• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.4
• /
• pp.23-30
• /
• 2019

Fiber-Reinforced Cement Composite (FRCC) is known to be effective in mechanical effects such as cracking width control as well as steel anticorrosive effect. In this study, we examined about steel anticorrosive effect by using metal fibers including zinc fibers by accelerated corrosion test. Moreover, it was examined for salt penetration, sacrificial anode effect and formation of electric circuit that was significant effect on the steel anticorrosive effect. As a result, Steel anticorrosive effect was confirmed with mixed metal fibers on FRCC. Especially, In the case of zinc fibers with a high sacrificial anode effect, it was confirmed that the suppression of penetration and corrosion resistance were improved.

• Journal of Advanced Marine Engineering and Technology
• /
• v.40 no.6
• /
• pp.510-515
• /
• 2016

Recently, corrosion occurred on the piles of a marine bridge located on the NamHae expressway in Korea. A sacrificial anode cathodic protection system was installed to prevent corrosion damage in the marine bridge. In the case of the marine bridge in this study, the sacrificial anode cathodic protection system was applied at the tidal and splash zones of the piles because the upper part of the structure was not corroded, and because corrosion occurs at the tidal and splash zones due to sea tides. To verify the performance of the sacrificial anode cathodic protection system 8 years later, cathodic protection (CP) current, CP potential, and degree of depolarization were measured. The experimental results on the performance of the sacrificial anode cathodic protection system from a total of 60 piles were classified into 4 categories: good CP effect results (13 piles), partial CP effect results (27 piles), temporarily erroneous results (5 piles), and need for maintenance because of delamination (15 piles). It was determined that additional repairs are required, such as the application of bulk anodes and jacket casings, for piles where the CP effect is poor.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.06a
• /
• pp.134-134
• /
• 2010

Fuel cell is a device that directly converts chemical energy in the form of a fuel into electrical energy by way of an electrochemical reaction. In the anode for a high temperature fuel cell, nickel or nickel alloy has been used in consideration of the cost, oxidation catalystic ability of hydrogen which is used as fuel, electron conductivity, and high temperature stability in reducing atmosphere. Most MCFC stacks currently operate at an average temperature of $650^{\circ}C$. There is some gains with decreased temperature in MCFC to diminish the electrolyte loss from evaporation and the material corrosion, which could improve the MCFC life. However, operating temperature has a strong related on a number of electrode reaction rates and ohmic losses. Baker et al. reported the effect of temperature (575 to $650^{\circ}C$). The rates of cell voltage loss were 1.4mV/$^{\circ}C$ for a reduction in temperature from 650 to $600^{\circ}C$, and 2.16mV/$^{\circ}C$ for a decrease from 600 to $575^{\circ}C$. The two major contributors responsible for the change in cell voltage with reducing operation temperature are the ohmic polarization and electrode polarization. It appears that in the temperature range of 550 to $650^{\circ}C$, about 1/3 of the total change in cell voltage with decreasing temperature is due to an increase in ohmic polarization, and the electrode polarization at the anode and cathode. In addition, the oxidation reaction of hydrogen on an ordinary nickel alloy anode in MCFC is generally considered to take place in the three phase zone, but anyway the area contributing to this reaction is limited. Therefore, in order to maintain a high performance of the fuel cell, it is necessary to keep this reaction responsible area as wide as possible, that is, it is needed to keep the porosity and specific surface area of the anode at a high level. In this study effective anodes are prepared for low temperature MCFC capable of enhancing the cell performance by using zirconium hydride at least in part of anode material.

• Journal of the Korean Electrochemical Society
• /
• v.2 no.2
• /
• pp.75-80
• /
• 1999

Li-ion cells employ lithium transtion metal oxide as the cathode material and carbon as anode material. To manufacture Li-ion cell with higher capacity and better cycle life, the utilization of electrode materials should be as high as possible without lithium deposition onto the carbon surface during charging. A careful design of cell balance between cathode and anode materials as well as a proper charge method is a key factor to design Li-ion cell with long cycle life. In this study, we investigated the effect of cathode/anode weight ratio on the performance of $LiCoO_2/MPCF$ cell. First we evaluated the charge-discharge behaviours of half-cells. And cylindrical Li-ion cells were fabricated using graphitized MPCF anode and $LiCoO_2$ cathode. The voltage profiles for each half-cell in $LiCoO_2/MPCF$ cell were measured by using lithium metal as a reference electrode. Also, we evaluated the cyclic performance of $LiCoO_2/MPCF$ cells according to weight ratio. From the result of experiment $LiCoO_2$ cathode utilization was independent of weight ratio, but MPCF anode utilization was dependant on weight ratio. Also, the optimal weight ratio of $LiCoO_2/MPCF$ cell was found to be $2.0\~2.2$.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.2
• /
• pp.79-85
• /
• 2014

Silicon (Si) has been investigated as promising negative-electrode (anode) materials because its theoretical specific capacity of 4200 mAh/g for $Li_{4.4}Si$ is far higher than that of carbonaceous anodes in current commercial products. However, in practice, the application of Si to Li-ion batteries is still quite challenging because Si suffers from severe volume expansion and contraction and lead to a continuous solid electrolyte interphase (SEI)-filming process by cracking of Si. This process consumes the limited $Li^+$ source, builds up thick and unstable SEI layer on the Si active materials, and will eventually disable the cell. Since unstable SEI reduces electrochemical performance and thermal stability of the Si anode, the surface chemistry of the anode should be modified by using a functional additive. It is found that lithium bis(oxalato)borate (LiBOB) as an additive effectively protected the Si anode surface, improved capacity retention when stored at $60^{\circ}C$, and alleviated exothermic thermal reactions of fully lithiated Si anode.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.42 no.11
• /
• pp.974-980
• /
• 2014

A power supply of cathode has been developed for hall-effect thruster for small satellite. A microwave cathode has been applied to the electric propulsion system and cathode power is necessary in oder to work securely. Anode current is varied by a flow rate controlled by anode tank pressure. Then cathode current has to be controled in proportion by anode current. So cathode power supply has been designed to offer a current proportional to anode current. Also cathode power has been tuned to work securely for cathode to emit more electron than anode within 0.03A. The function test of cathode power was performed by constructing an equivalent load for anode and cathode. It has been tested in a vacuum chamber in order to ensure a stable operation of the thruster. And it was confirmed that thruster normally has been operated in the space environment after the launch.

• Corrosion Science and Technology
• /
• v.14 no.4
• /
• pp.177-183
• /
• 2015

Prestressed Concrete steel Cylinder Pipe (PCCP) is extensively used as seawater pipes for cooling in nuclear power plants. The internal surface of PCCP is exposed to seawater, while the external surface is in direct contact with underground soil. Therefore, materials and strategies that would reduce the corrosion of its cylindrical steel body and external steel wiring need to be employed. To prevent against the failure of PCCP, operators provided a cathodic protection to the pre-stressing wires. The efficiency of cathodic protection is governed by the anodic performance of the system. A mixed metal oxide (MMO) electrode was developed to meet criteria of low over potential and high corrosion resistance. Increasing coating cycles improved the performance of the anode, but cycling should be minimized due to high materials cost. In this work, the effects of $RuCl_3$ concentration on the electrochemical properties and lifespan of MMO anode were evaluated. With increasing concentration of $RuCl_3$, the oxygen evolution potential lowered and polarization resistance were also reduced but demonstrated an increase in passive current density and oxygen evolution current density. To improve the electrochemical properties of the MMO anode, $RuCl_3$ concentration was increased. As a result, the number of required coating cycles were reduced substantially and the MMO anode achieved an excellent lifespan of over 80 years. Thus, we concluded that the relationship between $RuCl_3$ concentration and coating cycles can be summarized as follows: No. of coating cycle = 0.48*[$RuCl_3$ concentration, $M]^{-0.97}$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.168.1-168.1
• /
• 2014

We developed poly (3,4-ethylene dioxylene thiophene):poly (styrene sulfonic acid) (PEDOT:PSS)-free organic solar cells (OSCs) using buffer and anode combined Ta doped $In_2O_3$ (ITaO) electrodes. To optimize the ITaO electrodes, we investigated the effect of $Ta_2O_5$ doping power on the electrical, optical, and structural properties of the co-sputtered ITaO films. The optimized ITaO film doped with 20 W $Ta_2O_5$ radio frequency power showed sheet resistance of 17.11 Ohm/square, a transmittance of 93.45%, and a work function of 4.9 eV, all of which are comparable to the value of conventional ITO electrodes. The conventional bulk heterojunction OSC with ITaO anode showed a power conversion efficiency (PCE) of 3.348% similar to the OSCs (3.541%) with an ITO anode. In addition, OSCs fabricated on an ITaO electrode successfully operated without an acidic PEDOT:PSS buffer layer and showed a PCE of 2.634%, which was much higher than the comparable no buffer OSC with an ITO anode. Therefore, co-sputtered ITaO electrodes simultaneously acting as a buffer and an anode layer can be considered promising transparent electrodes for cost-efficient and reliable OSCs because they can eliminate the use of an acidic PEDOT:PSS buffer layer.

• Journal of the Semiconductor & Display Technology
• /
• v.10 no.3
• /
• pp.67-74
• /
• 2011

In this study, we have investigated the effect of the substrate temperature on the structural and the electrical characteristics of IZO thin films for the OLED (organic light emitting diodes) devices. For this purpose, IZO thin films were deposited by RF magnetron sputtering under various substrate temperature. The substrate temperature has been changed from room temperature to $400^{\circ}C$. Samples which were deposited under $250^{\circ}C$ show amorphous structure. The electrical resistivity of crystalline-IZO (c-IZO) film was higher than that of amorphous-IZO (a-IZO) film. And the electrical resistivity showed minimum value near $150^{\circ}C$ of deposition temperature. The OLED device was fabricated with different IZO substrates made by configuration of IZO/$\acute{a}$-NPD/DPVB/$Alq_3$/LiF/Al to elucidate the performance of IZO substrate. OLED devices with the amorphous-IZO (a-IZO) anode film show better current density-voltage-luminance characteristics than that of OLED devices with the commercial crystalline-ITO (c-ITO) anode film. It can be explained that very flat surface roughness and high work function of a-IZO anode film lead to more efficient hole injection by reduction of interface barrier height between anode and organic layers. This suggests that a-IZO film is a promising anode materials substituting conventional c-ITO anode in OLED devices.

• Journal of the Semiconductor & Display Technology
• /
• v.9 no.3
• /
• pp.53-58
• /
• 2010

In this study, we have investigated the effect of the ambient gases on the characteristics of IZO thin films for the OLED (organic light emitting diodes) devices. For this purpose, IZO thin films were deposited by RF magnetron sputtering under various ambient gases (Ar, $Ar+O_2$ and $Ar+H_2$) at $150^{\circ}C$. In order to investigate the influences of the oxygen and hydrogen, the flow rate of oxygen and hydrogen in argon mixing gas has been changed from 0.1sccm to 0.5sccm, respectively. All the samples show amorphous structure regardless of ambient gases. The electrical resistivity of IZO film increased with increasing flow rate of $O_2$ under $Ar+O_2$ while under $Ar+H_2$ atmosphere the electrical resistivity showed minimum value near 0.5sccm of $H_2$. All the films showed the average transmittance over 85% in the visible range. The OLED device was fabricated with different IZO substrates made by configuration of IZO/${\alpha}$-NPD/DPVB/$Alq_3$/LiF/Al to elucidate the performance of IZO substrate. OLED devices with the amorphous-IZO (a-IZO) anode film show better current densityvoltage-luminance characteristics than that of OLED devices with the commercial crystalline-ITO (c-ITO) anode film. It can be explained that very flat surface roughness and high work function of a-IZO anode film lead to more efficient hole injection by reduction of interface barrier height between anode and organic layers. This suggests that a-IZO film is a promising anode materials substituting conventional c-ITO anode in OLED devices.