• Journal of Korea Foundry Society
• /
• v.29 no.1
• /
• pp.45-51
• /
• 2009

Conventionally, Al-Sn bearing manufacturing involves casting the Al-Sn alloy and roll-bonding to a steel backing strip. This article will describe the microstructural control of Al-Sn metal bearing alloy following heat treatment. When the pure aluminum rod dipped in the melt of tin maintained below the melting point of aluminum, the melting of aluminum was accelerated with penetration of tin along the grain boundary of aluminum. The length of plate-shaped eutectic tin was decreased with heat treatment time. With even longer heat treatment time over 1 hour the length of eutectic tin didn't decrease any more, while resulting in coarsening of aluminum matrix. Exuded liquid of eutectic tin was formed at the surface of Al-Sn alloy after heat treatment even at below eutectic temperature.

• Journal of Korea Foundry Society
• /
• v.35 no.2
• /
• pp.36-43
• /
• 2015

In this study, the influences of aluminum and tin additions (individual and combined) on corrosion behavior of magnesium alloy have been determined. The studied alloys were fabricated by permanent mold casting method to measure the corrosion properties, a potentiodynamic test, hydrogen evolution test and immersion test were carried out in a 3.5% NaCl solution at pH 7.2. From the results of microstructure analysis, the Mg-9Al-1Zn alloy was found to be composed of ${\alpha}$-Mg and rod-like $Mg_{17}Al_{12}$ phase and the Mg-5Sn-5Al-1Zn alloy was found to be composed of ${\alpha}$-Mg, rod-like $Mg_{17}Al_{12}$ and $Mg_2Sn$ phases. In the case of the Mg-9Sn-1Zn alloy, the microstructure was composed of ${\alpha}$-Mg and eutectic $Mg_2Sn$ phase. With Sn addition (individual and combined), the corrosion resistance of the Mg alloys improved.

• Journal of Powder Materials
• /
• v.30 no.4
• /
• pp.339-345
• /
• 2023

This study investigates the melting point and brazing properties of the aluminum (Al)-copper (Cu)-silicon (Si)-tin (Sn) alloy fabricated for low-temperature brazing based on the alloy design. Specifically, the Al-20Cu-10Si-Sn alloy is examined and confirmed to possess a melting point of approximately 520℃. Analysis of the melting point of the alloy based on composition reveals that the melting temperature tends to decrease with increasing Cu and Si content, along with a corresponding decrease as the Sn content rises. This study verifies that the Al-20Cu-10Si-5Sn alloy exhibits high liquidity and favorable mechanical properties for brazing through the joint gap filling test and Vickers hardness measurements. Additionally, a powder fabricated using the Al-20Cu-10Si-5Sn alloy demonstrates a melting point of around 515℃ following melting point analysis. Consequently, it is deemed highly suitable for use as a low-temperature Al brazing material.

• Journal of the Korean Magnetics Society
• /
• v.23 no.4
• /
• pp.117-121
• /
• 2013

In this study we investigated magnetism and magnetostriction of B2-structured FeX (X = Al, Si, Ni, Ga, Ge, and Sn) using a first-principles method, in order to survey the possibility of developing a transition metal based magnetostriction material. The Full-potential Linearized Augmented Plane Wave method was employed for solving the Kohn-Sham equation within the generalized gradient approximation for exchange-correlation interaction between electrons. FeX alloys are stabilized in ferromagnetic states except for the FeSi and FeGe alloys. Magnetostrcition coefficients of FeX (X = Al, Ni, Ga, and Sn) were calculated to be -5, +6, -84, -522ppm, respectively. It is noteworthy that the magnetostriction coefficient (-522ppm) of FeSn is larger than that (+400ppm) of Gafenol.

• Journal of Powder Materials
• /
• v.21 no.5
• /
• pp.377-381
• /
• 2014

This work describes the coloration, chemical stability of $SiO_2$ and $SnO_2$-coated blue $CoAl_2O_4$ pigment. The $CoAl_2O_4$, raw materials, were synthesized by a co-precipitation method and coated with silica ($SiO_2$) and tin oxide ($SnO_2$) using sol-gel method, respectively. To study phase and coloration of $CoAl_2O_4$, we prepared nano sized $CoAl_2O_4$ pigments which were coated $SiO_2$ and $SnO_2$ using tetraethylorthosilicate, $Na_2SiO_3$ and $Na_2SiO_3$ as a coating material. To determine the stability of the coated samples and their colloidal solutions under acidic and basic conditions, colloidal nanoparticle solutions with various pH values were prepared and monitored over time. Blue $CoAl_2O_4$ solutions were tuned yellow color under all acidic/basic conditions. On the other hand, the chemical stability of $SiO_2$ and $SnO_2$-coated $CoAl_2O_4$ solution were improved when all samples pH values, respectively. Phase stability under acidic/basic condition of the core-shell type $CoAl_2O_4$ powders were characterized by transmission electron microscope, X-ray diffraction, CIE $L^*a^*b^*$ color parameter measurements.

• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.159-165
• /
• 1994

Two kinds of humidity sensor are made, one by anodizing pure aluminum and the other by evaporation Sn02 on the anodized pure alumia film, and their electrical characteristics are investigated in various humidity atmosphere. The change of surface resistance with humidity of $AI_2O_3/AI$ and $SnO_2-AI_2O_3/Al$ sensors are found to be $1.40 \times 10^{-2}\Omega$/RH and $1.56 \times 10^{-2}\Omega$/RH, respectively. The hysteresis phenomena associated with the irreversibility of surface resistance-humidity is less in $SnO_2-AI_2O_3/Al$ sensor than in $AI_2O_3/AI$. It is concluded that $SnO_2-AI_2O_3/Al$ film can be used as humidity sensor in room temperature region because temperature dependence of surface resistance of the film is found to be as $0.56 \times 10^{-2} \Omega /^{\circ}C$ in O~ $20^{\circ}C$ range, where as $2.50 \times 10^{-2} \Omega /^{\circ}C$ in 40-$50^{\circ}C$.

• Transactions of Materials Processing
• /
• v.21 no.5
• /
• pp.324-329
• /
• 2012

Mg-(9-x)Sn-xAl-1Zn (x=1, 2, 3 and 4 wt.%) alloys were subjected to indirect extrusion, and the microstructure and mechanical properties of the as-extruded Mg-Sn-Al-Zn (TAZ) alloys were investigated. The TAZ 811 alloy exhibited a finer grain structure than the TAZ 541 alloy due to a larger number of Mg2Sn particles, which pinned the grain boundaries and prevented growth of recrystallized grains. The TAZ alloys showed an unusual yield asymmetry behavior. The tension-compression yield asymmetry increased with decreasing average grain size. The TAZ 811 alloy with a small grain size exhibited a larger yield asymmetry than that of the TAZ 541 alloy having a relatively large grain size, which is mainly attributed to the low Al content and large number of second phase particles in the TAZ 811 alloy.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.3
• /
• pp.757-767
• /
• 2018

In the propane dehydrogenation reaction proceeding at high temperature, the main cause of deactivation of the catalyst is coke deposition and sintering. In order to investigate the catalysts for reducing such inactivation, we have investigated the applicability of $MgAl_2O_4$ as a carrier for the catalytic dehydrogenation reaction. $MgAl_2O_4$ was prepared by Alcohthermal method at calcination temperature of 800, 900, $1000^{\circ}C$, and $Pt-Sn/MgAl_2O_4$ catalyst was prepared by supporting Pt and Sn by co-impregnation method. The reaction temperature was conducted at a high temperature of 650, $600^{\circ}C$ to confirm the thermal stability. As a result of the reaction experiment, it was confirmed that the conversion rate and yield of propane dehydrogenation reaction test were higher than that of the carrier-applied catalyst having a carrier calcination temperature of 900 and $1000^{\circ}C$, when the carrier-applied catalyst having a calcination temperature of $800^{\circ}C$ was used, It was found that the yield was higher than that of $Pt-Sn/{\theta}-Al_2O_3$ at $650^{\circ}C$. TGA, BET, XRD, CO-chemisorption, and SEM-EDS analyzes were performed for characterization. $MgAl_2O_4-800^{\circ}C$ was correlated with the relationship between good yield, Pt dispersion and low deactivation rate.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.4
• /
• pp.251-260
• /
• 2000

Ta and Hf added Ti-l5Sn-4Nb alloys without V and Al elements for biomaterial were melted by arc furnace in response to recent concerns about the long term safety of Ti-6Al-4V alloy. All specimens were homogenized at $1000^{\circ}C$ and solution treatment was performed at $812^{\circ}C$ and aging treatment at $500^{\circ}C$. The microstructure and mechanical properties were analysed by optical micrograph, hardness tester and instron. Ti-l5Sn-4Nb system alloys showed widmanstatten microstructure which is typical microstructure in $\alpha$＋$\beta$ type Ti alloys. The Ti-l5Sn-4Nb-2Hf and Ti-l5Sn-4Nb-2Ta alloys showed better hardness and tensile strength compared with Ti-6Al-4V. The result of XPS analysis, Ti-l5Sn-4Nb alloy in air atmosphere consisted of $TiO_2$, SnO and NbO.

• Journal of Korea Foundry Society
• /
• v.12 no.3
• /
• pp.210-219
• /
• 1992

The measurement of the apparent and tap density for Al-Pb-X(Sn,Sn-Si) powders produced by centrifugal atomizer showed that the larger theoretically calculated densities the larger those densities. And tap densities were not over 50% of the theoretical densities. The nip angle of Al-5wt%Pb alloy powders produced with 38000 r.p.m. of disk rotation was $3^{\circ}$ degree larger than that of Al-8.5wt%Pb-3wt%Sn(-4wt%Si, 8wt%Si) with 50000 r.p.m. The effects of roll gap and rolling speed on thickness and density of the single strips by rolling were that rolling speed increasing the thickness and density of strip decreased and roll gap increasing, the thickness of strip increased but the density decresed. The compactibility of Al-Pb-X with Al by rerolling showed that the coarse powder-strips were better than fine powder-strips. From the SEM study with EDX analysis on the sintered strips, it was found that Pb and Sn were segregated with maximum size $5{\mu}m$, and Si existed surrounding the segregation zone. After sintering the clad strips at $500^{\circ}C$, the pores, which were spherical with $5{\mu}m$ of mean diameter, partly remained around the particles of alloy powders area, while completely disappeared at clad interface. The hardness of strips of alloy powders decreased linearly with increasing sintering temperature.