• 한국농공학회논문집
• /
• 제63권4호
• /
• pp.33-41
• /
• 2021

The emission characteristics and emission factors were determined by measuring the concentration of methane (CH₄) and nitrous oxide (N₂O), the amount of ventilation, etc. in the two fattening rooms which have the same environment in winter. As a result of monitoring, the average concentration of CH₄ and N₂O was 20.7-26.7 ppm and 1.4-1.6 ppm. The average temperature inside the room was measured at 20.0-21.4℃, and the average ventilation was 1345.4-1567.3 m³/h. The daily emission of CH₄ for the first 30 days showed a constant emission of 3.6-8.2 g/d/m²/pig, but thereafter, the emission increased rapidly. The daily emission of N₂O was 0.7-1.3 g/d/m²/pig, showing stable emission during the test period, and relatively insignificant emission compared to the emission of CH₄. After repeated test, it was confirmed that there was no significant difference between the two rooms. As a result, the CH₄ 6. 21 g/d/m²/pig and N₂O 1.02 g/d/m²/pig average emission for each room was derived.

• 한국표면공학회지
• /
• 제49권6호
• /
• pp.595-603
• /
• 2016

Rare-earth zirconates, including lanthanum zirconate and gadolinium zirconate, have been investigated as ones of the most promising candidates for next-generation thermal barrier coating (TBC) materials due to their excellent properties such as low thermal conductivity, chemical stability at high temperature and so on. In this study, TBCs with three compositions, in the $La_2O_3-Gd_2O_3-ZrO_2$ system with reduced rare-earth contents from $RE_2Zr_2O_7$ compositions, were fabricated by using suspension plasma spray with different suspension preparation methods. The phase formation, microstructure, and thermal properties of TBCs were examined. In particular, each coating exhibited single fluorite phase and a dense, vertically-separated microstructure. The potential of coatings with rare-earth zirconates for TBC applications was also discussed.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.364-371
• /
• 2013

The sintering behavior of monolithic SiC is examined using the binary sintering additive of $Al_2O_3$-rare earth oxide ($RE_2O_3$, where RE = Sc, Nd, Dy, Ho, or Yb). Through hot pressing at 20 MPa and $1750^{\circ}C$ for 1 h in an Ar atmosphere for 52 nm fine ${\beta}$-SiC powder added with 5 wt% sintering additive, a SiC density of > 97% is achieved, which indicates the effectiveness of $Al_2O_3-RE_2O_3$ system as a sintering of additive for SiC. Based on this result, 7 wt% of $Al_2O_3-Sc_2O_3$ is tested as an additive system for the fabrication of a continuous SiC fiber-reinforced SiC-matrix composite ($SiC_f$/SiC). Electrophoretic deposition combined with the application of ultrasonic pulses is used to efficiently infiltrate the matrix phase into the voids of $Tyranno^{TM}$-SA3 fabric. After hot pressing, a composite density of > 97% is obtained, along with a maximum flexural strength of 443 MPa.

• 대한임상검사과학회지
• /
• 제52권2호
• /
• pp.150-157
• /
• 2020

본 연구는 이산화망간(MnO₂)의 신경독성과 이에 대한 노박 덩굴 추출물의 보호 효과를 C6 glioma 세포를 배양하여 조사하였다. 본 연구를 위하여 세포생존율을 비롯하여 지질산화(LP) 억제능 및 XO 저해능과 같은 항산화 분석을 시행하였다. 그 결과 MnO₂는 배양 세포에 처리한 농도에 비례하여 세포생존율을 유의하게 감소시켰으며, 이 과정에서 XTT₅₀값은 146.7 μM로 나타나 Borenfreund and Puerner의 독성판정기준에 따라 중간독성(mid-cytotoxic)인 것으로 나타났다. 또한, 항산화제의 일종인 kaempferol (KAE)은 MnO₂의 독성에 의해 손상받은 세포의 생존율을 유의하게 증가시킴으로써 MnO₂의 독성을 방어하였다. 한편, MnO₂ 독성에 대한 노박덩굴(CO) 추출물의 영향 조사에 있어서, CO 추출물은 배양 세포에 MnO₂만을 처리한 것에 비하여 세포생존율을 유의하게 증가시킴으로써 MnO₂의 독성을 효과적으로 방어하였다. 이와 동시에 높은 LP 억제능과 XO 저해능과 같은 항산화 효과를 보여주었다. 이상의 결과에서 MnO₂의 독성에 산화적 손상이 관여하고 있음을 알 수 있었으며, CO 추출물은 LP 억제능과 XO 저해능과 같은 항산화능에 의하여 MnO₂의 독성을 효과적으로 방어한 것을 확인였다. 따라서, CO 추출물과 같은 천연소재는 파킨슨병 유발제인 MnO₂와 같이 산화적 손상과 관련된 질환적 중금속 독성을 경감 내지는 개선할 수 있는 유용한 물질이라 생각된다.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.451-453
• /
• 2013

Porous ceramic membranes consisting of $Ce_{1-x}Y_xO_{2-{\delta}}$ were developed for hydrogen permeation tests. Various amounts (x = 0, 0.05, 0.1, 0.2) of yttrium were doped to ceria to study the effect of yttrium doping on ceria membranes on various properties, including hydrogen permeability. $Ce_{1-x}Y_xO_{2-{\delta}}$ powder was synthesized by the sol-gel method. These membranes were fabricated by pressing and sintering at $1300^{\circ}C$ for 6 h. As the amount of yttrium increased, the grain size of the membrane decreased. Hydrogen permeability was improved as the yttrium content increased. Selective permeability of hydrogen compared to CO is explained by electric conductivity. As the temperature rose, both the hydrogen perm-selectivity and electric conductivity on $Ce_{0.8}Y_{0.2}O_{1.9}$ improved.

• 한국재료학회지
• /
• 제29권10호
• /
• pp.586-591
• /
• 2019

This study describes the doping effect of $Yb_2O_3$ on microstructure, electrical and dielectric properties of $ZnO-V_2O_5-MnO_2-Nb_2O_5$ (ZVMN) ceramic semiconductors sintered at a temperature as low as $900^{\circ}C$. As the doping content of $Yb_2O_3$ increases, the ceramic density slightly increases from 5.50 to $5.54g/cm^3$; also, the average ZnO grain size is in the range of $5.3-5.6{\mu}m$. The switching voltage increases from 4,874 to 5,494 V/cm when the doping content of $Yb_2O_3$ is less than 0.1 mol%, whereas further doping decreases this value. The ZVMN ceramic semiconductors doped with 0.1 mol% $Yb_2O_3$ reveal an excellent nonohmic coefficient as high as 70. The donor density of ZnO gain increases in the range of $2.46-7.41{\times}10^{17}cm^{-3}$ with increasing doping content of $Yb_2O_3$ and the potential barrier height and surface state density at the grain boundaries exhibits a maximum value (1.25 eV) at 0.1 mol%. The dielectric constant (at 1 kHz) decreases from 592.7 to 501.4 until the doping content of $Yb_2O_3$ reaches 0.1 mol%, whereas further doping increases it. The value of $tan{\delta}$ increases from 0.209 to 0.268 with the doping content of $Yb_2O_3$.

• 한국전기전자재료학회논문지
• /
• 제36권3호
• /
• pp.226-232
• /
• 2023

As a potential alternative to flash memory, HfO₂/Al₂O₃ stacks appear to be a viable option as charge capture layers in charge trapping memories. The paper undertakes a review of HfO₂/Al₂O₃ stacks as charge trapping layers, with a focus on comparing the number, thickness, and post-deposition heat treatment and γ-ray and white x-ray treatment of such stacks. Compared to a single HfO₂ layer, the memory window of the 5-layered stack increased by 152.4% after O₂ annealing at ±12 V. The memory window enlarged with the increase in number of layers in the stack and the increase in the Al/Hf content in the stack. Furthermore, our comparison of the treatment of HfO₂/Al₂O₃ stacks with varying annealing temperatures revealed that an increased annealing temperature resulted in a wider storage window. The samples treated with O₂ and subjected to various γ radiation intensities displayed superior resistance. and the memory window increased to 12.6 V at ±16 V for 100 kGy radiation intensity compared to the untreated samples. It has also been established that increasing doses of white x-rays induced a greater number of deep defects. The optimization of stacking layers along with post-deposition treatment condition can play significant role in extending the memory window.

• 한국결정성장학회지
• /
• 제32권1호
• /
• pp.40-44
• /
• 2022

35 % 농도의 염산 용액을 이용하여 α-Ga₂O₃ epitaxy 박막의 습식 식각을 수행하였다. 35 % 염산 용액의 온도가 증가함에 따라 α-Ga₂O₃ epitaxy 박막의 식각 속도가 증가하였고, 본 연구에서 시도한 가장 높은 온도인 75℃에서 119.6 nm/min의 식각 속도를 나타내었다. 식각 반응의 활성화 에너지는 0.776 eV로 계산되었고, HCl 용액에서의 습식 식각은 reaction-limited 반응 기구에 의해 지배됨을 확인하였다. 각 온도에서 식각된 표면들의 AFM 분석결과 식각 용액의 온도가 증가함에 따라 식각된 표면의 표면조도가 증가함을 알 수 있었다.

• 한국전기전자재료학회논문지
• /
• 제22권6호
• /
• pp.484-488
• /
• 2009

In this study, in order to develop the lead-free piezoelectric ceramics with high piezoelectric and dielectric properties, $[(K_{0.5}Na_{0.5})_{0.95}Li_{0.05}(Nb_{0.96}Sb_{0.04})]O_3$ ceramics were fabricated using $Ag_2O$ as sintering aid and a conventional mixed oxide process and their piezoelectric and dielectric characteristics were investigated according to the $SrTiO_3$ substitution. $SrTiO_3$ substitution enhanced density, dielectric constant(${\varepsilon}_r$) and electromechanical coupling factor($k_p$). However, mechanical quality factor was deteriorated. And also, Curie temperature ($T_c$), and phase transition temperature($T_p$) were rapidly decreased. At the 0.5 mol% $SrTiO_3$ substitution, density, electromechanical coupling factor($k_p$), dielectric constant(${\varepsilon}_r$) and piezoelectric constant($d_{33}$) of specimen showed the optimum value of $4.437\;g/cm^3$, 0.457, 1294, 265 pC/N, respectively.

• Advances in nano research
• /
• 제13권4호
• /
• pp.407-416
• /
• 2022

In this study, the gravitating mechanical stir casting method was used to fabricating the Nb₂O₅/AZ31 magnesium matrix nanocomposites. Niobium pentoxide (Nb₂O₅) used as reinforcement with two different weight percentages (3 wt % and 6 wt %). The influence of Nb₂O₅ on microstructure and mechanical properties has been investigated. The microstructure analysis showed that the composites are mainly composed of the primary α-magnesium phase and phase β-Mg₁₇Al₁₂ secondary phase. The secondary phase was dispersed evenly along the grain boundary of the Mg phase. The Nb₂O₅/AZ31 nanocomposites revealed that the grain size and its lamellar shape (β-Mg₁₇Al₁₂) were gradually refined. Different strengthening mechanisms were assessed in terms of their contributions. Results showed that composite material properties of hardness, yield strength, and fracture study were directly related to Nb₂O₅ as a reinforcement. The maximum values of the mechanical properties were achieved with the addition of 3 wt% Nb₂O₅ on the AZ31 alloy.