• Journal of dental hygiene science
• /
• v.14 no.1
• /
• pp.29-34
• /
• 2014

The purpose of this study was to evaluate the influence of low temperature degradation (LTD) on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP). The push-shear bond test method was used to investigate the core-veneer bonding strength of industrially manufactured Y-TZP core ceramic and manufacturer recommended veneering ceramic. Four groups from ceramic-zirconia specimens (n=28; n=7 per group) were assigned into four experimental aging conditions, namely storage in an autoclave at $134^{\circ}C$ for 0, 3, 5, 10 hours. Bonding strength was obtained using a universal testing machine with crosshead speed 0.5 mm/min. Data were statistically analyzed using one-way ANOVA and Tukey's test (${\alpha}=0.05$). In bonding strength test, the group which was treated with LTD showed lower bonding strength than no treated group. The ceramic-zirconia bonding strength was affected by LTD (p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in LTD with treated Y-TZP groups.

• The Journal of Advanced Prosthodontics
• /
• v.13 no.5
• /
• pp.269-280
• /
• 2021

PURPOSE. The objective of this study was to evaluate the effect of thickness reduction and fatigue on the failure load of monolithic zirconia crowns. MATERIALS AND METHODS. 140 CAD-CAM fabricated crowns (3Y-TZP, inCorisTZI, Dentsply-Sirona) with different ceramic thicknesses (2.0, 1.5, 1.0, 0.8, 0.5 mm, respectively, named G2, G1.5, G1, G0.8, and G0.5) were investigated. Dies of a mandibular first molar were made of composite resin. The zirconia crowns were luted with a resin composite cement (RelyX Unicem 2 Automix, 3M ESPE). Half of the specimens (n = 14 per group) were mouth-motion-fatigued (1.2 million cycles, 1.6 Hz, 200 N/ 5 - 55℃, groups named G2-F, G1.5-F, G1-F, G0.8-F, and G0.5-F). Single-load to failure was performed using a universal testing-machine. Fracture modes were analyzed. Data were statistically analyzed using a Weibull 2-parameter distribution (90% CI) to determine the characteristic strength and Weibull modulus differences among the groups. RESULTS. Three crowns (21%) of G0.8 and five crowns (36%) of G0.5 showed cracks after fatigue. Characteristic strength was the highest for G2, followed by G1.5. Intermediate values were observed for G1 and G1-F, followed by significantly lower values for G0.8, G0.8-F, and G0.5, and the lowest for G0.5-F. Weibull modulus was the lowest for G0.8, intermediate for G0.8-F and G0.5, and significantly higher for the remaining groups. Fatigue only affected G0.5-F. CONCLUSION. Reduced crown thickness lead to reduced characteristic strength, even under failure loads that exceed physiological chewing forces. Fatigue significantly reduced the failure load of 0.5 mm monolithic 3Y-TZP crowns.

• The Journal of the Korea Contents Association
• /
• v.18 no.10
• /
• pp.361-367
• /
• 2018

The purpose of this study was to evaluate the influence of hydrofluoric acid etching treatment on the bonding strength of yttria-stabilized tetragonal zirconia polycrystal(Y-TZP). Four groups of zirconia-resin cement specimens were prepared; 1) ZGS group (zirconia, no treatment), 2) ZGSH group (zirconia, hydrofluoric acid etching treatment) 3) H-ZGS group (Hybrid zirconia, no treatment) 4) H-ZGSH group (Hybrid zirconia, hydrofluoric acid etching treatment). The shear bond strength between zirconia and porcelain was measured using a Instron Universal Testing Machine(Model DBBP-500, Instron Corporation, Kyonggi, Korea). Data were statistically analyzed using independent t-test and two-way ANOVA(${\alpha}=0.05$). The ceramic-resin cement bonding strength was affected by hydrofluoric acid etching treatment(p<0.05). Digital microscope examination of the fracture surface showed mixed failures with adhesive and cohesive types in hydrofluoric acid etching treatment with treated zirconia and hybrid zirconia groups.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.1
• /
• pp.1-8
• /
• 2020

PURPOSE. To investigate the influence of crown material (lithium-disilicate, 3Y-TZP zirconia) and abutment type (rigid implant, resin tooth with artificial periodontium) on wear performance of their antagonist teeth and adjacent teeth. MATERIALS AND METHODS. A mandibular left first molar (#36) with adjacent human teeth (mandibular left second premolar: #35, mandibular left second molar: #37) and antagonistic human teeth (maxillary left second premolar: #25, maxillary left first molar: #26, maxillary left second molar: #27) was prepared simulating a section of the jaw. Samples were made with extracted human molars (Reference), crowned implants (Implant), or crowned resin tooth analogues (Tooth). Crowns (tooth #36; n = 16/material) were milled from lithium-disilicate (Li, IPS e.max CAD) or 3Y-TZP zirconia (Zr, IPS e.max ZirCAD, both Ivoclar Vivadent). Thermal cycling and mechanical loading (TCML) in the chewing simulator were applied simulating 15 years of clinical service. Wear traces were analyzed (frequency [n], depth [㎛]) and evaluated using scanning electron pictures. Wear results were compared by one-way-ANOVA and post-hoc-Bonferroni (α = 0.05). RESULTS. After TCML, no visible wear traces were found on Zr. Li showed more wear traces (n = 30-31) than the reference (n = 21). Antagonistic teeth #26 showed more wear traces in contact to both ceramics (n = 27-29) than to the reference (n = 21). Strong wear traces (> 350 ㎛) on antagonists and their adjacent teeth were found only in crowned groups. Abutment type influenced number and depth of wear facets on the antagonistic and adjacent teeth. CONCLUSION. The clinically relevant model with human antagonistic and adjacent teeth allowed for a limited comparison of the wear situation. The total number of wear traces and strong wear on crowns, antagonistic and adjacent teeth were influenced by crown material.

• Journal of Technologic Dentistry
• /
• v.34 no.2
• /
• pp.83-93
• /
• 2012

Purpose: The objective of this study is to find out physical properties and the flexural strength changed by the low temperature degradation of the block which is needed to make bio-prosthetic dentistry which is better than feldspar affiliated ceramic made by building up ceramic powder and also to apply this to the clinical use of zirconia monolithic all-ceramic crown. Methods: Flexural strength of each sample was evaluated before and after the Low Temperature Degradation, and physical properties of the Tetra Zirconia Block containing 3mol % was evaluated as well. The average and standard deviation of each experimental group were came out of the evaluation. Statistical package for social science 18.0 was used for statistics. Results: The average density of the monolithic all-ceramic crown was $6.0280{\pm}0.0147g/cm$, the relative density was 99.01 %. When the sample was sintered at $1480^{\circ}C$ the diameter of average particle was $396.62{\pm}33.71nm$. All the samples had no monolithic peak after XRD evaluation but only had tetragonal peak. There were statistically significant differences in the result of flexural strength of the samples evaluated after and before the low temperature degradation, the flexural strength before the low temperature degradation was $1747.40{\ss}{\acute{A}}$, at the temperature of $130^{\circ}C$ the flexural strength after the low temperature degradation was 1063.99MPa (p<0.001). There was statistically significant difference in the result of strength of 1020.07MPa after the low temperature degradation at the temperature of $200^{\circ}C$ (p<0.001). Conclusion: The block which was made for this evaluation possesses such an excellent strength among dental restorative materials that it is thought to have no problems to use for tetragonal zirconia polycrystal.

• The Journal of Korean Academy of Prosthodontics
• /
• v.48 no.4
• /
• pp.251-258
• /
• 2010

Purpose: To evaluate the effect of surface conditioning on the shear bond strength of zirconium-oxide ceramic to 4 luting agents. Materials and methods: A total of 120 diskshaped zirconium-oxide ceramic blocks (3Y-TZP, Kyoritsu, Japan) were treated as follows: (1) Sandblasting with $110\;{\mu}m$ aluminum-oxide ($Al_2O_3$) particles; (2) tribochemical silica coating (Rocatec) using $110\;{\mu}m$ $Al_2O_3$ particles modified by silica; (3) no treatment. Then zirconium-oxide ceramic blocks bonded with 4 luting cements (RelyX luting (3M ESPE), Maxcem (Kerr), Nexus3 (Kerr), Rely X Unicem (3M ESPE)). Each group was tested in shear bond strengths by UTM. A 1-way analysis of variance and 2-way analysis of variance was used to analyze the data ($\alpha$ = .05). Results: RelyX unicem in combination tribochemical silica-coating produced a highest bond strength (P < .05). Air abrasion group and Rocatec treatment groups resulted in significantly higher than no conditioning group (P < .05). RelyX Luting groups showed lower bond strength than other groups. There were significant differences among groups (P < .05). Conclusion: Within the limitation of this study, RelyX Unicem cement provided the highest bond strength and Rocatec treatment enhanced the bond strength.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.29 no.1
• /
• pp.69-79
• /
• 2013

The aim of this study was to evaluate the effect of surface conditioning on the shear bond strength of zirconium-oxide ceramic to resin cement. A total of 120 disk-shaped zirconium-oxide ceramic blocks(3-TZP, Kyoritsu, Tokyo, Japan) were treated as follows: (1) no treatment; (2) sandblasting with 110 ${\mu}m$ aluminum-oxide(Al2O3); (3) particles tribochemical silica coating(RocatecTM, 3M ESPE). Then zirconium-oxide ceramic blocks were divided into six groups(10 for each group) and bonded with resin cement(Rely X U-200, 3M ESPE). (1) No treatment / No treatment (2) No treatment / Sandblasting with 110 ${\mu}m$ aluminum-oxide particles (3) No treatment / Silica coating (4) Sandblasting with 110 ${\mu}m$ aluminum-oxide particles / Sandblasting with 110 ${\mu}m$ aluminum-oxide particles (5) Sandblasting with 110 ${\mu}m$ aluminum-oxide particles / Silica coating (6) Silica coating / Silica coating. Each group was tested in shear bond strengths by UTM. Data analysis included one-way analysis of variance(ANOVA) and the Tukey Honestly Significant Difference test (P=0.05). Group that bonded two silica coated specimen showed a highest bond strength(P<0.05). Two silica coated surface conditioning group and air-abrasion and silica coated surface conditioning group showed significantly difference with other groups(P<0.05). Other groups had no significantly difference each other. Within the limitation of this study, Surface conditioning with Rocatec treatment to each side of specimen provided the highest bond strength.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.654-660
• /
• 1991

Stabilized Zirconia (3 mol % Yttria, 3Y-TZP) was joined with intermetallic compound NiTi which has similar thermal expansion coefficient. The optimum bonding condition was determined by the Taguchi Method. Under the optimum bonding condition, the 4-point bending strength was as high as 400 MPa. bonding interfaces were examined by optical microscope, SEM, and TEM; reaction products were identified by XRD and TEM, The relationship between products and strength was examined.

• The Journal of Korean Academy of Prosthodontics
• /
• v.61 no.3
• /
• pp.179-188
• /
• 2023

Purpose. The purpose of this study was to evaluate the effect of surface treatments on the shear bond strength of two types of zirconia (3-TZP and 5Y-PSZ) with resin cement. Materials and methods. Two different types of zirconia specimens with a fully sintered size of 14.0×14.0×2.0 mm³ were prepared, polished with 400, 600, and 800 grit silicon carbide paper, and buried in epoxy resin. They were classified into four groups each control, sandblasting, primer, and sandblasting & primer. Cylindrical resin adhered to the surface-treated zirconia with resin cement. It was stored in distilled water (37℃) for 24 hours, and a shear bond strength test was performed. The normality of the experimental group was confirmed with the Kolmogorov-Smirnov & Shapiro-Wilk test. The interaction and statistical difference were analyzed using a two-way ANOVA. A post-hoc analysis was performed using Dunnett T3. Results. As a result of two-way ANOVA, there was no significant difference in shear bonding strength between zirconia types (P > .05), but there was a significant correlation in the sandblasting, primer, and alumina sandblasting & primer group (P < .05). Dunnett T3 post-test showed that, regardless of the type of zirconia, shear bonding strength was sandblasting & primer > Primer > sandblasting > control group (P < .05). Conclusion. There was no difference in shear bond strength between the types of zirconia. The highest shear bond strength was shown when the mechanical and chemical treatments of the zirconia surface was performed simultaneously.

• Journal of dental hygiene science
• /
• v.12 no.2
• /
• pp.123-129
• /
• 2012

The aim of study was to compare the color parameters and mean color difference of porcelain specimens by different veneering technique in order to examine the effect of veneering technique on esthetics of yttria-stabilized tetragonal zirconia polycrystalline(Y-TZP) all ceramic restoration. Three groups of square-shaped core ceramic specimens(14mm in diameter and 0.3, 0.5, 0.7 mm) and two groups of veneering ceramic specimen were prepared for analysis. Color parameter($L^*,a^*,b^*$) and color difference of zirconia core squares and core-veneer specimens were measured with ShadeEye $NCC^{(R)}$ spectrophotometer, respectively. Mean color difference(${\Delta}E^*$)were calculated using color difference formula. Two-way analysis of variance(ANOVA) combined with a Tukey multiple-range test were used to analysis the data(${\alpha}=0.05$). ${\Delta}E^*$ values were not significantly affected by core thickness and veneering porcelain(p=0.083). The color differences(${\Delta}E^*$) of core-veneer specimens with 0.5, 0.7 mm-A1,A2,A3.5 shade were mostly below 3.7 which was within the clinically acceptable range, while color differences between 0.3 mm-A1,A2 showed more than 3.7. All-ceramic system has color characteristics that clinicians have to consider when selecting materials. Also, manufacturers of different porcelain systems must make every effort to achieve color reproducibility.