Better electrical and optical properties of ITO thin films were demanded for the window layer of CdS/CdTe solar cells. To match that demand, an ion beam sputtering system was used for the deposition of ITO thin films. The substrate temperature and ion beam energy were controlled to deposit high quality ITO thin films in two cases of Ar ion sputtering and Ar+$O_2$ ion sputtering. The microstructure changed from domain structure in ITO deposited by Ar ions to grain structure in ITO deposited by Ar+$O_2$ ions. The lowest resistivity of ITO films was $1.5\times10^{-4}{\Omega}cm$ at $100^{\circ}C$ substrate temperature in case of Ar ions sputtering. Transmittance in the visible range was over 80% above $100^{\circ}C$ substrate temperature.

• Journal of the Korean Vacuum Society
• /
• v.11 no.3
• /
• pp.176-182
• /
• 2002

Amorphous $TiO_2$ thin films were deposited on glass substrates by ion beam sputtering in which the ratio of $O_2$/Ar gas used as discharged gas was varied from 0 to 2. After optical and microstructure properties and chemical composition of thin films was analyzed, antireflection coating layers were fabricated with $SiO_2$/$TiO_2$ multi-layers. Thin films deposition was performed at room temperature and ion beam voltage and ion current density for sputtering of target were fixed at 1.2 kV and 200 $\mu\textrm{A}/\textrm{cm}^2$, respectively. Refractive indexs of the deposited $TiO_2$films were 2.40-2.45 at a wavelength of 633 nm. $TiO_2$films had high transmission and stoichiometry when ratio of $O_2$/Ar was 1. Rms roughness of deposited $TiO_2$ film was below 7 $\AA$. In excessive $O_2$ environments, however Rms roughness increased over 50 $\AA$. Transmittance decreased by scattering of rough surface. Reflectance of $SiO_2$/$TiO_2$multi-layers was below 1% in visible light.

• Journal of the Korean Ceramic Society
• /
• v.40 no.12
• /
• pp.1165-1169
• /
• 2003

The Ta$_2$O$_{5}$ thin film was deposited on Si-(III) and glass substrate with the change of Ar:O$_2$ gas flow rate in the assist ion gun by the Dual ion-Beam Sputtering (DIBS). As the $O_2$ gas flow of the assist ion gun was decreased, the deposition rate of the thin films decreased. The refractive index was fixed (2.11, at 1550 nm) without regarding to $O_2$ gas flow of the range 3∼12 sccm in assist ion gun. The condition of Ar:O$_2$=3:12 was formatted stoichiometry composition of Ta$_2$O$_{5}$ and the ms roughness was small (0.183 nm).

• Journal of the Korean Vacuum Society
• /
• v.15 no.4
• /
• pp.395-403
• /
• 2006

It is known that $MgAl_2O_4$ has higher resistance to moisture than MgO, in humid ambient MgO is chemically unstable. It reacts very easily with moisture in the air. In this study, the characteristic of $MgAl_2O_4$ and $MgAl_2O_4/MgO$ layers as dielectric protection layers for AC- PDP (Plasma Display Panel) have been investigated and analysed in comparison for conventional MgO layers. MgO and $MgAl_2O_4$ films both with a thickness of $1000\AA$ and $MgAl_2O_4/MgO$ film with a thickness of $200/800\AA$ were grown on the Cu substrates using the electron beam evaporation. $1000\AA$ thick aluminium layers were deposited on the protective layers in order to avoid the charging effect of $Ga^+$ ion beam while the focused ion beam(FIB) is being used. We obtained sputtering yieds for the MgO, $MgAl_2O_4$ and $MgAl_2O_4/MgO$ films using the FIB system. $MgAl_2O_4/MgO$ protective layers have been found th show $24{\sim}30%$ lower sputtering yield values from 0.244 up to 0.357 than MgO layers with the values from 0.364 up to 0.449 for irradiated $Ga^+$ ion beam with energies ranged from 10 kV to 14 kV. And $MgAl_2O_4$ layers have been found to show lowest sputtering yield values from 0.88 up to 0.109. Secondary electron emission coefficient(g) using the ${\gamma}$- FIB. $MgAl_2O_4/MgO$ and MgO have been found to have similar g values from 0.09 up to 0.12 for indicated $Ne^+$ ion with energies ranged from 50 V to 200 V. Observed images for the surfaces of MgO and $MgAl_2O_4/MgO$ protective layers, after discharge degradation process for 72 hours by SEM and AFM. It is found that $MgAl_2O_4/MgO$ protective layer has superior hardness and degradation resistance properties to MgO protective layer.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.254.1-254.1
• /
• 2013

현재의 나노기술 및 부품은 나노미터 이하의 초고분해능을 요구하면서도 나노미터 이하의 정확도로 가공할 수 있는 기술을 요구하고 있다. 이온현미경은 위 두 요구조건을 만족하는 차세대 현미경으로써 초고분해능 이미징과 함께 기존의 갈륨이온을 사용하는 집속이온빔 장치보다 네온가스등을 이용하여 더 정밀하게 에칭 및 스퍼터링을 할 수 있다. 이온현미경은 전자현미경에 비해 더 깊은 초점심도를 갖으며, 색수차와 구면수차에 비교적 둔감하고 전자에 비해 무거운 이온의 무게 때문에 짧은 파장을 갖는 특징을 가지고 있다. 이와 같은 특징을 이용하면 전자현미경과 다른 여러 특징과 장점을 갖는 고분해능의 현미경을 제작할 수 있다. 이와 같이 차세대 현미경으로 주목받는 이온현미경의 중요한 부분인 이온총은 현재 가스장 이온 소스 방법으로 대부분 개발되고 있다. 가스장 이온 소스는 1950년대에 E. W. Muller에 의해 개발된 전계 이온 현미경(Field Ion Microscope)에서 응용된 방법으로 뾰족한 탐침에서의 가스 이온화를 기반으로 한다. 가장 보편적으로 사용되는 재질은 텅스텐으로 수십 nm 정도의 곡률 반경을 갖도록 제작하고 초고진공에 설치하여 강한 양전압을 인가함과 동시에 가스를 팁 주변에 넣어주면 팁표면에서 이온빔이 발생하게 된다. 본 연구에서는 위와 같이 차세대 나노장비로써 주목받는 이온현미경의 특징에 대해 소개하고, 특히 이온현미경의 이온총 원천기술 개발을 위해 연구하고 있는 가스장 이온 소스의 특성에 대해 소개한다. 수소, 네온, 헬륨의 전계 이온현미경과 함께 생성된 이온빔의 안정도 및 각전류 밀도를 계산하여 실제 이온총으로의 적용 가능성에 대해 보여준다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.376-376
• /
• 2010

이차이온질량분석기(SIMS)는 수 kV의 에너지를 갖는 일차이온($O_2^+$, $Cs^+$)을 시료표면에 충돌시켜 표면에서 떨어져 나온 이온의 질량 및 개수를 분석하는 장비이다. SIMS는 성분원소의 깊이분포도 측정, 질량분석, Image mapping등 다양한 분석을 할 수 있다. 특히 극미량 분석이나 깊이분포도 분석에서 가장 뛰어난 성능을 가지고 있어 아직까지 많이 사용하고 있다. 하지만 SIMS는 이온빔을 이용한 스퍼터링(Sputtering) 방법으로 분석을 하므로 파괴적이며 매질효과가 심하다. 또한 Matrix 물질의 함량이나 물질 자체가 변한다면 Sputtering rate도 그에 따라 변하게 된다. 이러한 현상에 의해 Sputtering rate는 다른 물질이 섞여 있는 경우 Sputtering rate이 빠른 물질이 먼저 Sputtering이 되는 Preferential Sputtering 현상이 나타나기 때문에 계면에서 깊이분해능에 좋지 않은 영향을 주게 된다. 본 연구에서는 SIMS로 Si(100) 기판 위에 약 100nm 두께로 Fe가 증착된 시료를 분석하였다. 이차이온으로 $O_2^+$이온을 사용하였으며 이온의 입사각을 변화시켜 각 조건에서 생기는 Fe 표면의 Topograph을 SEM으로 관찰하였으며, Topograph와 SIMS깊이분해능의 관계을 이해하고 $O_2^+$ 이온의 입사각 변화에 따른 Fe 표면의 Topograph의 형태와 산화도를 이해하고자 한다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2009.08a
• /
• pp.81-81
• /
• 2009

• Proceedings of the Korean Vacuum Society Conference
• /
• 2003.02a
• /
• pp.124-124
• /
• 2003

• Proceedings of the Korean Vacuum Society Conference
• /
• 2002.06a
• /
• pp.69-69
• /
• 2002