• 반도체디스플레이기술학회지
• /
• 제3권4호
• /
• pp.45-49
• /
• 2004

We examined large particles and filter size effects of Central Chemical Supplying (CCS) system for STI-CMP on Light Point Defects (LPDs) after polishing. As manufacturing process recently gets thinner below 0.1 um line width, it is very important to keep down post-CMP micro-scratch and LPDs in case of STI-CMP. Therefore, we must control the size distribution of large particles in a slurry. With optimization of final filter size, CCS system is one of the solutions for this issue. The oxide and nitride CMP tests were accomplished using nano-ceria slurries made by ourselves. The number of large particles in a slurry and the number of LPDs on the wafer surface after CMP were reduced with decrease of the final filter size. Oxide removal rates slightly changed according to the final filter size, showing the good performance of self-made nano ceria slurries.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.40-41
• /
• 2005

In this study, we proposed CMP micro-scratches generated by contaminative particle which existed on the wafer surface prior to CMP process. The CMP micro-scratches are one of the slurry abrasive related damage. To reduce the micro-scratches, research efforts have been devoted to the optimization of slurry abrasive size distribution. In addition of slurry abrasive, it was found that contaminative particles also were major CMP micro-scratch source.

• 한국전기전자재료학회논문지
• /
• 제13권7호
• /
• pp.568-574
• /
• 2000

We have been optimized tungsten(W) plug CMP(chemical mechanical polishing) characteristics using two different kinds of component of slurry and two different kinds of pad which have different hardness. The comparison of oxide film roughness on around W plug after polishing has been carried out. And W plug recess for consumable sets and dishing effect at dense area according to the rate of over-polishing has been investigated. Also the analysis of residue on surface after cleaning have been performed. As a experimental result we have concluded that the consumable set of slurry A and hard pad was good for W plug CMP process. After decreasing the rate of chemical reaction of silica slurry and adding two step buffering we could reduce the expanding of W plug void however we are still recognizing to need a more development for those kinds of CMP consumables.

• 한국재료학회지
• /
• 제16권12호
• /
• pp.731-738
• /
• 2006

It is seriously considered using Al CMP (chemical mechanical planarization) process for the next generation 45 nm Al wiring process. Al CMP is known that it has a possibility of reducing process time and steps comparing with conventional RIE (reactive ion etching) method. Also, it is more cost effective than Cu CMP and better electrical conductivity than W via process. In this study, we investigated 4 different kinds of slurries based on abrasives for reducing scratches which contributed to make defects in Al CMP. The abrasives used in this experiment were alumina, fumed silica, alkaline colloidal silica, and acidic colloidal silica. Al CMP process was conducted as functions of abrasive contents, $H_3PO_4$ contents and pressures to find out the optimized parameters and conditions. Al removal rates were slowed over 2 wt% of slurry contents in all types of slurries. The removal rates of alumina and fumed silica slurries were increased by phosphoric acid but acidic colloidal slurry was slightly increased at 2 vol% and soon decreased. The excessive addition of phosphoric acid affected the particle size distributions and increased scratches. Polishing pressure increased not only the removal rate but also the surface scratches. Acidic colloidal silica slurry showed the highest removal rate and the lowest roughness values among the 4 different slurry types.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1998년도 제28회 추계학술대회
• /
• pp.272-277
• /
• 1998

Chemical-Mechanical Polishing (CMP) refers to a material removal process done by rubbing a work piece against a polishing pad under load in the presence of chemically active, abrasive containing slurry. CMP process is a combination of chemical dissolution and mechanical action. The mechanical action of CMP involves tribology. The liquid slurry is trapped between the wafer(work piece) and pad(tooling) forming a lubricating film. For the first step to understand material removal rate of the CMP process, the lubricational analyses were done with commercial 100mm diameter silicon wafers to get nominal clearance of the slurry film, roll and pitch angle at the steady state. For this purpose, we calculate slurry pressure, resultant forces and moments at the steady state in the range of typical industrial polishing conditions.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.723-726
• /
• 2004

In this work, we have studied the CMP characteristics by mixing of original slurry and used slurry in order to investigated the possibility of recycle of used silica slurry. The removal rate and within-wafer non-uniformity (WIWNU) were measured as a function of different slurry composition. Also, we compared the CMP characteristics between self-developed KOH-based silica abrasive slurry and the original slurry. Our experimental results revealed comparable removal rate and good planarity with commercial products.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 1997년도 한국재료학회 추계학술발표회
• /
• pp.77-77
• /
• 1997

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2002년도 추계학술발표강연 및 논문개요집
• /
• pp.56-56
• /
• 2002

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.185-188
• /
• 2001

Chemical mechanical polishing(CMP) process is widely used for global planarization of inter-metal dielectric (IMD) layer and inter-layer dielectric (ILD) for deep sub-micron technology. However, as the IMD and ILD layer gets thinner, defects such as micro-scratch lead to severe circuit failure, which affect yield. In this paper, for the improvement of CMP Process, deionized water (DIW) pressure, purified $N_2$ (P$N_2$) gas, slurry filter and high spray bar were installed. Our experimental results show that DIW pressure and P$N_2$ gas factors were not related with removal rate, but edge hot-spot of patterned wafer had a serious relation. Also, the filter installation in CMP polisher could reduce defects after CMP process, it is shown that slurry filter plays an important role in determining consumable pad lifetime. The filter lifetime is dominated by the defects. However, the slurry filter is impossible to prevent defect-causing particles perfectly. Thus, we suggest that it is necessary to install the high spray bar of de-ionized water (DIW) with high pressure, to overcome the weak-point of slurry filter. Finally, we could expect the improvements of throughput, yield and stability in the ULSI fabrication process.

• 반도체공학회 논문지
• /
• 제2권2호
• /
• pp.1-9
• /
• 2024

반도체 소자의 집적도는 높아져 왔으며 이는 더 작고 밀도가 높은 회로 및 소자를 제조하는 것을 의미한다. 이에 따라 다양한 층간 표면을 매끄럽게 유지하여 미세한 패턴을 형성하고 고밀도 회로를 안정적으로 제작하는데 평탄화 기술이 중요한 역할을 한다. 결과적으로 반도체에서의 CMP(chemical mechanical polishing) 공정은 다층 구조 소자를 만들기 위해서 반드시 필요한 공정이 되었다. 일반적으로 CMP 공정의 슬러리 조성은 세리아(ceria), 분산제(dispersant), 물(DI water) 이렇게 3 가지 성분이 균형을 이루는 것이 중요하다. 본 연구에서는 AMP(2-Amino-2-methyle-1-propanol) 함량을 달리한 양쪽성 계면활성제를 사용한 세리아 슬러리 안정성 연구를 수행하였다. 결과적으로 AMP 함량에 따라 카복실기(-COOH) 영향으로 pH 안정화 되었으며, 세리아 슬러리 응집현상이 발생하지 않았으며 분산 안정성 문제가 없는 것으로 확인되었다.