Abstract
The service life of concrete structure is to a great extent influenced by crack developed at early ages of concrete material. Especially, hydration heat is a main cause of thermal cracking at mass concrete structures. The thermal cracking of massive structure is analyzed of the thermal cracking index which was presented Concrete Standard Specifications. The thesis analyzed the thermal cracking index which considered various variable (cement type, height of casting, curing condition, concrete mixing temperature, the unit cement content) at internal restricted mass concrete. The analysis result is denoted increase and decrease rate of thermal cracking index whenever the variables change. The results is helped to understand thermal cracking every time structures is designed and constructed. And I think that it is useful economic and stable design of mass concrete structures.
콘크리트 구조물의 사용수명은 콘크리트의 초기에 발생하는 균열에 큰 영향을 받는다. 특히 매스콘크리트 구조물에서는 수화열이 초기 온도균열의 주요한 원인이 된다. 이러한 온도균열은 콘크리트 표준시방서에 제시된 온도균열지수를 통해 분석할 수 있다. 따라서 본 논문은 내부구속이 지배적인 매스콘크리트에서 여러변수(시멘트종류, 타설높이, 양생조건, 타설온도, 단위시멘트량)에 따른 온도균열지수를 해석적으로 분석하였고, 분석결과는 변수의 변화에 따른 온도균열지수의 증감률로 나타내었다. 이러한 결과는 시공이나 설계시 온도균열을 파악하는 데 도움을 주어 경제적이고 안정적인 매스콘크리트 구조물의 설계에 유용하게 활용될 것으로 판단된다.