• Current Photovoltaic Research
• /
• 제2권4호
• /
• pp.173-176
• /
• 2014

We have investigated the seed layer formation of front side contact using the inkjet printing process. Conductive silver ink was printed on textured Si wafers with 80 nm thick $SiN_x$ anti reflection coating (ARC) layers and thickened by light induced plating (LIP). The inkjet printable sliver inks were specifically formulated for inkjet printing on these substrates. Also, a novel method to prepare nano-sized glass frits by the sol-gel process with particle sizes around 5 nm is presented. Furthermore, dispersion stability of the formulated ink was measured using a Turbiscan. By implementing these glass frits, it was found that a continuous and uniform seed layer with a line width of $40{\mu}m$ could be formed by a inkjet printing process. We also investigated the contact resistance between the front contact and emitter using the transfer length model (TLM). On an emitter with the sheet resistance of $60{\Omega}/sq$, a specific contact resistance (${\rho}_c$) below $10m{\Omega}{\cdot}cm^2$ could be achieved at a peak firing temperature around $700^{\circ}C$. In addition, the correlation between the contact resistance and interface microstructures were studied using scanning electron microscopy (SEM). We found that the added glass particles act as a very effective fire through agent, and Ag crystallites are formed along the interface glass layer.

• 반도체디스플레이기술학회지
• /
• 제13권3호
• /
• pp.27-33
• /
• 2014

To develop high efficiency crystalline solar cells, the $SiN_x$ film for surface passivation and anti-reflection coating is very important and it is generally deposited by PECVD. In this paper, the $SiN_x$ film deposited by Hot-Wire chemical vapor deposition(HWCVD) that has no plasma damage was studied. First, to optimize the $SiN_x$ film deposition process, $SiH_4$ gas rate and substrate temperature were varied and then refractive index and thickness were measured. When $SiH_4$ gas rate was 22sccm and substrate temperature was $100^{\circ}C$, refractive index was 1.94 and higher than that of other process conditions. Second, the lifetime was measured by varying the annealing temperature and time. The annealing process was made from 5 to 30 minutes at $300{\sim}500^{\circ}C$. When the annealing temperature was $100^{\circ}C$ and time was 10minute, the lifetime was the highest. The lifetime of annealed samples was also measured after the firing process at $975^{\circ}C$. Although the lifetime of all samples was decreased by firing process, the lifetime of annealed samples before the firing process was higher than that of fired samples only. Finally, the characteristics of solar cells with HWCVD $SiN_x$ film were measured.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2004년도 하계학술대회 논문집 C
• /
• pp.1737-1739
• /
• 2004

Diamond-like carbon (DLC) films were prepared with RF-PECVD (Plasma Enhanced Chemical Vapor Deposition) method on coming glass and silicon substrates using methane ($CH_4$) and hydrogen ($H_2$) gases. We examined the effects of $CH_4$ to $H_2$ ratios on tribological and optical properties of the DLC films. The structure and surface morphology of the films were examined using Raman spectroscopy and atomic force microscopy (AFM). The hardness of the DLC film was measured with nano-indentor. The optical properties of DLC thin film were investigated by UV/VIS spectrometer and ellipsometry. And also, solar cells were fabricated using DLC as antireflection coating before and after coating DLC on silicon substrate and compared the efficiency.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 춘계학술대회 초록집
• /
• pp.75.1-75.1
• /
• 2011

화석연료의 고갈과 온실가스 배출의 증가로 지속 가능한 친환경 에너지 생산이 요구되는 가운데, 태양광 발전은 이러한 조건을 만족시키는 에너지 생산 방안으로 주목받고 있다. 태양광 발전은 태양 직사광을 이용한 발전 방법 때문에 실외에 설치되어야 하며 이에 따라 외부의 충격이나 오염물질로부터 태양전지 패널을 보호하기 위한 보호층이 필수적이다. 그러나 보호층에 의한 입사광의 반사 및 먼지나 황사에 의한 보호층의 오염 등은 태양전지의 발전 효율을 감소시키는 요인으로 작용하여 이에 대한 대응이 필요하다. 본 연구에서는 PET 필름에 나노 임프린트 리소그래피 및 핫 엠보싱 공정을 이용하여 moth-eye 반사방지 패턴을 형성함으로써 보호층에서의 입사광 반사를 억제하였다. 또한, 이러한 반사방지 패턴에 초소수성 자기조립단분자막을 코팅하여 표면 에너지를 낮춤으로써 먼지 및 황사에 의해 오염되었을 경우에도 빗물에 의해 오염 물질이 쉽게 씻겨 내릴 수 있는 자정기능을 부여하였다. 이러한 반사방지를 통한 입사광 투과량의 향상 및 초소수성 표면에 의한 자정작용에 의하여 태양전지의 발전 효율이 증가되었다.

• 한국전기전자재료학회논문지
• /
• 제18권7호
• /
• pp.662-666
• /
• 2005

Silicon nitride $(SiN_x)$ film is a promising material for anti-reflection coating and passivation of multicrystalline silicon (me-Si) solar cells. In this work, a plasma-enhanced chemical vapor deposition (PECVD) system with batch-type reactor tube was used to prepare highly robust $SiN_x$ films for screen-printed mc-Si solar cells. The Gas flow ratio, $R=[SiH_4]/[NH_3]$, in a mixture of silane and ammonia was varied in the range of 0.0910.235 while maintaining the total flow rate of the process gases to 4,200 sccm. The refractive index of the $SiN_x$ film deposited with a gas flow ratio of 0.091 was measured to be 2.03 and increased to 2.37 as the gas flow ratio increased to 0.235. The highest efficiency of the cell was $14.99\%$ when the flow rate of $SiH_4$ was 350 sccm (R=0.091). Generally, we observed that the efficiency of the mc-Si solar cell decreased with increasing R. From the analysis of the reflectance and the quantum efficiency of the cell, the decrease in the efficiency was shown to originate mainly from an increase in the surface reflectance for a high flow rate of $SiH_4$ during the deposition of $SiN_x$ films.

• Transactions on Electrical and Electronic Materials
• /
• 제12권4호
• /
• pp.156-159
• /
• 2011

SiNx:H films have been widely used for anti-reflection coatings and passivation for crystalline silicon solar cells. In this study, SiNx:H films were deposited using high frequency (13.56 MHz) direct plasma enhanced chemical vapor deposition, and the optical and passivation properties were investigated. The radio frequency power, the spacing between the showerhead and wafer, the $NH_3/SiH_4$ ratio, the total gas flow, and the $N_2$ gas flow were changed over certain ranges for the film deposition. The thickness uniformity, the refractive index, and the minority carrier lifetime were then measured in order to study the properties of the film. The optimal deposition conditions for application to crystalline Si solar cells are determined from the results of this study.

• 반도체디스플레이기술학회지
• /
• 제11권2호
• /
• pp.7-11
• /
• 2012

SiNx films have been wildly used as anti-reflection coatings and passivation for crystalline silicon solar cells. In this study, the SiNx films were deposited by using high frequency (13.56MHz) PECVD and optical & passivation properties were investigated. The RF power was changed in a certain range for the film deposition. Then, the refractive index, etch rate, minority carrier lifetime and cell efficiency were measured to study the properties of the film respectively. The optimal deposition conditions for application to crystalline silicon solar cells were proposed as results of the study. Finally, the best cell efficiency of 16.98% was obtained from the solar cell with the SiNx films deposited by RF power of 550W.

• 한국전기전자재료학회논문지
• /
• 제21권9호
• /
• pp.808-811
• /
• 2008

Optical and mechanical properties of diamond-like carbon (DLC) films synthesized by RF plasma enhanced chemical vapor deposition were investigated as a function the C/H ratio in gas mixture. The C/H ratio was varied from 6 to 10 %, adjusting the amount of $CH_4$ and $H_2$ as the source gas. The optical and mechanical properties of DLC films were characterized by UV spectrometer, Ellipsometer and Nano-indenter. The change of the C/H ratio during synthesis of DLC films had many effects on the growth rate, transmittance, refractive index and hardness. The growth rate of the films increased exponentially with the increase in C/H ratio. The hardness of the films showed the tendency to improve with increasing C/H ratio, whereas the transmittance decreased. The refractive index was varied from 2.03 to 2.17, and these refractive indexes close to 2.0 indicates that it can be applied to Si-based solar cell.

• 한국진공학회지
• /
• 제4권1호
• /
• pp.12-17
• /
• 1995

Diamondlike carbon(DLC)films having good characteristics in mechanical and optical properties, were synthesized by rf-plasma enhanced chemical vapor deposition method. Methane, methane-hydrogen, or methane-argon were used as source gases. The infrared transparency and composition of the films were investigate. Especially, the anti-reflection effect of KLC film in infrared region was confirmed by depositing it on Ge/Si sample. When DLC films were deposited on the plastic substrates and thermal distortion, which were originated before and during deposition, respectively, played a role as a crack source of the films.

• Journal of Magnetics
• /
• 제14권1호
• /
• pp.31-35
• /
• 2009

Herein, the Magneto-Optical Kerr Effect (MOKE) signal enhancement in nanostructures in investigated. It is well known that the MOKE signals of ferromagnetic thin films are enhanced with an additional dielectric layer due to multiple reflections. The MOKE signal is modulated with the additional dielectric layer thickness and is at a maximum when reflectivity is at a minimum. This is not always true in the nanostructures due to the contribution from the non-magnetic substrate portion, especially when substrate reflectivity is minimized and the dependence of the additional dielectric layer thickness for the nanostructure is changed in the case of the continuous thin film. We showed that the MOKE signal for nanostructures could be enhanced with a properly designed, dielectric layer in addition to the anti-reflection coated substrates.