• Resources Recycling
• /
• v.7 no.5
• /
• pp.52-57
• /
• 1998

Effect of Si in the electrochemical corrosion characteristics of Mg-Li-Al light alloy has been investigated by means of potentiodynamic polarization study. The elecrochemical behaviors were evaluated in 003% NaCl solution and the solution buffered with KH$_{2}PO_{5}{\cdot}$NaOH at room temperature. It was found that the addition of very small quantity of Si (0.48 wt%) in Mg-Li-Al light alloy increased corrosion rates and amount of corrosion products and decreated the pitting resistance of the alloy. From the results it was concluded that Si which is added to increase the strength of Mg-Li-Al alloy is harmful to corrosion properties of the alloy.

• Journal of Korea Foundry Society
• /
• v.41 no.6
• /
• pp.528-534
• /
• 2021

To confirm effects of natural and artificial aging of precipitate on thermal diffusivity and hardness, the studied Al-Mg-Si alloy were manufactured by gravity casting method with 0.6 wt% and 1.0 wt% additional Cu element. The samples were used for measuring thermal diffusivity and hardness. The addition of Cu, promoted by intermediates such as Q'' and θ'' phases, contributing to the improvement of hardness and high-temperature thermal diffusivity. The natural aging decreased the hardness of the Al-Mg-Si-Cu alloys with increasing time, but did not affect the thermal diffusivity.

• Journal of Korea Foundry Society
• /
• v.24 no.6
• /
• pp.340-346
• /
• 2004

The plan for obtaining a good combination of strength and castability appeared feasible and the following observations were made. 1. In Al-12Mg-6.6Zn-xSi alloys, more primary $Mg_2Si$ phase formed with reduced $Al_3Mg_2$ phase, as Si content is necessary for an effective solution heat treatment because the solidus temperature is very low silicon contents. 2. A high tensile strength could be obtained in the heat-treated Al-12Mg-5.5Zn-5Si alloy attributed in the heat-treated Al-12Mg-5.5Zn-5Si alloy attributes to fine $MgZn_2$ particles that precipitated uniformly in the matrix. 3. Al-12Mg-5.5Zn-Si alloys showed excellent casting capabilities such as hot cracking resistance and fluidity compared to the reference commercial alloys. 4. The wear resistance of Al-12Mg-5.5Zn-5Si alloy was superior to that of A7075 alloy, and even higher resistance is expected if the morphology and size of primary $Mg_2Si$ phase is carefully controlled.

• Journal of Korea Foundry Society
• /
• v.43 no.6
• /
• pp.286-293
• /
• 2023

In this study, we investigated the microstructural evolution of Al-Mg-Zn aluminum alloy billet during homogenization treatment using OM, SEM, EDS and DSC. There were numerous phases found, such as; AlMgZn, AlMgFe, and AlMgZnSi phases, in the grain of the cast billet. After 6 hours homogenization treatment, Zn was mostly dissolved, whereas, Mg and Si were only partly dissolved. Accordingly, only AlMgFe and AlMgSi remained. After 18 hours, all of the leftover Mg and Si were dissolved, leaving only AlMgFe, which was also found after 24 hours. The results of the alloy design program, JMatPro showed that Mg dissloved more rapidly than Zn. According to the homogenization kinetic equation, Mg and Zn are completely dissolved within 1.9 and 3.5 hours, respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.685-690
• /
• 1998

The wetting behavior and the characteristic of spontaneous infiltration of pure Al and Al-(Si)-Mg alloys on {{{{ { {Al }_{ 2} O}_{3 } }} in vacuum argon and nitrogen atmosphere were investigated to find out the spontaneous in-filtration mechanism. The wetting of molten Al and Al alloys on {{{{ { {Al }_{ 2} O}_{3 } }} was only possible in cacuum at-mosphere but the sponataneous infiltration of molten Al-(Si)-Mg alloys was successfully made on {{{{ { {Al }_{ 2} O}_{3 } }} pre-form in nitrogen atmoshpere. The difference of wettability and spontaneous infiltration of molten Al and Al alloys on {{{{ { {Al }_{ 2} O}_{3 } }} were found to be related to formation of the Mg-N compound coated layer on {{{{ { {Al }_{ 2} O}_{3 } }} particles which was believd to increase wettability of molten Al alloys on {{{{ { {Al }_{ 2} O}_{3 }.

• Journal of Korea Foundry Society
• /
• v.41 no.1
• /
• pp.3-10
• /
• 2021

In the compound casting between the aluminum alloy and the cast iron, the iron component may be dissolved from the cast iron during the process and mixed into the aluminum melt, thereby forming various iron-containing intermetallic compounds and significantly deteriorating the tensile properties of the aluminum alloy. On the other hand, unlike Fe, which is added as an impurity, Cu is added to improve the mechanical properties of the aluminum alloy. In this study, the change in microstructure and tensile properties of aluminum alloys due to the addition of Fe and Cu was investigated. A large amount of iron-containing compounds such as coarse Al₅FeSi phases were formed when the iron content was 1% or more, and the tensile properties were significantly reduced. In the case of the aluminum alloy to which Cu was added, an Al₂Cu phase was additionally formed and the tensile strength was clearly improved.

• Journal of the Korean Society for Precision Engineering
• /
• v.20 no.12
• /
• pp.48-54
• /
• 2003

Alumium alloys casting are gaining increased acceptance in the automotive and electronic industeries and squeeze casting is the most efficient method of manufacturing such mass produced parts. This study has been investigated the microstructures and mechanical properties of Al-7.0Si-0.4Mg (AC4C) alloy fabricated by squeeze casting process for development of Fuel system Parts (Fuel rail). The microstructure of squeeze casted specimen were composed of eutectic structure Alumimim solid solution and $Mg_2$Si precipitates. The tensile strength of as-solid solution treatment Al-7.0Si-0.4Mg ahoy revealed 298.5MPa. It was found that Al-7.0Si-0.4Mg alloy have good corrosion resistance in electrochemical polarization test.

• Journal of Korea Foundry Society
• /
• v.42 no.6
• /
• pp.337-346
• /
• 2022

In order to optimize the solution treatment conditions of Al-7Si-(0.3~0.5)Mg-(0~0.5)Cu alloys, a series of heat treatment experiments were conducted under various solution treatment times up to 7 hours at 545℃, followed by a microstructural analysis using optical microscopy, FE-SEM, and Brinell hardness measurements. Rapid coarsening of eutectic Si particles was observed in the alloys during the first 3 hours of solution treatment but the size of those Si particles did not change at longer solution treatment conditions. Meanwhile, the degree of spheroidisation of eutectic Si particles increased until the solution treatment time was increased up to 7 hours. Q-Al5Cu2Mg8Si6 andθ-Al2Cu were observed in as-cast Cu-containing Al alloys but the intermetallic compounds were dissolved completely after 3 hours of solution treatment at 545℃. Depending on the initial Mg composition of the Al alloys, π-Al8FeMg3Si either disappeared in the alloy with 0.3wt% of Mg content after 5 hours of solution treatment or remained in the alloy with 0.5wt% of Mg content after 7 hours of solution treatment time. Mg and Cu content in the primary-α phase of the Al alloys increased until the solution treatment time reached 5 hours, which was in accordance with the dissolution behavior of Mg or Cu-containing intermetallic compounds with respect to the solution treatment time. From the results of microstructural changes in the Al-7Si-Mg-Cu alloys during solution treatment, it was concluded that at least 5 hours of solution treatment at 545℃ is required to maximize the age hardening effect of the present Al alloys. The same optimal solution treatment conditions could also be derived from Brinell hardness values of the present Al-7Si-Mg-Cu alloys measured at different solution treatment conditions.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.78-78
• /
• 2002

• Proceedings of the KWS Conference
• /
• v.43
• /
• pp.85-87
• /
• 2004