In this study, an automated jack-up system, applicable to various fields, was employed for 3D concrete printing and developed as a simultaneous liftable 3D concrete printing system. This developed printing system enables safe and precise jack-up by monitoring the measured jack-up distance using Pearson correlation coefficient analysis and a hydraulic system with interquartile range analysis in real-time during 3D concrete printing operations. It is possible to secure the quality of 3D concrete printing structures, which is essential for expanding the application of 3D concrete printing to construct larger structures. Specimens were printed using both conventional 3D concrete printing and simultaneous liftable 3D concrete printing to evaluate the system performance. The printed specimens were investigated using a 3D scanner. The layer-wise diameter and angle of intersection of the scanned specimens were measured, and an analysis was performed to verify the advantages of the simultaneous liftable 3D concrete printing.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.10
• /
• pp.386-392
• /
• 2020

The self-weight of the 3D printing concrete increases with increasing printing height. Therefore, the lower layer must be hardened within a suitable time to secure continuous printing performance. In particular, the hardening speed of concrete is slow in the winter season when the temperature was low. Hence, the early strength of 3D printing concrete requires improvement. In domestic and international literature, cases of increasing the early strength of concrete using inorganic chemical additives, such as amine-based, nitrate-based, sodium-based, and calcium-based, have been reported. In this study, early strength improvement-type additive samples (amine-based, nitrate-based, sodium-based) were prepared, and their performance was evaluated. When using a nitrate-based additive, the early strength was increased significantly in a 10 ℃ environment. In addition, it was possible to secure a higher early strength than the existing 3D printing concrete mixed at 20 ℃.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.4
• /
• pp.131-136
• /
• 2019

Buildability of fresh concrete, a key element of Concrete 3D printing, is the ability to build filaments at a desirable height without excessive deformation or collapse. Buildability is closely related to yield stress, and the higher the yield stress, the better. Also, the shear stress of fresh concrete increases as it hardens over the time after extruded, and consequently the buildability increases. Therefore, in concrete 3D printing, proper time gaps between printed layers (Printing Time Gap, PTG) are required to ensure the buildability of fresh concrete. As the PTG increases, the buildability increases; however, an excessive PTG reduces the bond performance between the printed layers, and the extrudability can be lowered as the printing time increases. In this research, therefore, 3D printing experiments were conducted with the variable of PTG to examine the buildability of 100 MPa-high strength concrete. In addition, a pseudo-layer loading method was applied to simulate the buildability test for 3D concrete printing and its applicability was examined.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.35 no.4
• /
• pp.227-233
• /
• 2022

The 3D-printing technique is used for manufacturing objects by adding multiple layers, and it is relatively easy to manufacture objects with complex shapes. The 3D concrete printing technique, which incorporates 3D printing into the construction industry, does not use a formwork when placing concrete, and it requires less workload and labor, so economical construction is possible. However, 3D-printed concrete is expected to have a lower strength than that of molded concrete. In this study, the properties of 3D-printed concrete were analyzed. To fabricate the 3D-printed concrete samples, the extrusion path and shape of the samples were designed with Ultimaker Cura. Based on this, G-codes were generated to control the 3D printer. The optimal concrete mixing proportion was selected considering such factors as extrudability and buildability. Molded samples with the same dimensions were also fabricated for comparative analysis. The properties of each sample were measured through a three-point bending test and uniaxial compression test, and a comparative analysis was performed.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.2
• /
• pp.267-272
• /
• 2021

In this study, the output results of 3D printed exterior materials for application to buildings of various shapes are output tests using test specimens, in which 3D printing concrete is cast in a mold and accelerating agents are used to ensure stackability. The unit weight and strength characteristics of the body were analyzed. Compared to the unit weight of concrete placed in the mold, the unit weight of 3D printing concrete using accelerating agents tends to decrease by approximately 3.5% to 5.0%, and the compressive strength is the compressive strength of the concrete placed in the mold. In comparison, the compression strength of the output by 3D printing tended to decrease by approximately 36% to 46%. In the flexural strength, the compressive strength of the output through 3D printing decreased by approximately 36% to 46% compared to the compressive strength of concrete placed in the mold. The impact on the strength characteristics of 3D printed concrete using accelerating agents tended to decrease by approximately 2.0 to 5.8%. Therefore, 3D printing output accelerating agents can be used.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.20 no.12
• /
• pp.37-43
• /
• 2019

Since 3D printed concrete can be constructed without formwork, it is easy to construct an atypical structure, and the construction time and labor cost can be reduced. However, since the construction is exposed to the outside, shrinkage cracking due to moisture loss inside and outside the concrete occurs. Therefore, in order to improve the durability of the 3D printed concrete, a shrinkage reduction plan of the 3D printed concrete is required. In this study, glycol-based and alcohol-based shrinkage reducing agents were fabricated and evaluated for their performance. The shrinkage reducing agent samples showing excellent performance were selected and applied to 3D printed concrete. As a result, the compressive strength was increased by more than 10% and the shrinkage was reduced by more than 36% when using a shrinkage reducing agent. It is expected that the production of high quality 3D printed concrete will be possible because it is possible to increase the compressive strength and reduce the amount of dry shrinkage by applying a shrinkage reducing agent for 3D printed concrete.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.375-382
• /
• 2019

In this study, an experimental study on the buildability of the structure using the developed printing materials and equipment was performed. Experimental variables included the moving speed of nozzles(=80 and 100mm/s), the revolutions per minute (RPM) of screw in discharge buckets, and the aspect ratio(=1.67 and 5.00) reflecting wall length of the structures. Buildability of the 3D printed concrete structures was analyzed based on the maximum decomposition layer and collapse patterns of the structures according to the experimental variables. The nozzle movement speed of 80mm/s and the aspect ratio of 1.67 were favorable for 3D printing in this study. The collapse process of structure due to uneven layer decomposition was also analyzed through the relative displacement measurement of the lower part of the structure during printing.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.28 no.1
• /
• pp.24-31
• /
• 2024

Mortar has been applied in most previous studies on 3D concrete printing. In such cases, however, the economic efficient cannot help decreasing due to higher binder contents and larger amount of fine aggregates. In order to enhance the applicability of 3D printing technology to construction industry, therefore, 3D concrete printing technology utilizing coarse aggregates needs to be developed further. This study aims at proposing the mix design process of concrete containing coarse aggregates for 3D printing. Based on extensive literature review and experimental studies, the mix proportion suitable for 3D printing has been derived, and the extrudability of concrete with coarse aggregates has been verified through 3D printing tests. The primary variable of the extrudability tests was the contents of viscosity modifying agent (VMA), and the extrudability was quantitatively evaluated by measuring dimensions, distribution of aggregates, and surface quality of 3D-printed filaments. The test results showed that the dimensional suitability and surface quality were improved as the VMA contents were larger, and the coarse aggregates were evenly distributed in the section of filament regardless of the VMA contents. Based on the test results, the mix design process for concrete containing coarse aggregates for 3D printing has been proposed.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.6
• /
• pp.199-208
• /
• 2021

The extrudability of 3D printed concrete and its member strength can be highly influenced by water cement ratio (W/C) and printing time gap (PTG). In this study, mold cast specimens and 3D printed specimens were fabricated with variables of W/C ratio and PTG, and their shear bond strength and interlayer surface moisture content were measured and analyzed. The test results showed that the shear bond strength is greatly influenced by the amount of interlayer surface moisture. It is thus recommended that proper amount of interlayer surface moisture with respect to PTG needs to be maintained to have a required interlayer shear bond strength. In addition, further research is required to estimate the effect of many environmental factors that can influence the interlayer surface moisture content.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.37 no.1
• /
• pp.33-40
• /
• 2024

The volume of shells, a prominent form of marine waste, is steadily increasing each year. However, a significant portion of these shells is either discarded or left near coastlines, posing environmental and social concerns. Utilizing shells as a substitute for traditional aggregates presents a potential solution, especially considering the diminishing availability of natural aggregates. This approach could effectively reduce transportation logistics costs, thereby promoting resource recycling. In this study, we explore the feasibility of employing wasted shell aggregates in 3D concrete printing technology for marine structures. Despite the advantages, it is observed that 3D printing concrete with wasted shells as aggregates results in lower strength compared to ordinary concrete, attributed to pores at the interface of shells and cement paste. Microstructure characterization becomes essential for evaluating mechanical properties. We conduct an analysis of the mechanical properties and microstructure of 3D printing concrete specimens incorporating wasted shells. Additionally, a mix design is proposed, taking into account flowability, extrudability, and buildability. To assess mechanical properties, compression and bonding strength specimens are fabricated using a 3D printer, and subsequent strength tests are conducted. Microstructure characteristics are analyzed through scanning electron microscope tests, providing high-resolution images. A histogram-based segmentation method is applied to segment pores, and porosity is compared based on the type of wasted shell. Pore characteristics are quantified using a probability function, establishing a correlation between the mechanical properties and microstructure characteristics of the specimens according to the type of wasted shell.