• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.107-108
• /
• 2016

When the construction in a low temperature, the concrete performance is deteriorated by frost damage at early age. In this study, the form utilizing heating sheet and insulation is measured the performance to prevent frost damage at 10 below zero. It produced five types of the form and to measure the temperature history and compressive strength. At first, form attached heating sheet showed the highest temperature. But the form attached vacuum insulation showed the highest temperature ever since 12hours. In the case of compressive strength, the form attached heating sheet + isopink(polystyrene foam board) showed the highest compressive strength. It was followed by vacuum insulation. As a result, the form utilizing insulation and heating sheet helped to prevent frost damage.

• Korean Journal of Agricultural Science
• /
• v.7 no.2
• /
• pp.119-130
• /
• 1980

This study was conducted to determine the effect of curing temperature on the strength of briquette ash mortar hardened by cement. The six different kinds of briquette ash mortars were made by mixing the cement : briquette ash, ((cement (90%)+lime (10%)) : briquette ash and cement : standard sand at the ratio of 1:2, 1:3, 1:4, 1:5, 1:7, and 1:9, respectively and the cu ring temperatures were $20^{\circ}C$, $30^{\circ}C$, and $35^{\circ}C$. The strength of compression, bending and tensile were measured at ${\sigma}_7$ and ${\sigma}_{28}$. The summarized results were as follows. 1. At the ${\sigma}_7$ of 1:2 the compressive strength of the cement : briquette ash and (cement+lime) : briquette ash were 69.3% and 75.1%, respectively of the mortar made of the standard sand. At the ${\sigma}_{28}$ the strength of those materials were 56.4% and 49.0%, respectively. 2. At the ${\sigma}_7$ of 1:2 the tensile strength of the cement : briquette and (cement+lime) : briquette ash were 64.4% and 47.1%, respectively of the mortar made of standard sand. At the ${\sigma}_{28}$ the tensile strength of those materials were 69.6% and 64.8%, respectively. 3. At the ${\sigma}_7$ of 1:2 the bending strength of the cement : briquette ash and (cement+lime) : briquette ash were 46.3% and 65.9%, respectively of the mortar made of the standard sand. At the ${\sigma}_{28}$ the strength of those materials were 89.9% and 96.7%, respectively. 4. The increment of strength per $1^{\circ}C$ increase of curing temperature were on the average $0.92{\sim}1.75kg/cm^2$ of compressive strength, $0.12{\sim}0.16kg/cm^2$ of the tensile strength and $0.21{\sim}0.38kg/cm^2$ of the bending strength.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.11 no.1
• /
• pp.57-67
• /
• 2007

The service life of concrete structure is to a great extent influenced by crack developed at early ages of concrete material. Especially, hydration heat is a main cause of thermal cracking at mass concrete structures. The thermal cracking of massive structure is analyzed of the thermal cracking index which was presented Concrete Standard Specifications. The thesis analyzed the thermal cracking index which considered various variable (cement type, height of casting, curing condition, concrete mixing temperature, the unit cement content) at internal restricted mass concrete. The analysis result is denoted increase and decrease rate of thermal cracking index whenever the variables change. The results is helped to understand thermal cracking every time structures is designed and constructed. And I think that it is useful economic and stable design of mass concrete structures.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.969-972
• /
• 2008

This study investigated the effect of the fundamental condition such as release agent, form conditions and types to the surface of concrete with aluminum form on the various temperatures. On the observation with the naked eyes, coated plywood and aluminum form without a scratch showed similar result, and the surface quality of the concrete with aluminum form was gradually decreased corresponding to the increase of the temperature.For the surface roughness, there is no remarkable tendency according to the temperature. However, the difference in accordance with release agent occurred.As void on the surface corresponding to the various temperature, the micro voids ranged $0.1{\sim}1mm$ were increased corresponding to the increasing temperature, so it was confirmed that the chemical reaction wae accelerated. And the voids of the other range also increased. the fundamental condition such as release agent, form conditions and types

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.487-494
• /
• 2011

In this research, the possibility of using bottom ash as a binder for the alkali-activated cement mortar is studied. Several experiments were performed to investigate the variation of the material properties according to the mix proportion. In the experimental program, the flowability and compressive strength were evaluated for various values of water/ash ratio, activator/ash ratio, sodium silicate to sodium hydroxide ratio, curing temperature, and the fineness of bottom ash as the main variables. The experimental results showed that high strength of 40 MPa or greater could be achieved in $60^{\circ}C$ high temperature curing condition with proper flowability. For $20^{\circ}C$ ambient temperature curing, the 28 days compressive strength of approximately 30MPa could be obtained although the early-age strength development was very slow. Based on the results, the range of optimized mix design of bottom-ash based alkali-activated cement mortar was suggested. In addition, using the artificial neural network analysis, the flowability and compressive strength were predicted with the difference in the mix proportion of the bottom-ash based alkali-activated cement mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.3
• /
• pp.102-109
• /
• 2011

In this study, in order to develop ultra rapid hardening mortar(URHM) for tunnel repairs using bottom ash of low recycle ratio and Admixture as Eco concept, watertightness and durability properties of URHM on temperature condition of construction field were performed. Test result, seepage quantity and water absorption coefficient regarding watertightness of URHM were as in the following : series II > series I. Seepage quantity for the standard condition were smaller than low temperatures. all specimens were satisfied below 20g as standards of seepage quantity on KS F 4042. Because of the decrease of unit cement content by to replacement of blast furnace slag, the neutrlization resistance for durability properties was reduced. The result of alkali resistance and acide resistance, compressive strengths for specimens soaked in calcium hydroxide solution of seriesI were lower than compressive strengths for specimens not soaked. On the other hand, the case of series II show that the deterioration of compressive strengths for specimens was not almost showed. Compressive strengths of specimens soaked were similar with specimens not soaked except series II-C in $5^{\circ}C$. Therefore, specimens using both blast furnace slag and bottom ash were good in alkali resistance and acide resistance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.4
• /
• pp.114-121
• /
• 2010

Portland cement production is under critical review due to high amount of CO2 gas released to the atmosphere. Attempts to increase the utilization of a by-products such as fly ash and ground granulated blast-furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. However, most study deal only with alkali-activated ground granulated blast furnace slag or fly ash, as for the combined use of the both, little information is reported. In this study, we investigated the influence of mixture ratio of fly ash/ blast furnace slag tand curing condition on the flowability and compressive strength of mortar in oder to develop cementless alkali-activated concrete. In view of the results, we found out that the mixture ratio of fly ash/blast furnace slag always results to be significant factors. But the influence of curing temperature in the strength development of mortar is lower than the contribution due to other factors. At the age of 28days, the mixture 50% fly ash and 50% ground granulated blast furnace slag activated with 1:1 the mass ratio of 9M NaOH and sodium silicate, develop compressive strength of about 65 MPa under $20^{\circ}C$ curing.

• Resources Recycling
• /
• v.19 no.4
• /
• pp.19-28
• /
• 2010

Attempts to increase the utilization of a by-products such as fly ash and blast furnace slag to partially replace the cement in concrete are gathering momentum. But most of by-products is currently dumped in landfills, thus creating a threat to the environment. Many researches on alkali-activated concrete that does not need the presence of cement as a binder have been carried out recently. However, most study deal only with alkali-activated blast furnace slag or fly ash, as for the combined use of the both, little information is reported. In this study, we investigated the influence of mixture ratio of fly ash/slag, type of alkaline activator and curing condition on the workability and compressive strength of mortar in oder to develop cementless alkali-activated concrete. In view of the results, we found out that the mixture ratio of fly ash/slag and the type of alkaline activator always results to be significant factors. But the influence of curing temperature in the strength development of mortar is lower than the contribution due to other factors. At the age of 28days, the mixture 50% fly ash and 50% slag activated with 1:1 the mass ratio of 9M NaOH and sodium silicate, develop compressive strength of about 65 MPa under $20^{\circ}C$ curing.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.203-210
• /
• 2018

Corrosion of the rebar is one of the main factors affecting the durability of reinforced concrete in the world which lead to the failure of the reinforced concrete structures. In this research, a new method of fixing $CO_2$ is practiced to improve the carbonation resistance of the concrete. Brucite($Mg(OH)_2$), a kind of common $CO_2$ fixation materials, was added into ordinary Portland cement paste. Samples containing 0%, 5%, 10%, and 15% $Mg(OH)_2$ were exposed to an accelerated carbonation curing regime with 20% concentration of $CO_2$, 60% relative humidity, and a temperature of $20^{\circ}C$ until tested at 3d, 7d, 14d and 28d. After 28d of $CO_2$ accelerated curing, in the paste containing $Mg(OH)_2$, magnesian calcite was detected by SEM-EDX. Meanwhile, the paste containing $Mg(OH)_2$ exhibit the better pore distribution than ordinary Portland cement paste and the compressive strength of the cement paste containing $Mg(OH)_2$ were more than 50Mpa.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.14 no.1
• /
• pp.156-164
• /
• 2010

A total of 6 stepwise constructions were made for building the floating mass concrete foundation. The optimal curing strategies and specialized construction guidelines were adoptively extracted from the 1.5m cube mock-up test prior to the main concrete work. Two different thermal crack index(TCI) calculations from current construction manual exhibit relatively low values as comparing the measured temperature data. This implies that the hydration-induced cracking could be developed in parts of concrete mass. However, the controversial phenomenons in reality were observed. No significant surface cracks are detected at the successive construction stages. Thereby, this paper raises the question regarding on the existence of characteristic length with varying size and shape of a target specimen which are missing in the current construction manual. The isothermal core area and high thermal gradient area in the edge volume should be identified and be introduced to TCI calculation for the purpose of an accuracy.