• Proceedings of the KIEE Conference
• /
• 2006.10d
• /
• pp.40-42
• /
• 2006

연자성 복합재료는 기존의 철판 대비 기계적, 자기적 특성 떨어지는 것이 사실 이였다. 본 연구에서는 이러한 문제점 개선을 위해서 저점도 윤활제 적용을 통한 빼기 압력 저감 방안을 도출하였다. 연자성체의 고강도화, 우수한 자기적 특성을 얻기 위해서 높은 압력의 성형이 필수적인데 높은 압력으로 성형시 빼기 압력이 높아져서 금형이 파손되는 등 문제점으로 인해 우수한 특성을 얻을 수 없었다. 본 연구에서는 이러한 문제점을 해결하기 위해서 저 점도액체 윤활제, 고점도 액체 윤활제, 고체 윤활제 3가지의 윤활제 특성을 검토 하였다. 또한 저점도 액체 윤활제 적용을 통해서 기존 대비 강도 10%, 철손 10%, 빼기 압력 30%를 저감 하였다.

• Applied Chemistry for Engineering
• /
• v.20 no.6
• /
• pp.685-691
• /
• 2009

Dispersions of fumed silica are made in 6 kinds of mono-solvents and mixed solvents which have hydroxyl group, non hydroxyl group, different polarity, and different molecular size. The viscosity and rheology behaviors of the each dispersion are investigated according to the viewpoint of solvent characteristic. The silica dispersion in polar solvent with hydroxyl group is stable and low viscous sol. The silica dispersion in non-polar solvent with non-hydroxyl group is high viscous gel. When the solvent with hydroxyl group is added to the silica dispersions with non-polar solvents, they show the reduction of viscosity with solvent content. They have minimum critical content which shows no viscosity change. The minimum critical solvent content is decreased according to the polarity of solvents with no hydroxyl group. The solvation layer which is formed on the silica surface through hydrogen bonding between hydroxyl-containing solvent and the silanol group of silica surface is the reason of stable and low viscous sol. In case of non-polar solvent, silanol on adjacent silica particles interacted directly by hydrogen bonding show high viscous and flocculated gel.

• Journal of the Korean Applied Science and Technology
• /
• v.35 no.3
• /
• pp.985-1001
• /
• 2018

In this study, we tried the various experiments using the emulsifier, electrolyte, stabilizer and gelling agent in order to improve a stability of low viscosity W/O emulsion. As a result, when we used polyglyceryl-4 diisostearate/polyhydroxystearate/sebacate as a main emulsifier, PEG-30 dipolyhydroxystearate and cetyl PEG/PPG-10/1 dimethicone as a co-emulsifier for stable emulsification system, 0.5 % sodium chloride as an electrolyte, 1 % distearyldimonium chloride as a stabilizer, 0.5 % glyceryl behenate/eicosadioate as an oil gelling agent, emulsion particle is the best. Also, we got the stable and low viscosity W/O emulsion maintained at a constant viscosity at 2,000 cps or less. In addition, we were able to examine the possibility of development of low viscosity fluids type sunscreens with excellent feeling and stability through the application of inorganic sunscreen agents.

• Journal of Adhesion and Interface
• /
• v.17 no.2
• /
• pp.67-71
• /
• 2016

In this study, low-viscosity polyurethane hot-melt were synthesized with polyether polyol / polyester polyol, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), 2-butanone oxime (MEKO) to improve the properties and peel strength. The properties of the synthesized low-viscosity polyurethane hot-melt was evaluated through FT-IR, viscosity meter and UTM. When the content of the reactive diluent increases and the NCO-blocked prepolymer decreases, the viscosity of low-viscosity polyurethane hot-melt adhesive was increased. When the ratio of OH-terminated oligomer, NCO-blocked prepolymer and content of reactive diluent is 1 : 0.5 : 0.5, low-viscosity polyurethane hot-melt showed 1.1 kgf/cm peel strength.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.43 no.4
• /
• pp.273-279
• /
• 2017

In this study, low viscous O/W (oil-in-water) nano-emulsion with fatty acid and fatty alcohol was prepared by phase inversion emulsification method using Tween 80 and Span 80 widely used in cosmetic products. The particle size of the nano-emulsion was increased as increasing the concentration of fatty alcohol in oil phase. Adjusting the HLB of mixed surfactants, a stable nano-emulsion with a narrow size distribution was produced. Similar change in viscosity and electrical conductivity in both systems containing fatty acid and fatty alcohol was shown in the vicinity of the phase inversion point. However, high viscosity was shown in a wide range of different aqueous fraction unlike the system consisting only oils and surfactants. The low viscous nano-emulsion with less than 100 nm droplet size was stable for one month or more at room temperature. O/W nano-emulsions with low viscosity containing fatty acid or fatty alcohol produced by low-energy emulsification method can be widely used as formulations of cosmetics.

• Journal of Conservation Science
• /
• v.24
• /
• pp.37-42
• /
• 2008

Stability of the moving historic sites have something to do with the degree of easiness of work as well as physical property of polymer product. These agents should be able to use without the effect of outer environments like water or low temperature and must have stability during progress of working the peel off Urethane pre-product from Epoxy surface. So, we synthesized low viscosity epoxy resin and hardener with best physical quality and separation media for the moving of historical sites. These products have very good tension strength, adhesion strength, low viscosity and various physical properties that the users want. Particularly, separation media products have good separation of Urethane pre-products surface and Epoxy final product surface.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.31 no.4
• /
• pp.294-300
• /
• 2015

Purpose: The purpose of this study was to measure the color of low viscosity bulk-fill resin with a capping layer and to compare it with the color of microhybrid composite resin. Materials and Methods: A low viscosity bulk-fill resin (SDR) and microhybrid composite resin of shade A2 (A2) or A3 (A3) were fabricated to 4 mm thickness and light cured for 20 seconds. CIE $L^*a^*b^*$ values of the resin specimens were measured with a colorimeter. Then shade A2 and A3 microhybrid composite resin was capped over low viscosity bulk-fill resins in 2 mm thickness (SA2, SA3). The resin specimens were light cured for 20 seconds and the color was measured and analyzed (n = 10). Color differences (${\Delta}E$) between SA2 and A2, SA3 and A3 were also calculated. Results: $L^*$ value was highest in SDR followed by SA2 and SA3. $L^*$ value of A2 and A3 was the lowest. $a^*$ value was lowest in SDR followed by SA2 and SA3, and A2 and A3 was the highest. $b^*$ value was lowest in SDR followed by A2 and SA2, and A3 and SA3 was the highest. ${\Delta}E$ between A2 and SA2 (${\Delta}E=3.4$), and that between A3 and SA3 (${\Delta}E=3.1$) was lower than the perceptible color difference threshold of ${\Delta}E=3.7$. Conclusion: ${\Delta}E$ between low viscosity bulk-fill resin with a capping layer and microhybrid resin was lower than the perceptible color difference threshold.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.42 no.2
• /
• pp.127-133
• /
• 2016

In this study, water-in-oil (W/O) nanoemulsions of water/Span 80-Nikkol BL 25/oil system were prepared by the PIC method at elevated temperature. This method allows the formation of finely dispersed W/O nanoemulsions with low viscosity in this system. However, macroemulsions rather than nanoemulsions were prepared by PIC method at room temperature. As a result of the significant change of interfacial tension with temperature, the emulsion droplet size decreases from $2{\mu}m$ to 100 nm with the increase in temperature from $30^{\circ}C$ to $80^{\circ}C$. The droplet size of nanoemulsions prepared at $80^{\circ}C$ was in the range of 50 ~ 200 nm and the internal phase content could reach as high as 15 wt%. The most stable nanoemulsion was formed in the vicinity of 7.0 of optimum HLB of the emulsifier mixture. The obtained nanoemulsions were stable without obvious change in droplet size in one month. This study provides valuable information for optimizing the formation of W/O nanoemulsions with low viscosity. These results suggest that W/O nanoemulsions of low viscosity could be useful for cosmetics with soft feeling.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2010.05a
• /
• pp.393-394
• /
• 2010

This paper was examined the plastic viscosity and yield stress of paste and mortar on the part of the research to develop low viscosity and high fluidity concrete for high pumpability. Through this study, we examined the suitable material properties of paste and mortar to low viscosity and high fluidity concrete for high pumpability.

• Polymer(Korea)
• /
• v.31 no.6
• /
• pp.491-496
• /
• 2007

In the polymeric dental restorative composites, the resin matrix mainly contains 70 wt% 2,2-bis[4-(2-hydroxy-3-methacryloyloxy propoxy) phenyl] propane (Bis-GMA), as a base resin and 30 wt% triethylene glycol dimethacrylate (TEGDMA) as a diluent. Even though the viscosity of the resin matrix is rapidly decreased by adding TEGDMA, addition of TEGDMA to the Bis-GMA results in reduction in the mechanical properties and increase in the curing shrinkage of the dental composite. In order to fabricate dental composite exhibiting excellent properties by reducing TEGDMA content in the resin matrix, in this study, Bis-GMA derivatives, which do not contain hydroxyl groups, were used instead of Bis-GMA. The curing characteristics of Bis-GMA derivatives were similar with those of Bis-GMA, while the former exhibited lower viscosity and water absorption than the latter. Comparing the curing shrinkage of the dental composite containing Bis-GMA derivative with that prepared from Bis-GMA, the reduction in curing shrinkage was about 25%. Dental composites prepared from new resin matrices also exhibited low water uptake and better properties in mechanical strength.