$BiFeO_3$(BFO), when forming a solid solution with $BaTiO_3$(BTO), shows structural transformations over the entire compositional range, which not only gives a way to increase structural stability and electrical resistivity but also applies a means to have better ferromagnetic ordering. In this respect, we have prepared and studied 0.7BFO-0.3BTO thin films on $Pt(111)/TiO_2/SiO_2/Si$ substrates by pulsed laser deposition. Various deposition parameters, such as deposition temperature and oxygen pressure, have been optimized to get better quality films. Based on the X-ray diffraction results, thin films were successfully deposited at the temperature of $600^{\circ}C$ and an oxygen partial pressure of 10mTorr. The dielectric, ferroelectric, and magnetic properties have then been characterized. It was found that the films deposited under lower oxygen pressure corresponded to lower leakage current. Magnetism measurement showed an induced ferromagnetism. The microstructures associated with. the magnetic and dielectric properties of this mixed-perovskite solid solutions were observed by transmission electron. microscopy, which revealed the existence of complicated ferroelectric domains, suggested that the weak spontaneous magnetization was closely associated with the decrease in the extent of rhombohedral distortion by a partial substitution of $BaTiO_3$ for $BiFeO_3$.

• Bulletin of the Korean Chemical Society
• /
• 제33권7호
• /
• pp.2305-2308
• /
• 2012

Perovskite structured barium titanate particles ($BaTiO_3$) platelets were synthesized by molten salt synthesis and topochemical microcrystal conversion. As the precursors of $BaTiO_3$, plate-like $BaBi_4Ti_4O_{15}$ particles were first synthesized by the reaction of $Bi_4Ti_3O_{12}$, $BaCO_3$, and $TiO_2$ at $1080^{\circ}C$ for 3 h in $BaCl_2$-KCl molten salt. After the topochemical reactions, layer-structured $BaBi_4Ti_4O_{15}$ particles transformed to the perovskite $BaTiO_3$ platelets. $BaTiO_3$ particles with thickness of approximately $0.5{\mu}m$ and a length of $10-15{\mu}m$ retained the morphology feature of the $BaBi_4Ti_4O_{15}$ precursor. For <001> $Pb(Mg_{1/3}Nb_{2/3})O_3-32.5PbTiO_3$ (PMNT)-5 wt % PbO piezoelectric ceramics textured with 5 vol % of $BaTiO_3$ templates, the Lotgering factor reached 0.82, and $d_{33}$ was 870 pC/N.

• 한국산학기술학회논문지
• /
• 제8권5호
• /
• pp.995-999
• /
• 2007

저온 소결용 압전 세라믹 소결체의 치밀화에 미치는 첨가제의 영향을 조사하기 위하여 $PbZrTiO_3$(PZT) 분말을 제조하였으며, 이 PZT 분말을 이용하여 제조한 압전 세라믹스의 치밀화에 미치는 첨가제의 영향을 조사하였다. 첨가제는 $wB_2O_3-xBi_2O_3-zCuO$와 $LiBiO_2-CuO$ 두 종류가 제조되었으며 이 들 첨가제의 양을 변화 시켜 효과를 조사하였다. PZT 분말에 소결조제로서 1wt.% 의 $LiBiO_2-CuO$를 첨가하여 시편을 제조한 후, $800{\sim}1200^{\circ}C$까지의 온도 범위에서에서 소결한 결과 $900^{\circ}C$에서 최고의 소결밀도를 나타내었다. 소결된 압전체의 결정상을 분석하기 위하여 X-선회절분석을 시행하였으며, $900^{\circ}C$의 저온에서 소결한 $PbZrTiO_3$의 시편의 미세조직을 관찰하기 위하여 주사전자현미경(SEM)을 이용하였다. X-선 회절분석에서는 잘 발달된 PZT 상이 나타났으며, SEM 관찰 결과 평균입경은 $2{\sim}4\;{\mu}m$의 페로브스카이트 결정으로 균일하고 치밀한 조직을 나타내었으며, 높은 소결성은 첨가제에 의한 액상소결에 기인한다.

• 한국세라믹학회지
• /
• 제35권10호
• /
• pp.1040-1048
• /
• 1998

Ferroelectric properties of{{{{ { { { {SrBi }_{2 }Ta }_{2-x }Nb }_{x }O }_{9 } }} (SBIN) thin films were affected by the amount of Bi content in SBTN. The addition of Bi into the SBTN films could be accomplished by heat treating SBTN/Bi2O3/SBTN het-erostructures fabricated by r.f. magnetron sputtering method. The variation of Bi content was controlled by changing the thickness of the sandwiched Bi2O3 in SBTN/Bi2O3/SBTN heterostructure from 50 to 400$\AA$. As changing the thickness of the sandwiched Bi2O3 in Bi2O3 films was increased from 0 to 100$\AA$ the grain grew faster and the ferroelectric pro-perties were improved. On the other hand when the thickness of Bi2O3 films was thicker than 150$\AA$ the fer-roelectric properties were deteriorated Especially for SBTN thin films inserted by 400$\AA$ Bi2O3 layer a Bi2Phase appeared as a second phase resulting in poor ferroelectric properties. The maximum remanent po-larization (2Pr) and coercive field(Ec) were obtained for the SBTN/Bi2O3/(100$\AA$)/SBTN thin films. In this case 2Pr and Ec were 14.75 $\mu$C/cm2 and 53.4kV/cm at an applied voltage of 3V respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.1
• /
• pp.245-248
• /
• 2003

Randomly oriented ferroelectric cerium-substituted $Bi_4Ti_3O_{12}$ thin films have been prepared by using metal-organic decomposition method. The layered perovskite structure was investigated using annealing for 1 h in the temperature range from $550\;{\sim}\;750\;^{\circ}C$. The structure and morphology of the films were characterized using X-ray diffraction and scanning electron microscopy The $Bi_{3.4}Ce_{0.6}Ti_3O_{12}$ (BCeT) thin films showed a perovskite phase and dense microstructure. The grain size of the BCeT films increasedwith increasing annealing temperature. The hysteresis loops of the films were well defined at temperatures above $600\;^{\circ}C$. The 200-nm-thick BCeT thin films annealed at $650\;^{\circ}C$ showed a large remanent polarization (2Pr) of 59.3 ${\mu}C/cm^2$ at an applied voltage of 10 V. The BCeT thin films showed good fatigue endurance up to $5\;{\times}\;10^9$ bipolar cycling at 5 V and 100 kHz.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.217-220
• /
• 2000

The SrBi$_2$Ta$_2$O$\_$9/(SBT) thin films are deposited on Pt-coated electrode(Pt/TiO$_2$/SiO$_2$/Si) using RF sputtering method. The SBT thin films deposited on substrate at 400-500[$^{\circ}C$]. SBT thin film deposited on Pt-coated electrodes have the cubic perovskite structure and polycrystalline state. With increasing annealing temperature from 600[$^{\circ}C$] to 850[$^{\circ}C$], flourite phase was crystallized to 650[。 and Bi-layered perovskite phase was crystallize ed above 700[$^{\circ}C$]. The maximum remnant polarization and the coercive electric field is 11.73[${\mu}$C/$\textrm{cm}^2$], 85[kV/cm] respectively at annealing temperature of 750[$^{\circ}C$]. The fatigue characteristics of SBT thin films deposited on Pt/TiO$_2$/SiO$_2$/Si substrate did not change up to 10$\^$10/ switching cycles.

• 한국결정성장학회지
• /
• 제25권4호
• /
• pp.160-165
• /
• 2015

Lead-free piezoelectric materials have been actively studied to substitute for conventional PZT based solid solution, $Pb(Zr_xTi_{1-x}O_3)$, which occurs unavoidable PbO during the sintering process. Among them, Bismuth Sodium Titanate, $Na_{0.5}Bi_{0.5}TiO_3$ (abbreviated as NBT) based solid solution is attracted for the one of excellent candidates which shows the strong ferroelectricity, Curie temperature (Tc), remnant polarization (Pr) and coercive field (Ec). Especially, the solid solution of rhombohedral phase NBT with tetragonal perovskite phase has a rhombohedral - tetragonal morphotropic phase boundary. Modified NBT with tetragonal perovskite at the region of MPB can be applied for high frequency ultrasonic application because of not only its low permittivity, high electrocoupling factor and high mechanical strength, but also effective piezoelectric activity by poling. In this study, solid state ceramic processing of NBT and modified NBT, $(Na_{0.5}Bi_{0.5})_{0.93}Ba_{0.7}TiO_3$ (abbreviated as NBT-7BT), at the region of MPB using 7 % $BaTiO_3$ as a tetragonal perovskite was introduced and the structure between NBT and NBT-7BT were analyzed using rietveld refinement. Also, the ferroelectric and piezoelectric properties of NBT-7BT such as permittivity, piezoelectric constant, polarization hysteresis and strain hysteresis loop were compared with those of pure NBT.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.32-32
• /
• 2008

Microstructure and positive temperature coefficient of resistivity (PTCR) characteristics of $0.9BaTiO_3-0.1(Bi_{0.5}Na_{0.5})TiO_3$ [BaBiNT] ceramics doped with $Nb_2O_5$ were investigated in order to develop the Pb-free high Curie temperature ($T_c$)(>$160^{\circ}C$) PTC thermistor. The BaBiNT ceramics showed a tetragonal perovskite structure, irrespective of the added amount of $Nb_2O_5$. They also have a homogeneous microstructure. The resistivity of BaBiNT ceramics was gradually decreased by doping $Nb_2O_5$, which might be due to $Nb^{+5}$ ions substituting for $Ti^{+4}$ sites. The PTCR characteristics of BaBiNT ceramics appeared when the amount of doped $Nb_2O_5$ exceeded 0.0025mol%. Moreover, the abrupt grain growth was observed for the 0.03mol% $Nb_2O_5$added BaBiNT ceramics. It showed an especially high $T_c$ of approximately $172^{\circ}C$ and good PTCR characteristics of a high $\rho_{max}/\rho_{min}$ ratio ($2.96\times10^3$), a high resistivity temperature factor (11.40/$^{\circ}C$) along with a relatively low resistivity ($3.5\times10^4\Omega{\cdot}cm$).

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2009년도 춘계학술발표대회
• /
• pp.33.2-33.2
• /
• 2009

Dielectric and piezoelectric properties of Lead-free $(1-x)(Bi_{0.5}K_{0.5})TiO_3-xBiFeO_3$ceramics prepared by a conventional solid state reaction method were investigated in the range of x = 0~10 mol%. Piezoelectric coefficient was increased from 31 pC/N at x = 0 mol% to 64 pC/N at x = 6 mol% then decreased with increasing x. Electromechanical coupling factor ($K_p$) was increased up to 0.18 at x = 10 mol%. On the other hand, mechanical quality factor ($Q_m$) was decreased. Grain size was not much changed with various x and a single perovskite with tetragonal symmetry was maintained at all compositions forming a solid solution between $(Bi_{0.5}K_{0.5})TiO_3$ and $BiFeO_3$. Depolarization temperature ($T_d$) was gradually decreased with increasing x from $302^{\circ}C$ at x = 0 to $245^{\circ}C$ at x = 10 mol%.

• 한국재료학회지
• /
• 제30권2호
• /
• pp.61-67
• /
• 2020

BiFeO₃ with perovskite structure is a well-known material that has both ferroelectric and antiferromagnetic properties called multiferroics. However, leaky electrical properties and difficulty of controlling stoichiometry due to Bi volatility and difficulty of obtaining high relative density due to high dependency on the ceramic process are issues for BiFeO₃ applications. In this work we investigated the sintering behavior of samples with different stoichiometries and sintering conditions. To understand the optimum sintering conditions, nonstoichiometric Bi_1±xFeO_3±δ ceramics and Ti-doped Bi_1.03Fe_1-4x/3Ti_xO₃ ceramics were synthesized by a conventional solid-state route. Dense single phase BiFeO₃ ceramics were successfully fabricated using a two-step sintering and quenching process. The effects of Bi volatility on microstructure were determined by Bi-excess and Ti doping. Bi-excess increased grain size, and Ti doping increased sintering temperature and decreased grain size. It should be noted that Ti-doping suppressed Bi volatility and stabilized the BiFeO₃ phase.