• Journal of Welding and Joining
• /
• v.19 no.4
• /
• pp.423-428
• /
• 2001

The bonding phenomena of Ni base single crystal superalloy. CMSX-4 during transient liquid phase(TLP) bonding was investigated using MBF-80 insert metal. Bonding of CMSX-4 was carried out at 1,373∼1,548K for 0∼19.6ks in vacuum. The (001) orientation of each test specimen was aligned perpendicular to the bonding interface. The dissolution width of base metal was increased when the bonding temperature and holding time were increased. The eutectic width diminished linearly with the square root of holding time during isothermal solidification process. Borides were formed in the bonded layer during TLP bonding operation. The solid phase grew epitaxially into the liquid phase from substrates and single crystallization could be readily achieved during the isothermal solidification.

• Journal of Welding and Joining
• /
• v.21 no.2
• /
• pp.82-88
• /
• 2003

The bonding phenomenon and mechanism in the transient liquid phase bonding(TLP Bonding) of directionally solidified Ni base superalloy, GTD-111 was investigated. At the bonding temperature of 1403K, liquid insert metal was eliminated by isothermal solidification which was controlled by the diffusion of B and Si into the base metal and solids in the bonded interlayer grew epitaxially from mating base metal inward the insert metal. The number of grain boundaries formed at the bonded interlayer was corresponded with those of base metal. The liquation of grain boundary and dendrite boundary occurred at 1433K. At the bonding temperature of 1453K which is higher than liquation temperature of grain boundary, liquids of the Insert metal were connected with liquated grain boundaries and compositions in each region mixed mutually. In Joints held for various time at 1453t phases formed at liquated grain boundary far from the interface were similar to those of bonded interlayer. With prolonged holding time, liquid phases decreased gradually and liquids of continuous band shape divided many island shape. But liquid phases did not disappeared after holding for 7.2ks at 1453k. Isothermal solidification process at the bonding temperature which is higher than the liquation temperature of the grain boundary was controlled by diffusion of Ti to be result in liquation than B or Si. in insert metal. (Received January 15, 2003)

• International Journal of Advanced Culture Technology
• /
• v.8 no.2
• /
• pp.246-251
• /
• 2020

Dimethyl Ether(DME) engine use a highly efficient alternative fuel having a great quantity of oxygen and has a advantage no polluting PM gas. The existing DME fuel cam material is a highly expensive carbide alloy, and it is difficult to take a price advantage. Therefore the study of replacing body area with inexpensive steel material excluding piston shoe and contact area which demands high characteristics is needed. The development of WC-Ni base carbide alloy optimal bonding composition technique was accomplished in this study. To check out the influence of bonding temperature and time, bonding characteristics of sintering temperature was experimented. The hardness of specimen and bonding rate were measured using ultrasound equipment. The bonding state of each condition was excellent, and the thickness of mid-layer, temperature and maintaining time were measured. The mid-layer thickness according to bonding temperature and maintaining time were observed with optical microscope. We analyzed the micro-structural analysis, formation of bonding specimen, wafer fabrication and fuel cam abrasion test. Throughout this study, we confirmed that the fuel cam for DME engine which demands high durability against velocity and pressure is excellent.

• Journal of Welding and Joining
• /
• v.18 no.1
• /
• pp.70-76
• /
• 2000

A rolled steel for structural parts and lead bronze alloy were bonded each other by a new semi-solid diffusion bonding process to investigate the effect of the process parameters, for example bonding temperature and bonding time, on the interface characteristics, and bonding behavior. It can be possible that manufacture of the bonded steel/lead bronze which has a cylindrical shape with inserted the lead bronze alloy into the steel ring by the diffusion bonding process under the semi-solid condition of the lead bronze alloy without any pressure and flux. It has been know that the control of the amount of the liquid phase in semi-solid lead bronze alloy was very important to obtain soundness interface, since the shear strength of the bonded steel/lead bronze at 850℃ for 60 minutes under the condition of about 40% of the liquid phase in the lead bronze alloy shows maximum value, 210 MPa. The shear strength increases with an increase in bonding time and show maximum value, and then decreases.

• Journal of the Korean Society of Industry Convergence
• /
• v.15 no.2
• /
• pp.55-58
• /
• 2012

This study is concerned about the design and structural analysis of high integrated Chip Bonding Machine. Recently, many studies have been undergoing to reduce a working time in a field of Chip Bonding Machine. Chip Bonding Machine belongs to reduce a stand-by time by Chip Moving time. The developed system can save tool moving distance in small space than other machine. The analysis is carried out by SoldEdge & Ansys software.

• International Journal of Highway Engineering
• /
• v.15 no.4
• /
• pp.85-94
• /
• 2013

PURPOSES: The performance of tack coat, commonly used for layer interface bonding, is affected by application rate and curing time. In this study, bonding strength tests were performed according to the application rate and curing time of asphalt emulsion. Based on finding from this study, optimum application rates and curing times are proposed. METHODS: In order to investigate bonding characteristic of asphalt emulsion, tests were performed on both asphalt concrete pavement and portland concrete pavement. Also, asphalt emulsions were tested at the application rate of 0, 0.2, 0.4, 0.6, and $0.8{\ell}/m^2$ and at the curing time of 0, 0.5, 1, 2, and 24 hours. Pull-off test and shear bonding strength test, which commonly used for bonding strength measurement of asphalt emulsion, were adopted for this study. To assess field performance under different testing condition, asphalt emulsions were applied to in-service pavement. Throughout coefficient of determination analysis between material index properties from asphalt emulsion and mechanical response from bonding strength tests, performance correlativity was analyzed. RESULTS: Test results show that optimum application rate for asphalt overlay on asphalt concrete pavement (AOA) and asphalt overlay on concrete pavement (AOC) was $0.4{\sim}0.5{\ell}/m^2$ and $0.3{\sim}0.5{\ell}/m^2$, respectively. According to the curing time increment, tensile strength and shear strength of AOC were increased to 22~44% and 20~39%, respectively. AOA case also show strength increment in tensile strength (42%) and shear strength (9%). We tested the applicability of tack coat materials at the field sites, and our findings demonstrated that the bonding (for D and E) and rapid curing (for B, C, and D, E) performances were superior than others. Among material index properties, there was a high correlation between penetration ratio and bonding strength test result. CONCLUSIONS : Result show that interlayer bonding strength was affected by asphalt emulsion type, application rate and curing time. AOC required slightly higher application ($0.1{\ell}/m^2$) than AOA. Both AOA and AOC cases show higher strength at longer curing time. Up to 2hours of curing, rapid strength increments were observed, but strength increment ratio was decreased after 2hours of curing. From the observed correlation between penetration ratio and bonding strength, it is expected that penetration ratio can be used as one of important factors affecting bonding strength analysis.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.7
• /
• pp.7-12
• /
• 2010

In this paper, chip-on-glass(COG) interconnection with anisotropic conductive film(ACF) using lateral thermosonic bonding technology is considered. In general, thermo-compression bonding which is used in practice for flip-chip bonding suffers from the low productivity due to the long bonding time. It will be shown that the bonding time can be improved by using lateral thermosonic bonding in which lateral ultrasonic vibration together with thermo-compression is utilized. By measuring the internal temperature of ACF, the fast curing of ACF thanks to lateral ultrasonic vibration will be verified. Moreover, to prove the reliability of the lateral thermosonic bonding, observation of pressured mark by conductive particles, shear test, and water absorption test will be conducted.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.1
• /
• pp.19-26
• /
• 2007

This study was focused on the feasibility of ultrasonic bonding of Au flip chip bumps for a practical complementary metal oxide semiconductor (CMOS) image sensor with electroplated Au substrate. The ultrasonic bonding was carried out with different bonding pressures and times after the atmospheric pressure plasma cleaning, and then the die shear test was performed to optimize the ultrasonic bonding parameters. The bonding pressure and time strongly affected the bonding strength of the bumps. The Au flip chip bumps were successfully bonded with the electroplated Au substrate at room temperature, and the bonding strength reached approximate 73 MPa under the optimum conditions.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.2
• /
• pp.174-181
• /
• 2009

Statement of problem: There is a reduction of dentin bonding strength when the bonding procedure is carried out immediately after bleaching with peroxides. Purpose: The aim of this study is to evaluate a proper time interval for in-office bleaching technique using 35% hydrogen peroxide. Material and methods: Fifty extracted non-caries human third molars were used in this study. Buccal enamel of each tooth was removed and polished by 600 grits silicone carbide paper. They were randomly divided into five groups and bleached 35% hydrogen peroxide except control group. All groups were bonded with Single Bond/Z 350 after each time intervals ; Group-A: control, no bleaching treatment. Group-B: resin bonding immediately after bleaching. Group-C: resin bonding 1day after bleaching. Group-D: resin bonding 2 days after bleaching. Group-E: resin bonding 7days after bleaching. Shear bond strengths were measured with a cross-head speed of 1.0 mm/min using an Instron machine. The data of results were statistically analyzed by analysis of variance(ANOVA) and Tukey multiple comparison test.(P=.05) Results: There were significant decreases in mean shear strength in immediately bonding group after bleaching. The reduction of bond strengths was 78% compared with the group of no bleaching treatment. Group C showed the recovery of 51%, and Group D showed recovery of 63%. Both of them have no statistical difference with non-bleaching group. Group E showed no statistical difference with no bleaching treatment group. Conclusion: Dentin bonding strength is significantly reduced when bonding is performed immediately after bleaching for in-office bleaching regimens using 35% hydrogen peroxide, and increases as time goes by. One week of elapsed time between bleaching and resin bonding significantly increases bonding strengths for the in-office bleaching technique.

• Journal of Welding and Joining
• /
• v.20 no.6
• /
• pp.106-106
• /
• 2002

This study investigated variations of micro-structures and mechanical properties of Ti / STS321L joint with various bonding temperature and time using brazing method. According to increasing bonding temperature and time, it was observed that the thickness of their reaction layer increased due So increasing diffusion rate and time. From the EPMA results, Ti diffused to the STS321L substrate according to increasing bending time to 30min. Hardness of bonded interface increased with increasing bonding temperature and time due to increasing their oxides and intermetallic compounds. XRD data indicated that Ag, Ag-Ti intermetallic compounds, TiAg and Ti₃Ag and titanium oxide, TiO₂were formed in interface. In tensile test, it was found that the tensile strength had a maximum value at the bonding temperature of 900℃ and time of 5min, and tensile strength decreased over bonding time of 5min. The critical thickness of intermetallic compounds was observed to about 30㎛, because of brittleness from their excessive intermetallic compounds and titanium oxide, and weakness from void.