• Journal of the Korean Applied Science and Technology
• /
• v.24 no.3
• /
• pp.272-277
• /
• 2007

Catalytic activity changes of perovskite catalysts were examined with their A-site substitution. For the preparation of catalysts, Mn was used for B-site component and La, Ce, Sr, Ba, Ca, Ag were used for A-site component of the perovskite $catalysts(ABO_3)$ The effect of calcination temperature on methane combustion and perovskite structure was also investigated. The surface area and adsorbed oxygen species were tested with BET apparatus and $O_2-TPD$, respectively. Perovskite catalysts whose A-site was partially substituted needed higher calcination temperature than un-substituted one to form the perovskite structure. From $O_2-TPD$ experiment, it was found that methane combustion activity was directly related to the oxygen desorbing ability of the catalysts. The prepared catalyst(LM-7) was stable at $600^{\circ}C$ for 72 hours of reaction.

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.103-107
• /
• 2009

$Bi_2Sr_2Ca_1Cu_2O_x$(BSCCO 2212) superconductors for current lead were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted at $1200^{\circ}\C$ in a resistance furnace using a Pt crucible and poured in a rotating cylindrical mold preheated at $550^{\circ}\C$ for 2 hour. The solidified BSCCO-2212 samples were heat-treated by partial melting process in oxygen atmosphere. The current-voltage curves at 77 K of the samples were obtained by transport measurement, and the microstructure was investigated by scanning electron microscope. The $J_c$ values at 77 K of the tubes partially melted at $840^{\circ}C,\;860^{\circ}C\;and\;880^{\circ}C$ were 492, 430 and 398 $A/cm^2$, respectively. It was observed that the plate-like grains in BSCCO 2212 tube was more developed in the sample heat-treated at $840^{\circ}C$. It was found that the critical current of the BSCCO 2212 samples was dependent on the partial melting schedule regarding the grain shape and size of the BSCCO 2212.

• Progress in Superconductivity and Cryogenics
• /
• v.1 no.2
• /
• pp.1-7
• /
• 1999

we evaluated the effects of joining process such as contact method. shape of joined area and pressure on the electrical and mechanical properties of Bi-2223 superconducting tape, Specifically. the current capacity of the jointed tape was measured as a function of uniaxial pressure. and the thermal shock, bonding strength and the thermal of the tape were evaluated and correlated to the microstructural evolution. It was observed that the current capacity was significanrly dependent on the uniaxial pressure The jointed tape, fabricated with a pressure of 1,000-1,600 Mpa. showed the highest value of current capacity results from improvements in core density, contacting area and grain alignment, ect. In addition, the strength of jointed tape was measured to be 86 Mpa, which is about 88% of the unjoined ape's strength. The irreversible strain($\varepsilon$irrev) for the jointed tape was measured to be 0.1%, smaller than that of unjoined tape ($\varepsilon$irrev= 0.3%). The decrease in the strength and irreversible strain for jointed tape is believed to be due to the irregular geometry/morphology of the transition area of the tape.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1218-1221
• /
• 2004

Bi2212 superconducting thin films fabricated by using the ion Beam Sputtering Method. As a result, although the composition of Bi2212 was set up, the phase of Bi2201, Bi2212 and Bi2223 was formed. The formation area of these stable phases is indicated as inclined line in the direction of the right lower end from the Arrhenius plot of the substrate temperature-oxidation gas pressure, and are distributed in very small area. The activation energy for the phase transformation from the Bi2201 to the Bi2212 is estimated in terms of the Avrami equation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.167-167
• /
• 2008

The barium strontium calcium titanate powders were prepared by sol-gel method. Ferroelectric $(Ba_{0.54}Sr_{0.36}Ca_{0.1})TiO_3$(BSCT) thick films were fabricated by the screen-printing method on alumina substrate. And we investigated the structural and dielectric properties of BSCT thick films with the variation of sintering temperature. As a result of thermal analysis, BSCT polycrystalline perovskite phase was formed at around $660^{\circ}C$. The results of X-ray diffraction analysis were showed a cubic perovskite structure without presence of the second phase in all BSCT thick films. The average grain size and the thickness of the specimen sintered at $1450^{\circ}C$ were about 1.6 mm and 45 mm, respectively. The relative dielectric constant increased and the dielectric loss decreased with increasing the sintering temperature, the values of the BSCT thick films sintered at $1450^{\circ}C$ were 5641 and 0.4% at 1kHz, respectively.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.12
• /
• pp.4316-4320
• /
• 2011

The effects of various hydroxide compounds on base stacking (BS) were investigated for pre-concentration of DNA molecules in capillary electrophoresis (CE). In BS, hydroxide ions ($OH^-$) were electrokinetically introduced after DNA sample injection. A neutralization reaction occurred between the $OH^-$ and $Tris^+$ of the running buffer, which resulted in a zone of lower conductivity. Within the low conductivity zone of the high electric field, the DNA molecules moved more rapidly and were concentrated in front of the low conductivity zone. At the same BS conditions of CE, the enhanced sensitivity of the DNA samples was dependent on the kind of multivalent cations in the hydroxide compounds. Except for LiOH, the hydroxide compounds with monovalent cations showed more effective BS than those with divalent cations because of solubility, ionic strength and electronegativity. The order of hydroxide compounds that enhance the detection sensitivity of DNA molecules was as follows: NaOH > $NH_4OH$ > KOH > $Ba(OH)_2$ > $Sr(OH)_2$ > LiOH > $Ca(OH)_2$ > $Mg(OH)_2$. $NH_4OH$, KOH and $Ba(OH)_2$ proved to be efficient hydroxide compounds to use as effective BS reagents in CE instead of NaOH.

• Proceedings of the KIEE Conference
• /
• 1996.07c
• /
• pp.1660-1662
• /
• 1996

Superconducting current lead is one of the promising applications of the oxide high-Tc superconductors, because they have the advantage of decreasing heat conduction to low temperature region, comparing with a conventional cooper alloy lead. High critical current density is a key factor for the applications such as current lead. $(Bi,Pb)_{2}Sr_{2}Ca_{2}Cu_{3}O_{x}$ high Tc superconductor hase been investigated in terms of critical current density. Bi-2223 superconducting current lead made by CIP and solid state sintering process. Bi-2223 current lead that heat treated at $836\;^{\circ}C$ for 240 h in 1/13 $PO_2$ had over $500\;A/cm^2$ of critical current density at 77K. We knew that the superconducting properties of tube type current leads were better than rods type of them. And we investigated the relation of Bi-2223 formation and heat treatment condition by XRD and SEM analysis.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.553-556
• /
• 2003

금속유기물 용액 증착법(MOD)법은 금속유기물 용액을 스핀 코팅하여 고온 열처리를 통해 대면적의 고온 초전도 박막을 만들 수 있으며, 고가의 진공 시스템이 필요하지 않기 때문에 매우 경제적인 박막 증착 방법이다. 본 연구에서는 MOD법을 이용해서 고온초전도체 마이크로파 필터나 터널접합 소자와 같은 전자 소자 응용 연구를 위해 요구되는 높은 임계전류 특성을 갖도록 박막 성장 조건을 변화시켜서 제작된 고온 초전도체 Bi2Sr2CaCu2O8+d (BSCCO2212) 박막을 제작하였다. 박막 특성은 x-ray diffraction (XRD), scanning electron microscope (SEM)으로 표면적, 구조적 특성을 관찰하고 저항-온도 (R-T) 변화 및 전류-전압 (I-V) 특성 측정을 통해 전기적 특성을 연구하여 임계전류를 향상 시킬 수 있는 박막제작 조건에 관해 논의하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.10
• /
• pp.923-930
• /
• 2003

We jointed Bi(Pb)-Sr-Ca-Cu-O multifilament tapes and evaluated their electrical and mechanical properties. In order to improve connectivity of multifilaments, one or two single-filament tape was inserted between two multifilament tapes. The critical current ratio(CCR) and n-value of the jointed tapes were evaluated as a function of uniaxial pressure. It was observed that critical current ratio and n-value were 24.8-29.0% and 2.5-2.8 for MM lap-jointed tape. On the other hand, the corresponding values were improved to 24.7-53.9% and 3.1-4.2 for MSM jointed tape, and 63.4-76.0% and 3.4-5.1 for double MS:vr lap-jointed tape, respectively. The highest electrical properties of double MSM lap-jointed tape are considered to be owing to the presence of single core, causing better interconnections of multifilaments between the two tapes. The mechanical property of jointed tape was evaluated and correlated to the microstructural evolution. The strength of jointed tapes was 44-64% less than that of the unjoined tape. The strain tolerance of jointed tape was also reduced compared to that of the unjoined tape. These lower mechanical properties of jointed tape are probably due to the induced nonuniform microstructure such as the existence of cracks and Ag-intrusion in the joined region.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.153-154
• /
• 2005

A high Tc superconducting with a nominal composition of $Bi_2Sr_2Ca_2Cu_3O_Y$ was prepared by the citarte method. The solid precursor produced by the dehydration of the gel at 120$^{\circ}C$ for 12h is not in the amorphous state as expected but in a crystalline state. X-ray diffraction peaks of nearly the same angular position as the peaks of high Tc phase were observed in the precursor. After pyrolysis at 400$^{\circ}C$ and calcination at 840$^{\circ}C$ for 4h, the (001)peak of the high Tc phase was cleary observed. Experimental results suggest that the intermediate phase formed before the formation of the superconducting phase may be the most important factro in determining whether it is easy to form the high Tc phase or not, because the nucleation barriers of the two superconducting phase may be altered by the variation of the crystal structures of those intermediate phase.