• Journal of Korean Ophthalmic Optics Society
• /
• v.12 no.2
• /
• pp.19-23
• /
• 2007

An investigation of the effects of CaO on microstructure and properties of SiC materials for spectacle lens cutting was described. Four materials with different composition have been fabricated by hot-pressing at $1,880^{\circ}C$ for 4h using CaO. SEM analysis and XRD of the surface of samples were carried out. Typical fracture toughness of materials for spectacle lens cutting was $5.4MPa{\cdot}m^{1/2}$. Also, The hardness of materials for spectacle lens cutting was relatively dependent on the density.

• Korean Chemical Engineering Research
• /
• v.47 no.3
• /
• pp.310-315
• /
• 2009

Perovskite-type ceramic powder, $La_{0.7}Sr_{0.3}Co_{0.3}Fe_{0.7}O_{3-{\delta}}$, have been synthesized successfully by the citrate method. As a result of TGA for precursor, metal-citrate complex in precursor was decomposed in the temperature range of $150{\sim}650^{\circ}C$. XRD analysis showed the single perovskite structure was observed over $1,000^{\circ}C$ without impurities. Typical dense membrane with 1.6 mm thickness has been prepared using as-prepared powder by pressing unilaterally and sintering at $1,300^{\circ}C$. The electrical conductivity of $La_{0.7}Sr_{0.3}Co_{0.3}Fe_{0.7}O_{3-{\delta}}$ membrane increased with increasing temperature at atmosphere of air and then decreased over $600^{\circ}C$ due to oxygen loss from the crystal lattice. The oxygen flux of $La_{0.7}Sr_{0.3}Co_{0.3}Fe_{0.7}O_{3-{\delta}}$ membrane in the range of 700 to $950^{\circ}C$ increased with the increasing temperature from 0.045 to $0.415ml/cm^2{\cdot}min$. The activation energy for oxygen permeation was calculated to be 89.17 kJ/mol.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.1
• /
• pp.7-13
• /
• 2007

We synthesized and investigated $La_{0.75}Sr_{0.25}FeO_3$ by Glycine Nitrate Process(GNP) method used as cathode materials for SOFC(solid oxide fuel cell). Optimized amount of glycine is 3.17 mol. ICP elemental composition analysis indicated that the stoichiometry of the synthesized powders have nearly nominal values. SEM images and XRD patterns reveal that the synthesized powder has uniform size distribution and high degree of crystallinity. The sample powders were isostatically pressed to form a pellet. The green body was sintered at $1200^{\circ}C$ and the relative density of the sintered specimens were measured by Archimedes mettled. We measured electrochemical performance of LSF by AC impedance spectroscopy. Resistance of LSF shows lower value than that of LSM throughout all temperature region. The anode-supported solid oxide fuel cell showed a performance of $342mW/cm^2(0.7V,\;488mA/cm^2)$ at $750^{\circ}C$. The electrochemical characteristics of the single cell were examined by at impedance method.

• Korean Chemical Engineering Research
• /
• v.57 no.4
• /
• pp.525-530
• /
• 2019

The performance and stability of solid oxide fuel cells (SOFCs) depend on the microstructure of the electrode and electrolyte. In anode, porosity and pore distribution affect the active site and fuel gas transfer. In an electrolyte, density and thickness determine the ohmic resistance. To optimizing these conditions, using costly method cannot be a suitable research plan for aiming at commercialization. To solve these drawbacks, we made high performance unit cells with low cost and highly efficient ceramic processes. We selected the NiO-YSZ cermet that is a commercial anode material and used facile methods like die pressing and dip coating process. The porosity of anode was controlled by the amount of carbon black (CB) pore former from 10 wt% to 20 wt% and final sintering temperature from $1350^{\circ}C$ to $1450^{\circ}C$. To achieve a dense thin film electrolyte, the thickness and microstructure of electrolyte were controlled by changing the YSZ loading (vol%) of the slurry from 1 vol% to 5 vol. From results, we achieved the 40% porosity that is well known as an optimum value in Ni-YSZ anode, by adding 15wt% of CB and sintering at $1350^{\circ}C$. YSZ electrolyte thickness was controllable from $2{\mu}m$ to $28{\mu}m$ and dense microstructure is formed at 3vol% of YSZ loading via dip coating process. Finally, a unit cell composed of Ni-YSZ anode with 40% porosity, YSZ electrolyte with a $22{\mu}m$ thickness and LSM-YSZ cathode had a maximum power density of $1.426Wcm^{-2}$ at $800^{\circ}C$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.29 no.6
• /
• pp.338-344
• /
• 2019

B₄C-SiC composites were fabricated using hot press sintering method without sintering additives at 1,900~2,000℃ under a pressure of 40 MPa. The crystal phase, relative density, microstructure, and mechanical properties of B₄C-SiC composites were evaluated. When B₄C and SiC were uniformly dispersed in the composite, grain growth was inhibited, and a sintered body with a fine and uniform microstructure, with improved mechanical properties, was fabricated. The relative density of B₄C-SiC composites sintered under 2,000℃ of temperature and 40 MPa of pressure was over 99.8 %, and the bending strength and Vicker's hardness at 50 wt% of B₄C were 645 MPa and 30.6 GPa, respectively.

• Journal of Powder Materials
• /
• v.28 no.1
• /
• pp.7-12
• /
• 2021

The change in the open porosity of bulk graphite as a function of the uniaxial molding pressure during manufacturing is studied using artificial graphite powder. Subsequently, the graphite is impregnated to determine the effect of the open porosity on the impregnation efficiency and to improve the density of the final bulk graphite. Bulk graphite is manufactured with different uniaxial molding pressures after mixing graphite powder, which is the by-product of processing the final graphite products and phenolic resin. The bulk density and open porosity are measured using the Archimedes method. The bulk density and open porosity of bulk graphite increase as the molding pressure increases. The open porosity of molded bulk graphite is 25.35% at 30 MPa and 29.84% at 300 MPa. It is confirmed that the impregnation efficiency increases when the impregnation process is performed on a specimen with large open porosity. In this study, the bulk density of bulk graphite molded at 300 MPa is 11.06% higher than that before impregnation, which is the highest reported increase. Therefore, it is expected that the higher the uniaxial pressure, the higher the density of bulk graphite.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.6
• /
• pp.271-276
• /
• 2020

In this study, an amorphous SiC block was manufactured using polycarbosilane (PCS), an organosilicon polymer. The dense SiC blocks were easily fabricated in various shapes via pyrolysis at 1100℃, 1200℃, 1300℃, 1400℃ after manufacturing a PCS molded body using cured PCS powder. Physical and chemical properties were analyzed using a thermogravimetric analyzer (TGA), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), and universal testing machine (UTM). The prepared SiC block was decomposed into SiO and CO gas as the temperature increased, and β-SiC crystal grains were grown in an amorphous structure. In addition, the density and flexural strength were the highest at 1.9038 g/㎤ and 6.189 MPa of SiC prepared at 1100℃. The manufactured amorphous silicon carbide block is expected to be applicable to other fields, such as the previously reported microwave assisted heating element.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.777-782
• /
• 2004

In this research, $5\times5cm^2$ unit cells were fabricated via liquid condensation process and uniaxial pressing followed by the screen printing of electrolyte and cathode layer. The SOFC stack was assembled with unit cells, gasket-type sealant and metal interconnect. The stack was designed to have a single column with internal-manifold and cross-flow type gas-channels. The SOFC stack produced 15 W, which is $50\%$ of the maximum power being expected from the maximum power density of the unit cell. Controlling factors for the proper operation of the SOFC stack and other designing factors of stack manifold and gas channels were discussed.

• Journal of the Korean Ceramic Society
• /
• v.42 no.3 s.274
• /
• pp.193-197
• /
• 2005

Wall and floor tiles were fabricated by a dry pressing method using waste glass and clay. The physical properties of the tiles such as absorption, bulk density, porosity, compressive strength, and abrasion loss are investigated with the firing temperature and glass contents. The physical properties are improved with increasing the firing temperature and glass contents. The composition containing the glass of $70 wt%$ and fired at $1050^{\circ}C$ for 2 h has the good properties. The optimal properties obtained in the tiles are the water absorprion of about $0.9\%$, the bulk density of about $2.3\;g/cm^3$, the apparent porosity of about $2.1 \%$, the compressive strength of about 210 MPa, and the abrasion loss of about 0.022 g, when the composition containing the glass of $70\;wt\%$ is fired at $1050^{\circ}C$. The physical proper1ies of tiles fabricated were enhanced compared to the commercial clay tiles, due to easy melting and densification of glassy phase during the firing process.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.438-445
• /
• 2002

In this study, the glass frit of $PbO-TiO-2-SiO_2-BaO-ZnO-Al_2O-3-CaO-B_2O_3-Bi_2O_3-MgO$ system was manufactured. The glass was melted at $1,400{\circ}C$, quenched and attrition-milled. The glass frit powder was pressed and fired for 2h at the range of $750~1,000{\circ}C$. The crystallization of glass frit began at about $750{\circ}$ and at low temperature, the main crystal phases were hexagonal celsian($BaAl_2Si_2O_8$) and alumina. As the firing temperature increased, the crystal phases of monoclinic celsian, zinc aluminate, zinc silicate, calcium titanium silicate and titania appeared. And the increase of firing temperature led to transformation of hexagonal celsian to monoclinic. The only glass frit containing 15wt% PbO had the crystal phase of solid solution of $PbTiO_3-CaTiO_3$. At the frequency of 1 MHz, the dielectric constant of glass frit crystallized was in the range of 11~16 and the dielectric loss less than 0.020. But the glass frit containing 15wt% PbO had the dielectric constant of 17~26 and loss of 0.010~0.015 because of crystal phase of solid solution of $PbTiO_3-CaTiO_3$.