• Journal of the Korean Vacuum Society
• /
• v.6 no.S1
• /
• pp.133-136
• /
• 1997

In this paper multi-arc plasma plating film equipment Bulat-6 and its technical characteristics were analyzed in detail. This machine is the first of its kind in China. Influential factors and reducing methods on microdroplets of titanium were investigated. By method of electromagnetic field control and ion beam enhanced deposition excellent titanium nitride film could be obtained. Bicrohardness and adhesion were 250Mpa and 6.5Kg respectively.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.5
• /
• pp.220-226
• /
• 2009

Cr-O-N coatings having different oxygen contents were deposited on Si wafer and SUS 304 substrates by an arc ion plating technique using Cr target in $Ar/O_2/N_2$ gaseous atmosphere. As increasing oxygen content in the coating, the microstructure of Cr-O-N coating changed from polycrystalline having NaCl structure to amorphous structure. Further increase of oxygen content resulted in phase transformation from amorphous to rhombohedral structure. From the variations of d value and average grain size, it was revealed that the maximum solubility of oxygen in Cr-O-N coating was about 21 at.%. And the maximum micro-hardness of 2751HK was obtained in this composition. The lowest friction coefficient was measured in the coating having 34.8 at.% of oxygen. However, more narrow width of wear track was found in the coating having 30.1 at.% of oxygen.

• Journal of the Korean institute of surface engineering
• /
• v.35 no.4
• /
• pp.199-205
• /
• 2002

TiN and TiAlN films were deposited on SKD 11 steel substrates by an arc ion plating (AIP) technique. The crystallinity and morphology for the deposited films were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The mechanical properties of both films were investigated through the indentation, impact, and wear test. Those films fairly adherent to SKD 11 steel substrate, showed hardness values of 2300 $\pm$ 100kg/$\textrm{mm}^2$ and 3200 $\pm$ 100kg/$\textrm{mm}^2$ with a load of 25g, respectively. During impact test, TiAlN films showed much superior impact wear resistance to TiN films. It could be suggested that the TiN films was failed relatively by plastic deformation with oxidation during impact test, while TiAlN films was failed by brittle fracture and resisted the oxidation by the impact energy. The friction coefficient of TiAlN films became lower than that of TiN films at high sliding speed condition although it was higher than that of TiN films at low speed. Therefore, TiAlN films was suggested to be more advantageous than TiN films for high speed machining fields.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2009.10a
• /
• pp.119-120
• /
• 2009

진공증착 및 이온플레이팅 방법을 이용하여 냉간 압연된 강판상에 알루미늄 피막을 형성시킨 후, 증발율 및 증기분포 변화를 측정하고 각 증착방법에서의 증발율에 따른 증기분포 변화를 비교 및 검토하였다. 본 실험에서의 이온플레이팅은 증발원 근처에 이온화전극을 설치하는 방법으로 고전류 아크 방전을 유도하여 $10^{-4}$ Torr 이하에서도 기존의 이온플레이팅에 비해 높은 이온화율을 얻을 수 있는 아크방전 유도형 이온플레이팅 (Arc-induced Ion Plating; AIIP) 방법을 이용하였다. 전자빔을 이용하면서 알루미나 크루시블을 사용하여 알루미늄을 증발시킬 경우 분당 $2.0{\mu}m$ 이상의 높은 증발율을 얻을 수 있었으며, 이온플레이팅의 경우 이온화된 증기의 상호작용에 따른 산란 효과로 증발율이 다소 낮아짐을 알 수 있었다. $cos^n\phi$로 이루어지는 증기분포의 결정인자(n)의 값이 진공증착의 경우는 1에 근접하는 것으로 나타났고 AIIP의 경우는 2 또는 그보다 더 큰 값으로 이루어지는 것을 확인하였다. 이로부터 이온플레이팅의 경우 불활성 가스의 존재 여부와 이온화율 또는 기판 바이어스 전압의 효과가 다른 조건에 비해 증기분포에 더 크게 영향을 미치는 것을 확인할 수 있었다.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.6
• /
• pp.280-284
• /
• 2020

Electron beam irradiation is widely used as a type of surface modification technology to advance surface properties. In this study, the effect of electron beam irradiation on properties, such as surface hardness, wear resistance, roughness, and critical load of Titanium Aluminium nitride (TiAlN) films was investigated. TiAlN films were deposited on the SKD-61 substrate by using cathode arc ion plating. After deposition, the films were bombarded with intense electron beam for 10 minutes. The surface hardness was increased up to 4520 HV at electron irradiation energy of 1500 eV. In addition, surface root mean square (RMS) roughness of the films irradiated at 1500 eV shows the lowest roughness of 484 nm in this study.

• Corrosion Science and Technology
• /
• v.22 no.4
• /
• pp.232-241
• /
• 2023

The mechanical properties of the hydrogen valve responsible for supplying and blocking hydrogen gas in a hydrogen fuel cell electric vehicle (FCEV) were researched. Mechanical properties by hydrogen embrittlement were investigated by coating chromium nitride (CrN) and titanium nitride (TiN) on aluminum alloy by arc ion plating method. The coating layer was deposited to a thickness of about 2 ㎛, and a slow strain rate test (SSRT) was conducted after hydrogen embrittlement to determine the hydrogen embrittlement resistance of the CrN and TiN coating layers. The CrN-coated specimen presented little decrease in mechanical properties until 12 hours of hydrogen charging due to its excellent resistance to hydrogen permeation. However, both the CrN and TiN-coated specimens exhibited deterioration in mechanical properties due to the peeling of the coating layer after 24 hours of hydrogen charging. The specimens coated at 350 ℃ presented a significant decrease in ultimate tensile strength due to abnormal grain growth.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.5
• /
• pp.421-428
• /
• 2001

New WC-CrN superlattice film was deposited on Si substrate (500$\mu\textrm{m}$) using cathodic arc ion plating system. The microstructure and mechanical properties of the film depend on the superlattice period (λ). In the X-ray diffraction analysis (XRD), preferred orientation of microstructure was changed according to various superlattice periods(λ). During the Transmission Electron Microscope analysis (TEM), microstructure and superlattice period (λ) of the WC - CrN superlattice film was confirmed. Hardness and adhesion of the deposited film was evaluated by nanoindentation test and scratch test, respectively. As a result of nanoindentation test, the hardness of WC - CrN superlattice film was gained about 40GPa at superlattice period (λ) with 7nm. Also residual stress with various superlattice period (λ) was measured on Si wafer (100$\mu\textrm{m}$) by conventional beam-bending technique. The residual stress of the film was reduced to a value of 0.2 GPa by introducing Ti - WC buffer layers periodically with a thickness ratio ($t_{buffer}$/$t_{buffer+superlattice}$ ). To the end, for the evaluation of oxidation resistance at the elevated temperature, CrN single layer and WC - CrN superlattice films with various superlattice periods on SKD61 substrate was measured and compared with the oxidation resistance.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.5
• /
• pp.335-340
• /
• 2023

Quinary component of 3㎛ thick Ti-Al-Si-Cu-N films were deposited onto WC-Co and Si wafer substrates by using an arc ion plating(AIP) system. In this study, the influence of copper(Cu) contents on the mechanical properties and microstructure of the films were investigated. The hardness of the films with 3.1 at.% Cu addition exhibited the hardness value of above 42 GPa due to the microstructural change as well as the solid-solution hardening. The instrumental analyses revealed that the deposited film with Cu content of 3.1 at.% was a nano-composites with nano-sized crystallites (5-7 nm in dia.) and a thin layer of amorphous Si₃N₄ phase.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.5
• /
• pp.512-518
• /
• 1996

Amorphous carbon nitride (a-C:N) multilayerfilms are formed by using altermating conditions during film deposition in are ion plating process. Because hard a-C:N films prepared with suitable megative bias voltages have large compressive stress, it is difficult to increase film thickness more than 200nm. Preparing multilayer films composed of hard layers and soft layers, we can grow thick multilayer films on Si and SKH steel substrate. The total thickness of multilayer films is more than 1$\mu\textrm{m}$. The multilayer films are several times thicker than the single layer films and almost equal in hardness and internal stress to the single layer ones. X-ray photoelectron spectroscopy(XPS) and Raman spectroscopy reveal that multilayer films equal to single layer films in structure, which is similar to the structure of DLC films.

• Corrosion Science and Technology
• /
• v.10 no.6
• /
• pp.212-217
• /
• 2011

In this study, corrosion characteristics of TiN and ZrN film on the abutment screw by arc-ion plating were investigated using a potentiodynamic anodic polarization test in deaerated 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The surface morphologies of the coating layers before and after corrosion test were investigated by a field-emission scanning electron microscope (FE-SEM) and a energy dispersive x-ray spectroscopy (EDS). The surfaces of the TiN and ZrN coated abutment screws showed the smooth surfaces without mechanical defects like scratches which can be formed during the manufacturing process, compared with those of the non-coated abutment screw. The corrosion and passive current densities of TiN and ZrN coated abutment screws were lower than those of the non-coated abutment screw.