• The Journal of Advanced Prosthodontics
• /
• v.7 no.5
• /
• pp.386-391
• /
• 2015

PURPOSE. The purpose of this preliminary study was to investigate the effects of adding 4,4'-bis(N,N-diethylamino) benzophenone (DEABP) as a co-initiator to a binary photoinitiating system (camphorquinone-amine) to analyze on the degree of conversion (DC) of a light-cured resin for dental 3D printing. MATERIALS AND METHODS. Cylindrical specimens (N=60, n=30 per group, ${\phi}5mm{\times}1mm$) were fabricated using bisphenol A glycerolate dimethacrylate (BisGMA) both with and without DEABP. The freshly mixed resins were exposed to light in a custom-made closed chamber with nine light-emitting diode lamps (wavelength: 405 nm; power: $840mW/cm^2$) for polymerization at each incidence of light-irradiation at 10, 30, 60, 180, and 300 seconds, while five specimens at a time were evaluated at each given irradiation point. Fourier-transform infrared (FTIR) spectroscopy was used to measure the DC values of the resins. Two-way analysis of variance and the Duncan post hoc test were used to analyze statistically significant differences between the groups and given times (${\alpha}$=.05). RESULTS. In the DEABP-containing resin, the DC values were significantly higher at all points in time (P<.001), and also the initial polymerization velocity was faster than in the DEABP-free resin. CONCLUSION. The addition of DEABP significantly enhanced the DC values and, thus, could potentially become an efficient photoinitiator when combined with a camphorquinone-amine system and may be utilized as a more advanced photopolymerization system for dental 3D printing.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.332-332
• /
• 2010

We have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films withouWe have successfully demonstrated the inkjet printing method to create $Al_2O_3$ films without a high temperature sintering process. In order to remove the coffee ring effect in the ink drop, we have introduced a co-solvent system in order to create Marangoni flow in the ink drop, which leads to the dense packing of ceramic powders on the substrate during inkjet process. The packing density of the Inkjet-printed $Al_2O_3$ films is around 60% (max. 70%) which is very high compared to the value obtained from the same material films by other conventional methods such as film casting, dip coating process, etc. The voids inside the films (which are around 40% of the entire film volume) are filled with the polymer resin (Cyanate ester) by the infiltration process. This resin infiltration is also implemented by the inkjet printing process right after the Ah03 film ink-jetting process. The microstructures of the printed $Al_2O_3$ films are investigated by Scanning Electron Microscope (SEM) to understand the degree of packing density in the printed films. The inkjet-printed $Al_2O_3$ films have been characterized to investigate its thickness and roughness. Quality factor of the printed $Al_2O_3$ film is also measured to be over 300 at 1MHz.

• The Journal of Advanced Prosthodontics
• /
• v.15 no.4
• /
• pp.189-201
• /
• 2023

PURPOSE. The aim of this study was to investigate the mechanical properties of three-dimensional (3D) printed denture base resin incorporating microcapsules containing plant essential oils. MATERIALS AND METHODS. Denture base specimens containing up to 3% w/v essential oil microcapsule powders (MCPs), i.e., eucalyptus, geranium, lavender, menthol, and tea tree, in two resins (Detax and NextDent 3D+) were 3D printed using two printers (Asiga and NextDent 5100). The dispersion and interaction of the MCPs in the resin were assessed by SEM while the mechanical properties of the incorporated denture base including flexural strength (MPa), flexural modulus (MPa), Vickers hardness (VHN), and surface roughness (Ra) were also subsequently evaluated. Statistical analysis of any differences in mean values was determined using a two-way ANOVA with Tukey's post hoc testing (α = .05). RESULTS. The spherical shape of the MCPs was maintained during the mixing and polymerization/printing process. However, the Detax-Asiga group showed significant agglomeration of the MCPs even at the lowest MCP concentration levels (0.5% w/v). Overall, as the microcapsule concentration increased, the mean flexural strength decreased, though the menthol MCP groups remained compliant with the ISO standard. The flexural modulus and harness remained relatively unchanged, and the flexural modulus complied with the ISO standard regardless of the MCP concentration. Surface roughness increased with the addition of the MCPs but also remained below that required for clinical acceptance. CONCLUSION. Incorporation of microencapsulated plant essential oils into 3D printed denture base resin was successfully achieved. While incorporation negatively influenced flexural strength and surface roughness, little effect on flexural modulus and Vickers hardness was demonstrated.

• Journal of Technologic Dentistry
• /
• v.46 no.1
• /
• pp.8-14
• /
• 2024

Purpose: This study compares the deformation of traditional resin dentures to resin dentures printed with digital light processing (DLP). Methods: Eleven edentulous research models were developed. Ten of them were made with traditional resin dentures. The remaining one was prepared for scanning and 3D (three-dimensional) printing. Ten traditional resin dentures were made, with the remaining artificial teeth created using 3D software and a DLP printer. Traditional resin dentures, 3D printed resin denture artificial teeth, and a denture base with artificial teeth were all cleaned simultaneously in an ultrasonic cleaner for 3 minutes. Three groups were assigned four artificial tooth measurement points, which were then measured with digital calipers. The measured data was analyzed using descriptive statistics. The significance test was conducted using a nonparametric test Kruskal-Wallis test due to the small number of specimens (α=0.05). Results: The traditional resin dentures had the lowest strain rate at -0.04%, while the group that manufactured only artificial teeth had the highest strain rate at -0.09%. However, no statistically significant difference was observed between the 3 groups (p>0.05). Conclusion: During ultraviolet-type ultrasonic cleaning, traditional resin dentures (TD group) and denture base with artificial teeth made of DLP (DD group) demonstrated stable durability, whereas the artificial teeth made of DLP (AD group) with only artificial teeth did not show a good deformation rate.

• Journal of Technologic Dentistry
• /
• v.42 no.3
• /
• pp.208-212
• /
• 2020

Purpose: This study aimed to analyze the shrinkage and expansion strain of ultraviolet (UV)-cured resin according to the wavelength of the light source and compare the shrinkage and expansion. Methods: We prepared the mold with according to the ISO 4049 specimen. The size of the circle in the mold was prepared with a height of 6.02 mm and a diameter of 4 mm. UV-curable resin for three-dimensional (3D) printing was injected into the circular mold. The control group was irradiated with a wavelength of 400~405 nm using UV-curing equipment (400 group), and the experimental group was irradiated with a wavelength of 460~465 nm (460 group). Both groups were produced ten specimens. The produced specimen was first measured with a digital micrometer. After the first measurement, the specimen was immersed in a constant temperature water bath for 15 days, after which the second measurement was performed, and the third measurement was taken after 30 days. The measured values were analyzed using the independent sample t-test (α=0.05). Results: In the non-immersion water tank, the contraction was 0.9% in the 400 group and 1.3% in the 460 group. In the constant temperature bath, the expansion was high at -0.4% in the 400 group for 15 days, and the smallest expansion was -0.03% for the 400 group for 30 days. There were significant differences between the two groups (p<0.05). Conclusion: The 400 group had a lower UV resin specimen strain than the 460 group. Therefore, it is recommended to use the wavelength required by the UV-curing resin.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.16 no.2
• /
• pp.94-101
• /
• 2017

Recently, the small quantity batch production method has come into the spotlight as there are more plastic processing methods. At the same time, the 3D printer market has become globally widespread due to expired 3D printer patents. In particular, the FDM method is widely used for cheap products and materials. However, the FDM scheme is not as good as the injection molding method for quality and strength. This study investigated the effect of the internal filling and strength according to layer thickness to search for the optimum printing of the factors (infill and layer thickness) that determine the strength of the model.

• Design & Manufacturing
• /
• v.13 no.2
• /
• pp.17-21
• /
• 2019

In this study, selective laser sintered 3D printing mold core and metal core were used to investigate the difference of the thickness shrinkage from the gate of the injection molded part at a constant interval. SLS 3D printing mold core was made of nylon-based PA2200 powder and the metal core was manufactured by conventional machining method. As the PA2200 powder material has low strength, thermal conductivity and high specific heat characteristics compared with metal, molding conditions were set with the consideration of molten temperature and injection pressure. Crystalline resin(PP) and amorphous resin(PS) with low melting temperature and viscosity were selected for the injection molding experiment. Cooling time for processing condition was selected by checking the temperature change of the cores with a cavity temperature sensor. The cooling time of the 3D printing core was required a longer time than that of the metal core. The thickness shrinkage of the molded part compared to the core depth was measured from the gate by a constant interval. It was shown that the thickness shrinkage of the 3D printing core was 2.02 ~ 4.34% larger than that of metal core. In additions, in the case of metal core, thickness shrinkage was increased with distance from the gate, on the contrary, in the case of polymer core showed reversed aspect.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2007.11a
• /
• pp.525-526
• /
• 2007

• Korean Chemical Engineering Research
• /
• v.62 no.1
• /
• pp.105-111
• /
• 2024

The SLA (Stereolithography Apparatus) method is a type of 3D printing technique predicated on the transformation of liquid photocurable resin into a solid form through UV laser exposure, and its application is increasing in various fields. In this study, we conducted research to enhance the hydrophobicity and transparency of SLA 3D printing surfaces for microfluidic system production. The enhancement of surface hydrophobicity in SLA outputs was attainable through the application of hydrophobic coating methods, but the coating durability under different conditions varied depending on the type of hydrophobic coating. Additionally, to simultaneously achieve the required transparency and hydrophobic properties for the fabrication of microfluidic systems, we applied hydrophobic coatings to the proposed transparency enhancement method from prior research and compared the changes in contact angles. Teflon coating was proposed as a suitable hydrophobic coating method for the fabrication of microfluidic systems, given its excellent transparency and high coating durability in various environmental conditions, in comparison to titanium dioxide coating. Finally, we produced an Electrophoresis of Charged Droplet (ECD) chip, one of the digital microfluidics systems, using SLA 3D printing with the proposed Teflon coating method (Fluoropel 800). Droplet manipulation was successfully demonstrated with the fabricated chip, confirming the potential application of SLA 3D printing technology in the production of microfluidic systems.

• Journal of Technologic Dentistry
• /
• v.42 no.1
• /
• pp.35-41
• /
• 2020

Purpose: The purpose of this study was to evaluate the accuracy of the DLP 3D printer by conducting 3-dimensional assesment of resin provisional restorations. Methods: The first premolar of the maxillary was prepared for the abutment. The abutment was scanned by using a scanner. The provisional restoration was designed by using CAD software. A total of 16 resin provisional restorations were produced using ZD200 and Veltz DLP 3D printer. Scanning was done of resin provisional restorations and 3-dimensional measurement was conducted for accuracy. The mean (SD) of RMS was reported for each group. Independent t-test was used to assess the statistical significance of the results. All analyses were done using SPSS 22.0. Results: The mean ± SD of RMS value for the accuracy of the resin provisional restorations that was fabricated by using ZD200 and Veltz DLP 3D printer were 50.85.±4.64㎛ and 70.33±6.31㎛. Independent t-test showed significant differences between groups(p<0.001). Conclusion: The resin provisional restorations made with DLP 3D printers showed clinically acceptable accuracy.