• Journal of the Korean Applied Science and Technology
• /
• v.17 no.4
• /
• pp.233-239
• /
• 2000

To prepare an environmental friendly high-solid coatings an acrylic resin containing 80% of solid content was synthesized by addition polymerization of caprolactone acrylate, n-butyl acrylate, ethyl methacrylate, and 2-hydroxyethyl methacrylate. The conversion was $78{\sim}93%$ and the prepared resin's physical properties are as follows: viscosity, $212{\sim}3424cps: $M_{n}$ $1740{\sim}2400$. There was a trend that viscosity and molecular weight of the resin increased with Tg, but no direct proportionality was observed.

• 대한치과보철학회:학술대회논문집
• /
• 2001.11a
• /
• pp.69-69
• /
• 2001

• Journal of the Korean Applied Science and Technology
• /
• v.31 no.3
• /
• pp.500-508
• /
• 2014

For this research, synthesis acrylic resin by ethyl acrylate monomer(EAM) and prepared samples which set by difference amount of monoammonium phosphate solution in waterborne acrylic resin. Use these resins, analyzed mechanical properties and thermal stability by films and leather surface coated. The test of DSC experiment sample WAC-APS3 was $410^{\circ}C$ Tm values which means the highest content of monoammonium phosphate had highest thermal stability in acrylic resin. According to measure data for solvent resistance, all samples showed good property. As known in the results, increase of ammonium phosphate constant did not influence to big change of resin properties. In abrasion test WAC-APS3 was good abrasion properties(68.729 mg.loss). Test of tensile strength, as increase as monoammonium phosphate resin analyzed low properties $1.505kgf/mm^2$ to $1.275kgf/mm^2$. In elongation case, same as strength test result 425 % to 384 % by increase to monoammonium phosphate amount in acrylic resin.

• Journal of Technologic Dentistry
• /
• v.5 no.1
• /
• pp.19-26
• /
• 1983

I got a conclusion as a result of that in case of constructing a full denture using acrylic resin teeth, porcelain teeth, and forming posterior occlusal surface of the artificial teeth by Type III Gold and Nickel crome alloy thus construdting a full denture and therefore comparing the above case with abrasion of Natural teeth. The result were as follows : 1. The abrasion of Natural teeth and the abrasion of full denture constructed by Type III gold has a close resemblance. 2. The one that has the hightest degree of abrasion is full denture that's using, with acrylic resin teeth, maxillary and mandibular And the lowest abrasion is natural teeth-natural teeth. 3. In case of single denture, that's opposing to natural teeth, the one that has the hightest degree of abrasion is a full denture that's using Acrylic resin teeth and the lowest abrasion is a full denture that's forming occlusal surface by Type III gold. 4. The single denture, which is opposing to type III gold teeth, was abraded above everything by full denture which is constructed by porcelain teeth. 5. In the same teeth, the abrasion of mandibular teeth was greater than that of mandibular teeth was greater than that of maxillary teeth. 6. The abrasion degree of Acrylic resin teeth has no direct mutual connection with material hardness which is opposing to.

• The Journal of Korean Academy of Prosthodontics
• /
• v.27 no.1
• /
• pp.193-211
• /
• 1989

The purpose of this study was to investigate the effect of secondary heat treatment on dimensional changes of acrylic resin partial denture base. For this study, 6 specimens were made: 2 groups of 2 specimens, each was treated with $125^{\circ}C$ dry heat and glycerine heat for 3 minutes, and the others were prepared for control group. The change of the internal diameter of specimens were measured after 3 hrs, 1 day, 1 week, 2 weeks, 4 weeks by three-dimensional space analyzer. The results were as follows : 1. All of the acrylic resin denture bases showed tissue ward thermal contraction. 2. Thermal contraction of the mesial area reinforced with metal framework was lesser than that of the distal area without metal framework. 3. Thermal contraction of the lingual flange reinforced with metal framework occured more slowly than that of the buccal flange without the metal framework. 4. The thermal contraction of dry heat treated acrylic resin base, compared to glycerine heat group, was moderately greater and occurred acutely.

• Journal of Technologic Dentistry
• /
• v.13 no.1
• /
• pp.27-31
• /
• 1991

The purpose of this study was to evaluate the effect of curing time and curing temperature on the hear - Curing of acrylic resin using ring furnace. Specimens were fabricated from 2 kinds(Laboron, Bertex) heat-cured resin. Total 200 samples were divided into 4 groups(70$^{\circ}C$, 100$^{\circ}C$, 13$^{\circ}C$, 150$^{\circ}C$) and each group was divided into 5 small groups(30 min., 45min., 60min., 75min., 90min.). A microscope(Olympus Coll Co. Japan) was used to examine a randomly selected central zone, midzone and surface for each complete specimen. The results of the experiment were as follows : 1. To obtain non-polymerzation, cure the resin for 30 minutes at 70$^{\circ}C$ and 100$^{\circ}C$ in a ring furnace. 2. To obtain with porosity, cure the resin for 45 minutes, 60 minutes and 75 mintes at 70$^{\circ}C$ and for 90 minutes at 150$^{\circ}C$ in ring furnace. Porosity appears in Laboron for 30 minutes, 45 minutes at 150$^{\circ}C$ in a ring furnace. 3. Every other specimens connot get a sight of special problem with makes eye in the made surface.

• Journal of Technologic Dentistry
• /
• v.12 no.1
• /
• pp.103-106
• /
• 1990

The purpose of this study was to determine if homogeneity of the resin associated with benchcuring could be obtained in the curing unit as the water increased from room temperature to curing temperature. The results of the experiment were as follows : 1. Long periods of bench-curing are not necessary. 2. Bench-curing can take place in the water bath of the curing unit. When this procedure is used, the water should be far enough below the temerature at which active polymerization of the resin proceeds to allow the bench-curing to occur.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.3
• /
• pp.477-486
• /
• 2008

Acrylic resin is widely used in dental practice. However, the residual monomer in acrylic resin could act as a negative biocompatability on human body. The aim of this study was to evaluate the amount of the monomer elution from polymerized orthodontic acrylic resin. Orthodontic acrylic resin was used in the study. The curing condition of the resin was controlled by temperature, pressure, aquatic and atmospheric environment. The duration and amount of monomer elution and timedependent plot was recorded by high performance liquid chromatography. The result showed that the only monomer eluted from the resin was methyl methacrylic acid. And the amount of the monomer elution has diminished considerably by time progress especially within 24 hours. Furthermore, elution of the residual monomer was significantly lower in group of pressure, moisture and elevated temperature than control (p<.05). According to this study, it was thought that the elution of residual monomer might be influenced by curing environment.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.2
• /
• pp.476-487
• /
• 2021

To prepare acrylic resin coatings containing 70% of solids, we used n-butyl methacrylate(BMA), methyl methacrylate(MMA), 2-hydroxyethyl methacrylate(2-HEMA), and acetoacetoxyethyl acrylate(AAEA), caprolactone acrylate(CLA) as raw materials, the glass transition temperature(T_g) of acrylic copolymer was adjusted around 50 ℃. The viscosity and molecular weight of the acrylic resins was increased with increasing OH values. Di-tert-amyl peroxide was found to be the suitable initiator to get high-solids acrylic resins. The optimum reaction conditions found in the study are 5 wt% of initiator, 4 wt% of chain transfer agent, 4 hrs of dropping time, and 140 ℃ of reaction temperature. The structure of the synthesized resins were characterized by FT-IR and ¹H-NMR spectroscopy. Number average molecular weight of 1900~2600 and molecular wight distribution of 1.4~2.1 were obtained. Crosslinked acrylic urethane clear coatings were obtained by curing reaction between the synthesized acrylic resins and hexamethylene diisocyanate trimer(Desmodur N-3300), the equivalent ratio of NCO/OH was 1.2/1.0. The physical properties from the following studies were carried out: viscosity(Zahn cup #2), adhesion, drying time, pot-life, pensil hardness, and 60° specular gloss. Various properties of the acrylic urethane clear coatings were also evaluated on the coating specimens. Adhesion property to a substrate, drying time, pot-life, pencil hardness, and 60° specular gloss of prepared paint showed quite good properties. Futhermore, prepared paint containing 10% of CLA showed quite good properties for adhesion, low viscosity and high hardness.

• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.1
• /
• pp.1-14
• /
• 1997

The purpose of this study was to investigate the physical effect of tissue conditioner on polymerized acrylic resins. Surface hardness and transverse strength were measured for evaluating physical effect of tissue conditioner on polymerized acrylic resins. 1) To measured surface hardness, the resin specimens($65{\times}10{\times}10mm$ size) of each resin material were made, applied tissue conditioner, stored in $37^{\circ}C$ water for 1 week, and changed tissue conditioner every week for 3 weeks. Surface hardness was measured every week with Shore hardness tester for 4 weeks. 2) To measured transverse strength, the resin specimens($65{\times}10{\times}3mm$ size & $65{\times}10{\times}1.5mm$) of each resin material were made. The specimens were divided into four groups, and measured by universial testing machine. Group I(control group) : The resin specimens were stored in $37^{\circ}C$ water for 5 weeks. Group II : The resin specimens were stored in $37^{\circ}C$ water for 5 weeks, and relined in 1.5mm thickness with same resin. Group III : The resin specimens were stored in $37^{\circ}C$ water for 1 week, applied tissue conditioner in 1.5mm thickness, stored in $37^{\circ}C$ water for 1 week, changed tissue conditioner and water every week for 3 weeks, removed tissue conditioner, reduced 1.5mm thickness from resin surface which was applied tissue conditioner, and relined in 1.5mm thickness with same resin. The following conclusions were obtained : 1. Surface hardness changes of Vertex RS and Vertex SC were not different significantly(p>0.01). 2. Surface hardness of K-33, Tokuso rebase, and Kooliner were decreased(p<0.01). 3. With the exception of Kooliner, transverse strength of all resin materials between control group and groups which applied with tissue conditioner were not different significantly(p>0.01).