• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.423-423
• /
• 2007

In this study, the effects of annealing conditions on the structural and optical properties of ZnO films were investigated. ZnO oxide (ZnO) films were deposited onto $SiO_2$/Si substrates by RF magnetron sputtering from a ZnO target. The substrate was not heated during deposition. ZnO films were annealed in temperature ranges of $500{\sim}650^{\circ}C$ in the $O_2$ flow for 5 ~ 20 min. The film average thicknesses were in the range of 291 nm. The surface morphologies and structures of the samples were characterized by SEM and XRD, respectively. The optical properties were evaluated by PL measurement at room temperature using a He-Cd 325 nm laser. According to the results, the optimal annealing conditions for the best photoluminescence (PL) characteristics were found to be oxygen fraction, ($O_2/O_2+Ar$) of 20%, RF power of 240W, substrate temperature of RT (room temperature), annealing condition of $600^{\circ}C$ for 20 min, and sputtering pressure of 20 mTorr. The obtained wavelength of light emission was found at 379 nm (ultraviolet-UV region). However, the optimal parameters for the best PL characteristics of ZnO thin films were not consistent with those obtained from the (002) intensities of XRD analyses. As a result, XRD pattern was not considered as the key issue concerning the intensity of PL of ZnO thin film. The intensity of the emitted UV light will correspond to the grain size of ZnO film.

• Proceedings of the KIEE Conference
• /
• 2007.07a
• /
• pp.1275-1276
• /
• 2007

For fabrication of $BaTiO_3$ system Ferroelectric thick films, (Ba,Sr,Ca)$TiO_3$ (BSCT) powders, prepared by using the alkoxide-based sol-gel method, were doped $MnCO_3$ as acceptor and $Dy_{2}O_{3}$ as donor. $MnCO_3$ and $Dy_{2}O_{3}$-doped (Ba,Sr,Ca)$TiO_3$ thick films were fabricated by screen printing techniques on high purity alumina substrates. The structure and dielectric properties were investigated with variation of $Dy_{2}O_{3}$ amount. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All the BSCT thick films, sintered at $1420^{\circ}C$ for 2h, showed the typical XRD patterns of perovskite polycrystalline structure and no pyrochlore phase was observed. The average grain size and thickness of specimens no doped with $Dy_{2}O_{3}$ was 1.32mm, 52mm, respectively. The relative dielectric constant decreased and dielectric loss increased with increasing amount of $Dy_{2}O_{3}$ dopant, the values of the BSCT thick films no doped with $Dy_{2}O_{3}$ were 4043 and 0.4% at 1 kHz, respectively. The relative dielectric constant gradually decreased in the measured frequency range from 0.1 to 100 kHz

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.296-296
• /
• 2007

Ferroelectric neodymium-substituted $Bi_4Ti_3O_{12}$(BTO) thin films have been successfully deposited on Pt/Ti/$SiO_2$/Si substrate by a sol-gel spin-coating process and the effect of crystallization temperature on their microstructure and ferroelectric properties were studied systematically. $Bi(TMHD)_3$, $Nd(TMHD)_3$, $Ti(O^iPr)_4$ were used as the precursors, which were dissolved in 2-methoxyethanol. The thin films were annealed at various temperatures from 600 to $720^{\circ}C$ in oxygen ambient for 1 hr, which was followed by post-annealed for 1 hr after depositing a Pt electrode to enhance the electrical properties. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to analyze the crystallinity and surface morphology of layered perovskite phase, respectively. The crystallinity of the BNT films was improved and the average grain size increased as the crystallization temperature increased from 600 to $720^{\circ}C$ at an interval of $40^{\circ}C$. The polarization values of the films were a monotonous function of the crystallization temperature. The remanent polarization value of the BNT thin films annealed at $720^{\circ}C$ was $24.82\;{\mu}C/cm^2$ at an applied voltage of 5 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.336-337
• /
• 2005

ZnO varistor ceramics were fabricated as a function of the amount of $Y_2O_3$ addition and sintered at $1250^{\circ}C$ for 2 hour. The average grain size was decreased from 14.2 ${\mu}m$ to 8.3 ${\mu}m$ with the amount of $Y_2O_3$ addition, and varistor voltage was increased from 433 V to 563 V with $Y_2O_3$ addition. Nonlinear coefficient a of all specimens were increased with the amount of $Y_2O_3$ more than 67, in case of $Y_2O_3$ 0.01wt% addition showed the excellent results of 87. And leakage current was less than $1{\mu}A$ at 82% of varistor voltage. The clamping voltage ratio of the specimens added 0.01wt% $Y_2O_3$ was 1.41 at 25A [8/20${\mu}s$]. At the specimen 0.01wt% $Y_2O_3$ addition. endurance of surge current and deviation of varistor voltage were 5700A/$cm^2$ and $\Delta$-2.86%, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.7
• /
• pp.581-586
• /
• 2007

[ $(Ba_{0.57}Sr_{0.33}Ca_{0.10})TiO_3$ ] (BSCT) powders, prepared by sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen printing method. The structural and dielectric properties were investigated as a function of the $Yb_2O_3$ doping contents. As a result of the TG-DTA, exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All BSCT thick films showed the typical XRD patterns of a cubic polycrystalline structure. The average thickness of all BSCT thick films was about $70{\mu}m$. The grain size of the BSCT thick film doped with 0.7 mol% $Yb_2O_3$ was approximately $6.2{\mu}m$. The Curie temperature and relative dielectric constant at room temperature decreased with increasing $Yb_2O_3$ amount. Relative dielectric constant and dielectric loss of the specimen doped with 0.1 mol% $Yb_2O_3$ were 4637 and 19 % at Curie temperature, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.204.2-204.2
• /
• 2013

Wide band gap II-VI semiconductors have attracted the interest of many research groups during the past few years due to the possibility of their applications in light-emitting diodes and laser diodes. Among the II-VI semiconductors, ZnO is an important optoelectronic device material for use in the violet and blue regions because of its wide direct band gap (Eg ~3.37 eV) and large exciton binding energy (60 meV). F-doped ZnO (FZO) and undoped ZnO thin films were grown onto quartz substrate by the sol-gel spin-coating method. The doping level in the solution, designated by F/Zn atomic ratio of was varied from 0 to 5 in 1 steps. To investigate the effects of the structure and optical properties of FZO thin films were investigated using X-ray diffraction (XRD), UV-visible spectroscopy, and photoluminescence (PL). In the XRD, the residual stress, FWHM, bond length, and average grain size were changed with increasing the doping concentration. For the PL spectra, the high INBE/IDLE ratio of the FZO thin films doping concentration at 1 at.% than the other samples.

• Korean Journal of Materials Research
• /
• v.13 no.10
• /
• pp.645-650
• /
• 2003

The microstructure and electrical characteristics of $Pr_{6}$ $O_{11}$ -based ZnO varistor ceramics composed of $ZnO-Pr_{6}$ $O_{ 11}$/$-CoO-Cr_2$$O_3$-$Dy_2$$O_3$-based ceramics were investigated with $Dy_2$$O_3$content in the range of 0.0∼2.0 mol%. As $Dy_2$$O_3$content was increased, the average grain size was decreased in the range of 18.6∼4.7 $\mu\textrm{m}$ and the density of the ceramic was decreased in the range of 5.53∼4.34 g/㎤. While, the varistor voltage was increased in the range of 39.4∼436.6 V/mm and the nonlinear exponent was in the range of 4.5∼66.6 with increasing $Dy_2$$O_3$content. The addition of $Dy_2$$O_3$highly enhanced the nonlinear properties of varistors, compared with the varistor without $Dy_2$$O_3$. In particular, the varistor with $Dy_2$$O_3$ content of 0.5 mol% exhibited the highest nonlinearity, in which the nonlinear exponent is 66.6 and the leakage current is 1.2 $\mu\textrm{A}$. The donor concentration and the density of interface states were decreased in the range of $(4.19∼0.33) ${\times}$10^{18}$ //㎤ and $(5.38∼1.74) ${\times}$10^{12}$ $\textrm{cm}^2$, respectively, with increasing $Dy_2$$O_3$content. The minimum dissipation factor of 0.0302 was obtained from 0.5mol% $Dy_2$$O_3$.

• Journal of Magnetics
• /
• v.18 no.3
• /
• pp.245-249
• /
• 2013

A finite element model was built for MnBi/${\alpha}$-Fe nanocomposite permanent magnets, and the demagnetization curves of the magnets were simulated by micro-magnetic calculation. The microstructure of the cubic model is composed of 64 irregular grains with an average grain size of 20 nm. With the volume fraction of soft magnetic phase (t vol. %) ranged from 5 to 20 vol. %, both isotropic and anisotropic nanocomposite magnets show typical single-phase permanent magnets behavior in their demagnetization curves, illustrating good intergranular exchange coupling effect between soft and hard magnetic phases. With the increase of volume fraction of soft magnetic phase in both isotropic and anisotropic magnets, the coercive force of the magnets decreases monotonically, while the remanence rises at first to a peak value, then decreases. The optimal values of maximum energy products of isotropic and anisotropic magnets are 84 and $200kJ/m^3$, respectively. Our simulation shows that the MnBi/${\alpha}$-Fe nanocomposite permanent magnets own excellent magnetic properties and therefore good potential for practical applications.

• Transactions of Materials Processing
• /
• v.30 no.1
• /
• pp.5-15
• /
• 2021

The effects of heat treatments (T6 and T73) on the microstructure, mechanical properties, and high cycle fatigue behavior of modified AA7075 alloys were investigated. A modified 7075 alloy was manufactured using modified-Mg (Mg-Al2Ca) instead of the conventional element Mg. Based on the microstructure, the average grain size was 4.5 ㎛ (T6) and 5.2 ㎛ (T73). Regardless of heat treatment, the modified AA7075 alloys consisted of Al matrix containing homogeneously distributed Al2CuMg and MgZn2 phases with reduced Fe-intermetallic compound. Room temperature tensile tests showed that the properties of modified 7075-T6 (Y.S.: 622MPa, T.S: 675MPa, elongation: 15.4%) were superior to those of T73 alloy (Y.S.: 492MPa, T.S: 548MPa, elongation: 12.8%). Experimental data show that the fatigue life of T6 was 400 MPa, about 64% of its yield strength. However, the fatigue life of T73 alloy was 330 MPa and 67%. Irrespective of the stress level, all crack initiation points were located on the specimen surface, and no inclusions acting as stress concentrators were seen. Superior mechanical properties and high cycle fatigue behavior of modified AA7075-T6 alloy are attributed to the fine grains and homogeneous distribution of small second phases such as MgZn2 and Al2CuMg, in addition to reduced Fe-intermetallic compounds.

• Korean Journal of Metals and Materials
• /
• v.46 no.4
• /
• pp.189-198
• /
• 2008

The changes in microstructure and mechanical properties of AZ31 alloy subjected hot-rolling process were investigated. The AZ31 plates fabricated by horizontal continuous casting process were prepared and have hot-rolled from 30 mm to 1 mm in thickness under different processing conditions. At the rolling temperature of $400^{\circ}C$, little surface and side crack was observed up to 20% reduction rate. As total reduction and reduction rate increase to more than 75% and 20% pass, respectively, Grains were more uniformly refined through overall thickness, and particularly lots of shear bands were appeared to be inclined at less than $20^{\circ}C$ along the rolling direction. Average grain size of less than $5{\mu}m$ and tensile properties of YS ${\geq}$ 250 MPa, UTS ${\geq}$ 300 MPa and El. ${\geq}$ 13% were acquired for hot-rolled AZ31 sheets without post-heat treatment. Maximum intensity of (0002) pole figure was decreased with an increase in reduction rate, indicating the improvement of texture by means of high reduction rate.