• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.08a
• /
• pp.109-109
• /
• 2011

CO oxidaition reacitvity of bare and $TiO_2$ -coated NiO/$Ni(OH)_2$ nanoparticles was studied. For the deposition of $TiO_2$ atomic layer deposition was used, and formation of three-dimensional island of $TiO_2$ on NiO/$Ni(OH)_2$ could be identified. Based on the data of X-ray Photoelectron Spectroscopy, we suggest that only $Ni(OH)_2$ existed on the surface, whereas NiO disappeared upon $TiO_2$ deposition. Both CO adsorption and CO oxidation took place on NiO/$Ni(OH)_2$ surfaces under our experimental conditions. CO adsorption was completely suppressed after $TiO_2$ deposition, whereas CO oxidation activity was maintained to large extent. It is proposed that bare NiO can uptake CO under our experimental condition, whereas hydroxylated surface of NiO can be active for CO oxidation.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.211-211
• /
• 2012

The electrical loss of the photo-generated carriers is dominated by the recombination at the metal- semiconductor interface. In order to enhance the performance of the solar cells, many studies have been performed on the surface treatment with passivation layer like SiN, SiO2, Al2O3, and a-Si:H. In this work, Al2O3 thin films were investigated to reduce recombination at surface. The Al2O3 thin films have two advantages, such as good passivation properties and back surface field (BSF) effect at rear surface. It is usually deposited by atomic layer deposition (ALD) technique. However, ALD process is a very expensive process and it has rather low deposition rate. In this study, the ICP-assisted reactive magnetron sputtering method was used to deposit Al2O3 thin films. For optimization of the properties of the Al2O3 thin film, various fabrication conditions were controlled, such as ICP RF power, substrate bias voltage and deposition temperature, and argon to oxygen ratio. Chemical states and atomic concentration ratio were analyzed by x-ray photoelectron spectroscopy (XPS). In order to investigate the electrical properties, Al/(Al2O3 or SiO2,/Al2O3)/Si (MIS) devices were fabricated and characterized using the C-V measurement technique (HP 4284A). The detailed characteristics of the Al2O3 passivation thin films manufactured by ICP-assisted reactive magnetron sputtering technique will be shown and discussed.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.264-264
• /
• 2016

최근에 charge trap flash (CTF) 기술은 절연막에 전하를 트랩과 디트랩 시킬 때 인접한 셀 간의 간섭현상을 최소화하여 오동작을 줄일 수 있으며 낸드 플래시 메모리 소자에 적용되고 있다. 낸드 플래시 메모리는 고집적화, 대용량화와 비휘발성 등의 장점으로 인해 핸드폰, USB, MP3와 컴퓨터 등에 이용되고 있다. 기존의 실리콘 기반의 플래시 메모리 소자는 좁은 밴드갭으로 인해 투명하지 않고 고온에서의 공정이 요구되는 문제점이 있다. 따라서, 이러한 문제점을 개선하기 위해 실리콘의 대체 물질로 산화물 반도체 기반의 플래시 메모리 소자들이 연구되고 있다. 산화물 반도체 기반의 플래시 메모리 소자는 넓은 밴드갭으로 인한 투명성을 가지고 있으며 저온에서 공정이 가능하여 투명하고 유연한 기판에 적용이 가능하다. 다양한 산화물 반도체 중에서 비정질 In-Ga-Zn-O (a-IGZO)는 비정질임에도 불구하고 우수한 전기적인 특성과 화학적 안정성을 갖기 때문에 많은 관심을 받고 있다. 플래시 메모리의 고집적화가 요구되면서 절연막에 high-k 물질을 atomic layer deposition (ALD) 방법으로 적용하고 있다. ALD 방법을 이용하면 우수한 계면 흡착력과 균일도를 가지는 박막을 정확한 두께로 형성할 수 있는 장점이 있다. 또한, high-k 물질을 절연막에 적용하면 높은 유전율로 인해 equivalent oxide thickness (EOT)를 줄일 수 있다. 특히, HfOx와 AlOx가 각각 trap layer와 blocking layer로 적용되면 program/erase 동작 속도를 증가시킬 수 있으며 넓은 밴드갭으로 인해 전하손실을 크게 줄일 수 있다. 따라서 본 연구에서는 ALD 방법으로 AlOx와 HfOx를 게이트 절연막으로 적용한 a-IGZO 기반의 thin-film transistor (TFT) 플래시 메모리 소자를 제작하여 메모리 특성을 평가하였다. 제작 방법으로는, p-Si 기판 위에 열성장을 통한 100 nm 두께의 SiO2를 형성한 뒤, 채널 형성을 위해 RF sputter를 이용하여 70 nm 두께의 a-IGZO를 증착하였다. 이후에 소스와 드레인 전극에는 150 nm 두께의 In-Sn-O (ITO)를 RF sputter를 이용하여 증착하였고, ALD 방법을 이용하여 tunnel layer에 AlOx 5 nm, trap layer에 HfOx 20 nm, blocking layer에 AlOx 30 nm를 증착하였다. 최종적으로, 상부 게이트 전극을 형성하기 위해 electron beam evaporator를 이용하여 platinum (Pt) 150 nm를 증착하였고, 계면 결함을 최소화하기 위해 퍼니스에서 질소 가스 분위기, $400^{\circ}C$, 30 분의 조건으로 열처리를 했다. 측정 결과, 103 번의 program/erase를 반복한 endurance와 104 초 동안의 retention 측정으로부터 큰 열화 없이 메모리 특성이 유지되는 것을 확인하였다. 결과적으로, high-k 물질과 산화물 반도체는 고성능과 고집적화가 요구되는 향후 플래시 메모리의 핵심적인 물질이 될 것으로 기대된다.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.3
• /
• pp.31-35
• /
• 2016

This paper demonstrates the successful application of yttria-stabilized zirconia thin films deposited by atomic layer deposition to the anode-side interlayer for cerium oxide electrolyte based solid oxide fuel cell. At the operating temperature over $500^{\circ}C$, the electrical conductivity of cerium oxide electrolyte is known to dramatically increase and, therefore, the open circuit voltage of the cell decreases leading to the decrease of the performance. Ultra-thin (60 nm) atomic layer deposited yttria-stabilized zirconia thin film in this study conformally coated the anode-side surface of the cerium oxide electrolyte and efficiently blocked the electrical conduction through the electrolyte. Accordingly, the open circuit voltage increased by up to 20%, and the maximum power density increased by 52% at $500^{\circ}C$

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.35 no.1
• /
• pp.80-85
• /
• 2022

ZnO-based transparent conductive films have been widely studied to achieve high performance optoelectronic devices such as next generation flexible and transparent display systems. In order to achieve a transparent flexible ZnO-based device, a low temperature growth technique using a flexible polymer substrate is required. In this work, high quality flexible ZnO films were grown on colorless polyimide substrate using atomic layer deposition (ALD). Transparent ZnO films grown from 80 to 200℃ were fabricated with a metal-semiconductor-metal structure photodetectors (PDs). As the growth temperature of ZnO film increases, the photocurrent of UV PDs increases, while the sensitivity of that decreases. In addition, it is found that the response times of the PDs become shorter as the growth temperature increases. Based on these results, we suggest that high-quality ZnO film can be grown below 200℃ in an atomic layer deposition system, and can be applied to transparent and flexible UV PDs with very fast response time and high photocurrent.

• Korean Journal of Materials Research
• /
• v.12 no.6
• /
• pp.493-498
• /
• 2002

$Al_2O_3$ is a promising gate dielectric because of its high dielectric constant, high resistivity and low leakage current. Since $OH^-$ radical in $Al_2O_3$ films deposited by ALD using TMA and $H_2O$ degrades the good properties of $Al_2O_3$, TMA and $O_3$ were used to deposite $Al_2O_3$ films and the effects of $O_3$ on the properties of the $Al_2O_3$ films were investigated. The growth rate of the $Al_2O_3$ film under the optimum condition was 0.85 $\AA$/cycle. According to the XPS analysis results the $OH^-$ concentration in the $Al_2O_3$ film deposited using $O_3$ is lower than that using $H_2O$. RBS analysis results indicate the chemical formula of the film is $Al_{2.2}O_{2.8}$. The carbon concentration in the film detected by AES is under 1 at%. SEM observation confirms that the step coverage of the $Al_2O_3$ film deposited by ALD using $O_3$ is nearly 100%.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.2C no.6
• /
• pp.314-320
• /
• 2002

Three different ZnO nanomaterials (nanobelts, nanorods, and nanowires) were synthesized at 138$0^{\circ}C$ from ball-milled ZnO powders by a thermal evaporation procedure with an argon carrier gas without any catalysts. Transmission electron microscopy (TEM) revealed that the ZnO nanobelts are single crystalline with the growth direction perpendicular to the (010) lattice plane, and that the ZnO nanorods and nanowires are single crystalline with the growth directions perpendicular to the (001) and (110) lattice Planes, respectively. In cathodoluminescence (CL), the energy Position of the near band-edge (NBE) peak is 3.280 eV for the 100-, 250-, and 500-nm thick nanobelts, 3.262 eV for the 100- and 250-nm thick nanorods, and 3.237 eV for the 500-nm thick nanorods. The synthesized ZnO nanorods were coated conformally with aluminum oxide (Al$_2$O$_3$) material by atomic layer deposition (ALD). $Al_2$O$_3$films were then deposited on these ZnO nanorods by ALD at a substrate temperature of 300 $^{\circ}C$ using trimethylaluminum (TMA) and distilled water ($H_2O$). Transmission electron microscopy (TEM) images of the deposited ZnO nanorods revealed that 40nm-thick $Al_2$O$_3$ cylindrical shells surround the ZnO nanorods.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.381-381
• /
• 2009

염료감응형 태양전지의 효율 향상을 위한 다양한 방법들 중 $TiO_2$ 나노 파우더의 표면 개질 및 페이스트의 분산성 향상을 위한 연구가 활발하게 진행되고 있다. 기존 나노 파우더의 표면 개질법으로는 액상 공정인 졸겔법이 있으나 표면 처리 공정에서의 응집현상은 아직 해결해야 할 과제 중 하나이다. 이에 본 연구에서는 진공증착방법인 ALD법을 이용하여 염료감응형 태양전지용 $TiO_2$ 나노 파우더의 $SiO_2$ 산화물 표면처리를 통한 분산특성을 파악하였다. 기존 ALD법의 경우 reactor의 온도가 $300{\sim}500^{\circ}C$ 정도의 고온에서 공정이 이루어졌지만 본 실험에서는 2차 아민계촉매(pyridine)을 사용하여 reactor의 온도를 $30^{\circ}C$정도의 저온공정에서 $SiO_2$ 산화물을 코팅을 하였다. MO source로는 액체상태의 TEOS$(Si(OC_2H_5)_4)$를, 반응가스로는 $H_2O$를 사용하였고, 불활성 기체인 Ar 가스는 purge 가스로 각각 사용 하였다. ALD 공정에 의해 표면처리 된 $TiO_2$ 나노 파우더의 분산특성은 각 공정 cycle에 따라 FESEM을 통하여 입자의 형상 및 분산성을 확인하였으며 입도 분석기를 통하여 부피의 변화 및 분산 특성을 확인하였다. 공정 cycle 이 증가함에 따라 입자간의 응집현상이 개선되는 것을 확인 할 수 있었으며, 100cycles에서 응집현상이 가장 많이 감소하는 것을 확인할 수 있었다. 또한 표면 처리된 $SiO_2$ 산화막은 XRD를 통한 결정 분석 및 EDX를 통한 정성 분석을 통하여 확인하였다.

• Korean Journal of Materials Research
• /
• v.28 no.5
• /
• pp.268-272
• /
• 2018

An $Al_2O_3/AlN$ bilayer deposited on GaN by atomic layer deposition (ALD) is employed to prepare $Al_2O_3/AlN/GaN$ metal-insulator-semiconductor (MIS) diodes, and their interfacial properties are investigated using X-ray photoelectron spectroscopy (XPS) with sputter etch treatment and current-voltage (I-V) measurements. XPS analyses reveal that the native oxides on the GaN surface are reduced significantly during the early ALD stage, indicating that AlN deposition effectively clelans up the GaN surface. In addition, the suppression of Al-OH bonds is observed through the ALD process. This result may be related to the improved device performance because Al-OH bonds act as interface defects. Finally, temperature dependent I-V analyses show that the barrier height increases and the ideality factor decreases with an increase in temperature, which is associated with the barrier inhomogeneity. A Modified Richardson plot produces the Richardson constant of $A^{**}$ as $30.45Acm^{-2}K^{-2}$, which is similar to the theoretical value of $26.4Acm^{-2}K^{-2}$ for n-GaN. This indicates that the barrier inhomogeneity appropriately explains the forward current transport across the $Au/Al_2O_3/AlN/GaN$ interface.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.126-126
• /
• 2012

In past decades, the themal inkjet (TIJ) printer has been widely used as one of the most well-known digital printing technology due to its low cost, and high printing quality. Since the printing speed of TIJ printers are much slower than that of laser printers, however, there has been intensive efforts to raise the printing speed of TIJ printers. One of the most plausible methods to raise the printing speed of TIJ printers is to adopt a page-wide array TIJ printhead. To accomplish this goal, the high efficiency inkjet heating resistor films should be developed to settle the high power consumption problem of a page-wide array TIJ printhead. In this study, we investigated noble metal based multicomponent thin film resistor films prepared by atomic layer deposition (ALD) for a high efficiency inkjet printhead. Design concept, preparation, material properties of noble metal based multicomponent thin films will be discussed in terms of mutlfunctionality.