the photoconductor doped with various concentrations of liquid crystal, 5CT, the initial voltage was found to increase with the concentration of 5CT and the dark decay decreased with the concentration of 5CT. The highest sensitivity was obtained at a specific concentration, 40wt% 5CT. The fluorescence behavior of the carrier transport layer (CTL) was also investigated. It was found that the charge-carrier transport properties of the organic photoconductor depend on the charge-carrier transport properties of the complex. The TNF : 5CT (40 wt%) and OXD : 5CT (40 wt%)samples showed the highest sensitivity because the greatest charge transport complex was termed between the charge-carrier transport materials in these samples.
유기광도전체에 있어서의 액정은 종래의 분자 배향성을 가지지 않는 비정성 고체계와는 달리 분자 배향성을 가지기 때문에 분자 사이의 질서도가 높아지게 되고, charge-carrier의 hopping을 방해하는 hopping site의 공간적인 틈이 작아져 고 이동도의 특성을 가질수 있다. 본 연구에서는 유기광도전체의 전하 수송층에 액정5CT를 혼합하여, charge-carrier수송특성에 있어서의 액정5CT의 영향을 관찰하였다. 액정5CT를 함유한 유기광도전체는 액정의 혼합비가 증가함에 따가 초기전위는 증가하였으며, 암감쇄는 감소하는 경향을 나타내었다. 감도는 5CT를 TNF와 OXD 각자에 대하여 40 wt%로 혼합한 시료의 경우에 가장 우수하게 나타났다. 형광거동을 관찰한 결과, 이는 전하수송재료와 액정5CT의 전하 수송착체에 의한 것으로, 액정5CT를 TNF와 OXD 각각에 대하여 40 wt%로 혼합한 시료의 경우가 다른 시료에 비해 전하 수송착체가 가장 잘 형성되어, 성공을 잘 수송하기 때문으로 나타났다.