• Journal of information and communication convergence engineering
• /
• v.1 no.1
• /
• pp.23-26
• /
• 2003

A photodiode capable of obtaining a sufficient photo/dark current ratio at both a forward bias state and a reverse bias state is proposed. The photodiode includes a glass substrate, an aluminum film formed as a lower electrode over the glass substrate, an alumina film formed as a schottky barrier over the aluminum film, a hydrogenated amorphous silicon film formed as a photo conduction layer over a portion of the alumina film, and a transparent conduction film formed as an upper electrode over the hydro-generated amorphous silicon film. Growth of high quality alumina($Al_{2}O_{3}$) film using anodizing technology is proposed and analyzed by experiment. We have obtained the film with a superior characteristics

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2008.11a
• /
• pp.68-68
• /
• 2008

There are several methods for oxide coating on metals, such as aluminum or carbon nanotubes(CNTs). Usually CVD method is introduced for various oxide coating on CNTs. Another method is electrochemical method which use potential-pH diagram for oxide coating on metal or CNTs. In this experiment, electrochemical coating parameter for oxide coating on aluminum template modified by acids and hydrogen peroxide ($H_2O_2$) were examined. SEM micrographs displayed clearly $Ni(OH)_2$ coating on template. For confirmation of electrochemical method application to EDLC electrode material fabrication, EDS spectrum was analyzed.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.6
• /
• pp.267-270
• /
• 2011

In the process of inkjet-printed zinc tin oxide thin-film transistor, the effect of metallic interlayer underneath of source and drain electrode was investigated. The reason for the improved electrical properties with thin molybdenum oxide ($MoO_3$) layer was due to the chemically intermixed state of metallic interlayer, aluminum source and drain, and oxide semiconductor together. The atomic configuration of three Mo $3d_3$ and $3d_5$ doublets, three different Al 2p core levels, two Sn $3d_5$, and four different types of oxygen O 1s in the interfaces among those layers was confirmed by X-ray photospectroscopy.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.53.2-53.2
• /
• 2010

In this study, we focused on our specialized electrode process for Si back-contact crystalline solar cell. It is different from other well-known back-contact cell process for thermal aspect and specialized process. In general, aluminum makes ohmic contact to the Si wafer and acts as a back surface reflector. And, silver is used for low series resistance metal grid lines. Aluminum was sputtered onto back side of wafer. Next, silver is directly patterned on the wafer by screen printing. The sputtered aluminum was removed by wet etching process after rear silver electrode was formed. In this process, the silver paste must have good printability, electrical property and adhesion strength, before and after the aluminum etching process. Silver paste also needs low temperature firing characteristics to reduce the thermal budget. So it was seriously collected by the products of several company of regarding low temperature firing (below $250^{\circ}C$) and aluminum etching endurance. First of all, silver pastes for etching selectivity were selected to evaluate as low temperature firing condition, electrical properties and adhesive strength. Using the nano- and micron-sized silver paste, so called hybrid type, made low temperature firing. So we could minimize the thermal budget in metallization process. Also the adhesion property greatly depended on the composition of paste, especially added resin and inorganic additives. In this paper, we will show that the metallization process of back-contact solar cell was realized as optimized nano-paste characteristics.

• Journal of Powder Materials
• /
• v.22 no.4
• /
• pp.240-246
• /
• 2015

Anodic aluminum oxide (AAO) has been widely used for the development and fabrication of nano-powder with various morphologies such as particle, wire, rod, and tube. So far, many researchers have reported about shape control and fabrication of AAO films. However, they have reported on the shape control with different diameter and length of anodic aluminum oxide mainly. We present a combined mild-hard (or hard-mild) anodization to prepare shape-controlled AAO films. Two main parameters which are combination mild-hard (or hard-mild) anodization and run-time of voltage control are applied in this work. The voltages of mild and hard anodization are respectively 40 and 80 V. Anodization was conducted on the aluminum sheet in 0.3 mole oxalic acid at $4^{\circ}C$. AAO films with morphologies of varying interpore distance, branch-shaped pore, diameter-modulated pore and long funnel-shaped pore were fabricated. Those shapes will be able to apply to fabricate novel nano-materials with potential application which is especially a support to prevent volume expansion of inserted active materials, such as metal silicon or tin powder, in lithium ion battery. The silicon powder electrode using an AAO as a support shows outstanding cycle performance as 1003 mAh/g up to 200 cycles.

• Current Photovoltaic Research
• /
• v.4 no.4
• /
• pp.145-149
• /
• 2016

Characteristic of aluminum-silicon alloy paste which is applied on the rear side of PERC cell was investigated. The paste was made by aluminum-silicon alloy with eutectic composition to avoid the formation of void which is responsible for the degradation of the open-circuit voltage. Also, the glass frit component of the paste was changed to improve the adhesion of aluminum-silicon paste. We observed the formation of void and local back surface field between aluminum electrode and silicon base by SEM. The light IV, quantum efficiency and reflectance of the solar cells were characterized and compared for each paste.

• Journal of the Korean Chemical Society
• /
• v.60 no.3
• /
• pp.169-176
• /
• 2016

In a borate buffer solution, the growth kinetics and the electronic properties of passive film on aluminum were investigated, using the potentiodynamic method, chronoamperometry, and multi-frequency electrochemical impedance spectroscopy. The corrosion of aluminum was heavily influenced by the degree of oxygen concentration because of the increasing reduction current. The oxide film formed during the passivation process of aluminum has showed the electronic properties of n-type semiconductor, which follow from the Mott-Schottky equation. It was found out that the passive film (Al(OH)₃) of Al formed in the low electrode potential changes to Al₂O₃ while the electrode potential increases. The growth kinetics data as measured by chronoamperometry suggests a mechanism in which the growth of the film of Al₂O₃ is determined by field-assisted transport of ions through the film.

• 제어로봇시스템학회:학술대회논문집
• /
• 1996.10a
• /
• pp.311-314
• /
• 1996

In contactless disk handling systems based on electrostatic suspension in which the stator is to be transferred, the limited stiffness in lateral direction severely restricts the achievable translational acceleration. In existing stator electrode pattern designs, the magnitude of the lateral force is determined by the magnitude of the control voltages which are applied to the individual electrodes to levitate the disk stably. As a result, the lateral force cannot be set arbitrarily. A new stator electrode pattern is presented for the electrostatic levitation of disk-shaped objects, in particular silicon wafers and aluminum hard disks, which allows the lateral forces to be controlled independently from the levitation voltages. Therefore, greater lateral forces can be obtained, compared with the existing stator designs. Experimental results will be presented for a 4-inch silicon wafer that clearly reveal the increased lateral stiffness by using the proposed stator electrode compared to the conventional electrode pattern.

• Journal of Power System Engineering
• /
• v.8 no.3
• /
• pp.44-51
• /
• 2004

Effect of corrosion characteristics in relation to loaded stress in the welded zone of A5083-H116 aluminum alloy, in the seawater was studied. The corrosion experiment was performed for 120 hours on the specimens in the natural seawater tank with four steps of the loaded stress. The corrosion crack, corrosion rate, electrode potential, current, and corrosion pattern, etc. were examined for the specimens with the elapse of the immersion time. The main result derived from this study is the crack growth length is increased with the increasing loaded stress. The electrode potential and the corrosion current are decreased rapidly in the early stage of the corrosion, and then decreased gradually and stabilized eventually with the elapse of the immersion time. The test condition of the longer crack growth tends to show the higher corrosion rate. Corrosion pattern of the welded zone indicates that the depth and width of the pitting become increasing with the increasing loaded stress.

• Journal of Environmental Science International
• /
• v.26 no.3
• /
• pp.269-280
• /
• 2017

To lower the operational cost of microbubble generation by electrolysis, optimization of parameters limiting the process must be carried out for the process to be fully adopted in environmental and industrial settings. In this study, four test electrodes were used namely aluminum, iron, stainless steel, and Dimensionally Sable Anode (DSA). We identified the effects and optimized each operational parameter including NaCl concentration, current density, pH, and electrode distance to reduce the operational cost of microbubble generation. The experimental results showed that was directly related to the rate and cost of microbubble generation. Adding NaCl and narrowing the distance between electrodes caused no substantial changes to the generation rate but greatly decreased the power requirement of the process, thus reducing operational cost. Moreover, comparison among the four electrodes operating under optimum conditions revealed that aluminum was the most efficient electrode in terms of generation rate and operational cost. This study therefore presents significant data on performing costefficient microbubble generation, which can be used in various environmental and industrial applications.