• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.296-303
• /
• 1998

The purpose of this study was to assess the effects of cavity designs on the marginal leakage of class 5 glass ionomer restorations. The five cavity designs were as follows ; notch shape(A group), notch shape with groove(B group), combined lesion(C group), combined lesion with groove and deep chamfer margin(D group) and combined lesion with groove and shoulder(E group), and each design had 10 cavities. After the cavities were restored with GIC, they were immersed in 0.5% basic fuchsin solution for 6 hours. The specimens were washed thoroughly and sectioned longitudinally in a buccolingual direction through the center of the restorations. The degree of marginal leakage was measured as the extent of dye penetration under the stereoscope. The results of this study were as follows 1. The enamel margins of all groups showed lesser leakage than dentin/cementum margins(p<0.05). 2. The combined lesion(C group) showed more leakage than notch shape(A group), but there was no siginificant difference(p>0.05). 3. In the notch shape, there was no influence on the marginal leakage by the groove preparation. 4. In the combined lesion, marginal leakage was decreased by the groove preparation and marginal modification.

• Restorative Dentistry and Endodontics
• /
• 제31권4호
• /
• pp.300-311
• /
• 2006

본 연구의 목적은 복합레진을 이용한 비우식성 치경부 5급 병소 수복에 있어서, 3가지 다른 접착제를, 유지구를 부여한 치아와 부여하지 않은 치아에 적용하였을 때의 임상적인 효능의 차이를 비교하기 위함이다. 총 150개의 치아를 각각 25개씩 6개의 군으로 나누었다. A군 : Scotchbond Multi-Purpose (SBMP, 3M ESPE, St. Paul, MN, USA, 4세대 접착제)를 사용하고 유지구를 부여하지 않음. B군 : SBMP 를 사용하고 유지구를 부여. C군 : BC Plus (Vericom Co., Anyang, Gyeonggido, Korea, 5 세대 접착제)를 사용하고 유지구를 부여하지 않음. D군 : BC Plus를 사용하고 유지구를 부여. E군 : Adper Prompt (3M ESPE, Seefeld, Germany, 6 세대 접착제)를 사용하고 유지구를 부여하지 않음. F군 : Adper Prompt를 사용하고 유지구를 부여. 모든 치아는 복합레진인 Denfil (Vericom Co., Anyang, Gyeonggido, Korea) 을 이용하여 충전하였다. 수복 직후와 수복 6 개월 후에 modified USPHS (United States Public Health Service) criteria에 따라 수복물을 임상적으로 평가하였다. 추가적으로 임상사진을 촬영하였으며, 에폭시 레진을 이용하여 복제한 후 주사전자현미경을 이용하여 이를 관찰하였다. 6개월 후 관찰 결과, alpha rating의 수가 각 실험군마다 동일하지는 않았지만, 통계적으로는 3가지의 접착제간에 유의할만한 차이는 없었고, 기계적인 유지구를 부여한 군과 부여하지 않은 군 간에도 유의할만한 차이는 없었다 (p < 0.05). 그러나 6개월의 관찰 기간은 일반적으로 기대되는 레진의 수명보다 짧기 때문에, 각 실험군 간의 차이를 알아보기 위해서는 추후 더 오랜 기간의 관찰이 요구 된다.

• Restorative Dentistry and Endodontics
• /
• 제23권1호
• /
• pp.304-315
• /
• 1998

The purpose of this study was to evaluate the microleakage of light cured glass ionomer restorative materials in class 5 cavities. In this in vitro study, class 5 cavities were prepared on buccal and lingual surfaces of forty extracted human premolars and molars on cementum margin. These specimen were randomly divided into four groups of 10 each : Group 1 was Fugi II (control), Group 2 was Fugi II LC, Group 3 was Vitremer, and Group 4 was Dyract. Group 2 was also divided once more into 2 groups of 5 each : Group 2-1 was pretreated with dentin conditioner and Group 2-2 was not. All teeth were restored according to the manufacturer's instructions. After 500 thermocycling between $5^{\circ}C$ and $55^{\circ}C$, the 40 teeth were placed in 2 % Methylene blue dye for 24hr, then rinsed with tab water. The specimen were embedded in clear resin, then sectioned buccolingually through the center of restoration with a low speed diamond saw. The dye penetration on each of the specimen were then observed with a stereomicroscope at 20. The results of the study were statistically analyzed using the Student-Newman-Keuls Methods and the Mann-Whitney Rank Sum Test. Tooth restorative interfaces were evaluated using SEM analysis. Results were as follows, 1. Compared to conventional glass ionomer restoratioqs, all light cured glass ionomer restorations were fairly resistant to microleakage (P<0.05). 2. Groups 3 (Vitremer) and Group 4 (Dyract) were found to be the most resistant, Group 2 (Fugi II LC) fairly resistant, and Group 1 (Fugi II) least resistant to microleakage(P<0.05). 3. No significant differences were found between Group 2-1 and Group 2-2 (P>0.08). 4. With the backscattered SEM analysis, the degrees to which tight bonding occurred were also observed in all the groups except for Group 1. Group 4 showed the highest degree of tight bonding than any other materials used in this study.

• Restorative Dentistry and Endodontics
• /
• 제35권3호
• /
• pp.164-172
• /
• 2010

복합레진 수복시, 일반적으로 연마, 산부식, 수세 및 건조 단계를 거쳐 저점도 레진을 적용하는 재접착 술식을 통해 예상되는 수축간극을 봉쇄한다. 그러나, 이 과정은 재접착제 적용 이전에 물이나 잔사가 간극을 매워버릴 수 있어 그 효과가 의심된다. 본 실험에서는 연마 단계 이전, 즉 복합레진을 중합한 직후에 재접착제를 도포한다면 변연누출을 더 줄일 수 있을 것이라는 가설을 검증하고자 하였다. 실험을 위해 35개의 발거한 대구치에서 협면과 설면에 교합면 변연은 법랑질에, 치은측 변연은 상아질에 위치하는 5급 와동을 형성하였다. 와동은 Z250 (3M ESPE, USA)로 충전하였고, 접착제로는 $Adper^{TM}$ Single Bond 2 (3M ESPE)을 사용하였다. 재접착제로는 Biscover LV (Bisco, USA) 레진 전색제와 ScotchBond Multi-purpose system (3M ESPE)의 접착제, 및 점도가 낮은 실험용 접착제를 연마 전 또는 일련의 연마 및 산부식 후 수복물의 변연에 적용하였다. 2% 메틸렌 블루 용액에 네 시간 동안 침적한 뒤 교합측 및 치은측 변연에서의 색소 침투 깊이를 광학 입체 현미경으로 측정하였다. 재접착제의 점도와 변연미세누출의 상관관계도 평가하였다. 재접착 술식, 재접착제, 및 변연의 위치, 그 각각에서는 통계적으로 유의한 차이를 관찰할 수 없었다. 그러나, 재접착 술식을 시행하지 않은 대조군의 경우에는 세 가지 재접착제를 사용한 재접착군에 비해 치은측 변연에서 미세누출이 통계적으로 유의하게 크게 나타났다(p < 0.05). 대조군과 재접착군의 미세누출의 차이는 교합측 변연에서는 관찰되지 않았다. 연마 및 산부식 후 치은변연에 재접착제를 적용한 경우에서 약한 음의 상관관계(r = -0.326, p = 0.041)를 보인 경우를 제외하고는, 재접착제의 점도와 미세누출은 유의한 상관관계를 보이지 않았다.

• 대한소아치과학회지
• /
• 제26권2호
• /
• pp.365-376
• /
• 1999

수복물의 연마의 중요성에 대하여 많은 연구들이 이루어져 왔으며, 이는 수복물의 금속성질의 개선, 변연적합성의 증가 그리고 치태축적의 감소 등을 이유로 시행된다. 그러나 불행하게도 수복물에 대한 연마시 열의 발생으로 인하여 치수부위에 손상을 초래하므로 열의 발생을 최소화하려는 노력이 뒤따라야 할 것이다. 이에 본 연구에서는 수복물의 연마시 회전속도의 차이, 냉각제의 적용 유무, 여러 종류의 수복물의 차이, 간헐적인 연마와 연속적인 연마의 차이 그리고 잔존 상아질의 두께의 정도에 따른 치수내부에서의 열의 변화를 알아보기 위하여 발거된 구치에 5급 와동을 형성한 후 복합레진(Z100, 3M co), resin-modified GIC(Dyract, Fuji II LC) 그리고 아말감(Degussa) 등으로 충전하였으며, 다양한 조건에서의 연마를 시행, 치수내부에서의 열의 변화를 측정하여 다음과 같은 결과를 얻었다. 1. Amalgam을 건조한 상태에서 연마시 다른 재료에 비해 가장 큰 치수내 온도 상승을 보였다(P<0.05). 그러나, Z100, Dyract Fuji II LC 간에는 간헐적 수복물 연마와 연속적인 수복물 연마 모두 어떤 경우든 유의차가 없었다(P>0.05). 2. 같은 조건으로 연마를 시행했을 때, 간헐적인 연마보다 연속적인 연마를 한 경우가 치수내 온도가 더 크게 상승하였다(P<0.01). 3. 아말감과 Dyract 에 있어서는 잔존 상아질의 차이에 따른 치수내 온도변화에 유의한 차이를 보였으나(P<0.01), Fuji II LC에 있어서는 유의성이 없었다(P>0.05). 4. 냉각제의 유무에는 관계없이 어떤 경우든 시간에 따른 온도 상승을 보였다. 그러나, 냉각제를 사용한 경우가 냉각제를 사용하지 않은 경우에 비해 온도 상승값이 훨씬 작았다(P<0.01).

• 구강회복응용과학지
• /
• 제21권1호
• /
• pp.69-81
• /
• 2005

The objective of this study was to evaluate the toothbrush abrasion characteristics of class V restorations. Thirty extracted human premolars, which were collected from oral surgery clinics were used. We mounted five teeth in a metal ring mold of 50 mm in diameter and 15 mm in height using chemically cured acrylic resin. Class V cavities were prepared in lingual cervical root surfaces and restored using one of following restorative materials : Dentin Conditioner/Fuji II LC (Group FL), All Bond II/Z-250 (Group ZT), One-up Bond F/Palfigue Estelite (Group PE), F2000 Primer/Adhesive (Group FT), and Prime & Bond 2.1/Dyract AP (Group DR). They were stored under distilled water at $37^{\circ}C$ for seven days. The toothbrush abrasion test was conducted using a wear testing machine of pin-on disk type under a load of 1.5 N for 100,000 cycles. We have examined the bonded interfaces, the changes of surface roughness and color of abraded surfaces. From this experiment, the following results were obtained. 1. The change of surface roughness showed high degree: RMGIC>compomer>composite resin (p<0.05). 2. Because of the protrusion and missing of filler particles, SEM observation of abraded surfaces of RMGIC and compomers revealed the increase of surface roughness due to the selective removal of matrix resin. 3. The color change by toothbrush abrasion was affected in large part by the change of $L^*$ and $b^*$ of resin composites (p<0.05). 4. The color change by toothbrush abrasion was so small to detect by human eyes. 5. SEM observation of abraded surfaces revealed the interface bonding was the best in the FT group.

• Restorative Dentistry and Endodontics
• /
• 제25권1호
• /
• pp.41-45
• /
• 2000

The purpose of this study was to evaluate the microleakage of compomers. In this in vitro study, class V cavities were prepared on buccal and lingual surfaces of thirty extracted human premolars and molars on cementum cervical margin. The experimental teeth were randomly divided into five groups of six samples (12 surfaces) each, Group 1 : Dyract AP, Group 2 : F2000 compomer(non-etch), Group 3 : F2000 compomer(etch), Group 4 : Elan, Group 5 : Compoglass. The bonding agents and compomer were applied for each group following the manufacturer's instructions. After 500 thermocycling between $5^{\circ}C$ and $55^{\circ}C$, the 30 teeth were placed 1% methylene blue dye for 24 hours then rinsed with tab water. The specimens were embedded in clear resin, then sectioned buccolingually through the center of the restoration with a low speed diamond saw. The dye penetration on each of the specimen was observed with a stereomicroscope. The results of study were statistically analyzed using the Student-Newmann-Kaul' s Test. The results were obtained as follows. 1. All compomer restoration systems did not completely prevent marginal leakage. 2. In enamel margin, F2000 compomer(etch) group showed lower leakage value than other systems. Elan and Compoglass groups showed lower leakage value than Dyract AP and F2000 compomer(non-etch) groups (p<0.05). 3. In cementum margin, F2000 compomer(etch) and F2000 compomer (non-etch) groups showed lower leakage value than other systems. Dyract AP and Elan groups showed lower leakage value than Compoglass group (p<0.05).

• 대한소아치과학회지
• /
• 제31권4호
• /
• pp.636-644
• /
• 2004

최근 자가 부식형 접착 시스템이 개발되어 법랑질 및 상아질에 모두 적용할 수 있고, 임상적 술식을 단순화 시켰다. 이 접착 시스템은 적용하기 용이하고 임상적으로도 법랑질 및 상아질에 높은 결합강도를 보인다고 보고되고 있다. 이 연구는 in vitro 상에서 복합레진 5급 와동의 법랑질 및 상아질 경계에서 전부식 처리를 동반한 one-bottle 접착시스템과 자가 부식형 접착 시스템을 사용하였을 때 미세 누출을 비교하기 위해 시행하였다. 교정적 목적으로 발치된 30개의 소구치를 무작위적으로 3개 군으로 나누었다; 1 군 (Single $Bond^{(R)}$ + Filtek $Z250^{(R)}$), 2 군 (Clearfil SE $Bond^{(R)}$ + Filtek $Z250^{(R)}$), 3 군 (Adper Prompt $L-Pop^{(R)}$ + Filtek $Z250^{(R)}$). 표준화된 5급 와동을 각 소구치 협면, 설면에서 백악-법랑경계에 평행하게 형성하였으며, 와동의 치은측 1/2은 백악법랑경계보다 1mm 치근단으로 연장하였다. 접착 시스템을 제조자의 지시대로 적용한 다음 복합레진을 충전하고 제조자의 지시대로 광중합하였다. 시편을 $37^{\circ}C$ 증류수에 5일 간 보관 후 $5^{\circ}C{\pm}2^{\circ}C$ 와 $55^{\circ}C{\pm}2^{\circ}$에서 1000회 열순환한 다음, 2% methylene blue 용액에 12시간 침잠시켰다. $Isomet^{TM}$ (Buehler Co., Lake Bluff, IL, USA)을 사용하여 치아를 충전물 중앙에서 종절단한 후 입체 현미 경하에서 25배의 배율로 색소 침투도를 평가하였다. 결과는 t-test 와 one-way ANOVA를 이용하여 통계처리 하였다. 결과는 다음과 같았다. ${\cdot}$ 실험에 사용 된 접착 시스템 중에 미세 누출을 완벽하게 방지하는 접착 시스템은 없었다. ${\cdot}$ 상아질 경계에서의 미세 누출이 법랑질 경계에서보다 통계학적으로 유의하게 더 많았다(p<0.0001). ${\cdot}$ 법랑질 경계에서 자가 부식형 접착 시스템은 전부식 처리를 동반한 one-bottle접착 시스템과 통계학적으로 유의한 차이를 보이지 않았다. ${\cdot}$ 상아질 경계에서, 자가 부식형 접착 시스템은 전부식 처리를 동반한 one-bottle 접착 시스템과 통계학적으로 유의한 차이를 보이지 않았다.

• Restorative Dentistry and Endodontics
• /
• 제14권2호
• /
• pp.20-29
• /
• 1989

발거된 소구치 80개의 협, 설면에 교합면쪽의 법량질변연과 치은쪽의 상아질변연을 부여한 제 5급와동을 형성한 후, 각 20개씩 4개의 군으로 나누었다. 각 군별로 초미세입자형 광중합 복합레진과 법랑질접착체인 Durafill$^{(R)}$-Durafill bond$^{(R)}$, Bisfil M$^{(R)}$-Resin bond$^{(R)}$, 초미세입자형 복합레진과 상아질 접착제인 Silux$^{(R)}$-Scotchbond$^{(R)}$ 그리고 글라스 아이오노머 시멘트인 Fuji ionomer$^{(R)}$로 충전하였다. 온도변화는 $40^{\circ}C$와 $60^{\circ}C$의 2% methylene blue 용액에 각각 30초간 침척을 반복시킨 후 $37^{\circ}C$ 동용액에 24시간 경과시켜 법랑질변연부와 상아질변연부에서의 색소침투를 관찰하므로써 변연누출의 정도률 비교한 바 다움과 같은 결과를 얻었다. 1. 법랑질변연부에서 Durafill$^{(R)}$-Durafill bond$^{(R)}$, Bisfil M$^{(R)}$-Resin bond$^{(R)}$ 및 Silux$^{(R)}$-Scotchbond$^{(R)}$군 상호간에는 대차가 없었으나(P>0.05), 3군 공히 Fuji ionomer$^{(R)}$군보다는 변연누출이 적었다(P<0.01). 2. 상아질변연부에서는 Silux$^{(R)}$-Scotchbond$^{(R)}$군과 Fuji ionomer$^{(R)}$군이 각각 Durafill$^{(R)}$-Durafill bond$^{(R)}$군 및 Bisfil M$^{(R)}$-Resin bond$^{(R)}$군에 비해 변연누출이 적었다(P<0.01). 3. 충전한 모든군의 5급 와동에서 법랑질변연부가 상아질변연부보다 변연누출이 적었다(P<0.01).

• Journal of Periodontal and Implant Science
• /
• 제39권1호
• /
• pp.17-26
• /
• 2009

Purpose: The non-carious cervical lesion(NCCL) is a loss of tooth structure at the neck of affected teeth that is unrelated to tooth caries. The reported prevalence of NCCL varies from 5% to 85%. Prevalence and severity of lesions have been found to increase with age. They are becoming more significant as people live longer and become more aware of the importance of oral health. The purposes of this study were first, to examine the periodontal conditions associated with NCCL, and second, to investigate the clinical effects of class V restorations of NCCL on periodontal tissues. Materials and methods: The sample size was 982 teeth of 50 subjects(25 male, mean age $52{\pm}7$) who were seen at the Department of Periodontology, Pusan National University Hospital. At the baseline examination, clinical periodontal parameters were measured. After the initial examination, 24 patients who were absent from hypersensitivity were selected. The teeth with NCCL were randomly divided into the test and control groups. The teeth in the test group were restored with flowable resin; the control teeth were not restored. Six months later, the clinical examinations were repeated. The data were analyzed using the SPSS program. Results: The results were as follows: 1) NCCL occurred on 45.8% of examined teeth. The percentage of affected teeth was higher in maxillary and premolar teeth. 2) The shallow saucer type was the most common. 3) Teeth with NCCL had more gingival recession, lower attachment level, and higher incidences of bleeding on probing(BOP) and plaque than NCCL-free teeth. 4) Six months later, gingival recession, attachment level, the percentages of BOP and plaque in the test group were lower than in the control group(p<0.05). Conclusion: NCCLs were more found in maxillary teeth, especially in premolar teeth. The results suggest that the restoration of NCCL could affect some periodontal parameters favorably.