• Proceedings of the Korean Society For Composite Materials Conference
• /
• 1999.11a
• /
• pp.164-167
• /
• 1999

This study concerns with the effect of fiber weight fraction on the fracture toughness of long glass-fiber reinforced polypropylene composites. Fracture tests were conducted using compact tension (CT) specimens made of glass fiber polypropylene composites. Three fiber weight fractions of 20%, 30%, and 40% were used. Fracture toughness was determined from the compliance method. Results showed that compliance decreased with increasing fiber weight fraction while critical load increased with fiber weight fraction. Averaged fracture toughness increased 14% as fiber weight fraction increased from 20% to 40%.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.5 no.3
• /
• pp.31-39
• /
• 1996

The objective of this study is to investigate the influence of welding residual stresses on the fatigue crack growth behavior of cracks located transverse to the weld bead. For this purpose, G. T. A (Gas Tungsten Arc) welding was performed on hte Al alloy 1100-O plate and the same initial crack is made on HAZ(Heat Affected Zone), weld metal and base meta respectively. Specimens were used CT(Compact Tension) specimens. Initial welding residual stresses were measured by using strai gage sectioning method. All specimens were tested under constant amplitude load with stress ratio R=0.1, It is possible to predict fatigue crack growth behaviors and the fatigue life, using numerical analysis together with distribution of initial residual stress and the values of C and m obtained from $da/dN-{\Delta}K$

• Journal of the Korean Society for Nondestructive Testing
• /
• v.31 no.1
• /
• pp.1-10
• /
• 2011

Nonlinear harmonic waves generated at cracked interfaces are investigated both experimentally and theoretically. A compact tension specimen is fabricated and the amplitude of transmitted wave is analyzed as a function of position along the fatigued crack surface. In order to measure as many nonlinear harmonic components as possible a broadband Lithium Niobate ($LiNbO_3$) transducers are employed together with a calibration technique for making absolute amplitude measurements with fluid-coupled receiving transducers. Cracked interfaces are shown to generate high acoustic nonlinearities which are manifested as harmonies in the power spectrum of the received signal. The first subharmonic (f/2) and the second harmonic (2f) waves are found to be dominant nonlinear components for an incident toneburst signal of frequency f. To explain the observed nonlinear behavior a partially closed crack is modeled by planar half interfaces that can account for crack parameters such as crack opening displacement and crack surface conditions. The simulation results show reasonable agreements with the experimental results.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.6
• /
• pp.868-875
• /
• 2015

In order to replace existing slit type steel plate on the wooden structure joint, the FRP-reinforced laminated plates were produced. Four types of FRP-reinforced laminated plates were produced according to the type of reinforcement and adhesive, and before applying to the joint, the adhesion performance test according to KSF 3021 and KSF 2160 and the Compact Tension (CT) type fracture toughness test specified in ASTM D5045-99 were carried out. As a result of adhesion performance test, all GFRP textile, GFRP sheet, and GFRP Textile-Sheet type FRP-reinforced laminated plates satisfied the requirement of soaking delamination percentage with smaller than 5% based on KS standard. However, aramid type specimen satisfied the standard as the soaking delamination percentage of 4.8% but it did not satisfied the standard as the water proof soaking delamination percentage of 70%. As a result of fracture toughness test, the volume ratio of reinforcement to timber became 23% so that the strength of FRP-reinforced laminated plates increased by two to four times in comparison to the control specimen. It was confirmed that the GFRP Textile-Sheet type specimen was most resistant to the fracture most since the ratio of stress intensity factor compared with that of the control increased to 61% owing to the parallel arrangement of glass fiber to the load. As a result of tensile shear strength test using FRP-reinforced laminated plates and nonmetal dowels, it is about 12% lower than metal connectors.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.24 no.1
• /
• pp.44-49
• /
• 1988

The paper presents the preliminary results of an esperimental study on crack growth under tension-tension fatigue loading. A purpose of the study is to find the effect of the specimen thickness on crack propagation behaviors. The thickness of the low catbon steel specimens the are used in the experiments are 5, 10, 15,20, and 25 mm. the type of specimen considering in the present study is compact tension specimen.Crack growth behaviors are obseved and measured by travelling microscope. From the study, the followings are found; 1. There is a certain specimen thickness that is the shortest farigue life. The fatigue life of 15mm specimen is the shorter then that of any other opecimen 2. The crack initiation of the thick specimen is slower than that of thin specimen. But the crack propagation rate is just the opposite. 3. The range which is the exponent, m of power law(paris) is 1.98-4.59. the thicker the spec-imen is, the higher the value of m is.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.7
• /
• pp.729-736
• /
• 2015

In this study, the effects of specimen size and side-groove on the results of the J-R test for leak-before-break (LBB) evaluation were investigated. A series of J-R tests were conducted at both RT and $316^{\circ}C$, using three different sizes of compact tension (CT) specimens machined from SA508 Gr.1a piping material: 12.7 mm-thick 1T-CT, 25.4 mm-thick 1T-CT, and 25.4 mm-thick 2T-CT with and without side-groove. The results showed that side-grooving reduced the J-R curve for all specimens and the effect of side-grooving was more significant at $316^{\circ}C$ than at RT. As the thickness of the specimens decreased and the width of the specimens increased, the J-R curve slightly decreased at RT but it increased at $316^{\circ}C$. However, the variation in the J-R curve of SA508 Gr.1a with the thickness and width of CT specimen was insignificant.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.15 no.2
• /
• pp.19-30
• /
• 2019

In this study, to evaluate conservatism of various fatigue life evaluation procedures, fatigue tests were conducted using compact tension (CT) specimens with a round notch, made of A516 Gr.70 carbon steel and A240 TP304 stainless steel, under load-controlled cyclic condition. Experimental fatigue failure cycles were measured and compared with predicted fatigue lives using two different life evaluation methods; (1) Design-By-Analysis (DBA) procedure given in ASME B&PV Code, Sec. III, Div. 1, Subsec. NB-3200 and (2) structural stress-based approach provided in ASME B&PV Code, Sec. VIII, Div. 2, Part 5. To predict fatigue failure cycles, three-dimensional elastic finite element analysis was conducted. Fatigue lives were predicted by both design fatigue curve given in ASME B&PV Code, Sec. III, Div. 1, Appendices and best-fit fatigue curve suggested in NUREG/CR-6815 for the DBA procedure. Finally, fatigue lives evaluated by various methods were compared with test results, and then conservatism between each evaluation procedure was discussed.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.05a
• /
• pp.104-109
• /
• 2002

In this paper, a statistical analysis of fatigue crack growth behavior under constant amplitude loads has been carried out. Fatigue crack growth tests were conducted on sixteen pre-cracked compact tension (CT) specimens of the pressure vessel (SPV50) steel in controlled identical load and environmental conditions. The assessment of the statistical distribution of fatigue crack growth experimental data obtained from SPV50 steel was studied and also the correlation of the parameter C and m in the Paris-Erdogan law was discussed. The probability distribution function of fatigue crack growth life seems to follow the 3-parameter Weibull. The fatigue crack growth rate seems to follow the 3-parameter Weibull and the log-normal distribution. The coefficient of variation (COV) of fatigue crack growth life was observed to decrease as the crack grows. A strong negative linear correlation exists between the coefficient C and the exponent m in Paris model. Fatigue crack growth rate data shows a normal distribution for both m and logC.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.32 no.4
• /
• pp.402-410
• /
• 1996

Recently carbon fiber reinforced plastic(CFRP) has been used structural materials in corrosive environment such as for water, chemical tank and chemical pipes. However, mechanical properties of such materials may change when CFRP are exposed to corrosive environment for long periods of time. Therefore, it is important to understand the effect of moisture absorption on mechanical properties of the CFRP. In this study, degradation behavior of immersed carbon fiber/epoxy resin composite material was investigated using acoustic emission(AE) technique. Fracture toughness test are performed on the compact tension(CT) test specimens that are pilled by two types of laminates $[0^{\circ}_2$/$90^{\circ}_2]_3s$ and $[0^{\circ}_2$/$90^{\circ}_2]_6s$During the fracture toughness test, AE test was carried out to monitor the damage of CFRP by moisture absorption. In spite of the change of moisture absorption rate, the fracture toughness of CFRP was not change. As immersion time increased, AE event count numbers decreased in low amplitude range of AE for amplitude distribution histogram. The event in low amplitude range was known to be generated by debonding of matrix-fiber interface. Therefore, decrease of AE event count numbers in low amplitude range represents that debonding of matrix-fiber interface which was probably generated by moisture absorption.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.6
• /
• pp.923-929
• /
• 2003

In this paper, an analysis of fatigue crack growth behavior from a statistical point of view has been carried out. Fatigue crack growth tests were conducted on sixteen pre-cracked compact tension (CT) specimens of the pressure vessel (SPV50) steel in controlled identical load and environmental conditions. The assessment of the statistical distribution of fatigue crack growth experimental data obtained from SPV50 steel was studied and also the correlation of the parameter C and m in the Paris-Erdogan law was discussed. The probability distribution function of fatigue crack growth life seems to follow the 3-parameter Weibull. The fatigue crack growth rate seems to follow the 3-parameter Weibull and the log-normal distribution. The coefficient of variation (COV) of fatigue crack growth life was observed to decrease as the crack grows. Fatigue crack growth rate data shows a normal distribution for both m and logC. A strong negative linear correlation exists between the coefficient C and the exponent m.