• Journal of the Korean Wood Science and Technology
• /
• v.42 no.6
• /
• pp.700-707
• /
• 2014

The effect of steam and ozone pretreatments on fibrillation efficiency by wet disk-milling was investigated. Hemicellulose (40%) and lignin (42%) of Korean white pine were partially removed by steam and ozone pretreatments, respectively. With increasing wet disk-milling time, the diameter of fibers was significantly decreased and its size distribution became narrow. Especially, the average diameters of lignocellulose nanofibers after steam and ozone pretreatments were 19 nm and 12 nm, respectively. Thus-obtained lignocellulose nanofibers-reinforced polyurethane composite was prepared. Tensile strength and elastic modulus were drastically improved with increasing wet disk-milling time and lignocellulose nanofiber content. Nanocomposite reinforced by lignocellulose nanofibers after two pretreatments showed higher tensile properties, compared to that reinforced by lignocellulose nanofiber without pretreatment, at the similar wet disk-milling time.

• Applied Chemistry for Engineering
• /
• v.20 no.6
• /
• pp.622-627
• /
• 2009

Using an alkali-solution developable photosensitive resin and a carbon black as a conductive filler, photo-patternable pastes for polymer thick film resistor were fabricated and evaluated. A photo solder resist (PSR), which is usually used as protecting layer of printed circuit board (PCB), was used as a photosensitive resin so that ultraviolet exposure and alkali-aqueous solution development of paste were possible. After fabricating the photosensitive polymer resistor paste, the electrical properties of thick film resistors were measured using PCB test boards. Sheet resistance was decreased with increasing amount of carbon black, but the developability was limited in excess loading of carbon black. The sheet resistance was also reduced by re-curing and the change rate was smaller in higher carbon black loading. Moreover, finely patterned meander-type thick film resistors were fabricated using photo-process and large resistance up to several tens of sheet resistance could be obtained in small area by this technique.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.21 no.5
• /
• pp.8-14
• /
• 2013

In this study, we propose the method of optimally selecting material of front pillar (A-pillar) and package tray for minimizing weight while satisfying vehicle requirements on static stiffness and dynamic stiffness. First, we formulate a material selection optimization problem. Next, we establish the CAE procedure of evaluating static stiffness and dynamic stiffness. Then, to enhance the efficiency of design work, we integrate and automate the established CAE procedure using a commercial process integration and design optimization (PIDO) tool, PIAnO. For effective optimization, we adopt the approach of metamodel based approximate optimization. As a sampling method, an orthogonal array (OA) is used for selecting sampling points. The response values are evaluated at the sampling points and then these response values are used to generate a metamodel of each response using the radial basis function regression (RBFr). Using the RBFr models, optimization is carried out an evolutionary algorithm that can handle discrete design variables. Material optimization result reveals that the weight is reduced by 49.8% while satisfying all the design constraints.

• The Journal of the Acoustical Society of Korea
• /
• v.21 no.7
• /
• pp.632-640
• /
• 2002

In this paper, we proposed ACM (Anti-filler confidence measure) to compensate shortcoming of conventional RLJ-CM (RLJ-CM) and NCM (normalized CM), and integrated proposed ACM and conventional NCM using HCM (hybrid CM). Proposed ACM analyzes that FA (false acceptance) happens by the construction method of anti-phone model, and presumed phoneme sequence in actuality using phoneme recognizer to compensate this. We defined this as anti-phone model and used in confidence measure calculation. Analyzing feature of two confidences measure, conventional NCM shows good performance to FR (false rejection) and proposed ACM shows good performance in FA. This shows that feature of each other are complementary. Use these feature, we integrated two confidence measures using weighting vector α And defined this as HCM. In MDR (missed detection rate) 10% neighborhood, HCM is 0.219 FA/KW/HR (false alarm/keyword/hour). This is that Performance improves 22% than used conventional NCM individually.

• Polymer(Korea)
• /
• v.35 no.2
• /
• pp.136-140
• /
• 2011

The plasma resistances of nitrile curable perfluoro elastomer (NT PFE) and peroxide curable PFE (PO PFE) after exposing to $NF_3$ and $O_2$ remote plasmas were investigated by analyzing weight loss and morphology of O-ring made of PFE. The compounds were designed following the typical formulations of O-ring/seal which were applied in semiconductor and LCD production site. They were blended by an open roll mill, and then, O-ring was finally made by hot press molding and oven curing. The weight loss was calculated and morphology was observed for each atmosphere and temperature by a digital weighing machine and SEM. As results, it was confirmed the weight loss and related morphology were meaningfully different according to the cure type of PFE, filler system, and the species of remote plasma.

• Restorative Dentistry and Endodontics
• /
• v.24 no.4
• /
• pp.604-613
• /
• 1999

This study was performed to evaluate the effect of resin and filler type on the fracture toughness of light-activated composites. Experimental composites were prepared using urethane tetramethacrylate(UTMA) and bisphenol glycidylmethacrylate(Bis-GMA) monomers and five different types of silica fillers. Fracture toughness was measured by a single edge V-notched beam(SEVNB) method, which was discussed from ASTM E399-78. Rectangular bars of $2.5{\times}5{\times}26mm$ were prepared with experimental composites and a notch about 2.25mm deep was carved at the center of the long axis of the specimen using a dental diamond disk driven by a dental micro engine. The flexural test was carried out at a crosshead speed of 0.05mm/min and fracture surfaces were observed under scanning electron microscope. The results obtained were summarized as follows: 1. The fracture toughness values of UTMA-based composites were relatively higher than those of Bis-GMA-based composites. 2. The highest fracture toughness value was observed in the UTMA-based composite containing the $1.5{\mu}m$-spherical fillers. 3 Aging in the distilled water at $37^{\circ}C$ for 10 days showed the increase of fracture toughness, which was severer in the Bis-GMA-based composites than those of UTMA-based composites. 4. The AE amplitude occurring during the fracture toughness tests was the highest at the point of macroscopic fracture.

• Composites Research
• /
• v.33 no.3
• /
• pp.91-100
• /
• 2020

Polyphenylene sulfide (PPS) is a semi-crystalline engineering thermoplastic resin that has outstanding thermal stability, mechanical strength, inherent flame retardancy, chemical resistance, and electrical properties. Due to these outstanding properties, it is preferred as a matrix for composite materials. Many studies have been conducted to produce composites with carbon fibers and glass fibers to improve mechanical properties and provide functionality of PPS. In this review paper, we report a brief introduction to the fabrication and applications of PPS composites with carbon nanotubes, graphene, carbon fibers, and glass fibers.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.765-768
• /
• 2008

Silica fume is a very important gradient in UHPC(Ultra High Performance Concrete) and its amount is normally over 25% of cement(wt.%). But we surely need to comprehend the influence of the amount of silica fume on the UHPC. In this paper, it was investigated how the amount of silica fume influence on the properties such as fluidity, compressive strength, elastic modulus, and flexural strength. Furthermore, it was examined the internal micro structure on UHPC through the test of SEM and MIP. In results, If we properly use silica fume in UHPC, fluidity and strength of UHPC was increased. It can be ascertained through the test of MIP that silica fume effectively increased density of UHPC by posolanic reaction and acting as filler. Especially, In case of Cement to silica fume ratio$0.1{\sim}0.25%$, we can be concluded that UHPC has similar to mechanical property.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.470-475
• /
• 2013

In this study, we report that effects of a filler with a high coefficient of thermal expansion on a sealant for high-temperature ($750{\sim}850^{\circ}C$) SOFC. We designed a $SiO_2-BaO-ZnO-B_2O_3-Al_2O_3$ glass system with a softening temperature higher than $750^{\circ}C$. The properties of the glass system show not only low volumetric shrinking but also low swelling. The glass system did not create a crystal phase during along-term heat treatment. We fabricated a seal gasket with 0, 10, 15, and 20 wt% cristobalite added as filler materials with glass powder. The coefficient of thermal expansion of the seal gasket increased according to cristobalite content. During along-term heat treatment, the leak rate decreased by about 5% after a heat treatment in an oxidizing atmosphere at $750^{\circ}C$ for 2000 h, also decreasing by about 6% after a heat treatment in a reducing atmosphere at $750^{\circ}C$ for 1000 h.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.532-532
• /
• 2008

본 연구에서는 Embedded 기판용 폴리머 후막저항의 허용편차 개선을 위하여 새로운 후막 패터닝 기술을 도입하는 연구를 실시하였다. 기존의 Embedded 기판용 폴리머 후막저항은 스크린 인쇄에 의하여 형성됨에 따라 패턴의 정밀성이 떨어지고 기판 상 위치별 두께편차에 의하여 저항값의 허용편차(tolerance)가 ${\pm}$20~30% 정도로 큰 단점을 가지고 있다. 따라서 경화 후 laser trimming 공정을 필수적으로 동반하게 된다. 이를 개선하기 위하여 본 연구에서는 알칼리 수용액에 현상이 가능한 감광성 레진을 이용하여 폴리머 후막저항 페이스트를 제작하는 것과 함께 기판 전면에 균일한 두께로 인쇄하는 roll coating 방법을 도입하는 실험을 수행하였다. 알칼리 현상형의 감광성 레진 시스템은 노광 및 현상에 의해 정밀한 패턴을 구현할 수 있는 장점을 가지고 있으며, 본 연구에는 A사의 일액형 레진과 T사의 이액형 레진을 사용하였다. 여기에 전도성 필러로서 카본블랙을 첨가하였는데, 그 첨가량의 조절에 따른 후막저항의 시트저항값 변화와 현상 특성을 관찰하였다. 테스트 보드는 FR-4 기판 상에 전극 형상의 동박을 패터닝 후 Ni/Au 도금까지 실시하여 제작하였고, 이 테스트 보드 상에 별도로 제작된 저항 페이스트를 도포한 후 저항체 패턴이 입혀져 있는 Cr 마스크를 이용하여 노광하였다. 이후 현상 공정을 통하여 저항체를 패터닝하고, 이를 $200^{\circ}C$에서 1시간 열경화하는 것으로 후막 저항 테스트쿠폰을 제작하였다. 실험결과 roll coating에 의해 도포된 후막저항체들은 균일한 두께 범위를 나타내었고, 이에 따라 최종 경화 후 허용편차도 통상 ${\pm}$5~10% 이내로 제어될 수 있었다.