• Journal of the Korean institute of surface engineering
• /
• v.49 no.4
• /
• pp.382-388
• /
• 2016

NiO nanoparticles were synthesized by hydrothermal method for the application to ethanol gas sensor. They were composited with $Co_3O_4$ nanoparticles to improve the sensitivity to ethanol gas. Scanning electron microscopy revealed that the synthesized NiO nanoparticles were plate-shaped with the approximate size and thickness of 60 - 120 nm and 20 nm, respectively. On the other hand, $Co_3O_4$ nanoparticles mixed with NiO was observed to be spherical with the size range of 30 - 50 nm. The sensitivities of NiO sensors composited with $Co_3O_4$ nanoparticles at an optimal ratio of 8 : 2 were enhanced to approximately 1.44 - 1.79 times as high as those of as-synthesized NiO sensors for the ethanol concentration of 10 - 200 ppm at $200^{\circ}C$. The mechanism of the improved ethanol gas sensing of the NiO sensors composited with $Co_3O_4$ nanoparticles was discussed.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.29A no.11
• /
• pp.84-90
• /
• 1992

The dependence of electrical characteristics of RuO$_2$-based thick film resistors on the RuO$_2$ contents, glass composition variation and the firing temperatures was measured. The sheet resistance of resistors decreased as the contents of RuO$_2$ increased and at firing temperatures higher than C, the sheet resistance increased as the firing temperature increased. In case of using lead borosilicate glass-containing $Bi_{2}O_{3}$, the sheet resistance decreased as the contents of $Bi_{2}O_{3}$ increased. TCR changes from negative to positive values as RuO$_2$ contents increased and from positive to negative values as the firing temperature increased. TCR increased to positive values as $Bi_{2}O_{3}$ increased in the glass.

• Corrosion Science and Technology
• /
• v.21 no.6
• /
• pp.445-453
• /
• 2022

SiO_x was prepared from a mixture of Si and SiO₂ via high-energy ball milling as a negative electrode material for Li-ion batteries. The molar ratio of Si to SiO₂ as precursors and the milling time were varied to identify the synthetic condition that could exhibit desirable anode performances. With an appropriate milling time, the material showed a unique microstructure in which amorphous Si nanoparticles were intimately embedded within the SiO₂ matrix. The interface between the Si and SiO₂ was composed of silicon suboxides with Si oxidation states from 0 to +4 as proven by X-ray photoelectron spectroscopy and electrochemical analysis. With the addition of a conductive carbon (Super P carbon black) as a coating material, the SiO_x/C manifested superior specific capacity to a commercial SiO_x/C composite without compromising its cycle-life performance. The simple mechanochemical method described in this study will shed light on cost-effective synthesis of high-capacity silicon oxides as promising anode materials.

• Korean Journal of Materials Research
• /
• v.26 no.6
• /
• pp.347-352
• /
• 2016

ZnO with wurtzite structure has a wide band gap of 3.37 eV. Because ZnO has a direct band gap and a large exciton binding energy, it has higher optical efficiency and thermal stability than the GaN material of blue light emitting devices. To fabricate ZnO devices with optical and thermal advantages, n-type and p-type doping are needed. Many research groups have devoted themselves to fabricating stable p-type ZnO. In this study, $As^+$ ion was implanted using an ion implanter to fabricate p-type ZnO. After the ion implant, rapid thermal annealing (RTA) was conducted to activate the arsenic dopants. First, the structural and optical properties of the ZnO thin films were investigated for as-grown, as-implanted, and annealed ZnO using FE-SEM, XRD, and PL, respectively. Then, the structural, optical, and electrical properties of the ZnO thin films, depending on the As ion dose variation and the RTA temperatures, were analyzed using the same methods. In our experiment, p-type ZnO thin films with a hole concentration of $1.263{\times}10^{18}cm^{-3}$ were obtained when the dose of $5{\times}10^{14}$ As $ions/cm^2$ was implanted and the RTA was conducted at $850^{\circ}C$ for 1 min.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.382-385
• /
• 2003

Chemical mechanical polishing(CMP) is an essential process in the production of copper-based chips. On this work, the stability of Hydrogen Peroxide($H_2O_2$) as oxidizer of Cu CMP slurry has been investigated. $H_2O_2$ is known as the most common oxidizer in Cu CMP slurry. Copper slowly dissolves in $H_2O_2$ solutions and the interaction of $H_2O_2$ with copper surface had been studied in the literature. Because hydrogen peroxide is a weak acid in aqueous solutions, a passivation-type slurry chemistry could be achieved only with pH buffered solution.[1] Moreover, $H_2O_2$ is so unstable that its stabilization is needed using as oxidizer. As adding KOH as pH buffering agent, stability of $H_2O_2$ decreased. However, stability went up with putting in small amount of BTA as film forming agent. There was no difference of $H_2O_2$ stability between KOH and TMAH at same pH. On the other hand, $H_2O_2$ dispersion of TMAH is lower than that of KOH. Furthermore, adding $H_2O_2$ in slurry in advance of bead milling lead to better stability than adding after bead milling. Generally, various solutions of phosphoric acids result in a higher stability. Using Alumina C as abrasive was good at stabilizing for $H_2O_2$; moreover, better stability was gotten by adding $H_3PO_4$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.286-287
• /
• 2006

Barium titanate ($BaTiO_3$) glycolate particles were synthesized at temperature as low as $100^{\circ}C$ through glycothermal reaction by using $Ba(OH)_2{\cdot}8H_2O$ and amorphous titanium hydrous gel as precursors and ethylene glycol as solvent. The particle size and morphology of $BaTiO_3$ glycolate powders can be controlled by varying the reaction conditions such as the reaction temperature and Ba:Ti molar ratio of starting precursors. After glycothermal treatment at $220^{\circ}C$ for 24 h in 1.25:1(Ba:Ti), the average particle size of the $BaTiO_3$ glycolate powder was about 200-400 nm and low agglomeration. $BaTiO_3$ powders were formed by heat-treating the glycolate powder in air at $500-1000^{\circ}C$. As a result, the size of $BaTiO_3$ crystallites changed from around 50-300 nm. It is also demonstrated that the size and shape of $BaTiO_3$ particles investigated as a function of calcination temperature. The $BaTiO_3$ particles obtained from optimum synthesis condition were pressed, sintered and measured for the dielectric property. The $BaTiO_3$ ceramics sintered at $1250^{\circ}C$ for 2 h had 98 % of theoretical density. The ceramics have an average grain size of about $1\;{\mu}m$ and displays the high dielectric constant (~3100) and low dielectric loss (<0.1) at room temperature.

• International Journal of Highway Engineering
• /
• v.19 no.1
• /
• pp.53-62
• /
• 2017

PURPOSES : This research was a fundamental study on the application of an integral $TiO_2$ solution to asphalt concrete pavement. The integral $TiO_2$ solution was produced in pilot production equipment; application of the integral $TiO_2$ solution to asphalt pavement was conducted to examine the pollution-reducing capability of photocatalytic compounds such as $TiO_2$. The photocatalytic $TiO_2$ reacted with air pollutants, converting them into small amounts of relatively benign molecules. METHODS : In this study, laboratory experiments were conducted using five various testing methods. Tensile strength ratio (TSR) and British pendulum test (BPT) were conducted in order to evaluate the properties of asphalt pavement subsequent to the integral $TiO_2$ solution coating. In addition, methylene blue testing, a measurement of nitrate on the coated pavement, and nitrogen oxide (NOx) reduction testing were conducted in order to evaluate photocatalytic reaction. Lastly, a UV-A lamp was used as a light source for photocatalytic reactions. RESULTS : Test results indicated no change in the properties of asphalt pavement following the integral $TiO_2$ solution coating. In order to evaluate the performance of asphalt pavement as a function of $TiO_2$, the moisture susceptibility and skid resistance were investigated. The moisture susceptibility and skid resistance satisfied there quirements related to pavement quality and safety specification. Furthermore, the effects of reduction of air pollution were significantly improved as determined via the methylene blue test and NOx reduction test. The $TiO_2$-paved asphalt specimen exhibited approximately 43% reduction of NOx. CONCLUSIONS : This study has suggested that applying $TiO_2$ rarely impacts asphalt pavement performance measures such as moisture susceptibility and skid resistance, and that its application may be a better means of reducing air pollution. Further studies, such as proper $TiO_2$ dosage rates and compatibility with various pavement types, are required to broaden and generalize its application.

• Korean Journal of Materials Research
• /
• v.29 no.11
• /
• pp.690-696
• /
• 2019

Geopolymer is an alumina silicate-based ceramic material that has good heat-resistance and fire-resistance; it can be cured at room temperature, and thus its manufacturing process is simple. Geopolymer can be used as a reinforcement or floor finish for high-speed curing applications. In this manuscript, we investigate a high-speed curing geopolymer achieved by adding calcium to augment the curing rate. Metakaolin is used as the main raw material, and aqueous solutions of KOH and $K_2SiO_3$ are used as the activators. As a result of optimizing the high bending strength as a target factor for geopolymers with $SiO_2/Al_2O_3$ ratio of 4.1 ~ 4.8, the optimum ranges of the active agent are found to be $0.1{\leq}K_2O/SiO_2{\leq}0.4$ and $10{\leq}H_2O/K_2O{\leq}32.5$, and the optimum range of the curing accelerator is found to be $$0.82{\leq_-}Ca(OH)_2/Al_2O_3{\leq_-}2.87$$. The maximum flexural strength is found to be 1.35 MPa at $Ca(OH)_2/Al_2O_3=2.82$, $K_2O/SiO_2=0.3$, and $H_2O/K_2O=11.3$. The physical and thermal properties are analyzed to validate the applicability of these materials as industrial insulating parts or repairing finishing materials in construction.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.335-340
• /
• 1992

Undoped PbTiO3 ceramics was successfully prepared by using sol-gel process, which had not been fabricated due to its microcracks created by anisotropic stress during phase transition from cubic to tetragonal phase. Fabrication of undoped PbTiO3 ceramics via sol-gel processing was very much affected by the PbO content of the samples as well as PbO vapor from sintering atmosphere. Excess PbO was found to promote rapid grain growth in PbTiO3 ceramics. After sintering at 1100$^{\circ}C$ average grain size of PbTiO3 ceramics with excess PbO was about 8 times greater than that of stoichiometric composition, which may be due to PbO liquid phase from excess PbO.

• Journal of the Korean Ceramic Society
• /
• v.28 no.5
• /
• pp.406-414
• /
• 1991

The composition of base glass was selected as MgO 8, Al2O3 24, SiO2 68 in weight percent. TiO2 and ZrO2 were added to the base glass to investigate their effects as nucleating agents. In the case of ZrO2 addition, the optimum temperature for nucleation, which was related to the precipitation of tetragonal ZrO2, was 80$0^{\circ}C$. The optimum growth condition for the crystal was 87$0^{\circ}C$ for 8 hrs, and the major crystal phases precipitated in the samples were $\beta$-quartz ss. and mullite. The light transmissivity turned out to be around 80 per cent. On the other hand, when the TiO2 was added, it was difficult to determine the nucleating temperature, because the samples turned easily into translucency during the heat treatment. Therefore, it was almost impossible to retain transparency in the samples. The light transmissivity was below 30 per cent.