• 열처리공학회지
• /
• 제23권1호
• /
• pp.10-16
• /
• 2010

The microstructure of Cu-Mg-P alloy sheet consisted of Cu matrix and very fine MgP precipitate, and it has been observed that the microstructure remains virtually unchanged by Ag additions up to 2%. Ag solutes were dissolved into the matrix and hardly found in the precipitates. The hardness increased with increase of the Ag content, while the conductivity slightly decreased. Strain hardening through cold rolling was found to be effective in improving the hardness, especially in high-Ag alloys. Aging treatment was conducted either before the first cold rolling or between the first and the final cold rolling, and the conductivity was significantly higher at the former case, regardless of the Ag content. Softening of Cu-Mg-P alloy sheet was remarkable above $400^{\circ}C$ and the Ag content did not show any significant effect on it.

• 한국주조공학회지
• /
• 제27권2호
• /
• pp.72-76
• /
• 2007

Contact materials are widely used as electrical parts. Ag-Cd alloy has a good wear resistance and stable contact resistance. But the Cd exists as coarse oxide in alloy so it have an effect on mechanical properties badly. Moreover, the Cd is an injury material to environment. Nowadays, the use of Cd is strictly restricted. Because of these disadvantage, Ag-Sn-In alloy has been developed. In Ag-Sn-In alloy, the Sn : In ratio affects the internal oxidation properties, such as the formation of the oxide layer on the surface. In this work, we changed and optimized the Sn : In ratio variety for good internal oxidation properties. We have shown that a internal oxidation process did not fully completed when the Sn : In ratio is over 4 : 1 because of the Sn oxide layer at surface. The increase of In decelerates the formation of Sn oxide layer.

• 한국재료학회지
• /
• 제16권10호
• /
• pp.639-646
• /
• 2006

Over the last two decades, microbiologically influenced corrosion (MIC) of metallic materials has received considerable attention due to its serious effects on industrial field. In this context, it is important to devise control methods which inhibit biofilm formation on various metallic compounds and are compatible with environment. It was change of various conditions (duty cycle, current density, $AgNO_3$ concentration and pH) for injection of Ag particles in anodized Aluminum alloy pore using pulsed current. Optimal condition was obtained by means of FE-SEM, ICP analysis etc. The antibacterial metal's specimen were manufactured under optimal condition and this specimen were tested the antibacterial characterization and anticorrosion characterization. In result of test, we can confirmed that the antibacterial characterization and anticorrosion characterization of the specimens of injected Ag particles in anodized Aluminum alloy pore using pulsed current were better than the anodized Aluminum alloy specimens.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2003년도 추계학술대회 논문집
• /
• pp.131-133
• /
• 2003

The effect of axial strain and thermal cycling on the critical current is investigated for the Bi-2223/Ag PIT tapes. The axial strain was applied to the tapes by the U-shape sample holder. Two kinds of Bi-2223/Ag tapes with different Ag sheath are used to know the effect of sheath alloying for the tensile strain. The influence of thermal cycling between room temperature and 77 K on critical current are examined. Critical current is drastically decreased for Ag/alloy and Ag/alloy/alloy sheathed tapes at tensile strain above 0.22％ and 0.3％, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1994년도 춘계학술대회 논문집
• /
• pp.120-122
• /
• 1994

We examined the magnetic properties as a function of annealing temperature of the as-quenched $Fe_{87}Zr_{7}B_{5}Ag_{1}$ amorphous alloy. The values of $H_{c}$=30m0e, $B_{a}$=0.44T and ${\mu}$i=146000 at $300^{\circ}C$ annealing treatment are obtained. The excel lent soft magnetic properties seem to result from the annihilation of quenching-Induced internal stress by the heat treatment and the change of microstructure due to the different relaxation behavior owing to adding insoluble element such as Ag. Therefore, the $Fe_{87}Zr_{7}B_{5}Ag_{1}$ amorphous alloy is quite promising for practical use as a core material in various transformers of high transformers of high frequency.

• 한국자동차공학회논문집
• /
• 제21권1호
• /
• pp.145-153
• /
• 2013

In this study, shear punch-creep (SP-Creep) at Sn-4Ag/Cu pad the joint was tested by using environment-friendly Pb-free solder alloy Sn-4Ag of electronic components. Pb eutectic alloy (Sn-37Pb) joints limited to environmental issues with reflow time (10sec, 30sec, 100sec, 300sec) according to two types of solder alloy joints are compared and evaluated by creep strain rate, rupture time and IMC (Intermetallic Compound) behavior. As the results, reflow time increases with increasing thickness of IMC can be seen at overall 100sec later in case of two solder joints on the IMC thickness of Sn-4Ag solder joints thicker than Sn-37Pb solder joints. In addition, when considering creep evaluation factors, lead-free solder alloy Sn-4Ag has excellent creep resistance more than Pb eutectic alloy. For this reason, the two solder joints, such as in the IMC (Cu6Sn5) was formed. However, the creep resistance of Sn-4Ag solder joints was largely increased in the precipitation strengthening effect of dispersed Ag3Sn with interface more than Sn-37Pb solder joints.

• 한국진공학회지
• /
• 제9권3호
• /
• pp.233-236
• /
• 2000

TFT-LCD(thin film transistor-liquid crystal display) 패널의 데이터 배선 재료로 사용하기 위하여 AlW(3 wt%)의 Al합금 박막을 dc 마그네트론 스퍼터링 방법으로 유리 기판에 증착하여 열처리전과 열처리 후의 박막 특성을 조사하였다. 또한 TFT-LCD의 식각 공정상에서 발생할 수 있는 chemical attack에 대한 저항성을 확인하기 위하여 순환전압전류법(cyclic voltammetry)을 사용하여 Ag/AgCl 전극에 대한 ITO와 AlW alloy의 전극 전위를 측정하였다. 증착된 박막을 $350^{\circ}C$에서 20분간 열처리하였을 때 AlW 박막은 비저항이 감소하였고 약 $11\;{\mu\Omega}cm$의 다소 높은 비저항 특성을 보였다. 주사전자현미경(SEM)과 원자힘현미경(AFM)으로 표면을 분석한 결과 좋은 힐록방지 특성을 보임을 알 수 있었다. 순환전압전류법을 사용하여 측정한 Ag/AgCl 에 대한 ITO의 전극 전위은 약 -1.8V이었고, AlW alloy의 전위 전극은 W의 wt.%가 3% 이상이었을 때, ITO의 전극 전위보다 작게 나타났다. 따라서 측정된 특성 값을 볼 때 AlW(over 3 wt.%) 박막은 data bus line으로 사용할 수 있는 것으로 나타났다.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2000년도 High Temperature Superconductivity Vol.X
• /
• pp.276-279
• /
• 2000

When high temperature superconducting tapes is fabricated using the PIT (Powder In Tube) method, the length of HTS tapes is increased more than 500 ${\sim}$ 1,000 times of initial powder packed billet. On mechanical processing, heterogeneous properties between the ceramic superconducting core and Ag/Ag alloy sheath occur the non-uniformity deformation as like sausaging that deteriorate the critical current properties of HTS tapes. In this study, we investigated the workability of Bi-2223/Ag/Ag alloy sheath tapes fabricated by the PIT method involving a number of different mechanical processes, multi drawing and rolling. In order to obtain the high critical current density and high uniformity of Bi-2223/Ag sheath tapes, the influences of powder packing density, drawing die angle and rolling parameters were studied. We found that the roll diameter is an important variable in the rolling process, as critical current of tapes rolled using 250 mm rolls was higher than that using 150 mm rolls.

• 한국세라믹학회지
• /
• 제33권9호
• /
• pp.1045-1049
• /
• 1996

Pressureless-sintered polycrystalline alumina and carbon steel were joined with Ag-33.5Cu-1.5Ti (wt%) brazing alloy. SEM observation revealed that two reaction layers with different thicknesses were continuously formed between the alumina and the brazing alloy. A thick layer formed on the brazing alloy side was identified as Ti3(Cu0.93Al0.07)3O phase with diamond cubic structure. Another thin layer adjacent to the alumina was revealed as $\delta$-TiO phase of which the crystal structure was HCP with a lattice parameter of a0=0.419 nm and c0=0.284 nm. It was confirmed using XPS analysis that $\delta$-TiO was formed directly by a redox reaction of alumina with titanium ir, molten brazing alloy.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.451-455
• /
• 1995

The composition and thickness dependence and the ferromagnetic under- and overlayer effect on the magnetoresistance ratio and saturation field of the Co-Ag nano-granular films were investigated. The maximum magnetoresistance (23% at R.T.) in the as-deposited state was obtained in the $3000{\AA}$ $Co_{30} Ag_{70}$ bare alloy film. As the thickness of the alloy films decreased below $500{\AA}$, the MR ratio decreased because of the resistivity increase and the non-uniform film formation. We showed that the ferromagnetic over- and underlayer could reduce the saturation field of the nano-granular films via exchange coupling effect. The magnetoresistance and the saturation field of the $100{\AA}$ alloy film were 3.65 % and 2.85 kOe respectively and those of the under- and overlayered alloy films with $200{\AA}$ Fe were 3.3 % and 1.23 kOe respectively.