• 한국분말재료학회지
• /
• 제7권3호
• /
• pp.161-167
• /
• 2000

Mechanically-alloyed NiAl powder and ball-milled (Ni+Al) powder mixture were sintered by spark-plasma sintering(SPS) process. Mechanical alloying was performed in a horizontal attritor for 20 h with rotation speed of 600 rpm. (Ni+Al) powder mixtures were prepared by ball milling for 1 and 10 h with 120 rpm. Both powders were sintered at $1150^{\circ}C$ for 5 min under $10^{-3}$ torr vacuum with 50 MPa die pressure in a SPS facility. Sintered densities of 97% and 99% were obtained from mechanically-alloyed NiAl powder and (Ni+Al) powder mixture, respectively. The sintered compact of (Ni+Al) powder mixture showed large grain size by a very rapid grain growth, while the grain size of mechanically-alloyed NiAl powder compact after sintering was extremely fine(80 nm). The difference in densification behavior of both powders were discussed.

• 한국재료학회지
• /
• 제16권2호
• /
• pp.137-143
• /
• 2006

The effects of Cu and Fe additions on the thermal stability, microstructure and mechanical properties of $Al_{85}-Ni_{8.5}-Mm_{6.5},\;Al_{84}-Ni_{8.5}-Mm_{6.5}Cu_1,\;Al_{84}-Ni_{8.5}-M_{m6.5}Fe_1$ alloys, manufactured by gas atomization, degassing and hot-extrusion were investigated. Gas atomization, with a wide super-cooled liquid region, allowed the alloy powders to exhibit varying microstructure depending primarily on the powder size and composition. Al hotextruded alloys consisted of homogeneously-distributed fine-grained fcc-Al matrix and intermetallic compounds. A substitution of 1 at.% Al by Cu increased the thermal stability of the amorphous phase and produced alloy microstructure with smaller fcc-Al grains. On the other hand, the same substitution of 1 at.% Al by Fe decreased the stability of the amorphous phase and produced larger fcc-Al grains. The formation of intermetallic compounds such as $Al_3Ni,\;Al_{11}Ce_3\;and\;Al_{11}La_3$ was suppressed by the addition of Cu or Fe. Among the three alloys examined, the highest Vickers hardness and compressive strength were obtained for $Al_{84}-Ni_{8.5}-M_{m6.5}Cu_1$ alloy, and related to the finest fcc-Al grain size attained from increased thermal stability with Cu addition.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2005년도 춘계학술대회 논문집
• /
• pp.303-306
• /
• 2005

Two composites of five plies of STS/Al/Al/Al/STS and STS/Al/STS/Al/STS were produced by roll-cladding at $350^{\circ}C$ from ferritic stainless steel (STS) and aluminum (Al) sheets. In order to analyze the strain states during roll-cladding, the evolution of textures at different through-thickness positions in the roll-clad composites was investigated. Simulations with the finite element method (FEM) disclosed that a strain state which was similar to that of normal rolling with a high friction between roll surface and Al sample led to the formation of texture gradients in the Al sheets in the STS/Al/Al/Al/STS composite. Differences in the material velocity of STS and Al in the rolling direction gave rise to the formation of the shear texture in the Al sheets in the STS/Al/STS/Al/STS composite.

• 한국세라믹학회지
• /
• 제36권8호
• /
• pp.782-790
• /
• 1999

The compressibility sinterability sintering behaviour and thermal stability of AlOOH added UO2 pellt and PVA-Al(III) complex added UO2 pellet were investigated respectively. Compared with characteristics of AlOOH added UO2 pellet the green density and the sintered density of PVA-Al(III) complex added UO2 pellet were lowered but the grain size and the pore size of that were more increased in accordance with higher compacting pressure. The AlOOH added UO2 pellet had the grain size of about 14${\mu}{\textrm}{m}$ with monomodal pore size distribution while the PVA-Al(III) complex added UO2 pellet had the grain size of about 42 ${\mu}{\textrm}{m}$ with bimodal pore size distribution. The PVA-A(III) complex added UO2 pellet had a similiar open porosity to the AlOOH added UO2 pellet and a lower resintered density change than the AlOOH added UO2 pellet.

• 열처리공학회지
• /
• 제20권4호
• /
• pp.187-194
• /
• 2007

A transmission electron microscope (TEM) investigation has been performed on the precipitation of $L2_1$-type $Ni_2AlTi$ phase in B2-ordered NiAl system. The hardness after solution treatment is high in NiAl-Ti alloys suggesting the large contribution of solid solution strengthening in this alloy system. However, the amount of age hardening is not large as compared to the large microstructural variations during aging. At the beginning of aging, the $L2_1$-type $Ni_2AlTi$ precipitates keep a lattice coherency with the NiAl matrix. By longer periods of aging $Ni_2AlTi$ precipitates lose their coherency and change their morphology to the globular ones surrounded by misfit dislocations. Misfit dislocations, which are observed on {100} planes of H-precipitates have the Burgers vector of a <100> with a pure edge type. The lattice misfits of NiAl-$Ni_2AlTi$ system is estimated from the spacings of misfit dislocations to be 1.1% at 1273 K. The lattice misfits decrease with increasing aging temperature in this system.

• 열처리공학회지
• /
• 제35권1호
• /
• pp.1-7
• /
• 2022

In this study, dissolution and melting phenomenon of the Al₂Cu was studied for the high-strength Al-Si-Cu aluminum alloy in automobile component. The Solution heat treatment was performed at 480℃ and 510℃ for 4hours. Microstructure analysis of the specimen was performed using the optical micrograph and scanning electron microscope for qualitative and quantitative analysis of various phases, the chemical composition of secondary phases was achieved by energy dispersive spectroscopy (EDS) and electron probe micro analysis (EPMA). As a result of the electron probe micro analysis, a plate like Al₂Cu phase was observed, and eutectic Si phase was observed of a coarsen plate shape. At a temperature of 510, necking phenomenon occurs in a specific part of plate like Al₂Cu, and it is segmented and dissolved in the Al matrix. When the temperature of the alloy exceeds the melting point of Al₂Cu, incipient melting occurs at the grain boundary of undissolved Cu particles

• 한국재료학회지
• /
• 제22권2호
• /
• pp.97-102
• /
• 2012

The microstructure and tensile properties of Al-Mn/Al-Si hybrid aluminum alloys prepared by electromagnetic duocasting were investigated. Only the Al-Mn alloy showed the typical cast microstructure of columnar and equiaxed crystals. The primary dendrites and eutectic structure were clearly observed in the Al-Si alloy. There existed a macro-interface of Al-Mn/Al-Si alloys in the hybrid aluminum alloys. The macro-interface was well bonded, and the growth of primary dendrites in Al-Si alloy occurred from the macro-interface. The Al-Mn/Al-Si hybrid aluminum alloys with a well-bonded macro-interface showed excellent tensile strength and 0.2% proof stress, both of which are comparable to those values for binary Al-Mn alloy, indicating that the strength is preferentially dominated by the deformation of the Al-Mn alloy side. However, the degree of elongation was between that of binary Al-Mn and Al-Si alloys. The Al-Mn/Al-Si hybrid aluminum alloys were fractured on the Al-Mn alloy side. This was considered to have resulted from the limited deformation in the Al-Mn alloy side, which led to relatively low elongation compared to the binary Al-Mn alloy.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2003년도 추계학술발표강연 및 논문개요집
• /
• pp.44-44
• /
• 2003

Scandium을 소량 첨가한 Al합금은 용체화 처리 후 시효에 의해 강화되며, 합금의 주 강화상은 Ll2 type의 규칙구조를 갖는 A1$_3$Sc상으로 열처리시 아주 미세한 정합의 구형입자로 석출한다. Scandium은 Al합금에서 첨가원소의 at%에 따른 경량화 효과가 Gold 다음으로 크다. 현재까지의 Al-Sc계 합금에 대한 연구는 시효경화에 따른 기계적 특성 변화에 대해서만 이루어져 왔으나 본 연구에서는 투과전자현미경을 이용하여 열처리에 따른 미세조직의 변화, 급냉 상태에서 생성된 A13Sc입자의 형성 및 계면구조, 시효에 따른 석출거동을 규명하였다. 실험에 사용된 alloy는 미국의 Ashurst 사에서 제조된 Al-2wt%Sc모합금과 순도 99.9%의 Al을 혼합하여 Arc melting법으로 제조하였다. Primary A13Sc상은 Ll2 type으로 응고시에 용융상태에서 먼저 핵생성되어 Al의 핵생성 site로 작용한다. 635$^{\circ}C$에서 용체화 처리한 시편에서는 수백 nm 크기를 갖는 $Al_3$Sc상이 계면과 matrix내에 구형으로 존재함을 확인하였다. 수백 nm 크기의 $Al_3$Sc상의 내부에는 역위상 경계(Antiphase boundary)이 존재로 인한 특징적인 contrast가 관찰되었으며, 이 $Al_3$Sc상은 응고시 생성된 작은 $Al_3$Sc상들이 모여져 생성된 것으로 추측된다. 수백 nm 크기 의 $Al_3$Sc사와 Al matrix 사이의 계면에는 격자상수 차이에 의한 많은 edge dislocation들이 관찰된다.

• 한국재료학회지
• /
• 제28권6호
• /
• pp.361-364
• /
• 2018

Binary Ti-Al alloys below 51.0 mass%Al content exhibit a breakaway, transferring from parabolic to linear rate law. The second $Al_2O_3$ layer might have some protectiveness before breakaway. Ti-63.1 mass%Al oxidized at 1173 K under parabolic law. Breakaway oxidation is observed in every alloy, except for Ti-63.1 mass%Al. After breakaway, oxidation rates of the binary TiAl alloys below 34.5 mass%Al obey almost linear kinetics. The corrosion rate of Ti-63.1 mass%Al appears to be almost parabolic. As content greater than 63.0 mass% is found to be necessary to form a protective alumina film. Addition of Mo improves the oxidation resistance dramatically. No breakaway is observed at 1123 K, and breakaway is delayed by Mo addition at 1173 K. At 1123 K, no breakaway, but a parabolic increase in mass gain, are observed in the Mo-added TiAl alloys. The binary Ti-34.5 mass%Al exhibits a transfer from parabolic to linear kinetics. At 1173 K, the binary alloys show vary fast linear oxidation and even the Mo-added alloys exhibit breakaway oxidation. The 2.0 mass%Mo-added TiAl exhibits a slope between linear and parabolic. At values of 4.0 and 6.0 mass% added TiAl alloys, slightly larger rates are observed than those for the parabolic rate law, even after breakaway. On those alloys, the second $Al_2O_3$ layer appears to be persistently continuous. Oxidation resistance is considerably degraded by the addition of Mn. Mn appears to have the effect of breaking the continuity of the second $Al_2O_3$ layer.

• 한국산림과학회지
• /
• 제90권1호
• /
• pp.74-82
• /
• 2001

Al과 Mn을 여러가지 농도로 조정한 배양액을 채운 포트에 소나무(Pinus densiflora) 2년생 묘목을 이식하여 수경재배법에 의해 90일간 온실내에서 육성한 후 소나무 묘목의 생장, 영양상태 및 가스교환속도에 미치는 Al과 Mn의 영향을 조사하였다. 배양액의 Al농도는 4수준(0, 10, 30, 60ppm)으로 처리하였으며, 이들 각각의 Al처리에 Mn농도를 3수준(0, 30, 60ppm)으로 처리하여 총 12처리구의 2요인배치법(two-factor design)의 실험을 실시하였다. Al과 Mn은 소나무 묘목의 건물생장에 상호작용효과(interaction effects)를 나타내지 않았으나, 소나무 묘목의 건물생장에 대한 Al과 Mn의 각각의 단독영향(main effects)은 유의적인 차이가 나타났다. 소나무 묘목의 건물생장은 Al은 10ppm이상, Mn은 60ppm의 농도에서 생장저하를 초래하였으며, 이는 소나무 묘목의 건물생장에 대한 Al의 독성이 Mn에 비해 클 수 있음을 시사한다. 뿌리의 암호흡속도는 Al의 경우 60ppm에서, Mn의 경우는 30ppm이상의 농도에서 저하하였다. 또한, 크로로필함량에 있어서는 Al의 영향은 인정되지 않았으나, 60ppm의 Mn처리구에서 낮아지는 경향을 보였다. 배양액의 Al과 Mn농도가 증가함에 따라서 소나무 묘목의 상대생장율(RGR) 및 순동화율(NAR)이 저하하였으며, 이는 광합성 효율의 감소가 원인으로 생각된다. 비록 본 연구결과는 수경재배법에 의하여 얻어진 결과이지만, 장래 우리나라에서 실제로 발생할 수 있는 산성강하물에 의한 수목피해 예측 및 산성화된 토양의 임지에서도 이와 유사와 현상이 발생될 수 있음을 시사하고 있다.