• Journal of Aerospace System Engineering
• /
• v.12 no.3
• /
• pp.64-69
• /
• 2018

The high-velocity electromagnetic forming (EMF) process is based on the Lorentz force and the energy of the magnetic field. The advantages of EMF include improved formability, wrinkle reduction, and non-contact forming. In this study, the electromagnetic-structural interlocking analysis was performed in order to analyze the moldability of aluminum pipe using electromagnetic molding. The magnetic flux density was decreased due to increasing electrical resistance as the temperature increased, and the stress-strain curve decreased. The higher the temperature, the lower the flow stress, increasing deformation.

• Journal of the Korea Concrete Institute
• /
• v.27 no.5
• /
• pp.569-577
• /
• 2015

The aim of this study is to qualitatively evaluate the cracking control effects of expansive concrete used in reinforced concrete building. The result of experiments in laboratory shows that autogenous shrinkage and drying shrinkage are suppressed by using expansive additive. The tensile stress-strength ratio is lower in expansive concrete than normal concrete under fully restrained condition. Compression stress could be effectively generated in early age in the walls in buildings by the use of expansive additive, and tensile stress due to drying shrinkage at later age eventually decreased. Additionally, visual observation at long-term ages shows that the cracking area of expansive concrete was approximately 35% of normal concrete, which confirms that the use of expansive additive reduces concrete cracking in reinforced concrete buildings.

• Membrane Journal
• /
• v.26 no.6
• /
• pp.421-431
• /
• 2016

Novel membrane technologies that harness ordered nanostructures have recently received much attention because they allow for high permeability due to their reduced flow resistance while also maintaining high selectivity due to their isoporous characteristics. In particular, the opaline structure (made from the self-assembly of colloidal particles) and its inverted form (inverse-opal) have shown strong potential for membrane applications on account of several advantages in processing and the resulting membrane properties. These include controllability over the pore size and surface functional moieties, which enable a wide range of applications ranging from size-exclusive separation to catalytically-reactive membranes. Furthermore, when combined with multiscale architecturing strategies, inverse-opal-structured membranes can be designed to have specific pores or channel structures. These materials are anticipated to be utilized for next-generation, high-performance, and high-value-added functional membranes. In this review article, various types of inverse-opal-structured membranes are reviewed and their functionalization through hierarchical structuring will be comprehensively investigated and discussed.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.23 no.1
• /
• pp.169-175
• /
• 2009

In this experiment molybdeum oxide($MoO_3$) films were prepared by a magnetic null discharge(MND) sputtering system and fundamental properties by XRD, XPS and SEM analysis were investigated. The initial and mean insulation resistance of the same with $MoO_3$ film were about 1.4[$M{\Omega}$] and 800[$k{\Omega}$] under the condition of applied voltage of 400[V]. The preferred orientation in the films changed from(100) to (210) with substrate temperature. Two XPS peaks of the $MoO_3$ photoelectron were detected at the binding energies of 228.9[eV] and 232.4[eV], while the binding energy of the O1s peak was 532.6[eV]. The substrate temperature and reactivity gives large effects to the structure and growth of the film and system is also very useful for performing the uniform reactive deposition. It can be found from the result of a $MoO_3$ film deposition that the system is very useful for performing the uniform reactive sputtering.

• Korean Chemical Engineering Research
• /
• v.54 no.3
• /
• pp.293-298
• /
• 2016

A hydrogel electrolyte consisting of 6 M KOH aqueous solution, potassium polyacrylate (PAAK, 3 wt.%), and a hydrophilic silica OX50 (1 wt.%) was prepared to use as an electrolyte medium coated on a Scimat separator of activated carbon supercapacitor. The silica particle distributed homogeneously on surface pores of the separator to increase ionic conductivity and electrochemical stability of the hydrogel electrolyte. The silica addition also involved superior specific capacitance even at higher scan rates due to decrease in interfacial resistance between hydrogel electrolyte and activated carbon electrode.

• Resources Recycling
• /
• v.12 no.6
• /
• pp.26-31
• /
• 2003

The power loss characteristics of Mn-Zn ferrite were observed with the sintering temperature. In case of $1150 ^{\circ}C$ sintering, the core loss increased with measuring temperature, and does not have minimum value at the point where the magnetocrystalline anisotropy be 'zero'. This reason mainly due to the change of core loss mechanism with grain size which affects residual loss. The grain size and sintered density slightly increased with equilibrium oxygen partial pressure at$ 1150 ^{\circ}C$ sintering. The resistivity and initial permeability showed no significance with atmosphere, these results due to complex effect of $Fe^{2+}$ concentration and microstructure change. The core loss at $100^{\circ}C$ decreased as the equilibrium oxygen partial pressure increased.e increased.

• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.185-188
• /
• 1999

Biepitaxial Y$_1Ba_2Cu_3O_{7-x}$ (YBCO) and La$_{0.2}Sr_{0.8}MnO_3$ (LSMO) thin films have been prepared on SrTiO$_3$ buffer layer and MgO seed layer grown on Al$_2O_3$(11${\bar{2}}$0)substrates by dc-sputtering with hollow cylindrical targets, respectively. We charaterized Josephson properties and significantly large magnetoresistance in YBCO and LSMO films with 45$^{\circ}$ grain boundary junction, respectively. The observed working voltage (I$_cR_n$) at 77 K in grain boundary junction was below 10${\mu}$V, which is typical I$_cR_n$ value of single biepitaxial Josephson junction. The field magnetoresistance ratio (MR) of LSMO grain boundary juncoon at 77K was enhanced to 13%, which it was significant MR value with high magnetic field sensitivity at a low field of 250 Oe. These results indicate that inserting the insulating layer instead of the grain boundary layer with metallic phase can be possible to apply a new SIS Josephson junction and a novel magnetic device using spin-polarized tunneling junction.

• Industry Promotion Research
• /
• v.3 no.2
• /
• pp.87-94
• /
• 2018

This study suggests that lifelong education is regarded as a support system for lifelong learning, which includes all activities of educational characteristics, which ultimately has the goal of universalization of self - education. The goal is to successfully adapt to life. Statements supporting the need for lifelong learning have been found to be based primarily on the impossibility of this system to provide sufficient education to accelerate social change and to last a lifetime. The obstacles to implementation included inertia, resistance to change, motivation and cost. Opponents are likely to regard lifelong education as an attempt to expand compulsory education for exploitation and control purposes. This study found that there is an important consensus among supporters, but many questions remain. The full feasibility of lifelong education is considered to be far removed, and lifelong education should be interpreted as a source of direction and purpose, and ideals that society should aim for.

• Journal of the Microelectronics and Packaging Society
• /
• v.19 no.4
• /
• pp.65-69
• /
• 2012

Composite coating can be manufactured during the electroplating with the bath containing a suspension of particles: ceramic, polymer, nanopowders. Improvement of hardness, wear resistance, corrosion resistance and lubrication properties are well-known advantage of composite coating. In this study, nano $TiO_2$ powder dispersed Ni composite plating was investigated. The improvement of surface hardness and photo decomposition effects can be expected in this coating. Zeta potential was measured with pH. The effect of ultrasonication time and types of ultrasonicator were studied to minimize the agglomeration of $TiO_2$ nanopowders in the electrolyte. Optimum conditions for nano $TiO_2$ dispersed Ni composite coating were $40mA/cm^2$ of current density, pH 3.5, and $50^{\circ}C$. At these conditions, $TiO_2$ nanoparticles contents in the Ni deposit was 15-20 at.%.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.6 no.2
• /
• pp.364-370
• /
• 2002

A banknote counter is a machine that automates counting the money in some agencies to treat much banknotes as well as general banking agencies. The banknote counter materialized in this paper is the machine that adds the function of banknote sorting, detecting plural banknote and detecting counterfeit banknote to an existing banknote counter. The technique of sensor signal processing are used for banknote sorting. The technique of sensor application and data processing are used for detecting counterfeit banknote. The technique of precision equipment design and microprocessor application are used for high speed count. Software improved in debugging and difficulties to link with additional hardware. It was materialized through effective control algorithm and real-time signal processing with C-language on the basis of RTOS(real-time operating system) Photodiode, its applications and a magnetic resistance sensor are used as a sensor device with regard to hardware cost -cutting and process velocity. PCF80C552-24 of Philips using Intel I8051 core is used as a control microprocessor. As the results so far achieved, counterfeit banknotes made by the use of a color duplicator and a color Printer, are distinguished from real banknotes through mixing an optical with a magnetic sensor. and, in case that there are some different banknotes while counting, it is prevented for them to be counted without discriminating from the same kind of banknotes in addition to the fu notion of banknote sorting.