[ $Bi_{3.25}La_{0.75}Ti_3O_{12}$ ] (BLT) thin films were prepared by using metal organic decomposition method onto the $LaNiO_3$ (LNO) bottom electrode. Both the structure and morphology of the films were analyzed by x-ray diffraction (XRD) and atomic force microscope (AFM). Even at low temperatures ranging from 450 to $650^{\circ}C$, the BLT thinfilms were successfully deposited on LNO bottom electrode and exhibited (117) orientation. The BLT thin films annealed as low as $600^{\circ}C$ showed excellent ferroelectricity, higher remanent polarization and no significant degradation of switching charge at least up to $5{\times}10^9$ switching cycles at a frequency of 100 kHz and 5 V. For the annealing temperature of $600^{\circ}C$, the remanent polarization Pr and coercive field were $23.5\;C/cm^2$ and 120 kV/cm, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.371-374
• /
• 2002

Bismuth lanthanum titanate thin films with excess Bi contents were prepared onto Pt/Ti/$SiO_2$/Si substrate by metalorganic decomposition (MOD) technique. The structure and morphology of the films were analyzed using X-ray diffraction (XRD) and atomic force microscopy (AFM), respectively. From the XRD analysis, BLT thin films show polycrystalline structure and the layered-perovskite phase was obtained over 10% excess of Bi contents. As a result of ferroelectric characteristics related to the Bi content of the BLT thin film, the remanent polarization and dielectric constant decreased with increasing over Bi content of 10 % excess. The BLT film with Bi content of 10% excess was measured to have a dielectric constant of n9 and dielectric loss of 1.85[%]. The BLT thin films showed little polarization fatigue test up to 3.5 x $10^{9}$ bipolar switching cycling.

• 한국전기전자재료학회논문지
• /
• 제15권9호
• /
• pp.764-769
• /
• 2002

The effect of excess Bi contents on the ferroelectric properties of B $i_{3.25}$ L $a_{0.75}$ $Ti_3$ $O_{12}$ (BLT) thin films has been investigated. Bismuth lanthanum titanate thin films with excess Bi contents were prepared onto Pt/Ti/ $SiO_2$/Si substrate by metalorganic decomposition (MOD) technique. The structure and morphology of the films were analyzed using X-ray diffraction (XRD) and atomic force microscopy (AFM), respectively. From the XRD analysis, BLT thin films show polycrystalline structure and the layered-perovskite phase was obtained over 10% excess of Bi contents. As a result of ferroelectric characteristics related to the Bi content of the BLT thin film, the remanent polarization and dielectric constant decreased with increasing over Bi content of 10% excess. The BLT film with Bi content of 10% excess was measured to have a dielectric constant of 326 and dielectric loss of 0.024. The BLT thin films showed little polarization fatigue test up to 3.5$\times$10$^{9}$ bipolar switching cycling.

• 한국전기전자재료학회논문지
• /
• 제20권7호
• /
• pp.575-580
• /
• 2007

A 16 Mb 1T1C FeRAM device was integrated with BLT capacitors. But a lot of cells were failed randomly during the measuring the bit-line signal distribution of each cell. The reason was revealed that the grain size and orientation of the BLT thin film were severely non-uniform. And the grain size and orientation were severely affected by the process conditions of post heat treatment, especially nucleation step. The optimized annealing temperature at the nucleation step was $560^{\circ}C$. The microstructure of the BLT thin film was also varied by the annealing time at the step. The longer process time showed the finer grain size. Therefore, the uniformity of the grain size and orientation could be improved by changing the process conditions of the nucleation step. The FeRAM device without random bit-fail cell was successfully fabricated with the optimized BLT capacitor and the sensing margin in bit-line signal distribution of it was about 340 mV.

• 한국전기전자재료학회논문지
• /
• 제18권5호
• /
• pp.439-444
• /
• 2005

We investigated the structural and electrical properties of BLT films grown on Si covered with $ZrO_{2}$ buffer layer. The BLT thin film and $ZrO_{2}$ buffer layer were fabricated using a metalorganic decomposition method. The electrical properties of the MFIS structure were investigated by varying thickness of the $ZrO_{2}$ layer. AES and TEM show no interdiffusion and reaction that suppressed using the $ZrO_{2}$ film as a buffer layer The width of the memory window in the C-V curves for the MFIS structure decreased with increasing thickness of the $ZrO_{2}$ layer. It is considered that the memory window width of MFIS is not affected by remanent polarization. Leakage current density decreased by about four orders of magnitude after using $ZrO_{2}$ buffer layer. The results show that the $ZrO_{2}$ buffer layers are prospective candidates for applications in MFIS-FET memory devices.

• 한국세라믹학회지
• /
• 제40권12호
• /
• pp.1189-1196
• /
• 2003

Sol-gel법으로 강유전성 B $i_{3.25}$L $a_{0.75}$ $Ti_3$ $O_{12}$ (BLT) stock solution을 합성하고 Pt/Ti $O_2$/ $SiO_2$/Si 기판위에 스핀코팅법으로 BLT 박막을 증착하였다. 본 실험에서는 Bi(TMHD)$_3$, La(III)2-Methoxyethoxide, Ti(IV)i-propoxide를 출발물질로 사용하였으며 2-Methoxyethanol을 용매로 사용하였다. 급속열처리(RTA)가 BLT 박막의 결정성장을 촉진시키기 위해 사용되었고, RTA를 실시한 시편과 RTA를 실시하지 않은 시편의 전기적 특성을 비교하였다. RTA를 실시한 후 72$0^{\circ}C$에서 로 열처리 한 BLT 박막의 경우 5V 인가 전압 하에서 2Pr 값은 RTA를 실시하지 않은 경우보다 27% 증가한 20.46$\mu$C/$ extrm{cm}^2$이었다.

• 한국결정성장학회지
• /
• 제13권2호
• /
• pp.56-62
• /
• 2003

졸-겔법을 이용하고 금속 나프테네이트를 출발원료로 사용하여 $SrTiO_3$(100), $LaA1O_3$(100) 및 MgO(100) 기판 위에 에피탁샬 $Bi_4Ti_3O_{12}$ 박막을 제조하였다. 코팅된 전구막은 $500^{\circ}C$에서 10분간 전열처리 하였고, $750^{\circ}C$에서 30분간 최종 열처리를 행하였다. 박막의 결정화도는 X-선회절 분석법 ($\theta$-2$\theta$ 스캔과 $\beta$ 스캔)으로 조사하였고, 표면 미세구조와 거칠기를 field emission-scanning electron microscope와 atomic force microscope를 이용하여 각각 분석하였다. MgO(100) 기판 위에 제조한 박막은 모든 기판 중에서 가장 낮은 결정화도와 면내 배향성을 보였다. 가장 낮은 결정화도와 배향성을 보인 MgO(100) 기판위의 박막은 침상 형태로 성장한 반면, 결정성과 배향성이 좋은 $LaA1O_3$(100)과 $SrTiO_3$(100) 기판위의 박막들은 원형의 입자 성장 형태를 보이고 있었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 춘계학술대회 논문집 센서 박막재료 반도체 세라믹
• /
• pp.116-119
• /
• 2003

Self-patterning of thin films using photosensitive sol solution has advantages such as simple manufacturing process compared to photoresist/dry etching process. In this study, ferroelectric $Sr_{0.9}Bi_{2.1}Ta_2O_9$(SBT) and $La_{0.5}Sr_{0.5}CoO_3$(LSCO)thin films have been prepared by spin coating method using photosensitive sol solution. $Sr(OC_2H5)_2$, $Bi(TMHD)_3$ and $Ta(OC_2H)_5)_5$ were used as starting materials for SBT solution and $La(OCH_2CH_2OCH_3)_3$, $Sr(OC_2H_5)_2$, $CO(OCH_2CH_2OCH_3)_2$ were used for LSCO solution. Solubility difference by UV irradiation on LSCO thin film allows to obtain a fine patterning due to M-O-M bond formation. The lowest resistivity($4{\times}10^{-3}{\Omega}cm$) of LSCO thin films was obtained by annealing at $740^{\circ}C$.