• Applied Science and Convergence Technology
• /
• v.25 no.6
• /
• pp.128-132
• /
• 2016

We investigated the effect of Ar ion sputtering on the surface electronic structure of indium tin oxide (ITO) using X-ray and ultraviolet photoelectron spectroscopy (XPS and UPS) measurements with increasing Ar ion sputtering time. XPS measurements revealed that surface contamination on ITO was rapidly removed by Ar ion sputtering for 10 s. UPS measurements showed that the work function of ITO increased by 0.2 eV after Ar ion sputtering for 10 s. This increase in work function was attributed to the removal of surface contamination, which formed a positive interface dipole relative to the ITO substrate. However, further Ar ion sputtering did not change the work function of ITO although the surface stoichiometry of ITO did change. Therefore, removing the surface contamination is critical for increasing the work function of ITO, and Ar ion sputtering for a short time (about 10 s) can efficiently remove surface contamination.

• Journal of the Korean Vacuum Society
• /
• v.12 no.S1
• /
• pp.92-94
• /
• 2003

The sputtering yield change of an amorphous Si layer on Si(100) was measured quantitatively for 0.5 keV $O_2^{+}$ and $Ar^{+}$ ion bombardment with in suit MEIS. In the case of 0.5 keV $O_2^{+}$ ion bombardment, at the initial stage of sputtering before surface oxidation, the sputtering yield of Si was 1.4 (Si atoms/$O_2^{+}$) and then decreased down to 0.06 at the ion dose of $3\times10^{16}O_2\;^{+}\textrm{/cm}^2$. In the case of 0.5 keV $Ar^{+}$ ion bombardment, the sputtering yield of Si for the surface normal incidence was 0.56 at the ion dose of 2.5 ${\times}$ 10$^{15}$ $Ar^{+}\textrm{cm}^2$, and rapidly saturated to 1.2 at dose of $7.5\times10^{15}Ar^+\textrm{cm}^2$. For the incidence angle of 80 from surface normal, the sputtering yield of Si was saturated to about 1.4 at the initial stage of sputtering. The surface transient effects, caused by change in sputtering yield at the initial stage of sputtering can be negligible when 0.5 keV $Ar^{+}$ ion at extremely grazing angle was used for sputter depth profiling.g.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.119-119
• /
• 2015

Ion beam sputtering has been widely used in Secondary Ion Mass Spectrometry (SIMS), X-ray Photoelectron Spectroscopy (XPS), and Auger Electron Spectroscopy (AES) for depth profile or surface cleaning. However, mainly due to severe matrix effects such as surface composition change from its original composition and damage of the surface generated by ion beam bombardment, conventional sputtering skills using mono-atomic primary ions with energy ranging from a few hundred to a thousand volts are not sufficient for the practical surface analysis of next-generation organic/inorganic device materials characterization. Therefore, minimization of the surface matrix effects caused by the ion beam sputtering is one of the key factors in surface analysis. In this work, the electronic structure of a $Ta_2O_5$ thin film on $SiO_2/Si$ (100) after Ar Gas Cluster Ion Beam (GCIB) sputtering was investigated using X-ray photoemission spectroscopy and compared with those obtained via mono-atomic Ar ion beam sputtering. The Ar ion sputtering had a great deal of influence on the electronic structure of the oxide thin film. Ar GCIB sputtering without sample rotation also affected the electronic structure of the oxide thin film. However, Ar GCIB sputtering during sample rotation did not exhibit any significant transition of the electronic structure of the $Ta_2O_5$ thin films. Our results showed that Ar GCIB can be useful for potential applications of oxide materials with sample rotation.

• Solar Energy
• /
• v.20 no.2
• /
• pp.55-65
• /
• 2000

Better electrical and optical properties of ITO thin films were demanded for the window layer of CdS/CdTe solar cells. To match that demand, an ion beam sputtering system was used for the deposition of ITO thin films. The substrate temperature and ion beam energy were controlled to deposit high quality ITO thin films in two cases of Ar ion sputtering and Ar+$O_2$ ion sputtering. The microstructure changed from domain structure in ITO deposited by Ar ions to grain structure in ITO deposited by Ar+$O_2$ ions. The lowest resistivity of ITO films was $1.5\times10^{-4}{\Omega}cm$ at $100^{\circ}C$ substrate temperature in case of Ar ions sputtering. Transmittance in the visible range was over 80% above $100^{\circ}C$ substrate temperature.

• Journal of the Korean Ceramic Society
• /
• v.40 no.12
• /
• pp.1165-1169
• /
• 2003

The Ta$_2$O$_{5}$ thin film was deposited on Si-(III) and glass substrate with the change of Ar:O$_2$ gas flow rate in the assist ion gun by the Dual ion-Beam Sputtering (DIBS). As the $O_2$ gas flow of the assist ion gun was decreased, the deposition rate of the thin films decreased. The refractive index was fixed (2.11, at 1550 nm) without regarding to $O_2$ gas flow of the range 3∼12 sccm in assist ion gun. The condition of Ar:O$_2$=3:12 was formatted stoichiometry composition of Ta$_2$O$_{5}$ and the ms roughness was small (0.183 nm).

• Journal of the Korean institute of surface engineering
• /
• v.45 no.5
• /
• pp.206-211
• /
• 2012

Process analysis was carried out during deposition of MgO by inductively coupled plasma assisted reactive magnetron sputtering in Ar and $O_2$ ambient. At the initiation of Mg sputtering with bipolar pulsed dc power in Ar ambient, total pressure showed sharp increase and then slow fall. To analyse partial pressure change, QMS was used in downstream region, where the total pressure was maintained as low as $10^{-5}$ Torr during plasma processing, good for ion source and quadrupole operation. At base pressure, the major impurity was $H_2O$ and the second major impurity was $CO/N_2$ about 10%. During sputtering of Mg in Ar, $H_2$ soared up to 10.7% of Ar and remained as the major impurity during all the later process time. When $O_2$ was mixed with Ar, the partial pressure of Ar decreased in proportion to $O_2$ flow rate and that of $H_2$ dropped down to 2%. It was understood as Mg target surface was oxidized to stop $H_2$ emission by Ar ion sputtering. With ICP turned on, the major impurity $H_2$ was converted into $H_2O$ consuming $O_2$ and C was also oxidized to evolve CO and $CO_2$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1998.02a
• /
• pp.20-20
• /
• 1998

I Ion beam technology has recently attracted much interest because it has exciting t technological p아:ential for surface analysis, ion beam mixing, surface cleaning and etching i in thin film growth and semiconductor fabrication processes, etc. Es야~cially, ion beam s sputtering has been widely used for sputter depth profiling with x-photoelectron S spectroscopy (XPS) , Auger electron s$\pi$~troscopy(AES), and secondary-ion mass S야i따oscopy(SIMS). However, The problem of surface compositional ch없1ge due to ion b bombardment remains to be understo여 없ld solved. So far sputtering processes have been s studied by s따face an외ysis tools such as XPS, AES, and SIMS which use the sputtering p process again. It would be improbable to measure the modified surface composition profiles a accurately due to ion beam bombardment with surface analysis techniques based on sputter d depth profiling. However, recently Medium energy ion scattering spectroscopy(MEIS) has b been applied to study the sputtering of solid surface at ion bombardment and has been p proved that it has been extremely valuable in probing the surface composition 뻐d s structure nondestructively and quantita디vely with less than 1.0 nm depth resolution. To u understand the sputtering processes of solid surface at ion bombardment, The Molecular D Dynamics(MD) and Monte Carlo(MC) simulation has been used and give an intimate i insight into the sputtering processes of solid surfaces. In this presentation, the sputtering processes of alloys and compound samples at ion b bombardment will be reviewed and the MEIS results for the Ar+ sputter induced altered l layer of the TazOs thin film 뻐dd없nage profiling of Ar+ ion sputt얹"ed Si(100) surface will b be discussed with the results of MD and MC simulation.tion.

• Transactions on Electrical and Electronic Materials
• /
• v.11 no.6
• /
• pp.266-270
• /
• 2010

The effect of an Ar plasma treatment on polycarbonate substrates was investigated using $TiO_2$ coatings produced by reactive ion-beam assisted sputtering. The typical pressure used during sputtering was about $10^{-4}$ Torr. After the Ar plasma treatment, the contact angle of a water droplet was reduced from $88^{\circ}$ to $52^{\circ}$ and then further decreased to $12^{\circ}$ with the addition of oxygen into the chamber. The surface of the polycarbonate substrate hanged from hydrophobic to hydrophilic with these treatments and revealed its changing nano-scale roughness. The $TiO_2$ films on the treated surface showed various colors and periodic ordering dependant on the film thickness due to optical interference.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.3
• /
• pp.192-197
• /
• 2017

A 6-way-cross consisting of a 2.75-inch CF flange was used as a main chamber on a PFEIFFER VACUUM TMP station based on a 67 l / sec turbo molecular pump and a diaphragm pump to produce a magnet array with a volume ratio of 5.5: 1.A 1-inch diameter copper target and graphite target were fabricated using MDX-1.5K from Advanced Energy Industries, Inc as a DC power supply. Ion current density of copper target and graphite target was measured by unbalanced magnetron sputtering. The basic pressure condition was $6.3{\times}10^{-7}mbar$ and the process pressure was Ar 50 sccm at $1.0{\times}10^{-2}mbar$ (7.5 mTorr) in the Ar atmosphere. Therefore, the relative density of copper ions reaching the substrate with the measured ion current density was derived.

• Journal of the Korean Vacuum Society
• /
• v.5 no.4
• /
• pp.371-376
• /
• 1996

Au films with a thickness around 1600 $\AA$ were deposited onto glass at room temperature by ion beam sputtering with a 5 cm cold-hollow ion gun at pressure $1\times 10^{-6}-1\times 10^{-5}$ Torr. Irradiation of the Au deposited samples was carried out at pressure of $7\times 10^{-6}$ Torr. For the sputter depositions, $Ar^+$ ion energy was 1 keV, and the current density at the substrate surface was 15 $\mu$A/$\textrm{cm}^2$. Effects of 1 keV $Ar^+$ ion dose($I_d$) between $1\times 10^{16}\; and\;2\times 10^{17}\;Ar^+\textrm{cm}^{-2}$on properties such as crystallinity, surface roughness and adhesion, etc. of the films have been investigated. The Au films sputtered by $Ar^+$ ion beam had only (111) plane and the X-ray intensity of the films decreased with increase of $I_d$. The thickness of Au films reduced with Id. $R_{ms}$ surface roughness of the films increased from 16 $\AA$ at as-deposited to 1118 $\AA$ at ion dose= $2\times 10^{17}\;Ar^+\textrm{cm}^{-2}$. Adhesion of Au film on sputtered at $I_d$= $2\times 10^{17}\;Ar^+\textrm{cm}^{-2}$ was 9 times greater than that of Au film with untreated, as determined by a scratch test.