• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.793-796
• /
• 2008

Recently early strength concrete has been required for economical assurance and the prevention of frost damage in winter through air reduction in construction of concrete structures. This study presented the optimum condition revealing compressive strength 5MPa which has the possibility of removal of form in 24 hours, and researched the changes of unit weight of cement types of high early strength AE water reducing agents, characteristic of compressive strength expression as cure temperature conditions and slump or airspace. Test results showed at $15^{\circ}C$ with compressive strength of 5MPa that premature removal of form was possible in case of using highly early strength PC water reducing agent with unit weight of cement 360 ; 22hours faster than 10, unit weight 360 ; 20hours faster than 7, unit weight 390 ; 18 hours faster than 4 comparing with OP water reducing agent. And at $5^{\circ}C$ in case of using highly early strength PC water reducing agent with unit weight of cement 330 ; 32hours faster than 10, unit weight 360 ; 30hours faster than 7, unit weight390 ; 27hours faster than 4 comparing with OP water reducing agent. Therefore as the temperature rises $10^{\circ}C$, compressive strength of 5MPa reaching hour shortens 10 hours.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.359-360
• /
• 2009

This Study is performed Mock-up test accounting for height of placement to review behavior of mass concrete according to kinds of cement & form. First, we measured hydration heat and show a different hydration heat generation characteristics as compared with each other. And we measured mortar outflow, the strength of concrete core and standard specimens, concrete's ability to resist chloride ion penetration in order to durability estimation of concrete. This study was aims to improve quality of mass concrete under marine environment.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.1
• /
• pp.51-59
• /
• 2012

The cold weather concrete poured in the winter season can cause the problem of the Due to recent high-rise building is made. In this research, the nominal mix of the early strength in concrete tried to be set through the mixing proportion experiment for each empirical variable and each component strength properties for the early strength improvement tries to be examined. In the cold weather concrete experiment, the cement and high early strength (type3) cement improving in OPC than OPC was excellent. The polycarboxylic acid based compound was exposed to be excellent in the intensity revelation properties. Because the using of the fly ash was disadvantageous it was excluded from this experiment. It showed the optimum temperature for the intensity revelation up over $12^{\circ}C$.

• Clean Technology
• /
• v.12 no.4
• /
• pp.238-243
• /
• 2006

The aggregate properties of chilled converter slag reformed by atomizing liquid converter slag were investigated. The properties of mortars with various replacement of standard sand by chilled converter slag as recycled fine aggregates were investigated. The particle shape of chilled converter slag by atomizing was a sphere with an open cavity which is enclosed with two layers like a bored coconut. Specific gravity, unit weight and fineness modulus increased with increasing the replacement, and solid content had the maximum at the replacement of 75% and water absorption rate had the minimum at the replacement. The hardened mortars with higher replacements have the higher specific gravity and the denser texture.

• Journal of the Korean Society for Advanced Composite Structures
• /
• v.2 no.3
• /
• pp.36-41
• /
• 2011

This study proposes a experimental method to evaluate bonding strength of FRPs used for retrofitting concrete structures. Specimens are designed so that debonding failure of FRPs can be induced from reinforced concrete beams retrofitted with two layers of carbon and glass FRPs. And three-point loading tests are performed to see if debonding failure with proper debonding strength is observed from the specimens. The test results show that the tested beams are failed due to debonding of FRPs, therefore, the proposed test method is capable of evaluating debonding strength of FRPs using relatively small normal strength concrete beams.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.2
• /
• pp.125-132
• /
• 2018

In this study, a direct tensile test was planned to identify the tensile performance of UHPC, and the irregularity of cracks, which is a problem of the direct tensile test, was complemented through the introduction of notches at the center of a specimen. In this regard, a number of specimens divided by batch to reduce the deviation of direct tensile test values were fabricated to present reference data with respect to highly reliable direct tensile strength values. In addition, the mechanical properties and reliability of the specimens were examined under the curing conditions of the specified design strength of 120MPa for the steel fiber reinforced concrete with 1.5% fiber volume fraction, which is most suitable for the field application. As a result, the deviation of averages by batch between compressive strength and direct tensile strength did not show a large difference, and all cracks occurred within 20mm in the direct tensile test. At the 95% confidence interval of the direct tensile strength, the range was considerably small in the mean and the standard deviation, and there was no significant difference depending on the curing conditions. The results confirmed that a stable direct tensile test was performed, and highly reliable results were obtained through the fabrication of specimens by batch and test progress.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.5
• /
• pp.54-59
• /
• 2020

Coarse aggregate is produced in various ways depending on the location and production method. Currently, the construction industry is in need of a stable supply of coarse aggregate and a way to secure standard quality. The purpose of this study is to examine whether the use of coarse aggregate in 3D printing can help solve this problem. ABS filament was selected for use in 3D printing. CATIA was used for the design of the coarse aggregate, and CUBICON Single Plus was used for the production. Six specimens were produced and cured in water for 28 days. Three of them were made with AE agent, and three were made without it. A compressive strength test confirmed that when the AE agent was used, the compressive strength was greater than the lightweight concrete design criterion specified in the concrete standard specification. This suggests that coarse aggregate produced by a 3D printer may be used for lightweight concrete. A mass production system using this method could help to solve the problems facing the construction industry, such as stable supply and demand for coarse aggregate and securing standard quality.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.35 no.2
• /
• pp.299-306
• /
• 2015

The quality for the domestic pavement is evaluated based on flexural strength at the age of 28 days in accordance with KS regulation. Most specimens of the flexural tensile strength used currently are relatively large ones with a dimension of $150{\times}150{\times}550mm$. Accordingly, it is difficult to treat the specimens, and the utilization of a curing tank is low. In this paper, the study tried to resolve the problem by specimen size specified in the code. For this purpose, a flexural strength test was conducted according to the log scale within the specimen size specified by the KS. And, based on the results of this experiment, a comparative analysis was conducted using the prediction formula of Size Effect Law (SEL) proposed by Bazant to examine the correlation between specimen sizes, so as to use the result as basic data for the reduction of the specimen size in the quality evaluation of concrete pavement.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.1
• /
• pp.57-67
• /
• 2007

The service life of concrete structure is to a great extent influenced by crack developed at early ages of concrete material. Especially, hydration heat is a main cause of thermal cracking at mass concrete structures. The thermal cracking of massive structure is analyzed of the thermal cracking index which was presented Concrete Standard Specifications. The thesis analyzed the thermal cracking index which considered various variable (cement type, height of casting, curing condition, concrete mixing temperature, the unit cement content) at internal restricted mass concrete. The analysis result is denoted increase and decrease rate of thermal cracking index whenever the variables change. The results is helped to understand thermal cracking every time structures is designed and constructed. And I think that it is useful economic and stable design of mass concrete structures.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.8 no.4
• /
• pp.537-544
• /
• 2020

The interfacial transition zone(ITZ) which is the boundary layer between cement composites and aggregates is considered to be the region of gradual transition, heterogeneous, and the weakest part of concrete. For the development of lightweight high strength concrete, it is essential to evaluate the mechanical properties of ITZ between high strength concrete with low water-binder ratio and lightweight aggregates. However, the mechanical properties of ITZ are not well established due to its high porosity and complex structure. Furthermore, the properties of ITZ in concrete using lightweight aggregates are dominated by more various variations (e.g. water-binder ratio, water absorption capacity of aggregate, curing conditions) than normal-weight aggregate concrete. This study aims to elucidate the mechanical properties of ITZ in lightweight high-strength cement composites according to the types of aggregates and the aggregate sizes. Nanoindentation analysis was used to evaluate the elastic modulus of ITZ between high strength cement composites with the water-binder ratio of 0.2 and normal sand, lightweight aggregate with different aggregate siz es of 2mm and 5mm in this study.