• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1998.03a
• /
• pp.45-52
• /
• 1998

This study is to investigate the effects of warm deep drawing with aluminum sheets of A1050-H16 and A5052-H32 for improving deep drawability. Experiments for procucing circular cups and square cups were carried out for various working conditions, such as forming temperature and blank shape. The limit drawing ratio(LDR) of 2.63 in warm deep drawing of circular cups in case of A5052-H32 sheet, whereas LDR of A1050-H16 is 2.25, could be obtained and the former was 8 times higher than the value at room temperature. The maximum relative drawing depth for square cups of A5052-H32 material was also about 2 times deeper than the depth drawn at room temperature. The effects of blank shape, and temperature on drawability of aluminum materials as well as thickness distribution of drawn cups were examined and discussed.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.42-42
• /
• 2010

알루미늄 합금은 질량 대비 강도가 우수하고 내식성 및 저온 특성이 양호하여 구조재로서 널리 사용되고 있다. 또한 그 사용 추세가 점점 증가 하고 있으며 알루미늄 합금의 용접을 위해 현재까지 다양한 용접 공정이 적용되었다. 일반적으로 GMAW, GTAW 등의 아크 용접과 박판의 경우 저항 점용접, 그 외의 $CO_2$ laser, Nd:YAG laser와 같은 고밀도 에너지 용접 공정에 의한 연구 결과들이 많이 발표 되었다. 하지만 알루미늄 합금의 특성 상 용접부에 기공과 균열과 같은 결함들이 각 공정에서 많이 발생하며 이러한 결함을 감소시키기 위한 용접기술에 관해 많은 연구가 진행되고 있다. 본 연구에서는 GMAW, Plasma-GMAW 공정을 적용하여 알루미늄 합금의 용접특성을 비교하였다. 알루미늄 합금 Al 5052, Al 6061 4mm 두께 모재에 대해 BOP(Bead On Plate) 용접실험을 실시하였으며 생산성 측면에서 각 공정에 따라 완전 용입 시 최대 용접 속도를 측정하여 비교하였다. 용접 품질 측면에서는 비드 표면 및 단면을 검사하고 인장시험을 수행하였으며, 용접 기공과 균열을 X-ray 촬영을 통해 비교하였다. 또한 고속카메라 촬영을 통해 용접 중 플라즈마로 인한 산화막 제거 효과를 확인하고 각 공정별 용접 시작부의 아크 안정성을 평가하였다. 인장시험 결과 모든 모드에서 모재에서 파단됨을 확인 하였고, Plasma-GMAW 공정의 경우 플라즈마의 예열효과로 인하여 GMAW 보다 완전용입 기준 용접속도가 빨랐으며, 청정작용도 우수한 것으로 확인되었다.

• Journal of the Korean Society of Safety
• /
• v.31 no.3
• /
• pp.1-7
• /
• 2016

In this study, static and fatigue tests on the self-piercing riveted (SPR) joint were conducted using cross-shaped specimens with aluminum alloy (Al-5052) sheets. Mixed mode loading was achieved by changing the loading angles of 0, 45, and 90 degrees using a special fixture to evaluate the static and fatigue strengths of the SPR joints under mixed mode loading conditions. Simulations of the specimens at three loading angles were carried out using the finite element code ABAQUS. The fatigue specimens failed in an interfacial mode where a crack initiated at the upper sheet and propagated along the longitudinal direction and finally fractured Maximum principal stress, von-Mises effective stress failed to correlate the fatigue lifetimes at three loading angles. However, the equivalent stress intensity factor was found to be appropriate to correlate the fatigue lifetimes at three loading angles.

• Transactions of Materials Processing
• /
• v.8 no.3
• /
• pp.252-261
• /
• 1999

The 3-dimensional finite element program is developed to analyze the non-isothermal forming processes of aluminum-alloy sheet metals. Bishop's method is introduced to solve the heat balance and force equilibrium equations. Also, Barlat's non-quadratic anisotropic yield function depicts the planar anisotropy of the aluminum-alloy sheet. To find an appropriate constitutive equation, four different forms are reviewed. For the verification of the reliability of the developed program, the computational try-outs of the non-isothermal cylindrical cupping processes of AL5052-H32 and Al1050-H16 are carried out. As results, the constitutive equation relating to strain and strain-rate, in which the constants are represented by the 5th-degree polynomials of temperature, is in good agreement with measurement. The computational try-outs can predict optimal forming conditions in non-isothermal forming processes.

• Transactions of Materials Processing
• /
• v.21 no.1
• /
• pp.5-12
• /
• 2012

The weight of the bipolar plate is one of the crucial aspects of improving power density in PEMFC stacks. Aluminum alloys have good mechanical properties such as density, electrical resistivity, and thermal conductivity. Furthermore, using aluminum in a bipolar plate instead of graphite reduces the bipolar plate cost and makes machining easier. Therefore in this study, an aluminum alloy was selected as the appropriate material for a bipolar plate. Results from feasibility experiments with the aim of developing fuel cells consisting of Al bipolar plates with multiple channels are presented. Dynamic loading was applied and the formability of micro channels was estimated as a function of punch pressure and die radius. Sheets of Al5052 with a thickness of 0.3mm were used. For a die radius of 0.1mm the formability was optimized with a sine wave dynamic load of 90kN at maximum pressure and 5 cycles of a sine wave punch travel. The experimental results demonstrate the feasibility of the proposed manufacturing technique for producing bipolar plates.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.80-84
• /
• 2011

The weight reduction of the transportations has become an important technical subject Al and Al alloys, especially Al 5052 alloys have been being applied as door materials for automobile. One of the most widely known car weight-reduction methods is to use light and corrosion-resistant aluminum alloys. However, because of high electrical and thermal conductivity and a low melting point, it is difficult to obtain good weld quality when working with the aluminum alloys. Also, Pulse MIG welding is the typical aluminum welding process, but it is difficult to apply to the thin plate, because of melt-through and humping-bead. In order to enhance weld quality, welding parameters should be considered in optimizing the welding process. In this experiment, Al 5052 sheets were used as specimens, and these materials were welded by adopting new Cold Metal Transfer (CMT) pulse process. The proper welding conditions such as welding current, welding speed, torch angle $50^{\circ}$ and gap 0~1mm are determined by tensile test and bead shape. Through this study, range of welding current are confirmed from 100A to 120A. And, the range of welding speed is confirmed from 1.2m/min to 1.5m/min.

• International Journal of Precision Engineering and Manufacturing
• /
• v.4 no.4
• /
• pp.45-50
• /
• 2003

In order to investigate the effect of surface treatment (Anodizing) and rolling on AI 5083-H131 alloy, under hyper velocity impact, a ballistic testing was conducted. Ballistic resistance of these materials was measured by a protection ballistic limit ($V_{50}$)' a statistical velocity with 50% probability of penetration. Perforation behavior and ballistic tolerance, described by penetration modes, were respectfully observed, by $V_{50}$ test and Projectile Through Plates (PTP) test at velocities greater than $V_{50}$. PTP tests were conducted with 0$^{\circ}$ obliquity at room temperature using 5.56mm ball projectiles. $V_{50}$ tests with 0$^{\circ}$ obliquity were also done with projectiles that were able to achieve near or complete penetration during PTP tests. Resistance to penetration, and penetration modes of Al 5052-H34 alloy were compared to those of Al 5083-H 131 alloy.

• Corrosion Science and Technology
• /
• v.10 no.4
• /
• pp.136-142
• /
• 2011

Al alloys have been used widely for commercial and military ships in most ocean countries since mid-1950s, and the value as light metal with high mechanical strength has been proven. As the safety and fuel efficiency of Al ships have improved, she can carry more freight, sail faster and travel longer distances. Furthermore, in the shipbuilding industry, Al alloys are applied as structural materials for ships to various areas including the deck of luxurious cruises, battleships and leisure ships. In addition, Al alloys are being spotlighted as environmental-friendly material as they can be recycled even after end of lifespan. However, Al alloys for ships must be carefully selected after considering corrosion resistance, endurance, strength, and weldability in sea water environment. Al alloys to satisfy these conditions are used widely include 5000 series Al-Mg alloy and 6000 series Al-Mg-Si alloy. Thus, this study selected and evaluated the cavitation characteristics of the 5000 series Al alloys that are used in hulls that directly contact seawater and the 6000 Al alloys that are used in the upper structures of ships. Results of cavitation test with time, weightloss and cavitation rate of 5456-H116 showed the smallest damage among 5052-O, 5456-H116 and 6061-T6.

• Korean Journal of Metals and Materials
• /
• v.49 no.11
• /
• pp.893-899
• /
• 2011

Fabrication of a complex aluminum alloy by the ARB process using dissimilar aluminum alloys has been carried out. Two-layer stack ARB was performed for up to six cycles at ambient temperature without a lubricant according to the conventional procedure. Dissimilar aluminum sheets of AA1050 and AA5052 with thickness of 1 mm were degreased and wire-brushed for the ARB process. The sheets were then stacked together and rolled to 50% reduction such that the thickness became 1 mm again. The sheet was then cut into two pieces of identical length and the same procedure was repeated for up to six cycles. A sound complex aluminum alloy sheet was successfully fabricated by the ARB process. The tensile strength increased as the number of ARB cycles was increased, reaching 298 MPa after 5 cycles, which is about 2.2 times that of the initial material. The average grain size was $24{\mu}m$ after 1 cycle, and became $1.8{\mu}m$ after 6 cycles.

• Journal of Welding and Joining
• /
• v.27 no.3
• /
• pp.73-79
• /
• 2009

This present paper investigated the mechanical properties and the microstructures of each penetration shapes classifying the conduction shape area and the keyhole shape area about electron beam welded 120(T)mm thick plated aluminum 5052 112H. As a result the penetration depth is increased linearly according to the output power, but the aspect ratio is decreased after the regular output power. In the conduction shape area, the Heat affected zone is observed relatively wider than the keyhole shape area. In the material front surface of the welded specimen, the width is decreased but the width in the material rear surface is increased. After the measuring the Micro Vikers Hardness, it showed almost similar hardness range in all parts, and after testing the tensile strength, the ultimate tensile strength is similar to the ultimate tensile strength of the base material in all the specimens, also the fracture point was generated in the base materials of all the samples. In the result of the impact test, impact absorbed energy of the Keyhole shape area is turned up very high, and also shown up the effect about four times of fracture toughness comparing the base material. In the last result of observing the fractographs, typical ductile fraction is shown in each weld metal, and in the basic material, the dimple fraction is shown. The weld metals are shown that there are no other developments of any new chemical compound during the fastness melting and solidification.