A Fracture Mechanics Study on the Fatigue Crack Growth Behaviors in Aluminum Alloy Weldments

알루미늄 합금 용접부의 피로균열성장거동에 관한 파괴력학적 연구

  • 차용훈 (조선대학교 기계공학과(수송기계부품공장자동화연구센터))
  • Published : 1996.09.01

Abstract

The objective of this study is to investigate the influence of welding residual stresses on the fatigue crack growth behavior of cracks located transverse to the weld bead. For this purpose, G. T. A (Gas Tungsten Arc) welding was performed on hte Al alloy 1100-O plate and the same initial crack is made on HAZ(Heat Affected Zone), weld metal and base meta respectively. Specimens were used CT(Compact Tension) specimens. Initial welding residual stresses were measured by using strai gage sectioning method. All specimens were tested under constant amplitude load with stress ratio R=0.1, It is possible to predict fatigue crack growth behaviors and the fatigue life, using numerical analysis together with distribution of initial residual stress and the values of C and m obtained from $da/dN-{\Delta}K$

Keywords

References

  1. International Series on Materials and Technology v.33 Analysis of Welded Structures K. Masubuchi
  2. Metallurgy of Welding(Third Edition) J. F. Lancaster
  3. 改訂最新熔接工學 鈴本春義
  4. 大宇造船工業株式會社 技術紙(大宇造船 技術) v.3 no.10 疲勞强度에 미치는 鎔接缺陷의 影響 이광주
  5. ASTM STP 743 v.8 Effect of Residual Stresses on Fatigue Crack Growth Rate Measurement R. J. Bucci
  6. ASTM STP 776 Stress Intensity Factor, Crack Profiles, and Fatigue Crack Growth Rate in Residual Stress Fields A. P. Parker
  7. ASTM STP 776 Effects of Residual Stress on Fatigue Crack Propagation D. V. Nelson
  8. Welding Handbook, (Seventh edition) v.5 W. H. Kearns
  9. 成均館大學校 博士 學位論文` CT形 變厚熔接板材에서의 疲勞龜裂成 長擧動에 미치는 殘留應力의 影響에 關한 破壞力學的 硏究 車龍勳
  10. 材料 v.35 no.391 コンペクト試驗片の疲勞き裂進展特性に及ぱす鎔接殘留應力の影響評價 小林英男;轟章
  11. ASTM STP 776 Effect of Residual Stresses on Fatigue Crack Growth Rate in Weldments of Aluminum Alloy 5456 Plate G. E. Nordmark;L. N. Muller;R. A. Kelsey
  12. 材料 v.32 no.363 SUS 304 鋼おわぴA533B鋼の鎔接繼手における疲勞き裂傳ぱ 擧動 橘內良雄
  13. ASTM STP 677 Effect of Residual Stresses on Fatigue Crack Growth in Steel Weldments under Constant and Variable Amplitude Loads G. Glinka
  14. ASTM Designation : E647-83 Standard Test Method for Constant-Load-Amplitude Fatigue Crack Growth Rate Above $10^{-8}$m/cycle
  15. ANSI/AWS D1.2-83 Structural Welding Commitee, Welding Code-Aluminum AWS
  16. ANSI/AWS D1.2-83 Structural Welding Commitee, Welding Code-Aluminum AWS
  17. Journal of Pressure Vessel Technology v.103 An Analytical Assesment of the Effects of Residual Stresses and Fracture Properties on Service Performance of Various Welds Repair Processes J. M. Bloom
  18. ICF(Fracture 84) v.3 Fatigue Crack Propagation Through Residuals Stress Fields B. L. Averbach;B. Lou