• Title/Summary/Keyword: Bonding agents

Search Result 181, Processing Time 0.031 seconds

Pinning retrofit technique in masonry with application of polymer-cement pastes as bonding agents

  • Shrestha, Kshitij C.;Pareek, Sanjay;Suzuki, Yusuke;Araki, Yoshikazu
    • Earthquakes and Structures
    • /
    • v.5 no.4
    • /
    • pp.477-497
    • /
    • 2013
  • This paper reports extensive experimental study done to compare workability and bond strength of five different types of polymer-based bonding agents for reinforcing bars in pinning retrofit. In pinning retrofit, steel pins of 6 to 10 mm diameters are inserted into holes drilled diagonally from mortar joints. This technique is superior to other techniques especially in retrofitting historic masonry constructions because it does not change the appearance of constructions. With an ordinary cement paste as bonding agent, it is very difficult to insert reinforcing bars at larger open times due to poor workability and very thin clearance available. Here, open time represents the time interval between the injection of bonding agent and the insertion of reinforcing bars. Use of polymer-cement paste (PCP), as bonding agent, is proposed in this study, with investigation on workability and bond strengths of various PCPs in brick masonry, at open times up to 10 minutes, which is unavoidable in practice. Corresponding nonlinear finite element models are developed to simulate the experimental observations. From the experimental and analytical study, the Styrene-Butadiene Rubber polymer-cement paste (SBR-PCP) with prior pretreatments of drilled holes showed strong bond with minimum strength variation at larger open times.

Effect of Dentin Bonding Agent Acidity on Surface Microhardness of Mineral Trioxide Aggregate

  • Yun-Hui Im;Yoon Lee
    • Journal of Korean Dental Science
    • /
    • v.17 no.1
    • /
    • pp.36-44
    • /
    • 2024
  • Purpose: This study investigated the effect of dentin bonding agent acidity on surface microhardness of MTA. Materials and Methods: Forty cylindrical molds (3 mm×5 mm) were prepared, and three dentin bonding agents with different acidities: Adper Single Bond 2 (ASB), Single Bond Universal (SBU), and Clearfil SE bond 2 (CSE) were applied to the inner surface of the molds (n=10). No bonding agent was applied in the control group. MTA was mixed and inserted into the molds and sealed with a wet cotton pellet for 4 days. After setting, the Vickers microhardness (HV) test was done at 200, 400, 600 ㎛ from the inner surface of the mold. One-way ANOVA was conducted for all samples. A P-value of less than .05 was considered significant. Tukey HSD test was performed for post-hoc analysis. Results: The mean HV values and standard deviations were 67.02±11.38 (Con), 48.76±11.33 (ASB), 43.78±11.19 (CSE), 37.84±9.36 (SBU), respectively. The difference between the control group and the experimental groups was statistically significant (P<0.001). The difference between ASB and SBU was statistically significant (P<0.001), while the difference between SBU and CSE was not. There were no statistically significant differences between the various points from the inner surface of the mold within each group (P>0.05). Conclusion: Results of the current study indicate that use of dentin bonding agents with MTA can reduce the surface microhardness of MTA. Moreover, there is a direct relationship between the acidity of dentin bonding agents and the surface microhardness of MTA.

The effects of desensitizing agents, bonding resin and tooth brushing on dentin permeability, in vitro (지각과민 처치제 후 접착레진 처리가 상아질 투과도에 미치는 영향)

  • Hong, Seung-Woo;Park, No-Je;Park, Young-Bum;Lee, Keun-Woo
    • The Journal of Korean Academy of Prosthodontics
    • /
    • v.52 no.3
    • /
    • pp.165-176
    • /
    • 2014
  • Purpose: The effects of desensitizing agent are often for a short duration. One of the reasons is believed to be wear of desensitizing agent by tooth brushing. To reduce the wear and make the duration longer, dental bonding resin was applied and the changes of dentin permeability after toothbrushing were measured. Materials and methods: Extracted teeth free from caries were chosen. Coronal dentin discs with thickness of 1 mm were prepared. Using the split chamber device developed by Pashely, hydraulic conductance and scanning electron microscope images (SEM) were compared and contrasted before and immediately after the application of desensitizing agent and bonding resin and then after equivalent tooth brushing of 1 week, 2 weeks, and 6 weeks. Four commercially available desensitizing agents were used in this study; they were All-Bond 2, Seal & Protect, Gluma, and MS Coat. And Dentin/Enamel Bonding resin (Bisco Inc.) was used. The results of this study are as follows. Results: On all specimens, the hydraulic conductance decreased after the application of tooth desensitizing agent and bonding resin. Compared with the specimens treated only with desensitizer, the specimens treated with All-Bond 2, Gluma, MS Coat and plus D/E bonding resin had a little increase in hydraulic conductance after 1, 2 and 6-week tooth brushing. In case of Seal & Protect, the specimens showed the same result only after 6-week tooth brushing. On examination of SEM, the dentinal tubule diameter had decreased after treatment of desensitizing agents and bonding resin. And the specimens treated with All-Bond2, Seal&Protect, Gluma, MS Coat and plus D/E bonding resin had an significant decrease in diameter of dentinal tubule after 6-week tooth brushing. Conclusion: According to the results of this study, it is effective to use bonding resin after application of desensitizer in reducing the wear by tooth brushing and making the duration longer. In this study, just 6-week tooth brushing was performed, and it is not enough to regard it as a long-term data. So further study is needed and more perfect method for treating dentin hypersensitivity should be developed.

MICROLEAKAGE OF DENTIN BONDING AGENTS IN PORCELAIN LAMINATE VENEER UNDER SIMULATED PHYSIOLOGIC PRESSURE (가상 생리적압력하에서 Porcelain Laminate Veneer 접착시 상아질 접착제의 변연 누출에 관한 연구)

  • Choi, Young-Jin;Lee, Ho-Young
    • The Journal of Korean Academy of Prosthodontics
    • /
    • v.31 no.1
    • /
    • pp.1-10
    • /
    • 1993
  • The purpose of this study was to evlauate the microleakage of 3 dentin bonding agents using different dentin pretreatment method under simulated physilogic pressure in cementing the porcelain laminate veneer. Noncarious 60 human maxillary molars were selected and randomly assigned to 4 groups of 15 each. The group with the margin placed on the enamel was classified as the control and the groups with the margin placed on root surface were subdivided into 3 groups according to the dentin bonding agents used. The group using All Bond 2 was classified as experimental group 1, the group using Scotchbond MP was classified as experimental group 2, and the group using Gluma was classified as experimental group 3. Roots were removed at 3mm below the cementoenamel junction, and reductions of the teeth for the porcelain laminate veneer were done on the mesial 1/2 of the buccal surface of each teeth. The pulp was extirpated and the pulp chamber was cleaned with 37% phosphoric acid for the patency of dentinal tubule. Under simulated physiologic pressure, porcelain laminate veneers were cemented to the teeth using each dentin bonding agent and luting cement. After cementation, all samples were stored at 36t in water for 24 hours and thermocycled for 1500 cycles, then immersed in 0.5% basic fuchsin solution and the teeth were sectioned longitudinally by using diamond saw and the extent of microleakage was measured. The following results were obtained, 1. Microleakage was observed in a few samples of control group but all the samples of experimental groups. 2. The control group showed the less extent of microleakage than the experimental groups. In experimental groups the experimental group 1 & the experimental group 2 showed similiar extent of microleakage and the experimental group 3 showed the greater extent of microleakage than other groups. Conclusively, practicing the porcelain laminate veneers in the clinic, although the margin of the porcelain laminate veneer should be placed on enamel, in the case that it is inevitable to place the margin of the porcelain laminate veneer on the root surface, it is recommened to use dentin bonding agents which use no dentin pretreatment or a dentin pretreatment which can leave the smear plugs.

  • PDF

The Study of the Effect of Thermocycling on Microleakage within Various Dentin Bonding Agents (열순환이 상아질접착제 처리 후 미세누출에 미치는 영향에 관한 연구)

  • Yoo, Seung-Hoon
    • Journal of Dental Rehabilitation and Applied Science
    • /
    • v.24 no.2
    • /
    • pp.147-155
    • /
    • 2008
  • Three groups of dentin bonding agents (5th generation Single Bond 2.0 and two 6the generation Prompt L-Pop, AdheSE) applied to class V cavities (upper portion with enamel margin and lower portion with dentin margin) prepared at buccal and lingual portion of premolars and molars. Each groups consist of 30 teeth. Devide into two groups, one without thermocycling and the other thermocycled. After then, infiltrate methylene blue into the gap between restoration and tooth. Within non-thermocycled groups, Single Bond 2.0 group shows lesser leakage at enamel margin than other two bonding agents (p <.05) but shows more leakage at dentin margin than other two bonding agents. (p <.05) Within thermocycled groups, Single Bond 2.0 group shows lesser leakage at both enamel and dentin margins. (p <.05)

Studies on Bonding Characteristics of Plywood by Kraft Black Liquor and Surface Activators (크라프트펄프 폐액(廢液)과 표면산화제(表面酸化劑)를 이용(利用)한 합판(合板)의 접착특성(接着特性)에 관(關)한 연구(硏究))

  • Chung, In-Ju;Lee, Phil-Woo
    • Journal of the Korean Wood Science and Technology
    • /
    • v.16 no.3
    • /
    • pp.5-16
    • /
    • 1988
  • This experiment was executed to investigate the effect of activation of veneer surface by oxidizing agents, hydrogen peroxide and nitric acid, on bonding characteristics of Malas(Homalium foetidum Benth) plywood, in which the effects of these oxidizing agents amount, pretreatment time, and pressing time and temperatue on shear strength of the plywood were examined and discussed. In this research the activation of veneer surface by oxidants was effective in raising shear strength but the difference in shear strength was not observed between hydrogen peroxide and nitric acid treatment. Hydrogen peroxide treatment, however, seemed to be more profitable to industrial application because of its lower concentration and easier handling than nitric acid. The bonding method by lignin-phenol adhesive through surface activation revealed inferior shear strength to phenol- and urea-formaldehyde adhesive but superior water resistance to urea-formaldehyde adhesive and this bonding method, in addition, have the advantage of lower cost compared with phenol-formaldehyde adhesive, Therefore, this bonding method by lignin-phenol adhesive through surface activation seemed to economical in manufacturing of water-resistant wood panel materials in future.

  • PDF

SHEAR BOND STRENGTH OF DENTIN BONDING AGENTS ON DENTIN SURFACE TREATED WITH EUGENOL (유지놀 처리된 상아질 표면의 상아질 접착제의 전단결합강도에 관한 연구)

  • Yu, Hwa-Sung;Choi, Gi-Woon;Choi, Kyung-Kyu;Park, Sang-Jin
    • Restorative Dentistry and Endodontics
    • /
    • v.25 no.4
    • /
    • pp.550-560
    • /
    • 2000
  • In this study, shear bond strength of two bonding systems were measured and appearance of dentin surfaces were observed with SEM according to the storage time of eugenol on dentin surface, thus evaluated the effect of eugenol on bond strength of two dentin bonding systems. Control groups were directly bonded to dentin surface with One Step, Prime & Bond 2.1. Experimental groups were divided into experimental I and II according to dentin bonding agents. After eugenol application, dentin surfaces were bonded with One Step and Prime & Bond 2.1 according to the each storage time of immediately, 3min, 24hour, 48hour and 1week, and then control and experimental groups were filled with light cured composite resin(Z-100). After 24 hours water storage at $37^{\circ}C$, all samples were subjected to a shear load to fracture at a cross head 1.0mm/min with Instron universal testing machine(No. 4467). Etched dentin surface storaged for each time of immediately, 3min, 24hour, 48hour and 1 week after eugenol application were observed under Scanning Electron Microscope(Hitachi S-2300) at 20kvp. The data were evaluated statistically with two-way ANOVA and Tukey's HSD. The results were as follows; 1. Shear bond strengths were higher in control groups than in the experimental groups. 2. As storage time was increased after eugenol application, the shear bond strengths were decreased in experimental groups. 3. In experimental I, II the shear bond strengths were the lowest in which storage time was 1 week after eugenol application. 4. As storage time was increased after eugenol application, etched dentin surfaces showed obstructed dentinal tubule.

  • PDF

STUDY ON DENTINAL TUBULES SEALING EFFECTS OF DENTIN BONDING AGENTS (DENTIN BONDING AGENTS들의 상아세관 밀봉 효과에 관한 연구)

  • Kown, O-Teak;Park, Dong-Soo
    • Restorative Dentistry and Endodontics
    • /
    • v.18 no.2
    • /
    • pp.483-496
    • /
    • 1993
  • Dentin hypersensitivity medicaments such as Gluma, Scotchbond 2, All-Bond 2, which are resin adhesives, were used to compare the sealing effects of dentinal tubule under mechanical stress. Topical application of above medicaments on the dentin surfaces of extracted teeth followed by artificial tooth brushing for 6 weeks was performed for the comparison. The following conclusions on the degree of dentinal tubule exposure versus time by were reached by using polyvinyl siloxane impression material for taking the impression, epoxy resin for the duplication and SEM for observing the surface. 1. SEM was used to compare the accuracy of the duplicated surface, but no differences were found when teeth samples and the duplicated surfaces were observed. 2. After comparing the degree of dentinal tubules exposure with varnish applied contrast group, resin adhesive materials showed much less exposure as time went by. 3. The results indicated that AU-Bond 2 adhesive, under mechanical stress, showed lesser exposure of dentinal tubules comparing with Gluma and Scotchbond 2 adhesives After the results were put together, it was demonstrated that resin replica method is an useful way to evaluate the treatment effects of the dentinal tubule hypersensitivity medicaments. Also, it was noticed that under mechanical stress, All-Bond 2, classified as fourth generation, illustrated the best dentinal tubules sealing effects.

  • PDF