Aluminum nitride (AlN) thin films were deposited on Si substrates by using polycrystalline (poly) 3C-SiC buffer layers, in which the AlN film was grown by pulsed reactive magnetron sputtering. Characteristics of grown AlN films were investigated experimentally by means of FE-SEM, X-ray diffraction, and FT-IR, respectively. The columnar structure of AlN thin films was observed by FE-SEM. X-ray diffraction pattern proved that the grown AlN film on 3C-SiC layers had highly (002) orientation with low value of FWHM (${\Theta}=1.3^{\circ}$) in the rocking curve around (002) reflections. These results were shown that almost free residual stress existed in the grown AlN film on 3C-SiC buffer layers from the infrared absorbance spectrum. Therefore, the presented results showed that AlN thin films grown on 3C-SiC buffer layers can be used for various piezoelectric fields and M/NEMS applications.

• Transactions on Electrical and Electronic Materials
• /
• 제11권4호
• /
• pp.166-169
• /
• 2010

In this study, we changed the etch parameters (gas mixing ratio, radio frequency [RF] power, direct current [DC]-bias voltage, and process pressure) and then monitored the effect on the $HfAlO_3$ thin film etch rate and the selectivity with $SiO_2$. A maximum etch rate of 108.7 nm/min was obtained in $Cl_2$ (3 sccm)/$BCl_3$ (4 sccm)/Ar (16 sccm) plasma. The etch selectivity of $HfAlO_3$ to $SiO_2$ reached 1.11. As the RF power and the DC-bias voltage increased, the etch rate of the $HfAlO_3$ thin film increased. As the process pressure increased, the etch rate of the $HfAlO_3$ thin films increased. The chemical state of the etched surfaces was investigated with X-ray photoelectron spectroscopy. According to the results, the etching of $HfAlO_3$ thin film follows the ion-assisted chemical etching.

• 한국재료학회지
• /
• 제23권12호
• /
• pp.714-721
• /
• 2013

A stoichiometric mixture of evaporating materials for $ZnAl_2Se_4$ single-crystal thin films was prepared in a horizontal electric furnace. These $ZnAl_2Se_4$ polycrystals had a defect chalcopyrite structure, and its lattice constants were $a_0=5.5563{\AA}$ and $c_0=10.8897{\AA}$.To obtain a single-crystal thin film, mixed $ZnAl_2Se_4$ crystal was deposited on the thoroughly etched semi-insulating GaAs(100) substrate by a hot wall epitaxy (HWE) system. The source and the substrate temperatures were $620^{\circ}C$ and $400^{\circ}C$, respectively. The crystalline structure of the single-crystal thin film was investigated by using a double crystal X-ray rocking curve and X-ray diffraction ${\omega}-2{\theta}$ scans. The carrier density and mobility of the $ZnAl_2Se_4$ single-crystal thin film were $8.23{\times}10^{16}cm^{-3}$ and $287m^2/vs$ at 293 K, respectively. To identify the band gap energy, the optical absorption spectra of the $ZnAl_2Se_4$ single-crystal thin film was investigated in the temperature region of 10-293 K. The temperature dependence of the direct optical energy gap is well presented by Varshni's relation: $E_g(T)=E_g(0)-({\alpha}T^2/T+{\beta})$. The constants of Varshni's equation had the values of $E_g(0)=3.5269eV$, ${\alpha}=2.03{\times}10^{-3}eV/K$ and ${\beta}=501.9K$ for the $ZnAl_2Se_4$ single-crystal thin film. The crystal field and the spin-orbit splitting energies for the valence band of the $ZnAl_2Se_4$ were estimated to be 109.5 meV and 124.6 meV, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}_5$ states of the valence band of the $ZnAl_2Se_4/GaAs$ epilayer. The three photocurrent peaks observed at 10 K are ascribed to the $A_1$-, $B_1$-exciton for n = 1 and $C_{21}$-exciton peaks for n = 21.

• 한국전기전자재료학회논문지
• /
• 제11권10호
• /
• pp.826-832
• /
• 1998

In this study the thin films with the structure of Si+SiO$_2$+TiN are made by RF supttering method. TiN, which has small diffusion coefficient and low resistivity, is evaporated between SiO$_2$ and Al layers. It investigates the V-R characteristics depending on the thickness of SiO$_2$ which is used as insulation layer and researches its effects on voltage stability of thin film and varistor. These films show very small resistance valus in negative(-) voltage and large and large value in positive voltage band, and with the increase of voltage, resistance value is rapidly reduced and the satisfactory characteristic of varistor is shown at +1[V]. It is found that resistance value of TiN thin film is small and also TiN thin film has more current than the thin film which is not evaporated by TiN thin film. When Al electrode is evaporated of SiO$_2$ thin film, spiking occurs, but the spiking can be prevented with evaporation of TiN between SiO$_2$ and Al layers and this thin films in made easily because of its good attachment. With the increase of voltage, the resistance is changed into non-linear pattern and the bidirectional varistor characteristic is shown and then its theory can be verified by this experiment. Accordingly, when TiN is evaporated of Si Wafer(n-100), it obtains better voltage-resistance than thin film which is not evaporated and also when varistor character is used electrically to automatic control element such as elimination of flame, power distribution arrestor and constant voltage compensation, satisfactory reproducibilities are expected.

• 열처리공학회지
• /
• 제23권2호
• /
• pp.69-74
• /
• 2010

AlN thin films were deposited by using a two-facing-targets type sputtering system (TFTS), and their deposition characteristics, microstructure and texture were investigated. Total gas pressure was kept constant at 0.4 Pa and the partial pressures of nitrogen, $PN_2$ (($N_2$ pressure)/($Ar+N_2$ pressure)) varied from 0 to 0.4 Pa. The texture of the film cross-sections and surface morphology were observed by field emission scanning electron microscope (FE-SEM). The crystallographic orientation of the films were analyzed by X-ray diffraction (XRD). Deposition of AlN film depends on $N_2$ partial pressure. The best preferred oriented AlN thin films can be deposited at a nitrogen partial pressure of $PN_2$ = 0.52. As-deposited AlN films show preferred orientation and columnar structure, and the grAlN size of AlN films increases with increasing sputtering current.

• 한국재료학회지
• /
• 제9권1호
• /
• pp.25-29
• /
• 1999

We have developed a laser molecular beam epitaxy system for the layer-by-layer growth of oxide thin films. Using this system, we could grow and control oxide thin films of LaAlO$_3$in a molecular layer epitaxy mode on the atomically flat SrTiO$_3$ substrate with a LaAlO$_3$single crystal target. Very clear RHEED oscillations were observed during to growth of a LaAlO$_3$ film for a long period under the optimized conditions of substrate temperature at $650^{\circ}C$, oxygen pressure at 1$\times$10\ulcorner torr, and an incident laser fluence of 4.6J/$\textrm{cm}^2$. The height of mono-layer-LaAlO$_3$ film grown during one period of RHEED intensity oscillation was 3.8$\AA$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.525-528
• /
• 2001

ZnO:Al thin film can be used as a transparent conducting oxide(TCO) which has low electric resistivity and high optical transmittance for the front electrode of amorphous silicon solar cells and display devices. This study of electrical, crystallographic and optical properties of Al doped ZnO thin films prepared by Facing Targets Sputtering (FTS), where strong internal magnets were contained in target holders to confine the plasma between the targets, is described. Optimal transmittance and resistivity was obtained by controlling flow rate of O$_2$ gas and substrate temperature. When the of gas rate of 0.3 and substrate temperature 200$^{\circ}C$ , ZnO:Al thin film had strongly oriented c-axis and lower resistivity(<10$\^$-4/Ω-cm).

• 한국진공학회지
• /
• 제22권3호
• /
• pp.126-130
• /
• 2013

PSG/$SiO_2$ 보호막 처리된 Al-1%Si 박막배선 내 sodium (Na)과 수분($H_2O$) 게터링(gettering) 현상을 측정, 분석하였다. PSG/$SiO_2$ 보호막과 Al-1%Si 박막을 상압CVD (APCVD: atmosphere pressure chemical vapor deposition)법과 DC 마그네트론 스퍼터로 각각 증착하였고, 이차이온 질량분석기(SIMS: secondary ion mass spectrometry)를 이용한 깊이분포측정(depth profiling) 분석을 통해 PSG/$SiO_2$ 보호막으로부터 Al-1%Si 박막배선 층까지의 sodium과 수분 등 성분들의 분포를 확인하였다. Sodium과 수분 피크 모두 Al-1%Si 박막배선 내부보다는 막 간 계면에서 강하게 나타났다. PSG와 $SiO_2$ 보호막 계면에서는 sodium 피크는 관찰되었지만 수분 피크는 관찰되지 않았다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.432-433
• /
• 2005

In this study, Al doped ZnO(AZO) thin film were prepared on glass substrates by FTS(Facing Targets Sputtering) system. We investigated electrical, optical and structural properties of AZO thin film with the substrate temperature of the R.T, $100^{\circ}C$, $200^{\circ}C$ and the post-annealing. The crystallinity of AZO thin film was increased with increasing the substrate temperature and post-annealing temperature $600^{\circ}C$. The remarkable change of the resistivity with the substrate temperature didn't found and the resistivity with post-annealing was increased slightly.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.614-617
• /
• 1995

Thin CoCrTa/Cr films were deposited on glass substrates at $280^{\circ}C$ with or without Al underlayer. The coercivity of CoCrTa increased considerably by introducing an Al underlayer. The grain size of Cr thin film deposited on Al underlayer became smaller than that of Cr thin film deposited on glass substrate. The grain size of CoCrTa thin film was determined by Cr grain size. The cause of the coercivity increase seems to be associated with the refinement and uniform distribution of CoCrTa grains.