• The Journal of the Convergence on Culture Technology
• /
• v.9 no.3
• /
• pp.587-592
• /
• 2023

Cobalt oxide (Co₃O₄·CoO) ultra fine particles were synthesized by liquid phase precursor method. cobalt(II) chloride hexahydrate (CoCl₂·6H₂O) was as a starting material. A plant-derived crystalline cellulose was used as impregnating materials. A impregnated precursor was calcined at a temperature of 350 to 900℃ to obtain cobalt oxide particles having a particle size of 1 to 10㎛. The crystallization process and morphology according to the calcination temperature were examined, and the properties of the synthesized powder were evaluated using SEM and XRD. It was confirmed that a crystal phase of Co₃O₄ began to form around 350℃ and crystal growth occurred up to 900℃. At a temperature above 500℃, the Co₃O₄ crystal was changed to another crystal phase CoO.

• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.251-255
• /
• 2001

SrTeO$_3$는 312$^{\circ}C$~485$^{\circ}C$의 제한된 온도범위에서 강유전성이 나타난다고 보고된 바 있다. 본 연구에서는 (Sr$_{1-x}$Pb$_{x}$)TeO$_3$(x=0~0.15) 고용체의 상형성 거동, 미세구조, 유전특성 등을 조사하였다. $700^{\circ}C$에서 하소하였을 때 질소 기체 분위기에서는 SrTeO$_3$상이 합성되었지만 공기 중에서는 더욱 산화된 상인 SrTeO$_4$상이 주된 상으로 존재하였다. (Sr$_{1-x}$Pb$_{x}$)TeO$_3$세라믹스에서 Pb 치환량이 0.15 몰까지 증가함에 따라 최적 소결온도가 80$0^{\circ}C$에서 $650^{\circ}C$로 감소하였고, 입자 크기는 증가하였으며, 유전상수가 13에서 25로 증가하였다. 또한, Pb 치환량이 0.05 이상일 때 강유전상이 안정한 온도 영역이 상온까지 확장되었다.

• Journal of the Korean Ceramic Society
• /
• v.38 no.6
• /
• pp.551-557
• /
• 2001

La$_{0.7}$Ca$_{0.3}$MnO$_3$분말을 용액연소법으로 제조하였으며 분말 특성과 CMR에 응용하기 위해 박막의 전기적, 자기적 특성을 조사하였다. 조성과 구조 특성을 XRD와 SEM으로부터 조사하였으며 분말의 하소온도를 TG 분석으로부터 결정하였다. 또한 소결성은 dilatometer에 의해 조사되었으며 분말 특성은 BET에 의해 조사되었다. 소결성이 우수한 분말을 이용하여 스퍼터 타겟으로 제조하였으며 SiO$_2$/Si 기판 위에 스퍼터링한 후, 온도에 따른 four point probe 측정으로 막의 MR비를 측정하였다. VSM (Vibrating Sample Magnetometer)를 이용하여 증착된 막의 온도에 따른 자화율(Magnetization:M)을 측정하였다. 분말 특성으로는 평균입자 크기가 sub-micron 이하로 초미세하고 49.44$m^2$/g의 비표면적 값을 얻을 수 있었으며 고순도의 perovskite 구조를 갖는 La$_{0.7}$Ca$_{0.3}$MnO$_3$분말을 쉽게 얻을 수 있었다. 온도에 따른 저항값의 변화로부터 96K에서 최고의 MR값을 얻을 수 있었으며, 240K에서 강자성체로 전이되었다.로 전이되었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.6
• /
• pp.244-250
• /
• 2020

β-Tricalcium phosphate (β-TCP, Ca3(PO4)2) is a kind of biodegradable calcium phosphate ceramics with chemical and mineral compositions similar to those of bone. It is a potential candidate for bone repair surgery. To improve the bioactivity and osteoinductivity of β-TCP, various ions doped calcium phosphate have been studied. Among them, Iron is a trace element and its deficiency in the human body causes various problems. In this study, we investigated the effect of Fe ions on the structural variation, degradation behavior of β-TCP. Fe-doped β-TCP powders were synthesized by the coprecipitation method, and the heat treatment temperature was set at 925 and 1100℃. The structural analysis was carried out by Rietveld refinement using the X-ray diffraction results. Fe ions existed in a different state (Fe2+ or Fe3+) with different heat treatment temperatures, and the substitution sites (Ca-(4) and Ca-(5)) also changed with temperature. The degradation rate was fastest at Fe-doped β-TCP with heated at 1100℃. The cell viability behavior was also enhanced with the substitution of Fe ions. Therefore, the substitution of Fe ion has accelerated the degradation of β-TCP and improved the biocompatibility. It could be more utilized in biomedical devices.

• Journal of the Korean Ceramic Society
• /
• v.37 no.10
• /
• pp.938-943
• /
• 2000

TiCl$_4$, 물 및 1-propanol의 혼합용액으로부터 미립 TiO$_2$분말 제조시, 1-propanol과 물의 부피비, 반응온도, 반응유지시간 및 TiCl$_4$mole 농도에 따른 분말 특성 및 결정상 생성에 대해 조사하였다. 반응온도가 3$0^{\circ}C$ 이상일 때 Ti 수화물의 초기 침전이 생성되었고 반응온도가 TiCl$_4$mole 농도가 증가함에 따라 입자크기는 증가하였고 $600^{\circ}C$ 하소시 1-propanol과 물의 부피비가 2보다 크고 반응온도가 7$0^{\circ}C$보다 낮을 때 주결정상은 anatase였다. 입자크기가 미세하고 입자크기 분포가 좁은 범위를 갖는 조건은 1-propanol과 물의 부피비가 2, 반응온도가 7$0^{\circ}C$, TiCl$_4$mole 농도가 0.2 mole/ι일 때였으며, 결정상의 생성은 1-propanol과 물의 부피비가 2, 반응온도가 3$0^{\circ}C$ 이상일 때 anatase에서 rutile로 전이하는 온도가 높아졌다. 이와 같은 반응인자에 따른 효과는 용매의 유전상수, 티타니아의 용해도, 입자의 표면전위 등의 효과와 관계가 있었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.3
• /
• pp.110-114
• /
• 2017

$NiO/NiCo_2O_4$ nanocubes were successfully synthesized via the calcination process of $Ni_3[Co(CN)_6]_2$ PBAs. The prepared monodispersed $Ni_3[Co(CN)_6]_2$ PBAs were aggregated by 'self-assembly' of the nuclei generated during the synthesis reaction. The self-assembly rate of the particles is affected by the temperature and the amount of surfactant SDBS (sodium dodecylbenzenesulfonate). FESEM analysis shows that monodispersed 200 nm PBA nanocubes are obtained at 0.25 g SDBS and $60^{\circ}C$ temperature. Thermal behavior was confirmed by thermogravimetric-differential thermal analysis (TG-DTA) to determine optimal calcination conditions. Then, field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) analyzes were performed to investigate the morphology and crystallinity of the particles precursors and $NiO/NiCo_2O_4$ nanocubes.

• Applied Chemistry for Engineering
• /
• v.26 no.4
• /
• pp.427-431
• /
• 2015

In this study, vanadium dioxide ($VO_2$) powder well known as a thermochromic material was prepared from $V_2O_5$ powder and oxalic acid dihydrate by hydrothermal and calcination process at various conditions. The chemical bonding and crystal structures in addition to thermal property of samples were determined using FE-SEM, XRD, XPS, and DSC. Also, spectroscopic and thermochromic properties of film samples were analyzed by UV-Vis-NIR spectroscopy after the thin film was prepared from the sol dispersed with the size of below 50 nm by the ball-milling of powder sample. With increasing the calcination temperature, the phase transition temperature of samples increased from $40^{\circ}C$ to $70^{\circ}C$ due to the increase of particle size.

• Journal of the Korean Ceramic Society
• /
• v.39 no.11
• /
• pp.1103-1107
• /
• 2002

Biocompatible ${\beta}$-Tricalcium Phosphate(${\beta}$-TCP) powder was successfully synthesized by using a re-cycled eggshell and phosphoric acid. The crystallization behavior of the synthesized powder was dependent on the mixing ratio between the eggshell and phosphoric acid, the starting condition of the eggshell and calcination temperature. The ${\beta}$-TCP was stably synthesized in the 1:1.3~1:1.5 (wt%) mixing ratios of calcined eggshell and phosphoric acid. The synthesis was achieved at about $900{\circ}$ for 1h in an air atmosphere. The crystalline development and microstructure of the synthesized powder were examined by X-ray diffractometer and scanning electron microscopy.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.198-198
• /
• 2006

Tin doped $In_2O_3$ sputtering target is widely used to produce a various kinds of flat panel display because of high transmittance in visible region and high electrical conductivity. In2O3 and SnO2 powders were prepared by a homogeneous precipitation method using metal source, respectively, the calcining and sintering behavior of the indium-tin oxide(In2O3-SnO2) composite powders were studied. The tin oxide(SnO2) dispersion condition in ITO sputtering target was improved by increasing calcining temperature. And the tin oxide dispersion was also improved by reducing the tin oxide contents in the ITO target from 30 to 5wt%. SnO2 dispersion and densification of ITO target is very difficult to control due to sublimation of SnO2 at over 1150C.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.15 no.2
• /
• pp.79-85
• /
• 2005

Commercial hydroxyapatite (HA) powders were calcined at the temperature range of $1000{\sim}1350^{\circ}C$ in air, for 2h, and the calcined powders were immersed in simulated body fluid (SBF) of pH 7.4 at $37^{\circ}C$ for 3 or 7 days. Thermal decomposition and their related dissolution behaviors of hydroxyapatite were investigated by XRD, FT-IR, and TEM. At the temperature of $1200^{\circ}C$, HA gradually releases its $OH^-$ ions and transforms to OHAP((oxyhydroxyapatite, ($Ca_{10}(PO_4)_6O_x(OH)_{2-2x}$)). HA thermally decomposes to ${\alpha}-TCP$ (${\alpha}-tricalcium$ phosphate) and TTCP (tetracalcium phosphate) phase at $1350^{\circ}C$. It was found that the surface dissolution of the hydroxyapatite powders was accelerated by non-stoichiometric composition and decomposed to ${\alpha}-TCP$ and TTCP.